Results for “Coating degradation” — Page 12

NASA NTRS1994

Results of the examination of LDEF polyurethane thermal control coatings

This report summarizes the condition of polyurethane thermal control coatings subjected to 69 months of low earth orbit (LEO) exposure on the Long Duration Exposure Facility (LDEF) mission. Specimens representing all environmental aspects obtainable by LDEF were analyzed. Widely varying changes in the thermo-optical and mechanical properties of these materials were observed, depending on atomic oxygen and ultraviolet radiation fluences. High atomic oxygen fluences, regardless of ultraviolet radiation exposure levels, resulted in near original optical properties for these coatings but with a degradation in their mechanical condition. A trend in solar absorptance increase with ultraviolet radiation fluence was observed. Contamination, though observed, exhibited minimal effects.

Golden, Johnny L.↗

NASA NTRS2011

Conformal Thin Film Packaging for SiC Sensor Circuits in Harsh Environments

In this investigation sputtered silicon carbide annealed at 300 C for one hour is used as a conformal thin film package. A RF magnetron sputterer was used to deposit 500 nm silicon carbide films on gold metal structures on alumina wafers. To determine the reliability and resistance to immersion in harsh environments, samples were submerged in gold etchant for 24 hours, in BOE for 24 hours, and in an O2 plasma etch for one hour. The adhesion strength of the thin film was measured by a pull test before and after the chemical immersion, which indicated that the film has an adhesion strength better than 10(exp 8) N/m2; this is similar to the adhesion of the gold layer to the alumina wafer. MIM capacitors are used to determine the dielectric constant, which is dependent on the SiC anneal temperature. Finally, to demonstrate that the SiC, conformal, thin film may be used to package RF circuits and sensors, an LC resonator circuit was fabricated and tested with and without the conformal SiC thin film packaging. The results indicate that the SiC coating adds no appreciable degradation to the circuits RF performance. Index Terms Sputter, silicon carbide, MIM capacitors, LC resonators, gold etchants, BOE, O2 plasma

Scardelletti, Maximilian C.↗

NASA NTRS2012

Mission Life Thermal Analysis and Environment Correlation for the Lunar Reconnaissance Orbiter

Standard thermal analysis practices include stacking worst-case conditions including environmental heat loads, thermo-optical properties and orbital beta angles. This results in the design being driven by a few bounding thermal cases, although those cases may only represent a very small portion of the actual mission life. The NASA Goddard Space Flight Center Thermal Branch developed a procedure to predict the flight temperatures over the entire mission life, assuming a known beta angle progression, variation in the thermal environment, and a degradation rate in the coatings. This was applied to the Global Precipitation Measurement core spacecraft. In order to assess the validity of this process, this work applies the similar process to the Lunar Reconnaissance Orbiter. A flight-correlated thermal model was exercised to give predictions of the thermal performance over the mission life. These results were then compared against flight data from the first two years of the spacecraft s use. This is used to validate the process and to suggest possible improvements for future analyses.

Garrison, Matthew B.↗

NASA NTRS2010

Launch Pad Coatings for Smart Corrosion Control

Corrosion is the degradation of a material as a result of its interaction with the environment. The environment at the KSC launch pads has been documented by ASM International (formerly American Society for Metals) as the most corrosive in the US. The 70 tons of highly corrosive hydrochloric acid that are generated by the solid rocket boosters during a launch exacerbate the corrosiveness of the environment at the pads. Numerous failures at the pads are caused by the pitting of stainless steels, rebar corrosion, and the degradation of concrete. Corrosion control of launch pad structures relies on the use of coatings selected from the qualified products list (QPL) of the NASA Standard 5008A for Protective Coating of Carbon Steel, Stainless Steel, and Aluminum on Launch Structures, Facilities, and Ground Support Equipment. This standard was developed to establish uniform engineering practices and methods and to ensure the inclusion of essential criteria in the coating of ground support equipment (GSE) and facilities used by or for NASA. This standard is applicable to GSE and facilities that support space vehicle or payload programs or projects and to critical facilities at all NASA locations worldwide. Environmental regulation changes have dramatically reduced the production, handling, use, and availability of conventional protective coatings for application to KSC launch structures and ground support equipment. Current attrition rate of qualified KSC coatings will drastically limit the number of commercial off the shelf (COTS) products available for the Constellation Program (CxP) ground operations (GO). CxP GO identified corrosion detection and control technologies as a critical, initial capability technology need for ground processing of Ares I and Ares V to meet Constellation Architecture Requirements Document (CARD) CxP 70000 operability requirements for reduced ground processing complexity, streamlined integrated testing, and operations phase affordability. Researchers at NASA's Corrosion Technology Laboratory at KSC are developing a smart, environmentally friendly coating system for early corrosion detection, inhibition, and self healing of mechanical damage without external intervention. This smart coating will detect and respond actively to corrosion and mechanical damage such as abrasion and scratches, in a functional and predictable manner, and will be capable of adapting its properties dynamically. This coating is being developed using corrosion sensitive microcapsules that deliver the contents of their core (corrosion inhibiting compounds, corrosion indicators, and self healing agents) on demand when corrosion or mechanical damage to the coating occurs.

Calle, Luz M.↗

NASA NTRSDate not supplied

Thermochemistry of Aerospace Materials

The reliability and development of aerospace materials in extreme environments relies on a comprehensive understanding of their thermochemical properties. Such properties are commonly used for equilibrium phase stability calculations of interactions with corrosive environments at very high temperatures. These calculations can lead to in-depth understanding of degradation mechanisms in both coatings and components for applications such as nuclear thermal propulsion and gas turbine engines, both of which are part of NASA’s current R&D focus for improving propulsion systems for aerospace missions. The first part of this talk summarizes and discuss our current thermochemical calculations of the behavior of ceramic-ceramic (cercer) UN-based fuels and their coating systems during nuclear thermal rocket operation. The second part of the talk summarizes and discuss the energetics of reactions of ceramic coating materials and their binary oxide components with silicate melts measured by high temperature reaction calorimetry.

Nuclear Thermal propulsion↗

NASA NTRSDate not supplied

Actively Controlled Louver for Human Spacecraft Radiator Ultraviolet (UV), Dust, and Freeze Protection

This paper examines the use of actively controlled louvers to attenuate UV and dust, as well as mitigate freezing concerns for human spacecraft radiators during Artemis missions. Artemis missions to the lunar orbit or surface will expose the radiators to high energy UV radiation and dust, which will degrade the radiator’s coating emissivity and consequently reduce heat rejection performance. In addition, subfreezing environmental temperatures during transit to lunar orbit and nighttime on lunar south pole can rupture coolant tubes, reduce heat rejection performance, and worst-case scenario result in a Loss of Mission (LOM). Louver technology would be a promising solution to maintaining radiator performance and integrity for Artemis missions, but heritage louvers are passively controlled. This technology needs maturing to active control, or motor actuation, to achieve faster thermal response times. Actively controlled louver design considerations are discussed in this paper. The analysis that follows shows actively controlled louvers can attenuate high energy UV radiation and dust, as well as protect the coolant from freezing.

Louver↗

NASA NTRS2023

Actively Controlled Louver for Human Spacecraft Radiator Ultraviolet (UV), Dust, and Freeze Protection

This paper examines the use of actively controlled louvers to attenuate UV and dust, as well as mitigate freezing concerns for human spacecraft radiators during Artemis missions. Artemis missions to the lunar orbit or surface will expose the radiators to high energy UV radiation and dust, which will degrade the radiator’s coating emissivity and consequently reduce heat rejection performance. In addition, subfreezing environmental temperatures during transit to lunar orbit and nighttime on lunar south pole can rupture coolant tubes, reduce heat rejection performance, and worst-case scenario result in a Loss of Mission (LOM). Louver technology would be a promising solution to maintaining radiator performance and integrity for Artemis missions, but heritage louvers are passively controlled. This technology needs maturing to active control, or motor actuation, to achieve faster thermal response times. Actively controlled louver design considerations are discussed in this paper. The analysis that follows shows actively controlled louvers can attenuate high energy UV radiation and dust, as well as protect the coolant from freezing.

Louver↗

NASA NTRS2008

The Effect of Simulated Lunar Dust on the Absorptivity, Emissivity, and Operating Temperature on AZ-93 and Ag/FEP Thermal Control Surfaces

JSC-1AF lunar simulant has been applied to AZ-93 and AgFEP thermal control surfaces on aluminum or composite substrates in a simulated lunar environment. The temperature of these surfaces was monitored as they were heated with a solar simulator and cooled in a 30 K coldbox. Thermal modeling was used to determine the absorptivity ( ) and emissivity ( ) of the thermal control surfaces in both their clean and dusted states. Then, a known amount of power was applied to the samples while in the coldbox and the steady state temperatures measured. It was found that even a submonolayer of simulated lunar dust can significantly degrade the performance of both white paint and second-surface mirror type thermal control surfaces under these conditions. Contrary to earlier studies, dust was found to affect as well as . Dust lowered the emissivity by as much as 16 percent in the case of AZ-93, and raised it by as much as 11 percent in the case of AgFEP. The degradation of thermal control surface by dust as measured by / rose linearly regardless of the thermal control coating or substrate, and extrapolated to degradation by a factor 3 at full coverage by dust. Submonolayer coatings of dust were found to not significantly change the steady state temperature at which a shadowed thermal control surface will radiate.

Gaier, James R.↗

NASA NTRS1982

Alumina fiber strength improvement

The effective fiber strength of alumina fibers in an aluminum composite was increased to 173,000 psi. A high temperature heat treatment, combined with a glassy carbon surface coating, was used to prevent degradation and improve fiber tensile strength. Attempts to achieve chemical strengthening of the alumina fiber by chromium oxide and boron oxide coatings proved unsuccessful. A major problem encountered on the program was the low and inconsistent strength of the Dupont Fiber FP used for the investigation.

Pepper, R. T.↗

NASA NTRS1979

Silicon Halide-alkali Metal Flames as a Source of Solar Grade Silicon

A program is presented which was aimed at determining the feasibility of using high temperature reactions of alkali metals and silicon halides to produce low cost solar-grade silicon. Experiments are being conducted to evaluate product separation and collection processes, measure heat release parameters for scaling purposes, and determine the effects of the reactants and/or products on materials of reactor construction. During the current reporting period, the results of heat release experiments were used to design and construct a new type of thick-wall graphite reactor to produce larger quantities of silicon. A reactor test facility was constructed. Material compatibility tests were performed for Na in contact with graphite and several coated graphites. All samples were rapidly degraded at T = 1200K, while samples retained structural strength at 1700K. Pyrolytic graphite coatings cracked and separated from substances in all cases.

Olson, D. B.↗

NASA NTRS1984

Mechanical property measurements of plasma-sprayed thermal-barrier coatings subjected to oxidation

Techniques have been developed for measuring the tensile properties of plasma-sprayed coatings which are used in thermal barrier applications. The measurements have included the average Young's modulus, bond strength and elongation at failure. The oxidation behavior of the bond coat plays an important role in the integrity and adhesion of plasma-sprayed thermal barrier coatings. This work studies the nature of the high temperature degradation on the mechanical properties of the coating. Furnace tests have been carried out on U-700 alloy with bond coats of NiCrAlY or NiCrAlZr and an overlay of ZrO2-8 percent Y2O3. Weight gain measurements on the coatings have been examined with relation to the adhesion strength and failure observations. The results from an initial study are reported in this work.

Berndt, C. C.↗

NASA NTRS1995

Some aspects of the hot corrosion of thermal barrier coatings

This paper provides a pro tem review of the hot corrosion of zirconia-based thermal barrier coatings for engine applications. Emphasis is placed on trying to understand the chemical reactions, and such other mechanisms as can be identified, that cause corrosive degradation of the thermal barrier coating. The various approaches taken in attempts to improve the hot corrosion resistance of thermal barrier coatings are also briefly described and critiqued.

Jones, R. L.↗

NASA NTRS1995

Some aspects of the hot corrosion of thermal barrier coatings

This paper provides a pro tem review of the hot corrosion of zirconia-based thermal barrier coatings for engine applications. Emphasis is placed on trying to understand the chemical reactions, and such other mechanisms as can be identified, that cause corrosive degradation of the thermal barrier coating. The various approaches taken in attempts to improve the hot corrosion resistance of thermal barrier coatings are also briefly described and critiqued.

Jones, Robert L.↗

NASA NTRS2007

Post Irradiation Evaluation of Thermal Control Coatings and Solid Lubricants to Support Fission Surface Power Systems

The development of a nuclear power system for space missions, such as the Jupiter Icy Moons Orbiter or a lunar outpost, requires substantially more compact reactor design than conventional terrestrial systems. In order to minimize shielding requirements and hence system weight, the radiation tolerance of component materials within the power conversion and heat rejection systems must be defined. Two classes of coatings, thermal control paints and solid lubricants, were identified as material systems for which limited radiation hardness information was available. Screening studies were designed to explore candidate coatings under a predominately fast neutron spectrum. The Ohio State Research Reactor Facility staff performed irradiation in a well characterized, mixed energy spectrum and performed post irradiation analysis of representative coatings for thermal control and solid lubricant applications. Thermal control paints were evaluated for 1 MeV equivalent fluences from 10(exp 13) to 10(exp 15) n per square centimeters. No optical degradation was noted although some adhesive degradation was found at higher fluence levels. Solid lubricant coatings were evaluated for 1 MeV equivalent fluences from 10(exp 15) to 10(exp 16) n per square centimeters with coating adhesion and flexibility used for post irradiation evaluation screening. The exposures studied did not lead to obvious property degradation indicating the coatings would have survived the radiation environment for the previously proposed Jupiter mission. The results are also applicable to space power development programs such as fission surface power for future lunar and Mars missions.

Bowman, Cheryl L.↗

NASA NTRSDate not supplied

A Dynamic Testing Approach for Particulate Erosion–Corrosion for Gas Turbine Coatings

Particle interactions in gas turbine engines can be multicomponent, complex phenomena leading to the degradation of thermal (TBCs) and environmental barrier coatings (EBCs) meant to protect engine components. Ingestion of particles into the engine can lead to recession of coatings due to particle erosion. Similarly, these same particles can become molten, adhere to coatings and result in thermochemical corrosion of coating materials. Particle erosion testing is often carried out where the particles are injected into a gas stream, accelerated within a nozzle, and impinge on sample. Conversely, most molten particle corrosion testing is often done in static laboratory furnaces, which does not capture the dynamic nature of deposition in application. Nevertheless, these damage mechanisms are often tested separately and no single standard exists to test both erosive and corrosive particle interactions with coating materials under relevant operating conditions for gas turbine engines. Understanding the synergies of particle interactions in engines is crucial in determining operating lifetimes of potential coating materials. Such considerations emphasize the need for realistic approaches in standardizing particle interaction testing in combustion environments. The current study outlines initial efforts at NASA Glenn’s Erosion Burner Rig Facility in improving dynamic erosion/corrosion testing methods by assessing the durability of state-of-the-art (SOA) TBC material 7 wt.% yttria stabilized zirconia (7YSZ) as a function of particle deposition rate, burner temperature, and particle size. Calibration data to determine particle deposition rate will be presented, and mass and optical profilometry measurements were utilized to estimate mass/volume loss versus deposition per increment of particulate used over time. Electron microscopy analyses were then carried out to assess coating damage after testing.

TBC↗

NASA NTRSDate not supplied

A Dynamic Testing Approach for Particulate Erosion–Corrosion for Gas Turbine Coatings

Particle interactions in gas turbine engines can be multicomponent, complex phenomena leading to the degradation of thermal (TBCs) and environmental barrier coatings (EBCs) meant to protect engine components. Ingestion of particles into the engine can lead to recession of coatings due to particle erosion. Similarly, these same particles can become molten, adhere to coatings and result in thermochemical corrosion of coating materials. Particle erosion testing is often carried out where the particles are injected into a gas stream, accelerated within a nozzle, and impinge on sample. Conversely, most molten particle corrosion testing is often done in static laboratory furnaces, which does not capture the dynamic nature of deposition in application. Nevertheless, these damage mechanisms are often tested separately and no single standard exists to test both erosive and corrosive particle interactions with coating materials under relevant operating conditions for gas turbine engines. Understanding the synergies of particle interactions in engines is crucial in determining operating lifetimes of potential coating materials. Such considerations emphasize the need for realistic approaches in standardizing particle interaction testing in combustion environments. The current study outlines initial efforts at NASA Glenn’s Erosion Burner Rig Facility in improving dynamic erosion/corrosion testing methods by assessing the durability of state-of-the-art (SOA) TBC material 7 wt.% yttria stabilized zirconia (7YSZ) as a function of particle deposition rate, burner temperature, and particle size. Calibration data to determine particle deposition rate will be presented, and mass and optical profilometry measurements were utilized to estimate mass/volume loss versus deposition per increment of particulate used over time. Electron microscopy analyses were then carried out to assess coating damage after testing.

TBC↗

NASA NTRSDate not supplied

A Dynamic Testing Approach for Particulate Erosion–Corrosion for Gas Turbine Coatings

Particle interactions in gas turbine engines can be multicomponent, complex phenomena leading to the degradation of thermal (TBCs) and environmental barrier coatings (EBCs) meant to protect engine components. Ingestion of particles into the engine can lead to recession of coatings due to particle erosion. Similarly, these same particles can become molten, adhere to coatings and result in thermochemical corrosion of coating materials. Particle erosion testing is often carried out where the particles are injected into a gas stream, accelerated within a nozzle, and impinge on sample. Conversely, most molten particle corrosion testing is often done in static laboratory furnaces, which does not capture the dynamic nature of deposition in application. Nevertheless, these damage mechanisms are often tested separately and no single standard exists to test both erosive and corrosive particle interactions with coating materials under relevant operating conditions for gas turbine engines. Understanding the synergies of particle interactions in engines is crucial in determining operating lifetimes of potential coating materials. Such considerations emphasize the need for realistic approaches in standardizing particle interaction testing in combustion environments. The current study outlines initial efforts at NASA Glenn’s Erosion Burner Rig Facility in improving dynamic erosion/corrosion testing methods by assessing the durability of state-of-the-art (SOA) TBC material 7 wt.% yttria stabilized zirconia (7YSZ) as a function of particle deposition rate, burner temperature, and particle size. Calibration data to determine particle deposition rate will be presented, and mass and optical profilometry measurements were utilized to estimate mass/volume loss versus deposition per increment of particulate used over time. Electron microscopy analyses were then carried out to assess coating damage after testing.

burner rig↗

NASA NTRS2016

Thermochemistry of CaO-MgO-Al2O3-SiO2 (CMAS) and Advanced Thermal and Environmental Barrier Coating Systems

CaO-MgO-Al2O3-SiO2 (CMAS) oxides are constituents in a broad number of materials and minerals which have recently inferred to discussions in materials science, planetary science, geochemistry and cosmochemistry communities. In materials science, there is increasing interest in the degradation studies of thermal (TBC) and environmental (EBC) barrier coatings of gas turbines by molten CMAS. These coatings have been explored to be applied on silicon-based ceramics and composites which are lighter and more temperature capable hot-section materials of gas turbines than the current Ni-based superalloys. The degradation of the coatings occurs when CMAS minerals carried by the intake air into gas turbines, e.g. in aircraft engines, reacts at high temperatures (1000C) with the coating materials. This causes premature failure of the static and rotating components of the turbine engines. We discuss some preliminary results of the reactions between CMAS and Rare-Earth (RE Y, Yb and Gd) oxide stabilized ZrO2 systems, and stability of the resulting oxides and silicates.

CaO-MgO-Al2O3-SiO2 (CMAS)↗