NASA NTRS1990

Influence of interfacial shear strength on the mechanical properties of SiC fiber reinforced reaction-bonded silicon nitride matrix composites

The influence of fiber/matrix interface microstructure and interfacial shear strength on the mechanical properties of a fiber-reinforced ceramic composite was evaluated. The composite consisted of approximately 30 vol percent uniaxially aligned 142 microns diameter SiC fibers (Textron SCS-6) in a reaction-bonded Si3N4 matrix (SiC/RBSN). The interface microstructure was varied by controlling the composite fabrication conditions and by heat treating the composite in an oxidizing environment. Interfacial shear strength was determined by the matrix crack spacing method. The results of microstructural examination indicate that the carbon-rich coating provided with the as-produced SiC fibers was stable in composites fabricated at 1200 C in a nitrogen or in a nitrogen plus 4 percent hydrogen mixture for 40 hr. However this coating degraded in composites fabricated at 1350 C in N2 + 4 percent H2 for 40 and 72 hr and also in composites heat treated in an oxidizing environment at 600 C for 100 hr after fabrication at 1200 C in a nitrogen. It was determined that degradation occurred by carbon removal which in turn had a strong influence on interfacial shear strength and other mechanical properties. Specifically, as the carbon coating was removed, the composite interfacial shear strength, primary elastic modulus, first matrix cracking stress, and ultimate tensile strength decreased, but the first matrix cracking strain remained nearly the same.

Bhatt, Ramakrishna T.↗
NASA NTRS1989

Microstructural changes in beta-silicon nitride grains upon crystallizing the grain-boundary glass

Crystallizing the grain-boundary glass of a liquid-phase-sintered Si3N4 ceramic for 2 h or less at 1500 C led to formation of delta-Y2Si2O7. After 5 h at 1500 C, the delta-Y2Si2O7 had transformed to beta-Y2Si2O7 with a concurrent dramatic increase in dislocation density within beta-Si3N4 grains. Reasons for the increased dislocation density are discussed. Annealing for 20 h at 1500 C reduced dislocation densities to the levels found in as-sintered material.

Lee, William E.↗
NASA NTRS1990

Burner rig hot corrosion of silicon carbide and silicon nitride

A number of commercially available SiC and Si3N4 materials were exposed to 1000 C for 40 h in a high-velocity, pressurized burner rig as a simulation of an aircraft turbine environment. Na impurities (2 ppm) added to the burner flame resulted in molten Na2SO4 deposition, attack of the SiC and Si3N4, and formation of substantial Na2O+x(SiO2) corrosion product. Room-temperature strength of the materials decreased as a result of the formation of corrosion pits in SiC and grain-boundary dissolution and pitting in Si3N4.

Fox, Dennis S.↗
NASA NTRS1990

Active-to-passive transition in the oxidation of silicon carbide and silicon nitride in air

The active-to-passive transition in the oxidation of SiC and Si3N4 was determined in a flowing air environment as a function of temperature and total pressure. The experimentally observed transition temperatures ranged from a low of 1347 C to a high of 1543 C for partial pressures of oxygen of 2.5 and 123.2 Pa, respectively. The SiC and Si3N4 samples had approximately the same transition point for a given pressure. In general, the higher the flow rate, the higher the transition temperature for a given pressure. The transitions for SiC measured in this study agree with previous data for the transition of SiC measured in pure oxygen at reduced pressures and in oxygen inert gas mixtures.

Vaughn, Wallace L.↗
NASA NTRS1990

Thermal effects on the mechanical properties of SiC fibre reinforced reaction-bonded silicon nitride matrix composites

The elevated temperature four-point flexural strength and the room temperature tensile and flexural strength properties after thermal shock were measured for ceramic composites consisting of 30 vol pct uniaxially aligned 142 micron diameter SiC fibers in a reaction bonded Si3N4 matrix. The elevated temperature strengths were measured after 15 min of exposure in air at temperatures to 1400 C. Thermal shock treatment was accomplished by heating the composite in air for 15 min at temperatures to 1200 C and then quenching in water at 25 C. The results indicate no significant loss in strength properties either at temperature or after thermal shock when compared with the strength data for composites in the as-fabricated condition.

Bhatt, R. T.↗
NASA NTRS1991

Microstructural changes in Beta-silicon nitride grains upon crystallizing the grain-boundary glass

Crystallizing the grain boundary glass of a liquid phase sintered Si3N4 ceramic for 2 h or less at 1500 C led to formation of gamma Y2Si2O7. After 5 h at 1500 C, the gamma Y2Si2O7 had transformed to beta Y2Si2O7 with a concurrent dramatic increase in dislocation density within beta Si3N4 grains. Reasons for the increased dislocation density is discussed. Annealing for 20 h at 1500 C reduced dislocation densities to the levels found in as-sintered materials.

Lee, William E.↗
NASA NTRS1991

Indirect measurement of the viscosity of the intergranular glass phase in yttria-sintered silicon nitride

Dense, sintered Si3N4 possesses a residual intergranular glass phase which softens at high temperatures, resulting in degradation of the ceramic's mechanical properties at high temperatures. An important parameter in the determination of the high temperature mechanical properties of sintered Si3N4 is the temperature-viscosity relationship of the intergranular glass. A method for indirectly measuring the intergranular glass viscosity at a given temperature using physical modelling of a two phase glass crystal microstructure and beam bending viscometry measurements of Si3N4 is described. Intergranular glass viscosities obtained by this method are presented for a yttria sintered Si3N4.

Dittmar, Mark B.↗
NASA NTRS1991

Crack healing in silicon nitride due to oxidation

The crack healing behavior of a commercial, MgO-containing, hot pressed Si3N4 was studied as a function of temperature in oxidizing and inert annealing environments. Crack healing occurred at a temperature 800 C or higher due to oxidation regardless of crack size, which ranged from 100 microns (indentation crack) to 1.7 mm (SEPB precrack). The resulting strength and apparent fracture toughness increased at crack healing temperature by 100 percent and 300 percent, respectively. The oxide layer present in the crack plane was found to be highly fatigue resistant, indicating that the oxide is not solely silicate glass, but a mixture of glass, enstatite, and/or cristobalite that was insensitive to fatigue in a room temperature water environment.

Choi, Sung R.↗
NASA NTRS1990

Influence of interfacial shear strength on the mechanical properties of SiC fiber reinforced reaction-bonded silicon nitride matrix composites

An evaluation is made of the influence of interfacial microstructure and shear strength on the mechanical properties of a 30 vol pct uniaxially-aligned SiC fiber-reinforced reaction-bonded Si3N4-matrix composite whose interface microstructure was varied through control of fabrication conditions and by heat-treatment in an oxidizing environment. The carbon-rich coating of the as-produced SiC fibers was stable in composites fabricated at 1200 C in an N or N + 4-percent H mixture for 40 hrs. This coating was degraded in composites fabricated at 1350 C in N + 4 percent H for 40 and 72 hrs, as well as after heat-treatment in an oxidizing environment at 600 C for 100 hrs even after fabrication at 1200 C in N. This degradation occurred via carbon removal.

Bhatt, Ramakrishna T.↗
NASA NTRS1992

Role of interfacial thermal barrier in the transverse thermal conductivity of uniaxial SiC fiber-reinforced reaction bonded silicon nitride

The transverse thermal conductivity of reaction-bonded Si3N4 is significantly affected by an interfacial barrier at the interface formed with SiC reinforcing fibers. A comparative study of composites with and without reinforcing-fiber carbon coatings found the coating to reduce effective thermal conductivity by a factor of about 2; this, however, is partially due to a thermal expansion-mismatch gap between fiber and matrix. HIPing of composites with coated fibers led to an enhancement of thermal conductivity via improved interfacial thermal contact and greater grain size and crystallinity of the fibers.

Bhatt, H.↗
NASA NTRS1992

Oxidation kinetics of CVD silicon carbide and silicon nitride

The long-term oxidation behavior of pure, monolithic CVD SiC and Si3N4 is studied, and the isothermal oxidation kinetics of these two materials are obtained for the case of 100 hrs at 1200-1500 C in flowing oxygen. Estimates are made of lifetimes at the various temperatures investigated. Parabolic rate constants for SiC are within an order of magnitude of shorter exposure time values reported in the literature. The resulting silica scales are in the form of cristobalite, with cracks visible after exposure. The oxidation protection afforded by silica for these materials is adequate for long service times under isothermal conditions in 1-atm dry oxygen.

Fox, Dennis S.↗
NASA NTRS1998

Liquid hydrogen testing of silicon nitride bearings for use in high speed turbomachinery

Hybrid ceramic rolling element bearings are being tested in liquid hydrogen at Marshall Space Flight Center. The testing will evaluate their long term durability for use at high speeds in cryogenic rocket engine turbomachinery. The use of hybrid ceramic bearings in liquid hydrogen follows successful development and flight in liquid oxygen turbopumps.

Moore, Chip↗
NASA NTRS1998

Liquid Hydrogen Testing of Silicon Nitride Bearings for Use In High Speed Turbomachinery

Hybrid ceramic rolling element bearings are being tested in liquid hydrogen at Marshall Space Flight Center. The testing will evaluate their long term durability for use at high speeds in cryogenic rocket engine turbomachinery. The use of hybrid ceramic bearings in liquid hydrogen follows successful development and flight in liquid oxygen turbopumps.

Moore, Lewis↗
NASA NTRS2000

Internally Cooled Monolithic Silicon Nitride Aerospace Components

A set of rapid prototyping (RP) processes have been combined with gelcasting to make ceramic aerospace components that contain internal cooling geometry. A mold and core combination is made using a MM6Pro (Sanders Prototyping, Inc.) and SLA-250/40 (3Dsystems, Inc.). The MM6Pro produces cores from ProtoBuild (trademarked) wax that are dissolved in room temperature ethanol following gelcasting. The SLA-250/40 yields epoxy/acrylate reusable molds. Parts produced by this method include two types of specimens containing a high density of thin long cooling channels, thin-walled cylinders and plates, as well as a model hollow airfoil shape that can be used for burner rig evaluation of coatings. Both uncoated and mullite-coated hollow airfoils has been tested in a Mach 0.3 burner rig with cooling air demonstrating internal cooling and confirming the effectiveness of mullite coatings.

Best, Jonathan E.↗
NASA NTRS2010

Microstructural and Mechanical Evaluation of a Cu-Based Active Braze Alloy to Join Silicon Nitride Ceramics

Self-joining of St. Gobain Si3N4 (NT-154) using a ductile Cu-Al-Si-Ti active braze (Cu-ABA) was demonstrated. A reaction zone approx.2.5-3.5 microns thick) developed at the interface after 30 min brazing at 1317 K. The interface was enriched in Ti and Si. The room temperature compressive shear strengths of Si3N4/Si3N4 and Inconel/Inconel joints (the latter created to access baseline data for use with the proposed Si3N4/Inconel joints) were 140+/-49MPa and 207+/-12MPa, respectively. High-temperature shear tests were performed at 1023K and 1073 K, and the strength of the Si3N4/Si3N4 and Inconel/Inconel joints were determined. The joints were metallurgically well-bonded for temperatures above 2/3 of the braze solidus. Scanning and transmission electron microscopy studies revealed a fine grain microstructure in the reaction layer, and large grains in the inner part of the joint with interfaces being crack-free. The observed formation of Ti5Si3 and AlN at the joint interface during brazing is discussed.

Singh, M.↗