DOE OSTI2026
Molten salt reactors (MSRs) offer a compelling pathway for next-generation nuclear energy, with advantages in thermal efficiency, inherent safety, and flexible fuel management. Yet, halide-based molten salts introduce significant materials challenges, particularly alloy corrosion. Alloy performance in these environments ultimately depends on understanding how corrosion initiates and progresses at the nanoscale, however most existing models rely on post-exposure characterization, leaving degradation mechanisms largely inferred rather than directly observed. NiCr alloys have garnered interest in MSRs applications as the Ni-based matrix provides strength and creep resistance, while Cr content offers oxidation resistance in air. However, NiCr corrosion resistance in chloride salts has proven poor due to preferential chromium dissolution, the formation of Cr-depleted pathways, and grain-boundary attack. This work aims to directly visualize corrosion of Ni-20Cr exposed to LiCl-KCl using in-situ Transmission Electron Microscopy (TEM) to capture real-time microstructural evolution during corrosion. Experiments will be performed at ~800 °C under controlled pressure conditions while utilizing Energy-Dispersive X-ray Spectroscopy (EDS) to analyze elemental redistribution. Observation of chromium depletion fronts, associated surface restructuring, and localized chloride enrichment are expected. Ultimately, this study is expected to provide a link between microscale processes and the macroscopic degradation behaviors relevant to MSR operation in advanced reactor environments. Simultaneously, this approach enables future in-situ investigations regarding alloy composition, salt chemistry, and their influence on corrosion pathways and long-term stability.?