DOE OSTI2022

Microstructural evolution and strengthening mechanisms in a heat-treated additively manufactured Al–Cu–Mn–Zr alloy

In this report the microstructural and strength evolution of an additively manufactured Al-8.6Cu-0.5Mn-0.9Zr alloy upon aging at 300, 350, and 400 °C is investigated. The strengthening phases of the alloy evolve significantly upon aging, with breakdown and spheroidization of the interconnected θ-Al 2 Cu network, dissolution of metastable θ'-Al 2 Cu precipitates, and precipitation of nanometric L1 2 -Al 3 Zr from a matrix supersaturated in Zr. In the peak-aged states, the alloy displays a favorable combination of strength and ductility, with a room-temperature yield strength of 314–341 MPa and ductility of 11–13%. The measured yield strengths for microstructures with different aging treatments are compared to predictions of yield strengths from grain boundary, solid solution, and particle strengthening contributions. The observed strain hardening behavior is related to fundamental precipitate and dislocation interactions. Comparison between predicted and measured strength values indicates a continued need for strengthening models specifically developed for the heterogeneous microstructures of additively manufactured alloys.

36 MATERIALS SCIENCE↗
DOE OSTI2017

Effect of different stages of deformation on the microstructure evolution of Ti-rich NiTi shape memory alloy

The main objective of this work was to investigate the thermomechanical behavior and microstructural changes of a Ti-rich NiTi shape memory alloy (SMA). The microstructural and texture evolution of aged NiTi alloy at different degrees of deformation were elicited by transmission electron microscopy (TEM). An effort was made to correlate results obtained from the tensile test with results from microstructure studies. The undeformed sample reveals a self-accommodated morphology with straight and well defined twin boundaries. At different stages of deformation, diverse mechanisms were involved. These mechanisms include marstraining, detwinning accompanied by dislocation movement, and finally, severe plastic deformation, subdivision and amorphization of the matrix. Under increasing strains, high density lattice defects were generated and the morphology of B19’ became disordered. - Graphical abstract: The summary of microstructure changes of the martensite twins during tensile deformation in polycrystalline NiTi SMAs. - Highlights: • Initial elastic response, dislocation avalanche and deformation bands were studied. • < 011 > Type II twin accompanied by detwinned area after 2% cold work was observed. • Visible parallel fine stacking faults showed plastic flow of the material. • At higher strains, subgrains changed to recrystallized, finely amorphous structure.

36 MATERIALS SCIENCE↗
DOE OSTI2023

Characterization of the radial microstructural evolution in LWR UO 2 using electron backscatter diffraction

Studies on high burnup UO 2 subjected to loss-of-coolant accident conditions have shown that restructured regions of the fuel are susceptible to pulverization and eventual dispersal. Due to a lack of pre-test characterization, the distinct microstructural features rendering the fuel prone to fragmentation remain ambiguous. Four samples of commercially irradiated light-water reactor UO 2 have been characterized utilizing electron backscatter diffraction to assess the susceptible microstructure. The microscopy focused on determining the burnup and temperature conditions responsible for the formation of the different microstructural regions where the regions were denoted as the high-burnup structure (HBS), HBS transition, mid-radial, restructured central, and central region. Previous works have outlined the specific conditions required for the restructuring of the microstructure into the HBS, but the conditions responsible for the restructuring in the central region of the fuel are not well understood. The four analyzed samples confirm a burnup threshold of 61 GWd/tU, and an unknown temperature range is needed to facilitate the formation of the restructured central region. In conclusion, additional fuel performance evaluations are needed to quantify the temperature range promoting restructuring in the central region.

11 NUCLEAR FUEL CYCLE AND FUEL MATERIALS↗
DOE OSTI2011

Texture and microstructure evolution in single-phase Ti{sub x}Ta{sub 1-x}N alloys of rocksalt structure

The mechanisms controlling the structural and morphological features (texture and microstructure) of ternary transition metal nitride thin films of the Ti{sub x}Ta{sub 1-x}N system, grown by various physical vapor deposition techniques, are reported. Films deposited by pulsed laser deposition, dual cathode magnetron sputtering, and dual ion beam sputtering have been investigated by means of x-ray diffraction in various geometries and scanning electron microscopy. We studied the effects of composition, energetic, and kinetics in the evolution of the microstructure and texture of the films. We obtain films with single and mixed texture as well as films with columnar ''zone-T'' and globular type morphology. The results have shown that the texture evolution of ternary transition metal nitrides as well as the microstructural features of such films can be well understood in the framework of the kinetic mechanisms proposed for their binary counterparts, thus giving these mechanisms a global application.

36 MATERIALS SCIENCE↗
DOE OSTI2015

Microstructure evolution of Al-doped zinc oxide and Sn-doped indium oxide deposited by radio-frequency magnetron sputtering: A comparison

The microstructure and morphology evolution of Al-doped zinc oxide (AZO) and Sn-doped indium oxide (ITO) thin films on borosilicate glass substrates deposited by radio-frequency magnetron sputtering at room temperature (RT) and 300 °C were investigated by X-ray diffraction and atomic force microscopy (AFM). One-dimensional power spectral density (1DPSD) functions derived from the AFM profiles, which can be used to distinguish different growth mechanisms, were used to compare the microstructure scaling behavior of the thin films. The rms roughness R{sub q} evolves with film thickness as a power law, R{sub q} ∼ d{sub f}{sup β}, and different growth exponents β were found for AZO and ITO films. For AZO films, β of 1.47 and 0.56 are obtained for RT and 300 °C depositions, respectively, which are caused by the high compressive stress in the film at RT and relaxation of the stress at 300 °C. While for ITO films, β{sub 1} = 0.14 and β{sub 2} = 0.64 for RT, and β{sub 1} = 0.89 and β{sub 2} = 0.3 for 300 °C deposition are obtained, respectively, which is related to the strong competition between the surface diffusion and shadowing effect and/or grain growth. Electrical properties of both materials as a function of film thickness were also compared. By the modified Fuchs-Sondheimer model fitting of the electrical transport in both materials, different nucleation states are pointed out for both types of films.

36 MATERIALS SCIENCE↗
DOE OSTI2022

Understanding Uncertainty in Microstructure Evolution and Constitutive Properties in Additive Process Modeling

Coupled process–microstructure–property modeling, and understanding the sources of uncertainty and their propagation toward error in part property prediction, are key steps toward full utilization of additive manufacturing (AM) for predictable quality part development. The OpenFOAM model for process conditions, the ExaCA model for as-solidified grain structure, and the ExaConstit model for constitutive mechanical properties are used as part of the ExaAM modeling framework to examine a few of the various sources of uncertainty in the modeling workflow. In addition to “random” uncertainty (due to random number generation in the orientations and locations of grains present), the heterogeneous nucleation density N 0 and the mean substrate grain spacing S 0 are varied to examine their impact of grain area development as a function of build height in the simulated microstructure. While mean grain area after 1 mm of build is found to be sensitive to N 0 and S 0 , particularly at small N 0 and large S 0 (despite some convergence toward similar values), the resulting grain shapes and overall textures develop in a reasonably similar manner. As a result of these similar textures, ExaConstit simulation using ExaCA representative volume elements (RVEs) from various permutations of N 0 , S 0 , and location within the build resulted in similar yield stress, stress–strain curve shape, and stress triaxiality distributions. It is concluded that for this particular material and scan pattern, 15 layers is sufficient for ExaCA texture and ExaConstit predicted properties to become relatively independent of additional layer simulation, provided that reasonable estimates for N 0 and S 0 are used. However, additional layers of ExaCA will need to be run to obtain mean grain areas independent of build height and baseplate structure.

36 MATERIALS SCIENCE↗
DOE OSTI2025

Friction surface layer deposition of triple-phase Al 10 Cr 12 Fe 35 Mn 23 Ni 20 high entropy alloy: Process optimization and microstructural evolution

A high-strength Co-free triple-phase Al 10 Cr 12 Fe 35 Mn 23 Ni 20 high-entropy alloy (HEA) was successfully fabricated using Friction Surface Layer Deposition (FSLD), a bulk manufacturing method. Multiple single-layer deposits were produced by varying forging force (F) and traverse speeds (T r ) to optimize the process parameters. The optimized conditions (F = 40 kN & T r = 200 mm/min) were then applied to manufacture a scaled-up multi-layer specimen. The initial microstructure of the HEA consisted of coarse grains of the soft FCC-phase, long columnar dendrites of the hard BCC-phase, and small precipitates of the harder B2-phase within the BCC-dendrites. During FSLD, the FCC-matrix underwent continuous dynamic recrystallization due to high-temperature severe plastic deformation, forming finer equiaxed grains. Simultaneously, the BCC-dendrites fractured into smaller fragments, some of which experienced partial growth and coarsening under applied stress, resulting in an hourglass morphology. In contrast, the small B2-precipitates within the BCC-fragments dissolved during the elevated temperatures of FSLD and reprecipitated as substantially finer precipitates during continuous cooling post-FSLD. Additionally, the orientation relationships between the FCC and BCC/B2 phases were completely destroyed by the severe thermoplastic deformation inherent to FSLD. The microstructural refinements led to a substantial improvement in hardness from 177 HV to 283 HV, driven by Hall-Petch strengthening. The increased number of interfaces, including coherent BCC-B2 interfaces, potentially enhances the sink strength and radiation tolerance of the HEA, making it a promising candidate for nuclear applications. In conclusion, this study also highlights FSLD as a versatile technique for achieving tunable properties in HEAs, with detailed schematics illustrating the complex mechanisms of phase transformations during processing.

Additive Manufacturing↗
DOE OSTI2018

Microstructure Evolution and Mechanical Properties of High-Speed Friction Stir Welded Aluminum Alloy Thin Plate Joints

Sound friction stir welded (FSW) joints of 6061-T6 aluminum alloy sheets with an 0.8 mm thickness were obtained at conventional speed (2000 rpm, 300 mm/min) and high speed (11,000 rpm, 1500 mm/min). The recrystallization mechanism, precipitate evolution, mechanical properties and fracture behavior were investigated in detail. Microstructure analyses revealed that the grain structure evolution in the nugget zone (NZ) was dominated by continuous dynamic recrystallization. In the process of FSW, high speed facilitates the formation of finer equiaxed recrystallized grains, higher density of dislocations and substructures, and a larger number of precipitates in the NZ compared to the conventional speed, which further significantly improves the hardness and tensile strength of the joints. The maximum tensile strength was obtained with 292.6 MPa, 83.2% for the 6061-T6 aluminum alloy and 122.6% for the conventional-speed FSW joints. This work provides an effective method for preparing FSW aluminum alloy thin plate joints with excellent mechanical properties.

36 MATERIALS SCIENCE↗
DOE OSTI2022

GrainNN: A neighbor-aware long short-term memory network for predicting microstructure evolution during polycrystalline grain formation

High fidelity simulations of grain formation in alloys are an indispensable tool for process-to-mechanical-properties characterization. Such simulations, however, can be computationally expensive as they require fine spatial and temporal discretizations. Their cost becomes an obstacle to parametric studies and ensemble runs and ultimately makes downstream tasks like optimal control and uncertainty quantification challenging. To enable such downstream tasks, we introduce GrainNN, an efficient and accurate reduced-order model for epitaxial grain growth in additive manufacturing conditions. GrainNN is a sequence-to-sequence long-short-term-memory (LSTM) deep neural network that evolves the dynamics of manually crafted features. Its innovations are (1) an attention mechanism with grain-microstructure-specific transformer architecture; and (2) an overlapping combination of several clones of the network to generalize to grain configurations that are different from those used for training. This design enables GrainNN to predict grain formation for unseen physical parameters, grain number, domain size and geometry. Furthermore, GrainNN not only reconstructs the quantities of interest but also can be pointwise accurate. In our numerical experiments, we use a polycrystalline phase field method to both generate the training data and assess GrainNN. For multiparametric, ensemble simulations with many grains, GrainNN can be orders of magnitude faster than phase field simulations, while delivering 5%–15% pointwise error. Additionally, this speedup includes the cost of the phase field simulations for generating training data.

36 MATERIALS SCIENCE↗
DOE OSTI2022

Microstructural evolution and precipitation in γ-LiAlO 2 during ion irradiation

Polycrystalline γ-LiAlO 2 pellets were sequentially irradiated with 120 keV He + and 80 keV D 2 + ions to the fluences of 1 × 10 17 and 2 × 10 17 (He + + D + )/cm 2 at 573 K. Additional irradiation was performed to a fluence of 2 × 10 17 (He + + D + )/cm 2 at 773 K. The irradiated pellets were characterized using scanning transmission electron microscopy, time-of-flight secondary ion mass spectrometry, and grazing incidence x-ray diffraction. Lattice damage, amorphization, and fractures are observed with no evidence for the formation of secondary-phase precipitates in the pellets irradiated up to an ion fluence of 2 × 10 17 (He + + D + )/cm 2 at 573 K. In contrast, faceted precipitates with sizes larger than 100 nm formed in a pellet irradiated to 2 × 10 17 (He + + D + )/cm 2 at 773 K. Analyses of the diffraction and composition data suggest that the precipitates have a spinel-type structure, likely a non-stoichiometric LiAl 5 O 8 with Li depletion. This could be an intermediate phase with Li atoms at the octahedral and possibly tetrahedral sites as well. It is speculated that as the dose increases, Li loss will continue and the precipitates will approach a composition of alumina primarily in phases of α-Al 2 O 3 and amorphized Al 2 O 3 .

38 RADIATION CHEMISTRY, RADIOCHEMISTRY, AND NUCLEA↗
DOE OSTI2018

Evolution of microstructure and microtexture during hot deformation in an advanced P/M nickel base superalloy

Highlights: • Microstructural evolution of PM superalloy sensitive to temperature and strain rate. • Highest DRX with finer grained structure at higher temperatures and strain rates. • Dominance of DDRX showed by serrated grain boundaries and misorientation gradient. • Weak microtextural evolution inclined towards [110] fiber compression texture seen. In the present study, the effect of hot deformation parameters on the microstructural evolution is investigated for an experimental powder metallurgy nickel superalloy. The hot isostatically pressed (HIPed) alloy is isothermally hot compressed at constant true strain rate over wide temperatures (1000 °C, 1050 °C, 1100 °C, 1150 °C) and strain rates (0.001 s{sup −1}, 0.01 s{sup −1}, 0.1 s{sup −1}, 1 s{sup −1}) regimes. Electron Back-Scattered Diffraction (EBSD) characterization of the hot deformed samples is carried out to evaluate the microstructural evolution, grain boundary characteristics, and microtextural behaviour. The strong dependence of dynamic recrystallization characteristics on the hot deformation conditions is divulged through EBSD derived colour inverse pole figure maps endorsed by grain/twin boundary characteristics and misorientation gradient. Dynamic recrystallization (DRX) is maximized at higher deformation temperatures, whereas limited DRX is observed at lower deformation temperatures, especially at higher strain rates. The dominance of discontinuous dynamic recrystallization (DDRX) is manifested through bulged/serrated grain boundaries resulting in the formation of necklace microstructure corroborated by grain boundary cumulative misorientation gradient. Although random microtexture is revealed in both deformed and recrystallized microstructures, the tendency towards the formation of 110 fiber compression texture is apparently evident.

36 MATERIALS SCIENCE↗
DOE OSTI2019

Effect of Heat Treatment on Microstructure Evolution and Mechanical Properties of Selective Laser Melted Inconel 718 Alloy

The microstructure characteristics of the selective laser melted Inconel 718 alloy under as-deposited, homogenization + solution + aging (HSA) and solution + aging (SA) conditions were studied. The anisotropy and heterogeneity of mechanical properties under different conditions were also investigated. Under the as-deposited condition, the morphology and size of the grains are heterogeneous. The dendrite structures which grow nearly perpendicular to the molten pool traces, accompanying interdendritic Laves phase, can be observed within the grains. The dendrite structure completely disappeared, and the Laves phases embedded in the interdendritic regions also dissolved into the matrix to precipitate γ′ and γ″ phases after heat treatments. Fully recrystallized grains were obtained under the HSA condition, while only incomplete recrystallized grains were obtained under the SA condition. However, the characteristics of γ′ and γ″ phases are very similar under the HSA and SA conditions. Significant improvement in strength after heat treatments was due to the dissolution of undesirable Laves phase and the precipitation of γ′ and γ″ phases. For all the three conditions, different tensile properties were observed depending on the orientation of the specimens. The scatter of mechanical properties is notable, and heat treatments increased the scatter of mechanical properties.

36 MATERIALS SCIENCE↗
DOE OSTI2018

Microstructure evolution of T91 irradiated in the BOR60 fast reactor

In this paper, microstructures of T91 neutron irradiated in the BOR60 reactor at five temperatures between 376 °C and 524 °C to doses between 15.4 and 35.1 dpa were characterized using transmission electron microscopy (TEM), scanning transmission electron microscopy (STEM), and atom probe tomography (APT). Type a<100> dislocation loops were observed at 376–415 °C and network dislocations dominated at 460 °C and 524 °C. Cavities appeared in a bimodal distribution with a high density of small bubbles less than 2 nm at irradiation temperatures between 376 °C and 415 °C. Small bubbles were also observed at 460 °C and 524 °C but cavities greater than 2 nm were absent. Enrichment of Cr, Ni, and Si at the grain boundary was observed at all irradiation temperatures. Radiation-induced segregation (RIS) of Cr, Ni and Si appeared to saturate at 17.1 dpa and 376 °C. The temperature dependence of RIS of Cr, Ni and Si at the grain boundary, which showed a peak Cr enrichment temperature of 460 °C and a lower peak Ni and Si enrichment temperature of ~400 °C, was consistent with observations of RIS of Cr in proton irradiated T91, suggesting that the same RIS mechanism may also apply to BOR60 irradiated T91. G-phase and Cu-rich precipitates were observed at 376–415 °C but were absent at 460 °C and 524 °C. Finally, the absence of G-phase at 524 °C could be related to the minimal segregation of Ni and Si in that condition.

22 GENERAL STUDIES OF NUCLEAR REACTORS↗
DOE OSTI2019

Influence of Single-Point Incremental Force Process Parameters on Forming Characteristics and Microstructure Evolution of AA-6061 Alloy Sheet

Single-point incremental forming (SPIF) process comprises a set of process variables, such as forming tool diameter, vertical pitch, spindle rotation speed, and tool velocity, which may affect the forming behavior of the sheet to be deformed. The objective of this work is to study the effect of SPIF process parameters on forming characteristics and microstructure development for the AA-6061 (T6) aluminum alloy sheet. The SPIF experiments and finite element (FE) simulations were performed at different process parameters to achieve conical shapes from the AA-6061 blanks. The effect of process parameters on forming forces, thickness uniformity in wall region of the cone and surface roughness of the blank was analyzed. A detailed microstructure study was performed to analyze the effect of process variables on microstructure and texture evolution during the SPIF process. This study reveals that the process parameters are likely to influence the texture development especially at high tool diameter and vertical pitch values. Therefore, suitability and consequences of using different combinations of tool diameter and vertical pitch values are discussed for AA-6061 alloy.

36 MATERIALS SCIENCE↗
DOE OSTI2016

A variational treatment of material configurations with application to interface motion and microstructural evolution

We present a unified variational treatment of evolving configurations in crystalline solids with microstructure. The crux of our treatment lies in the introduction of a vector configurational field. This field lies in the material, or configurational, manifold, in contrast with the traditional displacement field, which we regard as lying in the spatial manifold. We identify two distinct cases which describe (a) problems in which the configurational field's evolution is localized to a mathematically sharp interface, and (b) those in which the configurational field's evolution can extend throughout the volume. The first case is suitable for describing incoherent phase interfaces in polycrystalline solids, and the latter is useful for describing smooth changes in crystal structure and naturally incorporates coherent (diffuse) phase interfaces. These descriptions also lead to parameterizations of the free energies for the two cases, from which variational treatments can be developed and equilibrium conditions obtained. For sharp interfaces that are out-of-equilibrium, the second law of thermodynamics furnishes restrictions on the kinetic law for the interface velocity. The class of problems in which the material undergoes configurational changes between distinct, stable crystal structures are characterized by free energy density functions that are non-convex with respect to configurational strain. For physically meaningful solutions and mathematical well-posedness, it becomes necessary to incorporate interfacial energy. This we have done by introducing a configurational strain gradient dependence in the free energy density function following ideas laid out by Toupin (Arch. Rat. Mech. Anal., 11, 1962, 385-414). The variational treatment leads to a system of partial differential equations governing the configuration that is coupled with the traditional equations of nonlinear elasticity. The coupled system of equations governs the configurational change in crystal structure, and elastic deformation driven by elastic, Eshelbian, and configurational stresses. As a result, numerical examples are presented to demonstrate interface motion as well as evolving microstructures of crystal structures.

36 MATERIALS SCIENCE↗
DOE OSTI2020

Microstructural evolution of a silicon carbide-carbon coated nanostructured ferritic alloy composite during in-situ Kr ion irradiation at 300°C 450°C

This work focuses on irradiation behaviors of a novel silicon carbide and carbon coated nanostructured ferritic alloy (SiC-C@NFA) composite for potential applications as a cladding and structural material for next generation nuclear reactors. The SiC-C@NFA samples were irradiated with 1 MeV Kr ions up to 10 dpa at 300 and 450 °C. Microstructures and defect evolution were studied in-situ at the IVEM-Tandem facility at Argonne National Laboratory. The effects of ion irradiation on various phases such as α-ferrite matrix, (Fe,Cr) 7 C 3 , and (Ti,W)C precipitates were evaluated. The α-ferrite matrix showed a continuous increase in dislocation density along with spatial ordering of dislocation loops (or loop strings) at >5 dpa. The size of the dislocation loops at 450 °C was larger than that at 300 °C. The nucleation and growth of new (Ti,W)C precipitates in α-ferrite grains were enhanced with the ion dose at 450 °C. This study provides new insight into the irradiation resistance of the SiC-C@NFA system.

(FeCr)(7)C-3↗
DOE OSTI2019

Investigation of the mechanical and microstructural evolution of a Cu based bulk metallic glass during ion irradiation

Ion irradiation and annealing experiments were performed on Cu 60 Zr 20 Hf 10 Ti 10 bulk metallic glass (BMG) specimens to investigate their irradiation- and temperature-induced microstructural and mechanical property evolution. For the ion irradiations, samples were exposed to 9 MeV Ni 3+ ions to a midrange (~1.2 μm depth) dose of 10 displacements per atom (dpa) at temperatures ranging from room temperature to 360 °C (the corresponding peak dose at ~2.8 μm depth was ~25 dpa). Bulk X-ray diffraction (XRD) and transmission electron microscopy (TEM) characterization revealed that the alloy did not crystallize during irradiation up to 290 °C but did partially crystallize at 360 °C. XRD analysis revealed that the crystallization which occurred in the sample irradiated at 360 °C was caused by thermal effects instead of irradiation displacement damage. Subsequent Rietveld refinement analysis of the XRD measurements revealed the presence of two distinct crystal phases, namely a CuTiZr hexagonal structure belonging to the P63/mmc space group and a CuTi tetragonal structure belonging to the P4/mmm space group. Nanoindentation experiments revealed that no pronounced hardness changes occurred in the specimens irradiated at room temperature and 290°C, although significant hardening was observed in the sample irradiated at 360 °C. The significant increase in the hardness at 360°C was ascribed to thermally induced partial crystallization of the alloy instead of the ion irradiation. In general, the results of the nanoindentation experiments and XRD characterization suggest that although the Cu BMG exhibits good stability during irradiation at temperatures up to 290 °C it is not suitable for irradiation environments where the temperature is 360 °C for extended periods of time. The Lam and Chong extrapolation method, which has been used to study the indentation size effect (ISE) in amorphous alloys, was employed to quantify how irradiation and temperature affect this type of behavior in the BMG. However, the poor linear fitting of the indentation hardness data by this model indicate that a new ISE model is likely needed to quantify indentation hardening in BMGs.

36 MATERIALS SCIENCE↗
DOE OSTI2017

Microstructural evolution in Fe-20Cr-25Ni austenitic alloys under proton irradiation at 670 ºC

Austenitic stainless steels (SSs) are widely used in different components of nuclear plants. The NF709 (20Cr-25Ni-1.5MoTiNb) class of alloy was recently selected for development as a candidate structural material for sodium-cooled fast reactors due to its improved creep and corrosion resistance compared with 300-series austenitic SSs. This requires new understanding of the radiation response of the 709 class alloys. In this study, we correlated the mechanical changes with the proton-induced microstructural and chemical evolutions of a 20Cr-25Ni model alloy M709 and a 20Cr-25Ni-1.5MoNb alloy A709. The irradiation was conducted using 2 MeV protons at 670 ± 20 ºC to achieve 1.5 displacements per atom (dpa) at the middle of the proton project range. Sample characterization was achieved using nanoindentation, focused ion beam (FIB), scanning electron microscopy (SEM), energy-dispersive X-ray spectroscopy (EDS) and transmission electron microscopy techniques (TEM).

Chen, Tianyi↗