DOE OSTI2021

Clarification of creep deformation mechanism in heat-affected zone of 9Cr steels with In Situ experiments

This work quantified nonuniform creep deformation across the heterogeneous heat-affected zone (HAZ) of Grade 91 steel with sophisticated experiments, including an electric-thermal finite element model–assisted Gleeble thermomechanical simulation and a high-temperature creep testing with in situ digital image correlation (DIC). High temperature creep properties of HAZ sub-zones were quantitatively measured by the DIC. Furthermore, by utilizing peak temperature, hardness, local creep strain, and underlying microstructures, creep deformation mechanisms in HAZ were further understood. DIC measurements reveal a creep-vulnerable zone (CVZ) exposed to a peak temperature of 932°C (close to A C3 ) in the intercritical HAZ experienced the fastest creep strength degradation instead of the soft zone with the lowest hardness prior to creep. The significantly reduced precipitation strengthening from misplacement of undissolved and coarsened M 23 C 6 carbides led to a faster recrystallization of tempered martensite in the CVZ. Weak untransformed tempered martensite (ferrite grains) stabilized by local Cr enrichment from dissolved M 23 C 6 also harmed the CVZ's creep resistance.

36 MATERIALS SCIENCE↗
DOE OSTI2024

An Innovative Design of High-Temperature, Sensible Molten Salt Thermal Energy Storage Systems With Geopolymer Insulation

This project aims to mitigate the risks of the current molten salt TES tank designs. The goal is to create a more reliable and cost-effective TES by (1) developing a new material solution for internal thermal insulation and (2) by designing a concrete-based tank structure to eliminate metal-related issues (e.g., corrosion, thermomechanical failure, etc.). Firstly, the project aims to engineer a composite refractory insulation material that possesses sufficient thermal insulation properties without significantly sacrificing the resistance to salt permeation and mechanical strength, which is the major trade-off in traditional refractory insulation design. The primary objective is to perform materials design and optimization of the composite refractory to achieve the required thermal and mechanical properties as suitable internal insulation for molten salt TES. Secondly, the project aims to design a concrete-based TES system with conventional low- cost Portland cement serving as the primary tank structure and the aforementioned composite refractory as the internal thermal insulation and salt containment. The objective is to investigate the technical and economical feasibilities of concrete tanks for high- temperature molten salt storage applications.

14 SOLAR ENERGY↗
DOE OSTI2020

Report on partially complete post-irradiation-examination of the INL samples

Ferritic-martensitic steels (NF616 and T91), and austenitic stainless steel 800H and its Grain Boundary Engineering (GBE)-treated version 800H-TMP (ThermoMechanical Processing) were irradiated in the Advanced Test Reactor (ATR) at Idaho National Laboratory (INL) and their microstructures and mechanical properties were characterized. Ferritic-martensitic steels were irradiated up to 8.16 dpa in the irradiation temperatures ranging from 241 °C to 447.5 °C. Selected 800H and 800H-TMP samples were also irradiated up to 9.12 dpa at 359°C to 431°C. Vickers hardness measurement, fractography, and microstructural characterization were performed on the selected samples in the LAMDA lab. Radiation-induced hardening of NF616 and T91 was observed in the hardness measurements which show ~37% to ~65% increases, depending on irradiation dose and irradiation temperature. Within the irradiation conditions studied in this work, samples with a higher dose had a higher hardness. All the tested alloy 800H and 800H-TMP in this work showed irradiation-hardening by ~96±7% to ~152±10%. Alloy 800HTMP tended to have slightly smaller irradiation-hardening than alloy 800H. The fractography of NF616 samples D2 (2.96 dpa at 291.5°C), D4 (5.91 dpa at 359°C), and D6 (8.16 dpa at 431°C) indicated loss of ductility with negligible necking for the sample D2, yet obvious ductile failure for samples D4 and D6. Fractography of alloy 800H samples N4 (7.27 dpa at 359°C), N5 (3.9 dpa at 451.5°C), and N6 (9.01 dpa at 431°C), and alloy 800H-TMP samples P4 (7.36 dpa at 359°C), P5 (3.95 dpa at 451.5°C), and P6 (9.12 dpa at 431°C) indicated that all samples failed in a ductile mode, with obvious necking. Dimples were observed where large Ti-containing particles were observed for the samples. TEM characterization was performed on alloy 800H (N4, N5, N6) and 800H-TMP (P4, P5 and P6). Accumulation of M23C6 precipitates at grain boundaries was observed in all samples, and the presence of Ti(C,N) precipitates at grain boundaries and in the matrix was observed in alloy 800H-TMP. M23C6 precipitates were found to have the cube-on-cube orientation relationship with the matrix. In addition, nanoscale Si-rich clusters were observed in the matrix of all samples. Atom probe tomography was conducted on the same samples, and their results are being analyzed to be integrated with the TEM results for a confident description of the clustering behavior. Due to the low irradiation temperature (up to 451.5°C), dislocation loops formed in all samples, with the density and the average size of dislocation loops in the order of 1022 – 1023 m-3 and 11.7 – 15.9 nm, respectively. The loop densities in alloy 800H were higher than that in alloy 800H-TMP under the same irradiation conditions. Further systematic data analyses, together with some complementary experiments, will be pursued for these samples to foster peer-reviewed journal article publications.

21 SPECIFIC NUCLEAR REACTORS AND ASSOCIATED PLANTS↗
DOE OSTI2026

Formulation and Performance Evaluation of Epoxy Sealant Systems for Double-Shell Tank Bottom Refurbishment

The performance of epoxy sealants used in the refurbishment of double-shell tank (DST) systems requires balancing processability, thermomechanical stability, and adhesion to cementitious substrates. This study incorporates Heloxy 8 as a reactive diluent into Westlake 862 epoxy to tailor workability and cured-state properties. Rheological time-sweep analysis demonstrates that increasing the diluent content significantly reduces complex viscosity and extends workability, thereby improving pumpability and flow for large-area applications. However, the targeted 2-hour processing window is not fully achieved. Differential scanning calorimetry (DSC) confirms that all formulations cure at room temperature to glass transition temperatures ( T g ) at least 20 °C above the maximum DST operating temperature (27 °C), thereby ensuring service in the glassy regime. Dynamic mechanical analysis (DMA) reveals formulation-dependent reductions in tan delta and increases in storage modulus, indicating increasingly elastic and mechanically stable networks with diluent incorporation. Pull-off adhesion testing shows that modified formulations (70–90% Westlake epoxy) exhibit significantly higher adhesion strengths than the unmodified system. Grout cohesive failure indicates that interfacial bonding exceeds substrate strength. Collectively, these results demonstrate that controlled reactive diluent incorporation enables optimization of processing behavior, interfacial adhesion, and thermomechanical performance, supporting the suitability of the modified epoxy systems as durable sealant layers for cementitious barrier applications in hazardous waste containment infrastructure.

Differential scanning calorimetry↗
DOE OSTI2024

Thermo-mechanical behavior of hypoeutectic Ni-Y-Zr alloys

Microstructure refinement and optimized alloying can improve metallic alloy performance: stable nanocrystalline (NC) alloys with immiscible second phases, e.g., Cu-Ta, are stronger than unstable NC alloys and their coarse-grained (CG) counterparts, but higher melting point matrices are needed. Hypoeutectic, CG Ni-Y-Zr alloys were produced via arc-melting to explore their potential as high-performance materials. Microstructures were studied to determine phases present, local composition and length scales, while heat treatments allowed investigating microstructural stability. Alloys had a stable, hierarchical microstructure with ~250 nm ultrafine eutectic, ~10 µm dendritic arm spacing and ~1 mm grain size. Hardness and uniaxial compression tests revealed that mechanical properties of Ni-0.5Y-1.8Zr (in wt%) were comparable to Inconel 617 despite the small alloying additions, due to its hierarchical microstructure. Here, uniaxial compression at 600 °C showed that ternary alloys outperformed Ni-Zr and Ni-Y binary alloys in flow stress and hardening rates, which indicates that the Ni 17 Y 2 phase was an effective reinforcement for the eutectic, which supplemented the matrix hardening due to increased solubility of Zr. Results suggest that ternary Ni-Y-Zr alloys hold significant promise for high temperature applications.

36 MATERIALS SCIENCE↗
DOE OSTI2022

High-Fidelity Mock Development for the Insensitive High Explosive TATB

Due to the violent reaction potential of high explosives, in tests where a reaction is not desired, it can be safe and convenient to use an inert mock that can mimic relevant properties of the associated explosive. Use of mock materials is well-established in explosives work, but most existing mocks are generally meant to mimic only one or two properties of a given explosive, potentially failing to match the explosive in other critical ways. Recently, there has been interest in developing robust thermomechanical mocks for many common explosives. Here, eleven materials are systematically chosen and investigated as potential thermomechanical mocks for TATB, the explosive component of PBX 9502. DSC, nanoindentation, and compression testing are used to narrow down to most appropriate mocks and identify their advantages and limitations. Hardness and elastic modulus are reported for the first time for the molecular crystals iodoanthranilic acid, hexamine, melamine, and trithiolane dioxide, and the crystal structure is reported for the first time for the molecular crystals iodoanthranilic acid and iodosalicylic acid.

36 MATERIALS SCIENCE↗
DOE OSTI2022

Fundamental Investigations into the Properties and Performance of Advanced Materials

Intelligent engineering designs require an accurate understanding of material behavior, since any uncertainties or gaps in knowledge must be counterbalanced with heightened factors of safety, leading to overdesign. Therefore, building better structures and pushing the performance of new components requires an improved understanding of the thermomechanical response of advanced materials under service conditions. This dissertation provides fundamental investigations of several advanced materials: thermoset polymers, a common matrix material for fiber-reinforced composites and nanocomposites; aluminum alloy 7075-T6 (AA7075-T6), a high-performance aerospace material; and ceramic matrix composites (CMCs), an advanced composite for extreme-temperature applications. To understand matrix interactions with various interfaces and nanoinclusions at their fundamental scale, the properties of thermoset polymers are studied at the atomistic scale. An improved proximity-based molecular dynamics (MD) technique for modeling the crosslinking of thermoset polymers is carefully established, enabling realistic curing simulations through its ability to dynamically and probabilistically perform complex topology transformations. The proximity-based MD curing methodology is then used to explore damage initiation and the local anisotropic evolution of mechanical properties in thermoset polymers under uniaxial tension with an emphasis on changes in stiffness through a series of tensile loading, unloading, and reloading experiments. Aluminum alloys in aerospace applications often require a fatigue life of over 109 cycles, which is well over ii the number of cycles that can be practically tested using conventional fatigue testing equipment. In order to study these high-life regimes, a detailed ultrasonic cycle fatigue study is presented for AA7075-T6 under fully reversed tension-compression loading. The geometric sensitivity, frequency effects, size effects, surface roughness effects, and the corresponding failure mechanisms for ultrasonic fatigue across different fatigue regimes are investigated. Finally, because CMCs are utilized in extreme environments, oxidation plays an important role in their degradation. A multiphysics modeling methodology is thus developed to address the complex coupling between oxidation, mechanical stress, and oxygen diffusion in heterogeneous carbon fiber-reinforced CMC microstructures.

Schichtel, Jacob J.↗
DOE OSTI2023

Thermomechanical Cleave of Polycrystalline CdTe Solar Cells and its Applications: A Review

One of the primary research challenges for cadmium telluride (CdTe) solar cells is addressing its open‐circuit voltage ( V OC ) deficit. While theoretical studies and single crystal work show V OC > 1 V is possible, devices remain stubbornly low at ≈800–900 mV. As absorber opto‐electronic properties (e.g., hole density, carrier lifetime) are improved, device modeling suggests that interfaces become limiting. Because CdTe‐based devices are typically grown in the superstrate configuration, the back interface is relatively accessible for manipulation and study, while the front interface (i.e., the heterojunction region) is buried under microns of material and inaccessible. NREL has developed a novel technique to thermomechanically cleave polycrystalline CdTe device stacks directly at the front interface, enabling characterization and controlled manipulation of this important region. Herein, recent work, primarily from NREL, will be reviewed, including considerations for achieving successful delamination; key scientific discoveries about the front interface that have been enabled by this technique; and practical applications, such as flexible, low‐cost solar with high power‐to‐weight ratio.

14 SOLAR ENERGY↗
DOE OSTI2022

Stresses within rare-earth doped yttria-stabilized zirconia thermal barrier coatings from in-situ synchrotron X-ray diffraction at high temperatures

There is a growing interest for smart coatings that can be integrated into turbine engines for in-situ temperature measurements or health monitoring. The addition of rare-earth dopants into standard thermal barrier ceramic top coat materials is used to obtain luminescent coatings that enable spectral measurements, for real-time temperature or health monitoring. The thermomechanical performance and durability of such novel coating compositions in extreme environments still remains to be evaluated. Consequently, the ability to manufacture sensor coatings which present suitable thermal properties needs to be demonstrated. For this study, highly luminescent erbium and europium doped yttria-stabilized zirconia and state-of-the-art yttria-stabilized zirconia coatings manufactured by air plasma spray were characterized to determine the effects of the embedded rareearth dopants on coating internal strain and stress and to quantify and compare their high temperature response using synchrotron X-ray diffraction. In-situ depth-resolved strain measurements were performed at 15 μm intervals along the depth of the coatings to evaluate materials response at key locations, specifically at layer interfaces. In-plane stress was calculated for the coatings and a finite element model was implemented to supplement the results and enable further predictions. The results show that the sensor coatings that were manufactured in this work revealed only minor variations in the strain response of sensor coatings under a typical thermal cycle and especially at temperatures closer to that of gas turbine operating conditions, compared to state-of-the-art coatings. This work demonstrates the viability of manufacturing rare-earth doped yttria-stabilized zirconia coatings that provide beneficial spectroscopic monitoring capabilities while having minimal impact on the thermomechanical response of the thermal barrier coatings.

Air plasma spray↗
DOE OSTI2024

Finite element procedure for thermomechanical and structural integrity analysis of beam intercepting devices subjected to free electron laser

High-energy particles, including photons (x-ray, γ-ray, bremsstrahlung), electrons, and protons, possess the capability to penetrate materials and deposit energy within them. The degree of absorption depends on both the energy and type of particles, as well as the properties of the materials with which they interact. This energy deposition can manifest either at the material's surface or throughout its volume, potentially resulting in various failure modes. The primary aim of this paper is to establish a structured analysis methodology for evaluating the structural integrity of beam-intercepting devices when subjected to high-energy particles. Here, the paper also reviews some of the underlying physics, pertinent to the scope of the thermomechanical analysis, potential failure modes, and introduces verification and validation methodologies. Engineers and researchers can utilize the guidelines presented in this paper to effectively plan the development of beam intercepting devices, thereby ensuring their reliability and performance in the presence of high-energy particle exposure.

Finite element analysis↗
DOE OSTI2025

Recrystallization driven softening and heating rate dependencies of FeCrAl nuclear fuel cladding during accident transients

A refined understanding of FeCrAl cladding behavior during rapid transients is critical for its potential deployment in light-water reactors. Current assessments focus on transient burst testing metrics such as balloon geometry, burst temperature, and hoop stress, often used as proxies for simpler conventional tensile properties. However, directly correlating isothermal tensile and creep data with accident transient scenarios remains a challenge, although it is essential for high fidelity model development. Recent modeling based on tensile tests up to 800 °C, conducted with both immediate loading and a 10-minute soak, showed that immediate loading better predicts experimental burst temperatures, indicating a thermal softening effect. Building upon this observation, the current study connects transient performance, microstructural evolution, and high-temperature tensile properties by leveraging results from C26M claddings burst tests performed at heating rates of 1–50 °C/s and hoop stresses from 25 to 100 MPa. At 25 MPa, rupture temperatures varied by only 6 °C, but at 100 MPa, the difference reached 116 °C, with faster heating yielding higher burst temperatures. Microstructural analysis identified recrystallization as the primary cause of heating rate-dependent softening, eliminating prior cold-working. In-situ thermomechanical data linked ballooning onset to localized instabilities, similar to ultimate tensile strength behavior in conventional tensile tests. High heating rates correlated with immediate loading tensile data, while lower rates matched soaked data. Furthermore, by linking burst performance to microstructural evolution and tensile properties, this work provides a foundation for more accurate modeling of FeCrAl claddings and potentially other Fe-based materials under accident conditions.

11 - NUCLEAR FUEL CYCLE AND FUEL MATERIALS↗
DOE OSTI2021

Development of high B s Fe–Ni-based metal amorphous nanocomposite by optimization of glass-forming ability

Thermocalc simulations identified compositions with good glass-forming ability (GFA) by locating minima in liquidus temperature, and solidification range in (Fe 70 Ni 30 ) x (B-Si-Nb) 100-x alloys with x = 82% and x = 85%, increased compared to previously developed x = 80% alloys. 3 compositions in the x = 82% system and 1 in the x = 85% system were successfully cast as amorphous magnetic ribbon. Magnetic properties of as-cast alloys showed improvements in Curie temperature and saturation induction, especially for the 85% alloy. Crystallization behavior in the 85% alloy was determined to occur as a 2-step process. Annealing studies showed (Fe 70 Ni 30 ) 82 Nb 2 Si 0 B 16 and (Fe 70 Ni 30 ) 82 Nb 3 Si 0 B 15 alloys to exhibit low coercivity and high B s with annealing. TEM results show significant crystallization in as-cast ribbon. The (Fe 70 Ni 30 ) 85 Nb 0.5 Si 0 B 14.5 alloy as-cast has small, uniformly distributed grains, allowing a useful nanocrystalline alloy to be produced as cast. Lastly, the parameter ΔT xg , the temperature range in which the material can be thermomechanically processed, was in the range of 12–23 °C.

36 MATERIALS SCIENCE↗
DOE OSTI2023

Creep strength boosted by a high-density of stable nanoprecipitates in high-chromium steels

There is a need worldwide to develop materials for advanced power plants with steam temperatures of 700°C and above that will achieve long-term creep-rupture strength and low CO 2 emissions. The creep resistance of actual 9-12Cr steels is not enough to fulfil the engineering requirements above 600°C. In this paper, the authors report their advances in the improvement of creep properties of this type of steels by the microstructural optimization through nano-precipitation using two methodologies. 1) Applying a high temperature austenitization cycle followed by an ausforming step (thermomechanical treatment, TMT) to G91 steel, to increase the martensite dislocation density and, thus, the number density of MX precipitates (M = V,Nb; X = C,N) but at the expense of deteriorating the ductility. 2) Compositional adjustments, guided by computational thermodynamics, combined with a conventional heat treatment (no TMT), to design novel steels with a good ductility while still possessing a high number density of MX precipitates, similar to the one obtained after the TMT in G91. The microstructures have been characterized by optical, scanning and transmission electron microscopy, EBSD and atom probe tomography. The creep behaviour at 700°C has been evaluated under a load of 200 N using small punch creep tests.

36 MATERIALS SCIENCE↗
DOE OSTI2021

Robust, High-Performing Maize–Perovskite-Based Solar Cells with Improved Stability

Herein, we focus on improving the long-term chemical and thermomechan-ical stability of perovskite solar cells (PSCs), two major challenges currently limiting their commercial deployment. Our strategy incorporates a long-chain starch polymer into the perovskite precursor. The starch polymer confers multiple beneficial effects by forming hydrogen bonds with the methylammonium iodide precursor, templating perovskite growth that results in a compact and homogeneous film deposited in a simple one-step coating (antisolvent-free). The inclusion of starch in the methylammonium lead iodide films strongly improves their thermomechanical and environmental stability while maintaining a high photovoltaic performance. The fracture energy (G c ) of the film is increased to above 5 J/m 2 by creating a nanocomposite that provides intrinsic reinforcement at grain boundaries. Additionally, improved optoelectronic properties achieved with the starch polymer enable good photostability of the active layer and enhanced resistance to thermal cycling.

14 SOLAR ENERGY↗
DOE OSTI2020

Second Annual Progress Report on Correlation Between Microstructure and Mechanical Properties of Neutron-Irradiated Ferritic-Martensitic and Austenitic Steels

Ferritic-martensitic steels G92-2b (an optimized Grade 92 heat), NF616 and T91, and austenitic stainless steel 800H and its Grain Boundary Engineering (GBE)-treated version 800H-TMP (ThermoMechanical Processing) were irradiated in the High Flux Isotope Reactor (HFIR) of Oak Ridge National Laboratory (ORNL) and the Advanced Test Reactor (ATR) of Idaho National Laboratory (INL). Selected G92-2b samples were irradiated up to 14.66 dpa in the HFIR at two temperature ranges: 400–496.7°C and 683.3– 720°C. NF616 and T91 were irradiated in the ATR up to 8.16 dpa with the irradiation temperatures ranged from 241°C to 447.5°C. Alloy 800H and 800H-TMP samples were irradiated in both the HFIR and the ATR. Selected 800H and 800H-TMP samples had HFIR irradiation to 1.28 dpa at 580°C and ATR irradiation up to 9.12 dpa at 359°C to 431°C. Vickers hardness measurements, fractography, and microstructural characterization were performed on the selected samples in the Low Activation Materials Design and Analysis (LAMDA) laboratory. Radiation-hardening of G92-2b was observed at the lower doses and lower irradiation temperatures (400- 496.7°C), with GB03 (0.52 dpa at 400°C) and GB04 (7.44 dpa at ~490°C) showing ~12% and ~8% hardening, respectively. Softening by ~14% was observed for GB05 (14.66 dpa at 496.7°C). Radiationsoftening of G92-2b was more prevalent at the higher irradiation temperatures (683.3-~720°C), with GB10 (0.46 dpa at 683.3°C), GB11 (7.44 dpa at ~720°C), and GB12 (14.63 dpa at ~720°C) showing ~8%, ~8%, and ~40% softening, respectively. Radiation-hardening of NF616 and T91 was observed with the hardness increased by ~37% to ~65% depending on the irradiation doses and irradiation temperatures. Within the studied irradiation conditions of NF616 and T91, samples with a higher dose had a larger hardness after irradiation. All the tested alloy 800H and 800H-TMP samples in this work showed radiation-hardening by ~96±7% to ~152±10%. Alloy 800H-TMP tended to have slightly smaller radiation-hardening than alloy 800H. The fractography results of G92-2b sample GB03, GB10, and GB11, together with the previously characterized fractography of GB04, GB05, and GB12, indicated that the ductility of G92-2b was maintained up to 14.66 dpa at the lower irradiation temperatures of 400-496.7°C, while some loss of ductility (less necking) was observed for higher doses at the higher irradiation temperatures of 683.3-720°C. This agrees with the previously reported tensile test results of G92-2b, where the elongation of G92-2b was reduced at higher doses at the higher irradiation temperatures. Dimple sizes increased at higher doses, which are more evident at the higher irradiation temperatures of 683.3-~720°C. The fractography of NF616 sample D2 (2.96 dpa at 291.5°C), D4 (5.91 dpa at 359°C), and D6 (8.16 dpa at 431°C) indicated loss of ductility with negligible necking for sample D2, while ductile failure for samples D4 and D6. Fractography of alloy 800H and 800H-TMP samples in various irradiation conditions showed ductile failure with obvious necking. Dimples were observed, with some of them containing large Ti-rich particles, in all the 800H/800H-TMP samples. Electron backscatter diffraction characterization of GB12 indicated the recovery of the lath structure, which was generally replaced by an equiaxed grain structure. Transmission electron microscopy (TEM) characterization showed the presence of frequent M 23 C 6 (M = primarily Cr), MX (M = primarily V), spherical Nb(C,N) precipitates, and occasional Laves phase precipitates in the G92-2b samples. MX precipitates with sizes of 20-30 nm were observed at boundaries of smaller grains, indicating the pinning effect of the V-rich precipitates. The lath structure recovery was more evident at the higher irradiation temperatures (683.3-~720°C), with decreased densities of line dislocations and M23C6 precipitates. The irradiated T91 (TA04) showed the growth of M23C6 precipitates to 101 ± 40 nm from the initial 68 ± 22 nm in the unirradiated condition. Dislocation loops of both {100} and {111} types were present in TA04. TEM characterization was also performed on the irradiated 800H (N4, N5, N6, and AR2) and 800H-TMP (P4, P5, P6, and HG1). Accumulation of M 23 C 6 precipitates at grain boundaries was observed in all the xii 800H/800H-TMP samples, and the presence of Ti(C,N) precipitates at grain boundaries and in the matrix was observed in the irradiated 800H-TMP. Some Ti(C,N) precipitates are embedded in the M 23 C 6 precipitates, maintaining specific orientation relationships between the precipitates and between the precipitate and matrix. In addition, nanoscale Si-rich clusters were observed in the matrix of all the 800H/800H-TMP samples, with EDS Si maps tending to have a lower contrast in 800H-TMP samples. Atom probe tomography was conducted on the same samples, supported by a Rapid Turnaround Examination project under Nuclear Science User Facilities. The results are being analyzed to be integrated with the TEM results for a confident description of the γ’ precipitates. Dislocation loops also formed in all the 800H/800H-TMP samples. The density and the average size of dislocation loops were quantified to be in the order of 10 22 – 10 23 m -3 and 11.7 – 15.9 nm, respectively, in the ATR-irradiated 800H/800H-TMP samples. The loop densities in irradiated 800H were higher than that in irradiated 800H-TMP under the same irradiation conditions. Further systematic data analyses, together with some complementary experiments, will be pursued for these samples to foster peer-reviewed journal article publications.

36 MATERIALS SCIENCE↗
DOE OSTI2025

Characterization of Fuel-to-Coolant Heat Transfer During Reactivity-Initiated Accidents Using Tightly Coupled Thermal Hydraulics and Fuel Thermomechanics

The reactivity-initiated accident (RIA) is a complex scenario with several tightly interacting physical phenomena. Accurately predicting fuel behavior during these transients is difficult due to limitations in the modeling of fuel-to-coolant heat transfer. Common approaches to simulate RIAs involve standalone calculations using either a fuel performance code or a thermal-hydraulic code. The complex interdependencies of thermal-hydraulic and fuel mechanical behavior suggest that a tight coupling between these codes may provide more accurate predictions of fuel-to-coolant heat transfer and cladding mechanical response. Here, RELAP5-3D and BISON are coupled in this paper to simulate RIAs, and a sensitivity analysis is performed to rank key thermal properties and two-phase heat transfer parameters relevant for fuel-to-coolant heat transfer and cladding failure mechanisms in UO 2 –Zircaloy-4 systems. Gas gap conductance, film boiling heat transfer uncertainty, pulse width, fuel-specific heat capacity, and cladding-specific heat capacity were identified as important parameters. Variations in figures of merit resulting from changes to pulse width and the material thermal properties indicate that time-dependent heat transfer rates are significant for safety-relevant mechanical parameters due to the time dependence of cladding ductility and pellet-cladding mechanical interaction loading. The results suggest that the thermal-hydraulic factors have a nonnegligible influence on the thermomechanical solution and vice versa. Tight coupling of both sets of physics is recommended to improve prediction of fuel behavior during RIAs. Highlights include the following: 1. The RELAP5-3D thermal-hydraulic code and the BISON fuel performance code are tightly coupled for simulation of RIA transients with energy depositions at the Zircaloy-4 cladding failure threshold. 2. Departure from nucleate boiling occurred for all simulated cases. Due to the ductility of fresh fuel, substantial ballooning occurred in most cases. 3. Gas gap conductance, fuel-specific heat capacity, cladding-specific heat capacity, transient pulse width, and film boiling heat transfer were the dominant thermal factors impacting the safety figures of merit at energy depositions.

Critical Heat Flux (CHF)↗
DOE OSTI2021

Thermomechanical and sequential stress performance of photovoltaic backsheets

Photovoltaic backsheet technology is utilized to protect the interior components of solar modules from environmental stress as well as provide electrical insulation to the module. The growing demand for solar energy and longer module service life requirements have brought backsheet performance into focus. Despite being a protective packaging material, many backsheets have exhibited failure in the field, limiting the performance and service life of entire modules. Most backsheets consist of multiple polymeric layers laminated together using adhesives. A new backsheet, with a high performance polyamide structure, has been developed as the solution to module failure. Primarily, it contains a unique polyamide-ionomer alloy targeted at improved weather resistance. In this study, several photovoltaic industry standard backsheets, and the novel polyamide compositions of multilayered backsheets fabricated from the coextrusion process, were examined using thermomechanical analysis (TMA). The coefficient of thermal expansion (CTE) for entire backsheets and their constituent layers was used to model the thermomechanical behavior of various backsheet constructions. Subsequently, thermal cycling was performed in the TMA to examine the intrinsic thermal behavior of the backsheets. Thermal cycling in the TMA indicates the resilience and dimensional stability in the coextruded structures as opposed to the laminated structures. Lastly, results from a Module Accelerated Sequential Testing (MAST), are included to show the mechanical integrity of these backsheets after sequential exposure to stressors including damp heat, ultra-violet (UV) light radiation, and thermal cycling. The laminate backsheets deteriorated extensively after sequential exposure to these stressors, while the novel coextruded structures retained their physical properties.

14 SOLAR ENERGY↗
DOE OSTI2023

Decoupling the effects of texture and composition on magnetic properties of Fe-Si sheet processed by shear deformation

Soft magnetic Fe-Si alloys (electrical steels) possess exceptional functional properties such as high permeability, low coercivity, and low core loss, which generally improve with increasing Si content in the alloy. However, Fe-Si alloys containing > 3.5 wt% Si are also characterized by prohibitively low workability and poor ductility that have prevented their efficient commercial production in sheet form by rolling. This has limited their use for improving efficiency of motors and transformers. In this study, hybrid cutting-extrusion (HCE) is used as a single-step thermomechanical processing method to produce continuous Fe-Si alloy sheet with high Si compositions of 4 wt% to 6.5 wt%. HCE sheet is shown to have a homogeneous annealed grain structure and simple-shear crystallographic textures. By controlling the HCE deformation path, varied crystallographic shear textures are created in the sheet. Quasi-static magnetic properties of the HCE sheet are evaluated to decouple the effects of sheet texture and Si composition on resultant permeability and coercivity properties. The results suggest that HCE, with suitable process scaling, is a viable route for production of high-Si content electrical steel sheet for next-generation motors and transformers.

36 MATERIALS SCIENCE↗