A comparison of wrought and powder metallurgical FeCrAl claddings under simulated LWR accident transients

Iron-chromium-aluminum (FeCrAl) alloys are potential accident tolerant fuel (ATF) cladding candidates for light-water reactors but are difficult to fabricate as thin-walled tubes via conventional cast-and-wrought routes. Powder metallurgy (PM) offers a manufacturing alternative with improved compositional control, but its transient accident performance has not been directly benchmarked against wrought variants. This study evaluates the burst behavior of commercially developed PM-processed FeCrAl alloys, PM-C26M (Fe-12Cr-6Al-2Mo) and the high precipitate density FA-SMT (Fe-22Cr-5Al-3Mo), under simulated light-water reactor accident transient conditions. Burst testing was conducted using the Severe Accident Test Station with heating rates of 5 °C/s and 50 °C/s and internal pressures ranging from 25 MPa to 100 MPa. PM-C26M reproduced wrought C26M burst behavior within 7–37 °C across the stress range, indicating that PM processing does not compromise transient strength. FA-SMT exhibited markedly higher burst temperatures and reduced heating-rate sensitivity, consistent with its engineered precipitate strengthening. FA-SMT rupture exhibited axial "unzipping" rather than the lateral tearing characteristic of PM- and wrought C26M. Post-test EBSD and fractography indicate that this behavior is strongly correlated with strain-gated intergranular void nucleation associated with the dense precipitate architecture of FA-SMT, a response absent in the comparatively clean PM-C26M matrix and consistent with rupture morphologies reported for oxide-dispersion strengthened (ODS) FeCrAl of similar base-matrix chemistry to PM-C26M. These findings highlight the potential of powder metallurgy as a viable fabrication route for ATF claddings from an accident performance standpoint.

Bell, Sam [ORNL] (ORCID:0000000251905657)↗
DOE OSTI2020

Synergy of Ion Doping and Spiral Array Architecture on Ti 2 Nb 10 O 29 : A New Way to Achieve High-Power Electrodes

Ameliorating electronic/ionic transport and structural stability of electrode materials is important to the development of power-intensive lithium ion batteries. Despite its great potential as a high-power anode, titanium niobium oxide (Ti 2 Nb 10 O 29 , TNO) still underperforms due to its unsatisfactory electronic/ionic conductivity. In this work, a powerful synergistic strategy by combining ion doping and spiral array architecture to boost high-rate performance of TNO is reported. Cr 3+ doped TNO nanoparticles (Cr-TNO) of 5-10 nm intimately grow on a conductive vertical graphene@TiC-C (VGTC) skeleton, forming novel Cr-TNO@VGTC spiral arrays. The unique spiral growth of TNO is achieved due to the confinement effect of VGTC skeleton. Meanwhile, a more open TNO crystal structure with faster ion transfer paths and enhanced structural stability is realized by Cr 3+ doping, demonstrated via density functional theory calculation and in situ synchrotron X-ray diffraction technique. Benefiting from the superior conductive network, enhanced intrinsic electronic/ionic conductivity of Cr-TNO and reinforced structural stability, the Cr-TNO@VTC arrays show prominent high-power performance with a large capacity of 220 mAh g -1 at 40 C (power density of ≈11 kW kg -1 ) and superior durability (91% retention after 500 cycles). This work provides a new path for the construction of widespread high-power electrodes for fast energy storage.

36 MATERIALS SCIENCE↗
DOE OSTI2026

Electric field dependence of nanoscale cathodoluminescence inside Cr doped β-Ga 2 O 3 interfaces

Chromium (Cr) is a common impurity in β-Ga 2 O 3 crystals, where its characteristic R1 and R2 luminescence lines are susceptible to both the host crystal field and externally applied fields. Here, in this work, we demonstrate that the Cr cathodoluminescence (CL) quenches toward the bulk of the crystal but enhances with applied reverse bias, reflecting the effect of free carrier depletion with increasing electric field. Furthermore, we illustrate that the R1/R2 CL intensity ratio, measured as the integrated area ratio of R1 to R2, can be used as a direct probe of the electric field in a Ni-β-Ga 2 O 3 : Cr Schottky diode. This optical calibration method provides a complementary approach to conventional C–V and I–V measurements for determining electric field strength in the depletion region of β-Ga 2 O 3 -based Schottky diodes and can be extended to other semiconductors and multilayer device structures.

36 MATERIALS SCIENCE↗
DOE OSTI2024

Corrosion of Zinc Cold Spray Coatings in a Wet Sweet and Sour Gas Environment

Internal corrosion is a problem for steel pipelines transporting natural gas or CO 2 containing water and partial pressures of H 2 S higher than 0.3 kPa (0.05 psi). This work aims to mitigate internal corrosion in steel pipelines transporting natural gas containing H 2 S using cold spray coatings. Two types of the cold spray binary metallic coatings (zinc chromium [ZnCr]. zinc niobium [ZnNb]) were studied using electrochemical techniques: potentiodynamic polarization, linear polarization resistance, and electrochemical impedance spectroscopy. The corrosion resistance of cold spray coatings (ZnCr, ZnNb) was evaluated in an environment containing 4 bar CO 2 pressure, simulating the partial pressures found in gas transmission lines over a solution of 3.5 wt% NaCl heated to 40°C. A concentration of 0.003 M Na 2 S 2 O 3 ·5H 2 O, corresponding to H 2 S partial pressures around 0.079 bar (1.146 psi), was used to simulate sour conditions. Postcorrosion surface characterization was performed using a scanning electron microscope (SEM) equipped with an energy-dispersive x-ray spectroscope (EDS) and x-ray diffraction analysis. The data showed that the presence of 0.003 M Na 2 S 2 O 3 ·5H 2 O shifted the corrosion potential to more anodic values and decreased the corrosion current density. Both coatings showed similar behavior after 1 h of exposure in the CO 2 /H 2 S environment, indicating that similar electrochemical reactions were occurring on ZnNb and ZnCr. SEM images and EDS surface analyses for specimens showed a significant change in the surface chemical composition of carbon steel coated with ZnNb and ZnCr after 24 h of immersion. In the presence of thiosulfate (under sour conditions), the formation of corrosion product layers (ZnCO 3 and ZnS) on top of ZnNb and ZnCr coatings increased their corrosion resistance, which helped to reduce their corrosion by a factor of 2. Under a sweet environment, the corrosion rates for steel coated with cold spray coatings after 14 d of exposure are lower than that for galvanized steel by a factor of 5 due to the ZnCO 3 layer formed on top of the coatings. The ZnCO 3 layer formed on the steel surface acts as a physical barrier against corrosion by blocking the diffusion of corrosive species to the surface. No localized attack was observed. ZnCr Cold spray coating with defect showed promising corrosion protection against CO 2 corrosion (sweet corrosion) after 14 d of exposure to a CO 2 environment. Here, the scratch on the coating simulated damage created in service, and it was deep enough to expose the substrate material (steel). The formation of zinc oxide (ZnO) and zinc carbonate (ZnCO 3 ) on the scratch confirmed the cathodic protection of the steel by ZnCr and ZnNb coatings.

36 MATERIALS SCIENCE↗