NASA NTRS2003

Environmentally Compatible Vapor-Phase Corrosion Inhibitor for Space Shuttle Hardware

USA-SRB Element is responsible for the assembly and refurbishment of the non-motor components of the SRB as part of Space Shuttle. Thrust Vector Control (TVC) frames structurally support components of the TVC system located in the aft skirt of the SRB. TVC frames are exposed to the seacoast environment after refurbishment and, also, to seawater immersion after splashdown, and during tow-back to CCAFS-Hangar AF refurbishment facilities. During refurbishment operations it was found that numerous TVC frames were experiencing internal corrosion and coating failures, both from salt air and seawater intrusions. Inspectors using borescopes would visually examine the internal cavities of the complicated aluminum alloy welded tubular structure. It was very difficult for inspectors to examine cavity corners and tubing intersections and particularly, to determine the extent of the corrosion and coating anomalies. Physical access to TVC frame internal cavities for corrosion removal and coating repair was virtually impossible, and an improved method using a Liquid (water based) Vapor-phase Corrosion Inhibitor (LVCI) for preventing initiation of new corrosion, and mitigating and/or stopping existing corrosion growth was recommended in lieu of hazardous paint solvents and high VOC / solvent based corrosion inhibitors. In addition, the borescopic inspection method used to detect corrosion, and/or coating anomalies had severe limitations because of part geometry, and an improved non-destructive inspection (NDI) method using Neutron Radiography (N-Ray) was also recommended.

Novak, Howard L.↗
NASA NTRS1989

Glass corrosion in natural environment

A series of studies of the effects of solutes which appear in natural aqueous environments, specifically Mg and Al, under controlled conditions, permit characterization of the retardation of silicate glass leaching in water containing such solutes. In the case of Mg the interaction with the glass appears to consist of exchange with alkali ions present in the glass to a depth of several microns. The effect of Al can be observed at much lower levels, indicating that the mechanism in the case of Al involves irreversible formation of aluminosilicate species at the glass surface.

Thorpe, Arthur N.↗
NASA NTRS2002

Environmentally Compatible Vapor-Phase Corrosion Inhibitor for Space Shuttle Hardware

USA-SRB Element is responsible for the assembly and refurbishment of the non-motor components of the SRB as part of Space Shuttle. Thrust Vector Control (TVC) frames structurally support components of the TVC system located in the aft skirt of the SRB (Solid Rocket Booster). TVC frames are exposed to the seacoast environment after refurbishment and, also, to seawater immersion after splashdown, and during tow-back to CCAFS-Hangar AF refurbishment facilities. During refurbishment operations it was found that numerous TVC frames were experiencing internal corrosion and coating failures, both from salt air and seawater intrusions. Inspectors using borescopes would visually examine the internal cavities of the complicated aluminum alloy welded tubular structure. It was very difficult for inspectors to examine cavity corners and tubing intersections and particularly. to determine the extent of the corrosion and coating anomalies. Physical access to TVC frame internal cavities for corrosion removal and coating repair was virtually impossible, and an improved method using a Liquid (water based) Vapor-phase Corrosion Inhibitor (LVCI) for preventing initiation of new corrosion, and mitigating and/or stopping existing corrosion growth was recommended in lieu of hazardous paint solvents and high VOC/solvent based corrosion inhibitors. In addition, the borescopic inspection method used to detect corrosion, and/or coating anomalies had severe limitations because of part geometry, and an improved non-destructive inspection (NDI) method using Neutron Radiography (N-Ray) was also recommended.

Novak, Howard L.↗
DOE OSTI2025

Characterization of Build Parameters and Microstructure in Low Heat Input WAAM of Ni-Based Superalloy Haynes 282

Ni-based superalloy Haynes® 282® is being targeted for various applications in advanced power generation systems for its superior fabricability, weldability, and excellent high temperature creep and corrosion performance. This process optimization study aims to use a low heat-input, high deposition rate, controlled Gas Metal Arc Welding (GMAW) process, Cold Metal Transfer (CMT) by Fronius, attempting to achieve fully dense fabrication and possibly avoid the need for HIP. Twenty-one multilayer blocks (~25x100x40 mm3) were deposited to explore a large set of build parameters variations that focused on varying the travel speed from 14 to 42 inches per minute (ipm) and wire feed speed from 150 to 450 ipm. A strong correlation has been observed between arc energy – controlled primarily by travel and wire feed speed. Initial visual inspection, internal microstructural examination, and computed tomography (CT) have been used to determine the effects of built parameters on evolution of internal porosity and defects. Scanning electron microscopy techniques enabled structural and compositional imaging of heterogeneity and changes in microstructural properties.

additive manufacturing↗
DOE OSTI2025

Characterization of Build Parameters and Microstructure in Low Heat Input WAAM of Ni-Based Superalloy Haynes 282

Ni-based superalloy Haynes® 282® is being targeted for various applications in advanced power generation systems for its superior fabricability, weldability, and excellent high temperature creep and corrosion performance. This process optimization study aims to use a low heat-input, high deposition rate, controlled Gas Metal Arc Welding (GMAW) process, Cold Metal Transfer (CMT) by Fronius, attempting to achieve fully dense fabrication and possibly avoid the need for HIP. Twenty-one multilayer blocks (~25x100x40 mm3) were deposited to explore a large set of build parameters variations that focused on varying the travel speed from 14 to 42 inches per minute (ipm) and wire feed speed from 150 to 450 ipm. A strong correlation has been observed between arc energy – controlled primarily by travel and wire feed speed. Initial visual inspection, internal microstructural examination, and computed tomography (CT) have been used to determine the effects of built parameters on evolution of internal porosity and defects. Scanning electron microscopy techniques enabled structural and compositional imaging of heterogeneity and changes in microstructural properties.

additive manufacturing↗
NASA NTRS1972

Fundamental investigation of stress corrosion cracking

Two principle areas studied were stress corrosion crack growth rates of a titanium alloy in liquid environments containing halide ions and pitting corrosion of titanium in bromide solutions. Two initial assumptions were made, that the rate of propagation was controlled by a macroscopic solution parameter and that this parameter was viscosity. A series of solutions were prepared using lithium chloride as the solute and water, methanol, glycerin, formic acid, acetone, dimethyl sulphoxide, etc. As solvents, these solutions were prepared with a 5:1 solvent-solute ratio. Viscosity was varied by changing the temperature and it was found: (1) In all solvents the velocity of cracking was proportional to the reciprocal of the viscosity. (2) Each solvent gave a separate relationship, (3) The temperature dependence and numerical values for the apparent activation energy of cracking and viscosity were the same.

Beck, T. R.↗
NASA NTRS1976

Environmental effects on aluminum fracture

The sustained load stress corrosion cracking (SCC) threshold for aluminum alloy 214 was determined using smooth (sigma sub TH) and precracked (K sub ISCC) specimens, and cyclic load growth behavior in 3.5% NaCl salt solution was studied. The relationship between K sub ISCC and sigma sub TH was also studied. The work showed that 2124-T851 aluminum alloy in plate gage has a moderately high resistance to stress corrosion attack. Experimental results showed that no SCC occurred in the longitudinal and long transverse directions in any of the tests. Some SCC was found by smooth tests in the short transverse direction, and the data were confirmed by two test methods-sigma sub TH = 275 MN/sq m (40 ksi). No SCC was found from compact specimen tests in any direction: surface flaw and center notch specimens evaluated in the short transverse direction exhibited SCC. The data indicate that stress corrosion behavior is defect, size, and stress dependent, but not entirely in accordance with a stress intensity controlled mechanism.

Schwartzberg, F. R.↗
NASA NTRS1976

Materials and processes for Shuttle engine, external tank, and Solid Rocket Booster

The paper deals with the materials and processes for three Space Shuttle elements: Space Shuttle Main Engines (SSME), the External Tank (ET), and the Solid Rocket Boosters (SRB), beginning with an overview of the materials selection, tracking and control system. SSME materials and processes are considered with emphasis on hydrogen environment embrittlement, LOX/GOX compatibility, stress corrosion cracking, and hydraulic fluid testing and qualification. The ET is examined with attention given to welding and fracture mechanics, and the thermal protection system. The SRB is discussed with emphasis on corrosion prevention, stress corrosion and fracture toughness, the integrated test bed for in situ corrosion protection verification, aluminum processing, and the thermal protection system.

Schwinghamer, R. J.↗
NASA NTRS1977

Summary report of the Aircraft Design Committee

Meetings were held concerning aircraft design with considerable interest shown in aircraft operations. Topics covered were: (1) structural design for turbulence; (2) flight control; (3) data needs; and (4) lightning. Other factors discussed were temperature, rain, hail, icing, pressure, density, corrosives, and abrasives.

Woodcock, R. J.↗
NASA NTRS1980

Strong, corrosion-resistant aluminum tubing

When aluminum tubing having good corrosion resistance and postweld strength is needed, type 5083 alloy should be considered. Chemical composition is carefully controlled and can be drawn into thin-wall tubing with excellent mechanical properties. Uses of tubing are in aircraft, boats, docks, and process equipment.

Reed, M. W.↗
DOE OSTI2025

Combining four-point bending and corrosion to map stress-dependent corrosion susceptibility of 316H stainless steel in FLiNaK

Understanding the effect of stress on the corrosion of steels in molten salts is important for material screening and safety assessment of molten salt reactors. We present a method that combines four-point bending with corrosion testing, enabling the mapping of corrosion susceptibility as a function of local stress from a single specimen. Guided by finite element analysis, a four-point bending setup was used to bend a 316H stainless-steel bar under controlled elastic stress during a 100-hour exposure in FLiNaK at 700 °C. Post-exposure characterization using scanning electron microscopy and energy-dispersive X-ray spectroscopy revealed a pronounced correlation between stress and corrosion. Regions under tensile stress exhibited significantly deeper attack depths and greater chromium depletion along grain boundaries, whereas compressive zones showed shallower corrosion cracks. The stress effect is attributed to stress concentration under tensile loading, which promotes chromium dissolution and crack propagation. This technique can be readily applied to other structural alloys, enabling quantitative measurement of corrosion susceptibility as a function of local stress.

316H↗
DOE OSTI2024

Molecular-scale insights into the electrical double layer at oxide-electrolyte interfaces

The electrical double layer (EDL) at metal oxide-electrolyte interfaces critically affects fundamental processes in water splitting, batteries, and corrosion. However, limitations in the microscopic-level understanding of the EDL have been a major bottleneck in controlling these interfacial processes. Herein, we use ab initio-based machine learning potential simulations incorporating long-range electrostatics to unravel the molecular-scale picture of the EDL at the prototypical anatase TiO 2 -electrolyte interface under various pH conditions. Our large-scale simulations, capable of capturing interfacial water dissociation/recombination reactions and electrolytic proton transport, provide unprecedented insights into the detailed structure of the EDL. Moreover, the larger capacitance of the EDL under basic relative to acidic conditions, originating from the higher affinity of the cations for the oxide surface, is found to give rise to distinct charging mechanisms on negative and positive surfaces. Our results are validated by the agreement between the computed EDL capacitance and experimental data.

Chemical physics↗
NASA NTRS1980

Fouling and the inhibition of salt corrosion

In an attempt to reduce fouling while retaining the beneficial effects of alkaline earth inhibitors on the hot corrosion of superalloys, the use of both additives and the intermittent application of the inhibitors were evaluated. Additions of alkaline earth compounds to combustion gases containing sodium sulfate were shown to inhibit hot corrosion. However, sulfate deposits can lead to turbine fouling in service. For that reason, dual additives and intermittant inhibitor applications were evaluated to reduce such deposit formation. Silicon in conjunction with varium showed some promise. Total deposition was apparently reduced while the inhibition of hot corrosion by barium was unimpaired. The intermittant application of the inhibitor was found to be more effective and controllable.

Deadmore, D. L.↗
NASA NTRS1982

Oceanic corrosion test of bare and zinc-protected aluminum alloys for seawater heat exchangers

Bare 3004 tubes, 7072 Alclad 3004 tubes, and bare and zinc diffusion treated 3003 extrusions from a brazed aluminum, plate-fin heat exchanger were exposed to 1.8 m/sec flowing seawater aboard an open ocean test facility moored 3.4 km off the southeast coast of Puerto Rico. After six months exposure, the average corrosion rates for most varieties of aluminum materials converged to a low value of 0.015 mm/yr (0.6 mils/yr). Pitting did not occur in bare 3003 and 3004 samples during the six month test. Pitting did occur to varying degrees in the Alclad and zinc diffusion treated material, but did not penetrate to the base metal. Biofouling countermeasures (intermittent chlorination and brushing) did not affect the corrosion rates to any significant extent. Intermittent chlorination at a level of 0.5 ppm for 28 minutes daily controlled microbiofouling of the samples but did not prevent the development of a macrobiofouling community in areas of the plumbing with low flow.

Sasscer, D. S.↗
NASA NTRS2015

Hexavalent Chromium IV-Free Primer Development

Primer materials provide corrosion protection for metal parts as well as an increased adhesion between metallic substrates and thermal protection systems (TPSs). Current primers for use in cryogenic applications contain hexavalent chromium. This hexavalent chromium provides excellent corrosion protection even in a cryogenic environment, but it is a carcinogen that requires special equipment and waste control procedures to use. The hazardous nature of hexavalent chromium makes it an obsolescence risk in the future. This study included two phases of evaluation. Thirteen primers were initially identified as candidates and twelve of those primers were tested in phase 1. Four of the best performing candidates from phase 1 continued into phase 2 testing. Phase 1 testing consisted mostly of liquid constituent and physical property testing. Cryoflex and salt fog testing were included in phase 1 because of their importance to the overall success of a candidate material. Phase 2 consisted of physical, thermal, and mechanical properties for nominally processed and fabricated specimens.

Alldredge, Michael J.↗
DOE OSTI2026

Controlling Nb(IV) Defects in SrNbO 2 N Oxygen Evolution Photocatalyst by Ammonolysis With Dinitrogen–Ammonia Mixtures

Strontium niobium oxynitride (SrNbO 2 N) is a promising, corrosion resistant semiconductor for the visible light-driven water splitting reaction, a non-photovoltaic pathway to green hydrogen fuel. However, SrNbO 2 N materials made by ammonolysis usually contain Nb 4+ defect states that cause electron–hole recombination. Here, in this work, we demonstrate that such defects can be minimized by synthesizing SrNbO 2 N from metal oxides in a mixed 13%:87% (vol) NH 3 /N 2 atmosphere. According to electron paramagnetic resonance (EPR), SrNbO 2 N made in pure NH 3 contains paramagnetic impurities with g = 2.002 and 2.195, which can be assigned to lattice and surface Nb 4+ defects. These states also cause broad optical absorptions centered at 800 and 1020 nm, respectively, and the lattice defect produces a 1.55–1.63 eV signal in surface photovoltage spectra. The improved SrNbO 2 N contains five times fewer lattice Nb 4+ defects (8.95 × 10 15 cm −3 ), based on the integrated EPR signal intensity, and supports a water oxidation photocurrent of 1.07 mA cm −2 at 1.23 V versus RHE under simulated sunlight and an apparent quantum efficiency of 5.1% at 400 nm during photocatalytic oxygen evolution. Based on earlier results with LaTiO 2 N and BaTaO 2 N, dilution of NH 3 during synthesis appears generally beneficial to transition metal oxynitrides.