NASA NTRS1986

Thermal cyclic durability testing of ceramic materials for turbine engines

The thermal cyclic durability of commercial ceramic materials for turbine engines was under evaluation since 1978. Ceramic materials are exposed to cyclic diesel-fired burner exhaust at either 1204 or 1371 C (2200 or 2500 F) for up to 3500 hours. The test conditions are selected to simulate the environment experienced by the hot flow path components in an automotive gas turbine engine. The silicon nitride and silicon carbide materials tested are the same ceramic materials currently used on the AGT100 and AGT101 ceramic turbine engine program.

Lindberg, L. J.↗
NASA NTRS1996

Durability Testing of Commercial Ceramic Materials

Technical efforts by AlliedSignal Engines in DOE/NASA-funded project from February, 1978 through December, 1995 are reported in the fields ceramic materials for gas turbine engines and cyclic thermal durability testing. A total of 29 materials were evaluated in 40 cyclic oxidation exposure durability tests. Ceramic test bars were cyclically thermally exposed to a hot combustion environment at temperatures up to 1371 C (2500 F) for periods of up to 3500 hours, simulating conditions typically encountered by hot flowpath components in an automotive gas turbine engine. Before and after exposure, quarter-point flexure strength tests were performed on the specimens, and fractography examinations including scanning electron microscopy (SEM) were performed to determine failure origins.

Schienle, J. L.↗
DOE OSTI2026

Mechanism, Thermochemistry, and Kinetics for the CH + N 2 Reaction Leading to Prompt NO Formation in Combustion

Here, the reaction of CH + N 2 forming H + NCN is a remarkable example of activation of the nitrogen triple bond and is an important source of prompt NO in combustion. The reaction pathway is complex and proceeds through two competing mechanisms: a cyclic addition channel initiated by c-HC(NN) and a chain-addition channel initiated by HCNN, both of which eventually form HNCN prior to dissociation to H + NCN. This work reinvestigates this reaction with composite coupled cluster protocols, including a novel spin-flip equation of motion coupled cluster scheme, combined with pragmatic two-dimensional master equation simulations of the resulting rate coefficients. These improved calculations predict the CH + N 2 rate coefficient between the two more recent previous theoretical results and reduce the uncertainties of the best theoretical models of this reaction to less than a factor of 1.3. Additionally, we provide a closer theoretical investigation of the simultaneous dependence of the CH + N 2 rate coefficient on pressure and temperature, and affirm that collisionally stabilized HNCN, another potential source of prompt NO, emerges as an appreciable product of this reaction under conditions relevant to automotive internal combustion engines and aircraft gas turbine engines.

Nguyen, Thanh Lam [Univ. of Florida, Gainesville, ↗
NASA NTRS1973

Effect of timed secondary-air injection on automotive emissions

A single cylinder of an automotive V-8 engine was fitted with an electronically timed system for the pulsed injection of secondary air. A straight-tube exhaust minimized any mixing other than that produced by secondary-air pulsing. The device was operated over a range of engine loads and speeds. Effects attributable to secondary-air pulsing were found, but emission levels were generally no better than using the engine's own injection system. Under nontypical fast-idle, no-load conditions, emission levels were reduced by roughly a factor of 2.

Coffin, K. P.↗
NASA NTRS1974

Analytical description of the modern steam automobile

The sensitivity of operating conditions upon performance of the modern steam automobile is discussed. The word modern has been used in the title to indicate that emphasis is upon miles per gallon rather than theoretical thermal efficiency. This has been accomplished by combining classical power analysis with the ideal Pressure-Volume diagram. Several parameters are derived which characterize performance capability of the modern steam car. The report illustrates that performance is dictated by the characteristics of the working medium, and the supply temperature. Performance is nearly independent of pressures above 800 psia. Analysis techniques were developed specifically for reciprocating steam engines suitable for automotive application. Specific performance charts have been constructed on the basis of water as a working medium. The conclusions and data interpretation are therefore limited within this scope.

Peoples, J. A.↗
NASA NTRS1976

Strainrange partitioning behavior of an automotive turbine alloy

This report addresses Strainrange Partitioning, an advanced life prediction analysis procedure, as applied to CA-101 (cast IN 792 + Hf), an alloy proposed for turbine disks in automotive gas turbine engines. The methodology was successful in predicting specimen life under thermal-mechanical cycling, to within a factor of + or - 2.

Annis, C. G.↗
NASA NTRS1977

Emissions and performance of catalysts for gas turbine catalytic combustors

Three noble-metal monolithic catalysts were tested in a 12-centimeter diameter combustion test rig to obtain emissions and performance data at conditions simulating the operation of a catalytic combustor for an automotive gas turbine engine. Tests with one of the catalysts at 800 K inlet mixture temperature 300,000 pa (3 atm) pressure, and a reference velocity (catalyst bed inlet velocity) of 10 m/sec demonstrated greater than 99 percent combustion efficiency for reaction temperatures higher than 1300 K. With a reference velocity of 25 m/sec the reaction temperature required to achieve the same combustion efficiency increased to 1380 K. The exit temperature pattern factors for all three catalysts were below 0.1 when adiabatic reaction temperatures were higher than 1400 K. The highest pressure drop was 4.5 percent at 25 m/sec reference velocity. Nitrogen oxides emissions were less than 0.1 g NO2/kg fuel for all test conditions.

Anderson, D. N.↗
NASA NTRS1977

Air cooling of disk of a solid integrally cast turbine rotor for an automotive gas turbine

A thermal analysis is made of surface cooling of a solid, integrally cast turbine rotor disk for an automotive gas turbine engine. Air purge and impingement cooling schemes are considered and compared with an uncooled reference case. Substantial reductions in blade temperature are predicted with each of the cooling schemes studied. It is shown that air cooling can result in a substantial gain in the stress-rupture life of the blade. Alternatively, increases in the turbine inlet temperature are possible.

Gladden, H. J.↗
NASA NTRS1977

Emissions and performance of catalysts for gas turbine catalytic combustors

Three noble-metal monolithic catalysts were tested in a 12-cm-dia. combustion test rig to obtain emissions and performance data at conditions simulating the operation of a catalytic combustor for an automotive gas turbine engine. Tests with one of the catalysts at 800 K inlet mixture temperature, 3 x 10 to the 5th Pa pressure, and a reference velocity (catalyst bed inlet velocity) of 10 m/sec demonstrated greater than 99 percent combustion efficiency for reaction temperatures higher than 1300 K. With a reference velocity of 25 m/sec the reaction temperature required to achieve the same combustion-efficiency increased to 1380 K. The exit temperature pattern factors for all three catalysts were below 0.1 when adiabatic reaction temperatures were higher than 1400 K. The highest pressure drop was 4.5 percent at 25 m/sec reference velocity. Nitrogen oxides emissions were less than 0.1 g NO2/kg fuel for all test conditions.

Anderson, D. N.↗
NASA NTRS1978

Evaluation of advanced regenerator systems

The major considerations are discussed which will affect the selection of a ceramic regenerative heat exchanger for an improved 100 HP automotive gas turbine engine. The regenerator considered for this application is about 36cm in diameter. Regenerator comparisons are made on the basis of material, method of fabrication, cost, and performance. A regenerator inlet temperature of 1000 C is assumed for performance comparisons, and laboratory test results are discussed for material comparisons at 1100 and 1200 C. Engine test results using the Ford 707 industrial gas turbine engine are also discussed.

Cook, J. A.↗
NASA NTRS1978

Development of surface coatings for air-lubricated, compliant journal bearings to 650 C

Surface coatings for an air-lubricated, compliant journal for an automotive gas turbine engine were tested to find those capable of withstanding temperatures of either 540 C (1000 F) or 650 C (1200 F). Also, the coatings have to be capable of surviving the start-stop sliding contact cycles prior to rotor lift-off and at touchdown. Selected coating combinations were tested in start-stop tests at 14 kPa (2 psi) loading for 2000 cycles at room and maximum temperatures. Specific coating recommendations are: Cdo and graphite on foil versus chrome carbide on journal up to 370 C (700 F); NASA PS-120 (Tribaloy 400, silver, and CaF2) on journal versus uncoated foil up to 540 C (1000 F); and chemically adherent Cr2O3 on journal and foil up to 650 C (1200 F). The chemically adherent Cr2O3 coating system was further tested successfully at 35 kPa (5 psi) loading for 2000 start-stop cycles.

Bhushan, B.↗
NASA NTRS1978

Static evaluation of surface coatings for compliant gas bearings in an oxidizing atmosphere to 650 C

Hard wear-resistant coatings and soft low shear strength coatings were developed for an air-lubricated compliant journal bearing for a future automotive gas turbine engine. The coatings were expected to function in either 540 or 650 C ambient. Soft lubricant coatings were generally limited in temperature. Therefore emphasis was on the hard wear-resistant coatings. The coating materials covered were TiC, B4C, Cr3C2, WC, SiC, CrB2, TiB2, Cr2O3, Al2O3, Si3N4, Tribaloy 800, CaF2, CaF2-BaF2 eutectic, Ni-Co, silver, CdO-graphite and proprietary compounds. The coatings on test coupons were subjected to static oven screening tests. The test consisted of exposure of material samples in an oven for 300 h at the maximum temperature (540 or 650 C) and ten temperature cycles from room temperature to the maximum service temperature. On the basis of the specimen examinations the following coatings were recommended for future wear tests: TiC (sputtered), Cr2O3 (sputtered), Si3N4 (sputtered), CdO and graphite (fused), Kaman DES (a proprietary coating), CrB2 (plasma sprayed), Cr3C2 (detonation gun) and NASA PS-106 (plasma sprayed).

Bhushan, B.↗
NASA NTRS1980

Evaluation of a high performance fixed-ratio traction drive

The results of a test program to evaluate a compact, high performance, fixed ratio traction drive are presented. This transmission, the Nasvytis Multiroller Traction Drive, is a fixed ratio, single stage planetary with two rows of stepped planet rollers. Two versions of the drive were parametrically tested back-to-back at speeds to 73,000 rpm and power levels to 180 kW (240 hp). Parametric tests were also conducted with the Nasvytis drive retrofitted to an automotive gas turbine engine. The drives exhibited good performance, with a nominal peak efficiency of 94 to 96 percent and a maximum speed loss due to creep of approximately 3.5 percent.

Loewenthal, S. H.↗
NASA NTRS1980

Evaluation of a high performance fixed-ratio traction drive

The results of a test program to evaluate a compact, high performance, fixed-ratio traction drive are presented. This transmission, the Nasvytis Multiroller Traction Drive, is a fixed-ratio, single-stage planetary with two rows of stepped planet-rollers. Two versions of the drive were parametrically tested back-to-back at speeds to 73,000 rpm and power levels to 180 kW (240 hp). Parametric tests were also conducted with the Nasvytis drive retrofitted to an automotive gas turbine engine. The drives exhibited good performance, with a nominal peak efficiency of 94 to 96 percent and a maximum speed loss due to creep of approximately 3.5 percent.

Loewenthal, S. H.↗
NASA NTRS1980

Improved ceramic heat exchanger materials

The development and evaluation of materials for potential application as heat exchanger structures in automotive gas turbine engines is discussed. Test specimens in the form of small monolithic bars were evaluated for thermal expansion and dimensional stability before and after exposure to sea salt and sulfuric acid, followed by short and long term cycling at temperatures up to 1200 C. The material finally selected, GE-7808, consists of the oxides, ZrO2-MgO-Al2O3-S1O2, and is described generically as ZrMAS. The original version was based on a commercially available cordierite (MAS) frit. However, a clay/talc mixture was demonstrated to be a satisfactory very low cost source of the cordierite (MAS) phase. Several full size honeycomb regenerator cores, about 10.2 cm thick and 55 cm diameter were fabricated from both the frit and mineral versions of GE-7808. The honeycomb cells in these cores had rectangular dimensions of about 0.5 mm x 2.5 mm and a wall thickness of approximately 0.2 mm. The test data show that GE-7808 is significantly more stable at 1100 C in the presence of sodium than the aluminosilicate reference materials. In addition, thermal exposure up to 1100 C, with and without sodium present, results in essentially no change in thermal expansion of GE-7808.

Rauch, H. W.↗
NASA NTRS1981

Ultra-lean combustion at high inlet temperatures

Combustion at inlet air temperatures of 1100 to 1250 K was studied for application to advanced automotive gas turbine engines. Combustion was initiated by the hot environment, and therefore no external ignition source was used. Combustion was stabilized without a flameholder. The tests were performed in a 12 cm diameter test section at a pressure of 2.5 x 10 to the 5th power Pa, with reference velocities of 32 to 60 m/sec and at maximum combustion temperatures of 1350 to 1850 K. Number 2 diesel fuel was injected by means of a multiple source fuel injector. Unburned hydrocarbons emissions were negligible for all test conditions. Nitrogen oxides emissions were less than 1.9 g NO2/kg fuel for combustion temperatures below 1680 K. Carbon monoxide emissions were less than 16 g CO/kg fuel for combustion temperatures greater than 1600 K, inlet air temperatures higher than 1150 K, and residence times greater than 4.3 microseconds.

Anderson, D. N.↗
NASA NTRS1979

Thermal energy storage for the Stirling engine powered automobile

A thermal energy storage (TES) system developed for use with the Stirling engine as an automotive power system has gravimetric and volumetric storage densities which are competitive with electric battery storage systems, meets all operational requirements for a practical vehicle, and can be packaged in compact sized automobiles with minimum impact on passenger and freight volume. The TES/Stirling system is the only storage approach for direct use of combustion heat from fuel sources not suitable for direct transport and use on the vehicle. The particular concept described is also useful for a dual mode TES/liquid fuel system in which the TES (recharged from an external energy source) is used for short duration trips (approximately 10 miles or less) and liquid fuel carried on board the vehicle used for long duration trips. The dual mode approach offers the potential of 50 percent savings in the consumption of premium liquid fuels for automotive propulsion in the United States.

Morgan, D. T.↗
NASA NTRS1981

Ultra-lean combustion at high inlet temperatures

Combustion at inlet-air temperatures of 1100 to 1250 K was studied for application to advanced automotive gas turbine engines. Combustion was initiated by the hot environment, and therefore no external ignition source was used. Combustion was stabilized without a flameholder. The tests were performed in a 12-cm-diameter test section at a pressure of 250,000 Pa, with reference velocities of 32 to 60 m/s and at maximum combustion temperatures of 1350 to 1850 K. Number 2 diesel fuel was injected by means of a multiple-source fuel injector. Unburned hydrocarbon emissions were negligible for all test conditions. Nitrogen oxide emissions were less than 1.9 g NO2/kg fuel for combustion temperatures below 1680 K. Carbon monoxide emissions were less than 16 g CO/kg fuel for combustion temperatures greater than 1600 K, inlet-air temperatures higher than 1150 K, and residence times greater than 4.3 ms.

Anderson, D. N.↗