The fabrication of full-size structural rings from composite materials is described. Results of glass/epoxy and graphite/epoxy hat stringer sections prepared by pultrusion are discussed.
A method is described for compression molding of thermosetting plastics composition. Heat is applied to the compressed load in a mold cavity and adjusted to hold molding temperature at the interface of the cavity surface and the compressed compound to produce a thermal front. This thermal front advances into the evacuated compound at mean right angles to the compression load and toward a thermal fence formed at the opposite surface of the compressed compound.
Following Fried, the statistics of images formed by an annular telescope aperture looking through the turbulent atmosphere are calculated; the deleterious effect of a central obscuration is much larger in the presence of seeing that for the telescope alone. A method of optimizing resolution through the atmosphere is explained in detail, with particular attention to the requirements for image-motion compensation; under ideal conditions, about a factor-of-four increase in effective resolution over conventional photography can be obtained. The effective resolution can be large or smaller than the 'seeing disk', depending on the recorded signal-to-noise ratio. Some common misconceptions about image structure and motion, and various unsound proposals for beating the seeing, are criticized.
Thermally and chemically stable polymers are needed for materials applications, particularly highly-stable elastomers for solid propellant binders where initial high temperature required for dissolving anhydride in polymer is deerimental. Solvent reactant system allows polymerization without condensation of products under low heat. Solvents utilized were dimethylacetamide, dimethyflormamide, etc.
Flame and temperature resistant polyimide foams are prepared by the reaction of an aromatic dianhydride, (pyromellitic dianhydride) with an aromatic polyisocyanate, (polymethylene polyphenylisocyanate), in the presence of an inorganic acid and furfuryl alcohol. Usable acids include dilute sulfuric acid, dilute nitric acid, hydrochloric acid, polyphosphoric acid, and phosphoric acid, with the latter being preferred. The dianhydride and the isocyanate in about equimolar proportions constitute about 50% of the reaction mixture, the rest being made up with the acid and the alcohol in a ratio of about 1:10. An exothermic reaction between the acid and the alcohol provides the heat necessary for the other components to polymerize without recourse to external heat sources. The mixture can be sprayed on any surface to form polymeric foam in locations where the application of heat is not practical or possible, for instance, between walls or on mine tunnel surfaces.
Sample titles of the space shuttle reusable surface insulation was subjected alternately to simulated mission heating and either real or simulated environmental exposure for up to 34 cycles. The coating cracked as a result of exposure to high temperature and moisture conditions, and insulation with cracked coatings absorbed significant quantities of water in the launch-pad environment. Cracking was a complex function of time, temperature, and moisture exposure. Cracked coatings remained adherent to the insulation for up to 24 cycles past initial cracking.
The thermal expansion and swelling of resin material as influenced by variations in temperature during moisture absorption is discussed. Comparison measurements using composites constructed of graphite fibers and each of two epoxy resin matrices are included. Polymer theory relative to these findings is discussed and modifications are proposed.
Classical laminate theory and a finite element model were used to predict stress states prior to the first formation of damage in laminates fabricated from T/300/5208. Crack patterns characteristic of the laminate in a wet or dry condition were also predicted using a shear lag model. Development of edge damage was recorded and observed during the test by transferring an image of the damage from the edge surface on to a thin acetate sheet such that the damage imprinted could be immediately viewed on a microfiche card reader. Moisture was shown to significantly alter the interior and edge dry stress states due to swelling and a reduction of elastic properties and to reduce the transverse strength in 90 deg plies. A model was developed in order to predict changes in first ply failure laminate loads due to differences in stacking sequence together with a wet or dry environmental condition.
New surface treatment is a rapid, convenient, and effective method for converting unused amines and amine functional groups into neutral, noncorrosive substituted urea. Reaction proceeds at room temperature, takes only a few minutes, and leaves no corrosive residue. Surface should first be washed with alcohol to remove as much as possible of unreacted amine. Then it should be dried, since residual moisture or alcohol may consume some of treatment reagent and neutralization may then be incomplete.
Copper lining helps to distribute heat under heating blanket. Bond during setup employs heating blanket over copper sheet within vacuum bag. Copper sheet smoothes out temperature distribution under hotspots in heater. Method applicable to uniformly heating such low-thermal-conductivity metals as titanium or stainless steel.
This investigation demonstrates how moisture absorbed in (0/+ or - 45/90)s and (0/90/+ or - 45)s graphite epoxy laminates significantly alters the stress state and chronology of damage development along the laminate edge during static tension and tension-tension cyclic loading. Emphasis is placed on using reasonable approximations for wet and dry elastic properties, including out-of-plane properties (nu sub 23 and G sub 23), since these properties are required by finite element and shear lag models to predict the stress state at the laminate edge. Moisture was observed to alter the dry edge stress state in the 90-deg plies of the (0/+ or - 45/90)s laminate such that delaminations occurred at a lower load and transverse cracks occurred at a higher load. A model was developed which predicted the differences in loads required to initiate damage in the 90-deg plies of the two laminates in the wet and dry conditions. Although moisture can alter the chronology of damage development, the damage state in each laminate observed prior to fracture appeared to be independent of moisture content.
The effects of prepreg water contamination on interlaminar shear strength, tranverse compressive strength, and longitudinal compressive strength were determined. Decreases in these properties due to water contamination were sugstantial: 28 percent for the interlaminar shear strength, 21 percent for the transverse compressive strength and 31 percent for the longitudinal compressive strength. Since voids were not detected by X-ray analysis, the most likely cause for these results is fiber-matrix debounding in the laminate.
Charge coupled devices (CCDs) have opened new horizons in the optical astronomy. Most of the presently existing astronomical CCD systems are oriented and designed primarily for work on faint objects. The use of CCDs for high precision work on bright objects remains to be explored. Issues and problems specific to (CCDs) are covered in detail. The important structural characteristics of CCDs are that they are integrating, self scanned, photon counting (one selection for each detected photon), solid state devices. The typical physical sizes are of the order of 1 - 3 cm, and typical raster formats of 500x500 pixels (TI), 320x512 (RCA), 385x576 (GEC), 800x800 (TI), and 1500x1500 (GEC) should be available soon. Typical (and optimal) operating temperatures are around -100 C, with liquid N2 as the most common coolant. Some CCDs are physically warped. This causes focus variations across the surface, which amount to a spatially variable PSF. Other relevant properties of CCDs as detectors and a comparison with some other astronomical detectors are given.
Amine terminated bisaspartimides are prepared by a Michael type reaction of an aromatic bismaleimide and an aromatic diamine in an aprotic solvent. These bisaspartimides are thermally polymerized to yield tough, resinous polymers crosslinked through -NH- groups. Such polymers are useful in applications requiring materials with resistance to change at elevated temperatures.
Studies were conducted to develop autoclave processing parameters for graphite reinforced PMR-2 resin composite materials intended for use in applications at temperatures up to 371 degrees (700 F). The effect of resin composition on autoclaveability was investigated. The effect of various graphite fibers and resin composition on 343 C (650 F) and 371 C (700 F) thermo-oxidative stability and mechanical properties was also investigated. The results of the processing studies show that PMR-2 resin composites can be easily fabricated under autoclave conditions. Autoclaved laminates exposed to 1 atm of air at 343 C (650 F) and 371 C (700 F) exhibited less than 5 percent weight loss after 750 hr exposure to 650 F air and 8 percent weight loss during exposure to 700 F air for 500 hr. After 500 hr exposure, autoclaved laminates exhibited greater than 90 percent retention of initial 650 and 700 F flexural and interlaminar shear strengths. The effect of resin formulated molecular weight and postcure conditions on laminate glass transition temperature is also discussed.
This paper describes the synthesis of maleimide terminated poly(ether ketones) using the solution imidization process described by Summers et al. (1987). Amorphous poly(arylene ether ketones), as well as poly(arylene ether sulfones, of controlled end group functionalities and molecular weights were synthesized by nucleophilic step polymerization of bisphehol-A phenolates with activated halides, such as 4,4'-difluorobenzophenone, and 'monofunctional' end cappers such as m-aminophenol. The thermal properties of the system included glass transition temperature (Tg) values of 160-170 C, with modulus above Tg proportional to cross-link density, which in turn was reciprocally related to oligomer molecular weight. The measurements of the fracture toughness values showed the materials to be very ductile, with the toughness increasing with oligomer molecular weight.
Studies were conducted to develop autoclave processing parameters for graphite reinforced PMR-2 resin composite materials intended for use in applications at temperatures up to 371 degrees (700 F). The effect of resin composition on autoclaveability was investigated. The effect of various graphite fibers and resin composition on 343 C (650 F) and 371 C (700 F) thermo-oxidative stability and mechanical properties was also investigated. The results of the processing studies show that PMR-2 resin composites can be easily fabricated under autoclave conditions. Autoclaved laminates exposed to 1 atm of air at 343 C (650 F) and 371 C (700 F) exhibited less than 5 percent weight loss after 750 hr exposure to 650 F air and 8 percent weight loss during exposure to 700 F air for 500 hr. After 500 hr exposure, autoclaved laminates exhibited greater than 90 percent retention of initial 650 and 700 F flexural and interlaminar shear strengths. The effect of resin formulated molecular weight and postcure conditions on laminate glass transition temperature is also discussed.
The development of a mass spectrometer/thermal analyzer/computer (MS/TA/Computer) system capable of providing simultaneous thermogravimetry (TG), differential thermal analysis (DTA), derivative thermogravimetry (DTG) and evolved gas detection and analysis (EGD and EGA) under both atmospheric and high pressure conditions is described. The combined system was used to study the thermal decomposition of the nozzle material that constitutes the throat of the solid rocket boosters (SRB).