Qualitative comparison of oxidation resistance of nickel-aluminum alloys with additions of chromium, silicon, and titanium at high temperatures
Heat treatment of carbide and boride strengthened chromium alloys to improve tensile and creep rupture strength
Precipitation with refractory metal carbides for creep resistant chromium-base alloys
Rare earth and thorium alloying of chromium and mechanism for controlling nitrogen embrittlement
Friction wear of human hip joint prostheses made from cobalt molybdenum and cobalt molybdenum chromium alloys
Effectivness of yttrium, lanthanum, and hafnium coatings for preventing nitridation embrittlement of chromium alloys at high temperatures
Finely divided powder mixture produced by vapor deposition of CR on small ThO2 particles was hot pressed or pressure bonded. Resulting alloy has lower ductile-to-brittle transition temperature than pure chromium, and high strength and oxidation resistance at elevated temperatures, both in as-rolled condition and after annealing.
The resistance of thin TD-NiCr sheet to cyclic deformation was compared with that of TD-Ni and a conventional nickel-chromium alloy. Strains were determined by a calibration technique which combines room-temperature strain gage and deflection measurements with high-temperature deflection measurements. Analyses of the cyclic tests using measured tensile and creep-rupture data indicated that the TD-NiCr and NiCr alloy specimens failed by a cyclic creep mechanism. The TD-Ni specimens, on the other hand, failed by a fatigue mechanism.
A pack process was developed which permits the introduction of nearly six weight percent aluminum into solid solution in the near-surface region of TDNiCr (Ni-20Cr-2ThO2. At this aluminum concentration an adherent alumina scale is produced on the alloy surface upon exposure to an environment of 1330 n/sq m (10 torr) or 101,000 n/sq m (760 torr) air at temperatures of 1093 C (2000 F) and 1204 C (2200 F). Room temperature mechanical properties of the aluminized alloys compare favorably with those of TDNiCr as received. While diffusivities for aluminum are a factor of three higher than those for chromium in TDNiCr or Ni-20Cr, the diffusion rates are similar for either of these elements in the thoriated or unthoriated alloy for a given temperature and grain size.
The alloys Ni3Al and NiAl with and without 1 and 3 atomic percent chromium, silicon, and titanium replacing the aluminum were cyclically oxidized at 1200 C for times to 200 hours, and the results were compared with those obtained with the alloy B-1900 subjected to the same oxidation process. The evaluation was based on metal recession, specific weight change, metallography, electron microprobe analysis, and X-ray diffraction. The oxidation resistance of Ni3Al was improved by Si, unaffected by Ti, and degraded by Cr. The oxidation resistance of NiAl was slightly improved by Ti, unaffected by Si, and degraded by Cr. The oxidation resistance of Ni3Al with 1 atomic percent Si was nearly equal to that of NiAl. Alloy B-1900 exhibited oxidation resistance comparable to that of Ni3Al + Cr compositions.
The Cr2O3 content of powder metallurgy nickel-20 chromium-3 thoria was reduced with atmospheres consisting of hydrogen plus hydrogen chloride (HCl) or hydrogen bromide (HBr). The nonthoria oxygen content or 'oxygen excess' was reduced from an initial amount of greater than 50,000 ppm to less than 100 ppm. Low temperatures were effective, but lowest oxygen levels were achieved with the highest cleaning temperature of 1200 C.
Modified thoria-dispersed nickel-chromium alloy has been developed that exhibits greatly improved resistance to high-temperature oxidation. Additions of aluminum have been made to change nature of protective oxide scale entirely and to essentially inhibit oxidation at temperatures up to 1260 C.
A dispersion-strengthened alloy, TD nickel chromium (TDNiCr) is being developed for use on the thermal protection system of the space shuttle at temperatures up to 1204 C(2200 F). Manufacturing processes were developed for the fabrication of sheet and foil to specifications. The addition of aluminum to the basic TDNiCr composition provides outstanding oxidation resistance up to 1260 C(2300 F); aluminum levels of 2 to 4% are considered optimum for space shuttle application.
The formation and breakdown of a protective layer of Cr2O3 on the cobalt-base alloy L-605 during oxidation at 1100 C was evaluated. Deformed surface layers, pressure, and moisture were variables. Increasing surface deformation, decreasing pressure, and decreasing moisture increased time to breakdown. A model was deduced. The breakdown of the Cr2O3 layer was caused by a combination of growth stresses and volatilization. Breakdown exposed a chromium-depleted alloy to air, resulting in very rapid oxidation, which continued until consumption of the depletion zone was complete.
The deformation and annealing response of TD-nickel chromium (TD-NiCr) 0.1 inch thick sheet was examined using various cold-rolling and annealing treatments. Upon annealing (above 816 C (1500 F), the as-received material was converted from an initially ultra-fine grain size (average grain dimension 0.51 micron) to a large grain structure. Increases in grain size by a factor of 100 to 200 were observed for this transformation. However, in those material states where the large grain transformation was absent, a fine grain recrystallized structure formed upon annealing (above 732 C (1350 F)). The deformation and annealing response of TD-NiCr sheet was evaluated with respect to the processing related variables as mode and severity of deformation and annealing temperature. Results indicate that the large grain transformation, classical primary recrystallization occurs. Using selected materials produced during the deformation and annealing study, the elevated temperature tensile properties of TD-NiCr sheet were examined in the temperature range 593 C (1100 F) to 1093 C (2000 F). It was observed that the elevated temperature tensile properties of TD-NiCr sheet could be optimized by the stabilization of a large grain size in this material using the cold working and/or annealing treatments developed during the present investigation.
Two coatings for a Rayleigh step thrust bearing were tested when coasting down and stopping under self-acting operation in air. The thrust bearing had an outside diameter of 8.9 cm (3.5 in.), an inside diameter of 5.4 cm (2.1 in.), and nine sectors. The load was 73 N (16.4 lbf). The load pressure was 19.1 kN/per square meter (2.77 lbf/per square inch) on the total thrust bearing area. The chromium oxide coating was good to 150 stops without bearing deterioration, and the molybdenum disulfide coating was good for only four stops before bearing deterioration. The molybdenum disulfide coated bearing failed after nine stops.
Rates of oxidative vaporization of Cr2O3 on preoxidized resistively heated chromium were determined in flowing oxygen at 0.115 torr for temperatures from 1270 to 1570 K. Reaction controlled rates were obtained from experimental rates by a gold calibration technique. These rates were shown to agree with those predicted by thermochemical analysis. The activation energy obtained for the oxidative vaporation reaction corresponded numerically with the thermochemical enthalpy of the reaction. A theoretical equation is given for calculating the rate from thermodynamic data by using boundary layer theory.
The deformation behavior of thoria nickel-chromium (TD-NiCr) was examined over the temperature range 593 C (1100 F) to 1260 C (2300 F) in tension and compression and at 1093 C (2000 F) in creep. Major emphasis was placed on: (1) the effects of the material and test related variables (grain size, temperature, stress and strain rate) on the deformation process; and (2) the evaluation of single crystal TD-NiCr material produced by a directional recrystallization process. Elevated temperature yield strength levels and creep activation enthalpies were found to increase with increasing grain size reaching maximum values for the single crystal TD-NiCr. Stress exponent of the steady state creep rate was also significantly higher for the single crystal TD-NiCr as compared to that determined for the polycrystalline materials. The elevated temperature deformation of TD-NiCr was analyzed in terms of two concurrent, parallel processes: diffusion controlled grain boundary sliding, and dislocation motion.