Results for “Li-ion Cell Performance” — Page 12

NASA NTRSDate not supplied

Solid-State Architecture Batteries for Enhanced Rechargeability and Safety (SABERS) Beyond Li-Ion: Technology to Enable Next-Generation Sustainable Electric

All-electric vertical take-off and landing vehicles (eVTOL) for urban air mobility (UAM) concepts face numerous challenging technical barriers before their introduction into the consumer marketplace. The primary barrier to overcome is developing an energy storage system that meets rigorous aerospace safety and performance criteria. The performance metrics for eVTOL vehicles are at least two times greater than those of electric ground vehicles. Furthermore, inherently non-flammable batteries are essential for the safe operation of commercial electric aero vehicles. The SABERS concept proposes a battery that meets the critical performance criteria by developing a solid-state architecture battery utilizing a high-capacity sulfur-selenium cathode and lithium metal anode. The combination of sulfur and selenium offers a balanced energy-to-power density ratio, which can be tailored to the specific application by altering the stoichiometric ratios of sulfur to selenium. This hybrid cathode will be developed using NASA-patented holey graphene technology as a highly conductive, ultra-lightweight electrode scaffold. A solid-state electrolyte will be used as a safe, non-flammable replacement for the highly flammable liquid organic electrolytes currently in SOA lithium-ion batteries. This solid-state lithium-sulfur/selenium cell will be designed in a serial stacking configuration to enable the dense packaging of the battery cells. The serial stacking configuration is termed a bipolar stack, which has the advantages of reducing overall cell weight, simplifying the interfaced connections for the cell, and minimizing the cooling requirements. Lastly, the optimization of battery components will occur through a robust and rigorous combination of various computational modeling techniques covering multiple length scales. The expected result will be a fully solid-state battery with operational temperatures up to 150°C, providing the required energy density, discharge rates, and inherent safety to meet the strict aerospace mission performance criteria. The SABERS team employed novel materials development, computational modeling, and design-of-experiments (DOE) optimization studies in their research. This presentation will show the results of these studies and demonstrate a feasible path for solid-state cells with a specific energy greater than 400 Wh/kg to enable electric aircraft.

Computational Modeling↗

DOE OSTI2026

Surface heterogeneity propagation and homogenization for pouch cell-scale Li metal anodes

Li metal anode is a promising candidate for next-generation energy storage systems and is widely explored in Li-ion and solid-state batteries. Despite its potential, Li metal anodes face instabilities during long-term cycling, especially when paired with NMC or sulfur-based cathodes, where Li is cycled at high capacities of 6-8 mAh/cm2, equivalent to a thickness of 30-40 µm. During such extensive utilization, degradation mechanisms such as excessive solid electrolyte interphase (SEI), dendrites, and dead Li emerge, and ultimately lead to sudden failure and reduced cycle life. The origin of the degradation mechanisms stem from surface heterogeneities introduced during Li foil manufacturing and storage [1, 2]. As cycling progresses, the local heterogeneities propagate, resulting in uneven Li utilization and degradation-prone regions across the electrode [3], which consequently induce performance variations at the cell level. This heterogeneity propagation is particularly pronounced in large-format pouch cells in practical applications, where the surface effects are magnified. Without a clear understanding of the multi-scale heterogeneities and the development of surface homogenization methods, the performance consistency will be compromised, hindering the commercialization of Li metal batteries. In this presentation, we investigate the evolution of surface heterogeneity propagation on commercially available Li foils. We discover that inhomogeneous Li utilization appears as early as the first half-cycle of formation, manifesting as localized clusters and pits. In pouch cell configurations, these features exhibit areal density variations across the electrode on a scale of millimeters. To improve Li utilization homogeneity, a scalable mechanical brushing method is introduced to remove the chemically heterogeneous surface passivation layer. Furtherore, the influence of utilization homogeneity on cell-to-cell consistency is evaluated using 32 Li-NMC811 pouch cells divided into as-received and brushed Li groups. On the brushed Li, clusters and pits are no longer observable, and the cells exhibit significantly improved consistency in discharge capacity trajectories and cycle lifetime. Overall, this study highlights the role of Li surface utilization homogeneity on long-term cycling performance. Our research provides a pathway for improving large-area electrode uniformity and establishing evaluation methods for cell-to-cell consistency, both are key steps toward the commercialization of Li metal batteries and beyond. [1] Otto, Svenja-K., et al. "In-depth characterization of lithium-metal surfaces with XPS and ToF-SIMS: toward better understanding of the passivation layer." Chemistry of Materials 33.3 (2021): 859-867. [2] Hatzell, Kelsey, et al. "Aligning lithium metal battery research and development across academia and industry." Joule (2024). [3] Kim, Sangwook, et al. "Calendar life of lithium metal batteries: Accelerated aging and failure analysis." Energy Storage Materials 65 (2024): 103147.

25 - ENERGY STORAGE↗