Inhomogeneous Distribution and Coarsening of y″ Precipitates in a Ni-Based Superalloy and Their Effect on Creep
It has been reported that the addition of Nb or Ta in the high Ti/Al ratio alloys promotes the formation of y″ precipitates solely and greatly contributes to the elevated temperature strength and resistance to creep deformation. In this study, the y''-dominant INCONEL alloy 725 (IN725) variants (named M725-Nb/Ta) modified with a high level of Nb/Ta additions and high Ti/Al ratio was chosen as a model alloy for microstructural observation of y'' variants upon creep. Following the high temperature aging (HTA), y'' was found to be the main strengthening precipitate with no detectable y’ in both M725 alloys. After creep, the grip/gage sections of the crept M725-Nb/Ta exhibited preferential coarsening and inhomogeneous distribution of y''. That is, one or two of the variants were preferentially coarsened at the expense of another variant, and sandwich-like structures, comprising of cubic y′ precipitates with small y″ discs on each face, were formed. This variant selection behavior taking place in the grip section with no stress applied was different from the typical stress-induced variant selection in previous literature. However, the sample with prior high temperature exposure (700 °C for 500 hours) with varying y″ characteristics demonstrated a similar trend of creep when compared with those in the HTA sample, suggesting that the coarsening and the inhomogeneous distribution of y'' was not the determinant of creep life in bulk M725-Nb/Ta alloys.