FY24 Progress Report: Disposition of Cracks & Features Observed in the Inner Can Closure Weld Region (ICCWR) of the 3013 Package
The long-term integrity of the 3013 containers is of interest for the safe storage of Pu materials. Although the 3013 standard embodies multiple barrier concept, the integrity of the inner container is considered to be crucial since it protects the Safety Class outer container from its contents. The container is designed to withstand high pressures that could result from the complete radiolysis of the maximum water content permissible by the 3013 standard. Shelf-life studies and destructive examination have not found high gas pressures but have found that corrosive gases are generated. Pitting and stress corrosion cracking (SCC) are considered to be critical corrosion modes for the performance of the inner container and have been observed during destructive examinations. Considerable research has been conducted on the possibility of aqueous electrolytes condensing on the inner container that can promote SCC. These studies indicate the uncertainties surrounding the formation of corrosive environments and the corrosion behavior of container materials. In this initial report, a Bayesian network (BN) model is described that can consider the uncertainties and the causal connections between various factors influencing the corrosion modes of the inner container. The BN model is preliminary and provides an initial framework to identify the necessary information. The report also provides initial experimental results on the electrochemical behavior of stainless steels in anticipated condensed environments from gas phase migration of acidic gases. The experimental results are consistent with the corrosion model. Recommendation for further work on the BN model include assembling an expert group to provide input to the BN structure and quantification of the conditional probability matrix, experimental studies to characterize the microstructure of the container, electrochemical studies to identify critical potentials for localized corrosion and SCC, and crack growth rate studies