NASA NTRS1972

Mach 1 oxidation of thoriated nickel chromium at 1204 C /2200 F/.

Electropolished and ground samples of TD-NiCr were exposed to a 1-atm, Mach 1 gas stream at 1204 C for times up to 50 hr. The samples were subjected to both cyclic and isothermal exposure. Weight change, metal loss, X-ray diffraction, metallographic, and electron microprobe analyses were performed. Neither surface preparation nor cyclic-against-isothermal-exposure conditions had a strong effect on the oxidation behavior of the alloy. Initially, a Cr2O3 layer was formed whose volatilization resulted in a very rapid loss of metal - more than 40 microns in the first hour. At about 1 hr, the Cr2O3 layer broke down and NiO began to cover the surface. By 5 hr, the NiO had covered the surface and the rate of loss slowed. The rate-controlling step was diffusion of Cr through NiO.

Lowell, C. E.↗
NASA NTRS1973

Development of high-emittance scales on thoriated nickel-chromium-aluminum-base alloys

The surface regions of a DSNiCrAl alloy have been doped, by a pack diffusion process, with small amounts of Mn, Fe, or Co, and the effect of these dopants on the total normal emissivity of the scales produced by subsequent high temperature oxidation has been measured. While all three elements lead to a modest increase in emissivity, (up to 23% greater than the undoped alloy) only the change caused by manganese is thermally stable. However, this increased emissivity is within 85 percent of that of TDNiCr oxidized to form a chromia scale. The maganese-doped alloy is some 50 percent weaker than undoped DSNiCrAl after the doping treatment, and approximately 30 percent weaker after oxidation.

Seltzer, M. S.↗
NASA NTRS1974

Properties of dispersion-strengthened chromium - 4-volume-percent-thoria alloys produced by ball milling in hydrogen iodide

The effects of processing variables on the tensile properties and ductile-to-brittle transition temperature (DBTT) of Cr + 4 vol. %ThO2 alloys and of pure Cr produced by ball milling in hydrogen iodide were investigated. Hot rolled Cr + ThO2 was stronger than either hot pressed Cr + ThO2 or pure Cr at temperatures up to 1537 C. Hot pressed Cr + ThO2 had a DBTT of 501 C as compared with minus 8 to 24 C for the hot rolled Cr + ThO2 and with 139 C for pure Cr. It is postulated that the dispersoid in the hot rolled alloys lowers the DBTT by inhibiting recovery and recrystallization of the strained structure.

Arias, A.↗
NASA NTRS1974

High-velocity-oxidation performance of metal-chromium-aluminum (MCrAl), cermet, and modified aluminide coatings on IN-100 and type VIA alloys at 1093 C

Cermet, MCrAl, and modified aluminide types of coatings applied to IN-100 and NASA-TRW-VIA alloy specimens were cyclically oxidation tested in a high velocity (Mach 1) gas flame at 1093 C. Several coating compositions of each type were evaluated for oxidation resistance. The modified aluminide coating, Pt-Al, applied to alloy 6A proved to be the best, providing oxidation protection to approximately 750 hours based on weight change measurements. The second best, a CoCrAlY coating applied to 6A, provided protection to 450 hours. The third best was a cermet + aluminide coating on 6A with a protection time to 385 hours.

Deadmore, D. L.↗
NASA NTRS1973

Thermogravimetric study of the reduction of oxides of nickel and chromium

The effectiveness of hydrogen, carbon and hydrogen-carbon in reducing NiO, Cr2O3, mixed NiO-Cr2O3 and oxidized Ni-20Cr was evaluated by thermogravimetry. NiO was effectively reduced by all three atmospheres, Cr2O3 only by hydrogen-carbon, NiO-Cr2O3 by hydrogen and hydrogen-carbon and oxidized Ni-20Cr by hydrogen, hydrogen-carbon and partially by carbon alone. The results indicate that nickel and carbon promote the reduction of Cr2O3.

Herbell, T. P.↗
NASA NTRS1975

Solid state welding processes for an oxide dispersion strengthened nickel-chromium-aluminum alloy

Solid-state welding processes were evaluated for joining TD-NiCrAl (Ni-16Cr-4Al-2ThO2) alloy sheet. Both hot-press and resistance spot welding techniques were successfully applied in terms of achieving grain growth across the bond line. Less success was achieved with a resistance seam welding process. In stress-rupture shear and tensile shear tests of lap joints at 1100 C, most failures occurred in the parent material, which indicates that the weld quality was good and that the welds were not a plane of weakness. The overall weld quality was not as good as previously attained with TD-NiCr, probably because the presence of alumina at the faying surfaces and the developmental TD-NiCrAl sheet, which was not of the quality of the TD-NiCr sheet in terms of surface flatness and dimensional control.

Moore, T. J.↗
NASA NTRS1975

Relation of structure to mechanical properties of thin thoria dispersion strengthened nickel-chromium (TD-NiCr alloy sheet

A study of the relation between structure and mechanical properties of thin TD-NiCr sheet indicated that the elevated temperature tensile, stress-rupture, and creep strength properties depend primarily on the grain aspect ratio and sheet thickness. In general, the strength properties increased with increasing grain aspect ratio and sheet thickness. Tensile testing revealed an absence of ductility at elevated temperatures. A threshold stress for creep appears to exist. Even small amounts of prior creep deformation at elevated temperatures can produce severe creep damage.

Whittenberger, J. D.↗
NASA NTRS1975

Several braze filler metals for joining an oxide-dispersion-strengthened nickel-chromium-aluminum alloy

An evaluation was made of five braze filler metals for joining an aluminum-containing oxide dispersion-strengthened (ODS) alloy, TD-NiCrAl. All five braze filler metals evaluated are considered suitable for joining TD-NiCrAl in terms of wettability and flow. Also, the braze alloys appear to be tolerant of slight variations in brazing procedures since joints prepared by three sources using three of the braze filler metals exhibited similar brazing characteristics and essentially equivalent 1100 C stress-rupture properties in a brazed butt-joint configuration. Recommendations are provided for brazing the aluminum-containing ODS alloys.

Gyorgak, C. A.↗
NASA NTRS1975

Deformation and annealing response of TD-nickel chromium

The recrystallization and grain growth processes occurring in TD-NiCr were examined with respect to deformation severity, annealing time, and temperature. Results indicated that two different annealing responses of TD-NiCr are possible, depending on the initial state and processing history prior to annealing. As-received sheet showed a dramatic increase in grain size with decreasing annealing temperature, whereas sheet prior-annealed at 1316 C for 1 hr exhibited very little variation with subsequent annealing temperature.

Kane, R. D.↗
NASA NTRS1976

Resistance of nickel-chromium-aluminum alloys to cyclic oxidation at 1100 C and 1200 C

Nickel-rich alloys in the Ni-Cr-Al system were evaluated for cyclic oxidation resistance in still air at 1,100 and 1,200 C. A first approximation oxidation attack parameter Ka was derived from specific weight change data involving both a scaling growth constant and a spalling constant. An estimating equation was derived with Ka as a function of the Cr and Al content by multiple linear regression and translated into countour ternary diagrams showing regions of minimum attack. An additional factor inferred from the regression analysis was that alloys melted in zirconia crucibles had significantly greater oxidation resistance than comparable alloys melted otherwise.

Barrett, C. A.↗
NASA NTRS1976

Creep deformation of TD-nickel chromium

An investigation was conducted of the mechanical behavioral characteristics of thoria-dispersed (TD) NiCr materials at elevated temperatures. The experimental procedure used is discussed along with the significance of the obtained results. Attention is given to basic creep behavior and creep thermal activation parameter measurements. It is found that the overall creep behavior of TD-NiCr can be explained on the basis of the relative contributions of two parallel-concurrent deformation mechanisms, including diffusion controlled grain boundary sliding and dislocation motion.

Kane, R. D.↗
NASA NTRS1975

Production of chromium base alloys by ball milling in hydrogen iodide

The effects of processing variables on the tensile properties and ductile-to-brittle transition temperature (DBTT) of Cr + 4 vol% ThO2 alloys and of pure Cr produced by ball milling in hydrogen iodide were investigated. Hot rolled Cr + ThO2 was stronger than either hot pressed Cr + ThO2 or pure Cr at temperatures up to 1540 C. Hot pressed Cr + ThO2 had a DBTT of 500 C as compared with -8 to 24 C for the hot rolled Cr + ThO2 and with 140 C for pure Cr. It is postulated that the dispersoid in the hot rolled alloys lowers the DBTT by inhibiting recovery and recrystallization of the strained structure.

Arias, A.↗