Evaluating methods to reduce duration of near-threshold fatigue crack growth rate measurements for low-alloy steels in hydrogen gas
Measurement of the near-threshold fatigue crack growth rate (da/dN) vs. stress-intensity factor range (∆K) relationship in hydrogen gas is essential for maximizing the calculated design fatigue life of high-pressure hydrogen storage vessels. However, such measurements are rarely performed, since the low cyclic loading frequencies applied in standard practice lead to prohibitively protracted test durations. The objective of this study was to demonstrate two means for reducing test durations when measuring near-threshold da/dN vs. ΔK relationships under decreasing ΔK for low-alloy pressure vessel steels in hydrogen gas: 1) imposing steeper K-gradients relative to the recommended limits in standards such as ASTM E647, and 2) increasing cyclic loading frequency relative to typical values applied during fatigue crack growth testing of low-alloy steels in hydrogen gas. Recognizing that steeper K-gradients could amplify loading-history effects, test methods employing this approach were designed to mitigate such effects by either maintaining constant K max or gradually increasing the K-gradient as the threshold was approached. Although the varying K-gradient method was vulnerable to loading-history effects in the form of plasticity-induced crack closure, particularly at lower stress ratio (R) and higher starting K max values, these effects could be compensated by applying the adjusted compliance ratio (ACR) method. Here, it was demonstrated that steeper K-gradients in concert with increased cyclic loading frequency reduced the duration of near-threshold fatigue crack growth tests in hydrogen gas by more than 99% relative to standard practices.