Report evaluates protective coatings for metal structures in seashore and acid-cloud environments. Evaluation result of study of coating application characteristics, repair techniques, and field performance. Products from variety of manufacturers included in study. Also factory-coated panels and industrial galvanized panels with and without topcoats.
Solar absorptance by satellite coating with measurement as function of incidence angle using thermal vacuum
Blistering and peeling of topcoats used over ethyl silicate, inorganic, zinc-rich protective coatings are virtually eliminated when primer is allowed to cure outdoors for extended period of time and is moistened during process.
Bell & Howell Company (at their own expense) arranged to work with an Ames Research Center scientist to learn NASA's technique of plasma polymerization. Plastic is easily formed into aspherical surfaces and compound lenses are made from plastics of different refractive indexes. Plastic lenses are injection molded at a tenth the cost of making glass lenses and are lighter than glass and cannot shatter. Scratches scatter light reducing light transmission. This technique is used for coating plastic lenses of film projectors and other optical equipment.
Four thermal barrier coatings were subjected to a 500-hour gas turbine engine test. The coatings were two yttria stabilized zirconias, calcium ortho silicate and calcium meta titanate. The calcium silicate coating exhibited significant spalling. Yttria stabilized zirconia and calcium titanate coatings showed little degradation except in blade leading edge areas. Post-test examination showed variations in the coating due to manual application techniques. Improved process control is required if engineering quality coatings are to be developed. The results indicate that some leading edge loss of the coating can be expected near the tip.
To lower the cost of hydrogen produced by anion exchange membrane water electrolysis (AEMWE), it is critical to reduce the use of platinum group metal (PGM) catalysts within the device. While iridium has been successfully replaced with PGM-free catalysts at the anode, platinum-based (Pt) cathode catalysts are still required to meet the activity and durability targets. This study investigates the impact of commercial Pt/C catalyst loading, ionomer type and content, and electrode fabrication method on the cathode catalyst layer properties and AEMWE performance with the aim of determining the feasibility of reduced Pt loadings. While increased Pt loading is found to improve beginning-of-life performance, the effects are minimal above 0.6 mg/cm 2 . Ink characterization shows that ionomer type and content affect the ink stability, particle size, and percent of unbound ionomer, which further impact the homogeneity of the sprayed catalyst layers. The 5% PiperION cathode exhibited the highest performance, which may be attributed to a balance between the small particle size and the low proportion of unbound ionomer, minimizing kinetic and transport losses. Theoretical calculations show that the ionomers interact differently with the Pt surface, causing different surface charges and water adsorption strength and activating different mechanisms for hydrogen evolution. Pt-PiperION lowered the enthalpy of water-splitting by 0.1 eV compared to Pt alone and allowed for equal site access between adsorbed H* and OH* (both adsorbed at circa −2.2 eV). Although catalyst-coated membrane (CCM) fabrication techniques are desirable for scale-up, no performance enhancement is observed compared with the catalyst-coated substrate approach. Durability, as measured by degradation rates, Pt loss, and catalyst layer restructuring, was found to improve with increased Pt loadings, higher ionomer content, and CCM architectures. These findings provide important insight into the significant role of the cathode in AEMWE and strategies for maintaining the performance with low Pt loading or PGM-free catalysts.
Barrier layers were coated onto high-modulus fibers, and nickel and titanium layers were overcoated as simulated matrix materials. The objective was to coat the high-strength fibers with unreactive selected materials without degrading the fibers. The fibers were tungsten, niobium, and single-crystal sapphire, while the materials used as barrier coating layers were Al2O3, Y2O3, TiC, ZrC, WC with 14% Co, and HfO2. An ion-plating technique was used to coat the fibers. The fibers were subjected to high-temperature heat treatments to evaluate the effectiveness of the barrier layer in preventing fiber-metal interactions. Results indicate that Al2O3, Y2O3, and HfO2 can be used as barrier layers to minimize the nickel-tungsten interaction. Further investigation, including thermal cycling tests at 1090 C, revealed that HfO2 is probably the best of the three.
A process for fabricating a precise, diffraction- limited, ultra-lightweight, composite- material (matrix/fiber) paraboloidal telescope mirror has been devised. Unlike the traditional process of fabrication of heavier glass-based mirrors, this process involves a minimum of manual steps and subjective judgment. Instead, this process involves objectively controllable, repeatable steps; hence, this process is better suited for mass production. Other processes that have been investigated for fabrication of precise composite-material lightweight mirrors have resulted in print-through of fiber patterns onto reflecting surfaces, and have not provided adequate structural support for maintenance of stable, diffraction-limited surface figures. In contrast, this process does not result in print-through of the fiber pattern onto the reflecting surface and does provide a lightweight, rigid structure capable of maintaining a diffraction-limited surface figure in the face of changing temperature, humidity, and air pressure. The process consists mainly of the following steps: 1. A precise glass mandrel is fabricated by conventional optical grinding and polishing. 2. The mandrel is coated with a release agent and covered with layers of a carbon- fiber composite material. 3. The outer surface of the outer layer of the carbon-fiber composite material is coated with a surfactant chosen to provide for the proper flow of an epoxy resin to be applied subsequently. 4. The mandrel as thus covered is mounted on a temperature-controlled spin table. 5. The table is heated to a suitable temperature and spun at a suitable speed as the epoxy resin is poured onto the coated carbon-fiber composite material. 6. The surface figure of the optic is monitored and adjusted by use of traditional Ronchi, Focault, and interferometric optical measurement techniques while the speed of rotation and the temperature are adjusted to obtain the desired figure. The proper selection of surfactant, speed or rotation, viscosity of the epoxy, and temperature make it possible to obtain the desired diffraction-limited, smooth (1/50th wave) parabolic outer surface, suitable for reflective coating. 7. A reflective coat is applied by use of conventional coating techniques. 8. Once the final figure is set, a lightweight structural foam is applied to the rear of the optic to ensure stability of the figure.
Grit-blasting technique for cutting line gaps in paints, hard coats, lubricants, and other coating films undergoing development. Line gaps cut in chevron patterns, groups of parallel lines, or other prescribed patterns, in preparation for testing adhesions of coats to substrates by attempting to peel patterned areas off with adhesive tapes. Damage to substrate reduced.
The paper provides an overview of the short history, current status, and future prospects of ceramic thermal barrier coatings for gas turbine engines. Particular attention is given to plasma-sprayed and electron beam-physical vapor deposited yttria-stabilized (7 wt pct Y2O3) zirconia systems. Recent advances include improvements in the spallation life of thermal barrier coatings, improved bond coat composition and spraying techniques, and improved component design. The discussion also covers field experience, life prediction modeling, and future directions in ceramic coatings in relation to gas turbine engine design.
Contemporary trends in rotating machinery development have produced a continuous evolution towards ever increasing speeds and higher operating temperatures. This process has been particularly evident in aerospace and automotive applications such as turbochargers. The combination of high temperature and high speed has exceeded the capacity of mainstream liquid lubrication technology. The NASA Glenn Research Center has been at the forefront in developing innovative solid lubricants for the oil free protection of rotating machinery under these extreme environmental conditions. The most recent of these is the PS 300 series of plasma sprayed solid lubricant coatings. St Louis University and NASA Glenn Research Center entered into this cooperative agreement to investigate potential thermal processing techniques for the enhancement of the PS 304 solid lubricant.
This work was undertaken as a LightMAT project funded by the DOE-Vehicles Technology Office. The goal of this work was to develop corrosion protection strategies that simultaneously mitigate corrosion and achieve Class-A surface finish for Mg components in automotive applications. While automotive metals such as steel and aluminum are protected against corrosion through a variety of coating schemes/packages, the efficacy of these existing coating schemes for Mg and Mg- joints is not clear and needs to be determined. Therefore, five commercially available coating schemes and two joining techniques (riveting and Arplas resistance spot welding) were evaluated. The corresponding individual Mg sheet coupons or Mg/Mg joint test coupons were provided by Magna that were then corrosion tested at PNNL using ASTM B117 procedure. The microstructures and mechanical properties of the coupons were analyzed to determine the effectiveness of the joining and corrosion mitigation strategies. Of the coating schemes evaluated, Henkel Bonderite MgC 2.0 pre-treatment + E-coat showed the best corrosion protection and surface finish for individual Mg coupons and Arplas resistance spot welded coupons. However, the strength of Mg/Mg welded joint was reduced after corrosion testing due to some corrosion at the weld nugget. Mg/Mg rivet joints in conjunction with Chemetall oxisilan pre-treatment + polyurethane coating showed good corrosion resistance and some discoloration on the surface finish. Coating schemes comprising pre-treatment with Alodine 5200 + E-coat or Bonderite 1455 + polyurethane coating, in conjunction with Al rivet joints, showed significant corrosion and extensive discoloration of the surface. We anticipate that the results from this work will provide useful guidance to the automotive industry in selecting the appropriate combinations of corrosion protection coatings and joining techniques to fabricate light-weight Mg-based automotive components.
Formulation of electrically conductive, thermal-control coatings was undertaken for use on the International Sun Earth Explorer (ISEE) spacecraft. Unsuccessful formulation efforts as well as the successful use of oxide pigments fired at 1175 C are described. Problems attributed to reactivity of specific coating vehicles exposed to high humidity are discussed. Measurement and testing methods, including resulting data are mentioned, but the emphasis, in this report, is placed on coating formulation and application techniques. Methods of varying, as desired, optical properties are also described as well as formulations of white, low-absorptance coatings.
A study is conducted of the effect of substrate temperature during coating on the properties of coated SiC films on Si wafers, using a scratch test technique. While specimen temperature during coating has little effect on deposition rate, it significantly affects the durability of the coating. Scratch test damage to both film coating and substrate decreased with increasing deposition temperature, perhaps due to the rapid diffusion of the deposited atoms.
Ion beam sputter deposition techniques were used to investigate simultaneous sputter etching of two component targets so as to produce mixed composition films. Although sputter deposition has been largely confined to metals and metal oxides, at least one polymeric material, poly-tetra-fluorethylene, has been demonstrated to produce sputtered fragments which repolymerize upon deposition to produce a highly cross-linked fluoropolymer resembling that of the parent target Fluoropolymer-filled silicon dioxide and fluoropolymer-filled aluminum oxide coatings have been deposited by means of ion beam sputter coat deposition resulting in films having material properties suitable for aerospace and commercial applications. The addition of fluoropolymer to silicon dioxide films was found to increase the hydrophobicity of the resulting mixed films; however, adding fluoropolymer to aluminum oxide films resulted in a reduction in hydrophobicity, thought to be caused by aluminum fluoride formation.
The design of the next generation of reusable launch vehicles calls for using GRCop-84 copper alloy liners based on a composition invented at the NASA Glenn Research Center. Despite its considerable advantage over other copper alloys, it is expected that GRCop-84 will suffer from environmental degradation depending on the type of rocket fuels used and on thermomechanical fatigue. Applying protective coatings on GRCop-84 substrates can minimize or eliminate many of these problems and extend the operational life of the combustion liner. This could increase component reliability, shorten depot maintenance turnaround times, and lower operating costs. Therefore, Glenn is actively pursuing the development of advanced coatings technology for GRCop-84 liners. Technology is being developed in four major areas: (1) new metallic coating compositions, (2) application techniques, (3) test methods, and (4) life prediction design methodology using finite element analysis. The role of finite element analysis in guiding the coating effort is discussed in this report. Thermal analyses were performed at Glenn for different combinations of top- and bondcoat compositions to determine the temperature variation across the coated cross section with the thickness of the top coat. These calculations were conducted for simulated LH2/LO2 booster engine conditions assuming that the bond coat had a constant thickness of 50 m. The preceding graphs show the predicted temperatures at the outer surface of the top coat (hot wall), at the top-coat/bond-coat interface, at the bond-coat/GRCop-84 interface, and at the GRCop-84 cold wall as a function of top-coat thickness for Cu- 26(wt%)Cr top coat (top graph), Ni-17(wt%)Cr-6%Al-0.5%Y top coat and Cu-26%Cr bond coat, and NiAl top coat and Ni bond coat. In all cases, the temperature of the top coat at the hot wall increased with increasing top-coat thickness and with corresponding decreases in the temperatures at the two interfaces and the cold wall. These temperatures are not acutely sensitive to the thermal conductivity of the top coat when it exceeds 25 and 50 W/m/K for low and high heat flux engines. This observation is significant for two reasons. First, several different top-coat compositions can be evaluated as potential protective coatings without loss in the heat-transfer efficiency of the coated system. Second, materials with thermal conductivities less than the critical values of 25 or 50 W/m/K are more likely to act as thermal barrier coatings. The deposition of overlay coatings on GRCop-84 substrates results in the development of residual stresses. The presence of these residual stresses influences the probability of coating spallation, the thermal cycling life, and the fatigue properties of the coated substrate during use. Since it is important to understand how these stresses develop during the vacuum-plasma-spraying coating deposition process, the nature and magnitudes of the cool-down residual stresses were calculated and compared with experimentally determined values across the coated cross section of a disk specimen. The calculations were conducted assuming that the specimen cools down to room temperature from vacuum plasma-spraying temperatures of either 250 or 650 C. The effects of coating the substrate with and without grit blasting were also theoretically examined. The final graph compares the predicted and the experimental results for a GRCop-84 disk coated with about a 50- m-thick Ni bond coat and a 75- to 100- m NiAl top coat, where the curves for NASA-2 assume the presence of a prior residual stress generated by grit blasting under conditions similar to the experimental situation. The predicted cool-down in-plane stresses were compressive in both the NiAl top coat and the Ni bond coat. They were also compressive in the substrate to a depth of about 0.25 mm from the Ni/GRCop-84 interface when the vacuum-plasma-spraying temperature was low. However, using a higher plasma spraying temperaturs likely to leave the substrate under a small tensile stress to counter the compressive stresses in the bond and top coats because of the relaxation of residual stresses generated in the substrate during the grit blasting of its surface prior to spraying. These results suggest that the NiAl and Ni coatings are unlikely to spall after spraying as confirmed by the microstructural observations shown in the following photomicrograph of an as-sprayed specimen. Finally, it is noted that the calculated and experimental results are not in complete agreement, which indicates that both the experimental and modeling techniques need further refinement.
A physical characterization of coating materials by analytical techniques such as XPS, AES, ellipsometry, and nuclear reaction analysis can contribute to the understanding of adhesion and friction of the coatings and can partially predict the tribological properties of the coatings. This two-part paper describes the tribological properties and physical characteristics of (1) diamondlike carbon (DLC) films and (2) silicon nitride (SiN(x)) films. Emphasis is to relate plasma deposition conditions to the film chemistry and composition and to the adhesion and friction of the films. With the DLC films, the higher the plasma deposition power, the less the hydrogen concentration and the greater the film density and the hardness. The friction behavior of DLC films deposited at higher deposition powers (200 to 300 W) is similar to that of bulk diamond. Even in a vacuum, the DLC films effectively lubricate ceramic surfaces (Si3N4) at temperatures to 500 C. With SiN(x) films, the silicon to nitrogen ratios and the amount of amorphous silicon depend on deposition frequency. The presence of rich amorphous silicon in the high-frequency plasma-deposited SiN(x) films increases their adhesion and friction above 500 C in vacuum.
Processing techniques were developed for applying several diffusion barriers to TD-Ni and TD-NiCr. Barrier coated specimens of both substrates were clad with Ni-Cr-Al and Fe-Cr-Al alloys and diffusion annealed in argon. Measurement of the aluminum distribution after annealing showed that, of the readily applicable diffusion barriers, a slurry applied tungsten barrier most effectively inhibited the diffusion of aluminum from the Ni-Cr-Al clad into the TD-alloy substrates. No barrier effectively limited interdiffusion of the Fe-Cr-Al clad with the substrates. A duplex process was then developed for applying Ni-Cr-Al coating compositions to the tungsten barrier coated substrates. A Ni-(16 to 32)Cr-3Si modifier was applied by slurry spraying and firing in vacuum, and was then aluminized by a fusion slurry process. Cyclic oxidation tests at 2300 F resulted in early coating failure due to inadequate edge coverage and areas of coating porosity. EMP analysis showed that oxidation had consumed 70 to 80 percent of the aluminum in the coating in less than 50 hours.