Electron microscopic, fractographic, and microprobe observations of crack initiation and propagation phenomena associated with stress corrosion of aluminum alloys
This experimental program was divided into two parts. The first part evaluated stress corrosion cracking in 2219-T87 aluminum and 5Al-2.5Sn (ELI) titanium alloy plate and weld metal. Both uniform height double cantilever beam and surface flawed specimens were tested in environments normally encountered during the fabrication and operation of pressure vessels in spacecraft and booster systems. The second part studied compatibility of material-environment combinations suitable for high energy upper stage propulsion systems. Surface flawed specimens having thicknesses representative of minimum gage fuel and oxidizer tanks were tested. Titanium alloys 5Al-2.5Sn (ELI), 6Al-4V annealed, and 6Al-4V STA were tested in both liquid and gaseous methane. Aluminum alloy 2219 in the T87 and T6E46 condition was tested in fluorine, a fluorine-oxygen mixture, and methane. Results were evaluated using modified linear elastic fracture mechanics parameters.
Vapor phase interaction of methanol and carbon tetrachloride with Ti thin films, discussing Ti stress corrosion cracking implications
This document sets forth the criteria to be used in the selection of materials for space vehicles and associated equipment and facilities so that failure resulting from stress corrosion will be prevented. The requirements established herein apply to all metallic components proposed for use in space vehicles and other flight hardware, ground support equipment, and facilities for testing. These requirements are applicable not only to items designed and fabricated by MSFC (Marshall Space Flight Center) and its prime contractors, but also to items supplied to the prime contractor by subcontractors and vendors.
An experimental fracture mechanics program was performed to determine the stress corrosion crack growth sensitivity of the propellant tank material, titanium alloy Ti-6Al-4V, for aerospace satellite applications involving long term exposure to Freon PCA and nitrogen tetroxide MON-1. Sustained load tests were made at a 49 C (120 F) constant temperature using thin gauge tensile test specimens containing semielliptical surface flaws. Test specimen types included parent metal, center of weld, and weld heat affected zone. It was concluded that Ti-6Al-4V alloy is not adversely affected in a stress environment when exposed to Freon PCA for 1000 hours followed by exposure to nitrogen tetroxide MON-1 for 2000 hours at stress levels up to 80% of the experimental critical plane strain stress intensity factor.
Examinations of the inside surface of irradiated fuel cladding from two reactors show the Zircaloy cladding is exposed to a number of aggressive substances, among them iodine, cadmium, and iron-contaminated cesium. Iodine-induced stress corrosion cracking (SCC) of well characterized samples of Zircaloy sheet and tubing was studied. Results indicate that a threshold stress must be exceeded for iodine SCC to occur. The existence of a threshold stress indicates that crack formation probably is the key step in iodine SCC. Investigation of the crack formation process showed that the cracks responsible for SCC failure nucleated at locations in the metal surface that contained higher than average concentrations of alloying elements and impurities. A four-stage model of iodine SCC is proposed based on the experimental results and the relevance of the observations to pellet cladding interaction failures is discussed.
Rigidly controlled shot peening retards the incompatibility between titanium alloys and nitrogen tetroxide in rocket-propellant storage tanks. This sets up a residual compressive stress in the surface of a material which reduces tensile stresses in the material fibers, alleviating stress corrosion.
The ambient and cryogenic temperature mechanical properties and the ambient temperature stress corrosion results of 18-3 Mn (Nitronic 33)stainless steel, longitudinal and transverse, as received and as welded (TIG) material specimens manufactured from 0.063 inch thick sheet material, were described. The tensile test results indicate an increase in ultimate tensile and yield strengths with decreasing temperature. The elongation remained fairly constant to -200 F, but below that temperature the elongation decreased to less than 6.0% at liquid hydrogen temperature. The notched tensile strength (NTS) for the parent metal increased with decreasing temperature to liquid nitrogen temperature. Below -320 F the NTS decreased rapidly. The notched/unnotched (N/U) tensile ratio of the parent material specimens remained above 0.9 from ambient to -200 F, and decreased to approximately 0.65 and 0.62, respectively, for the longitudinal and transverse directions at liquid hydrogen temperature. After 180 days of testing, only those specimens exposed to the salt spray indicated pitting and some degradation of mechanical properties.
Stress corrosion cracking of titanium alloys and aluminum alloys
Overaging during heat treatment of the aluminum alloys immediately followed by moderate plastic deformation, preferably by shock loading achieves near optimum values of both yield strength and resistance to stress corrosion. Similar results may be obtained by substituting a conventional deformation process for the shock loading step.
An investigation has been carried out to examine the relationship of the observed chemical and mechanical properties of Al-Cu and Al-Zn-Mg alloys to the stress corrosion mechanisms which dominate in each case. Two high purity alloys and analogous commercial alloys were selected. Fundamental differences between the behavior of Al-Cu and of Al-Zn-Mg alloys were observed. These differences in the corrosion behavior of the two types of alloys are augmented by substantial differences in their mechanical behavior. The relative cleavage energy of the grain boundaries is of particular importance.
Point defects were introduced into specimens of three heat-treated tempers of alloy 7075 by neutron irradiation. Continuous ultrasonic monitoring allowed crack growth to be observed. Effects on stress-corrosion susceptibility, elongation, hardness, and yield strength are noted and compared for the three tempers.
Measurements of electrical conductivity, ultrasonic surface wave attenuation, and internal friction loss were made on aluminum alloys 7079-T6, 2219-T31, and 2219-T81 as a function of the onset of stress corrosion.
Stress corrosion cracking behavior in titanium, molybdenum, and aluminum alloys, and electrochemical kinetic studies
Advanced testing of structural materials was developed by Lewis Research Center and Langley Research Center working with the American Society for Testing and Materials (ASTM). Under contract, Aluminum Company of America (Alcoa) conducted a study for evaluating stress corrosion cracking, and recommended the "breaking load" method which determines fracture strengths as well as measuring environmental degradation. Alcoa and Langley plan to submit the procedure to ASTM as a new testing method.
An investigation was conducted to determine the cause of the failure of a massive AISI Type 316 stainless steel valve which controlled combustion air to a jet engine test facility. Several through-the-wall cracks were present near welded joints in the valve skirt. The valve had been in outdoor service for 18 years. Samples were taken in the cracked regions for metallographic and chemical analyses. Insulating material and sources of water mist in the vicinity of the failed valve were analyzed for chlorides. A scanning electron microscope was used to determine whether foreign elements were present in a crack. On the basis of the information generated, the failure was characterized as external stress-corrosion cracking. The cracking resulted from a combination of residual tensile stress from welding and the presence of aqueous chlorides. Recommended countermeasures are included.
Fusion-welded austenitic stainless steel (ASS) was predominantly employed to manufacture dry storage canisters (DSCs) for the storage applications of spent nuclear fuel (SNF). However, the ASS weld joints are prone to chloride-induced stress corrosion cracking (CISCC), a critical safety issue in the nuclear industry. DSCs were exposed to a chloride-rich environment during storage, creating CISCC precursors. The CISCC failure leads to nuclear radiation leakage. Therefore, there is a critical need to enhance the CISCC resistance of DSC weld joints using promising repair techniques. This review article encapsulates the current state-of-the-art of peening techniques for mitigating the CISCC in DSCs. More specifically, conventional shot peening (CSP), ultrasonic impact peening (UIP), and laser shock peening (LSP) were elucidated with a focus on CISCC mitigation. The underlying mechanism of CISCC mitigation in each process was summarized. Finally, this review provides recent advances in surface modification techniques, repair techniques, and developments in welding techniques for CISCC mitigation in DSCs.
The sodium super-ionic conductor (NaSICON) has versatile applications as a ceramic electrolyte for energy storage, where it can serve as an impermeable separator in solid-state batteries and redox flow systems. In particular, NaSICON systems have been proposed to be relatively stable in contact with water, making them compatible with aqueous battery chemistries. However, owing to their brittle nature and metal oxide constituents, stress-corrosion cracking (SCC) is an important failure mechanism that has not been previously explored. In this study, we assess the fracture toughness of NaSICON membranes in contact with aqueous solutions that are relevant to redox flow systems. Microindentation was performed to generate visible surface cracks and residual stress, which were observed to grow in length after exposure to aqueous solutions. This allows for a quantitative measurement of fracture toughness, which decreases after exposure to water. To contextualize these results, we develop a simplified model of the fracture behavior in aqueous redox-flow batteries that incorporate NaSICON membranes, illustrating the importance of SCC in cell design. This work provides quantitative insights into SCC as a failure mode in NaSICON, enhancing our understanding of the chemo-mechanical behavior of ceramic electrolytes in contact with aqueous solutions.