Direct Air Capture Using Trapped Small Amines in Hierarchical Nanoporous Capsules on Porous Electrospun Fibers (Final Technical Report)
This report summarizes the carbon capture research and development conducted by The State University of New York at Buffalo (UB) and GTI Energy (GTI) for award “DE-FE0031969: Direct Air Capture Using Trapped Small Amines in Hierarchical Nanoporous Capsules on Porous Electrospun Fibers” sponsored by the U.S. Department of Energy (DOE). The objective of this project is to develop an innovative sorbent structure of trapped small amines in HNC embedded in PEF for DAC. This involves tailoring both sorbent and PEF materials to achieve a compact system for DAC with high capacity for CO 2 at concentrations typically available in air and at near ambient conditions. An innovative sorbent structure of trapped small amines in hierarchical nanoporous capsules (HNC) embedded in porous electrospun fibers (PEF) was developed for direct air capture (DAC). This involves tailoring both sorbent and PEF materials to achieve a compact system for DAC with high capacity for CO 2 at concentrations typically available in air and at near ambient conditions. An interfacial polymerization process was developed, which utilized loaded amines inside mesoporous silica and trimesoyl chloride (TMC) dissolved in organic solvents as the precursors, to generate a polyamide (PA) coating layer on mesoporous silica and thus trap amines. Reaction conditions, including TMC concentration, organic solvents, reaction time, etc., for interfacial polymerization were optimized to effectively trap loaded amines, and cyclic heating-cooling operation was conducted to evaluate the coating quality. Larger pore volume mesoporous silica was also synthesized to increase amine loading and thus increase CO 2 capacity. The optimized sorbent material exhibited CO 2 capacity as high as 4.88 mmol/g under humid DAC conditions and negligible loss (<1%) during 10 cyclic heating-cooling operations. The optimized PA-coated sorbent also showed fast adsorption and desorption kinetics, with <20% t1/2 increase compared to uncoated sorbent. PEF fabrication conditions, including organic solvents for dissolving core and shell polymers, voltage, distance from the nozzle to the collection panel, etc. were adjusted to better incorporate HNC. After incorporating the optimized sorbent material into PEF, the structured sorbent had a CO 2 capacity of approximately 4.0 mmol/g under humid DAC conditions, with capacity loss of 0.17% per cycle and t1/2 increase less than 10%. A techno-economic analysis (TEA) for the process design for a DAC system based on our developed sorbent structure of trapped small amines in HNC embedded in PEF was conducted. The process design included process description and major equipment sizing and energy and mass balances in addition to scale-up research results and estimated capture cost. Aspen Adsorption Simulator was used to fit the experimentally measured breakthrough curves and extract equilibrium and kinetic data of the optimized sorbent. Our results indicated that for a DAC plant with CO 2 productivity of 3,000 tonne/year, the levelized cost of CO 2 capture was $\$$612/tonne, with the largest contribution of 44.33% from the fixed operation cost. Increasing CO 2 productivity, while maintaining similar fixed operation cost, is expected to significantly reduce the CO 2 capture cost. A sensitivity study was also conducted to understand the influence of total plant cost, sorbent cost, CO 2 concentration in the feed, sorbent mat lifetime, sorbent regeneration electricity, and adsorption blower pressure drop on the levelized cost of CO 2 capture, revealing a capture cost range of $\$$520-870/tonne.