NASA NTRS1982

Strength advantages of chemically polished boron fibers before and after reaction with aluminum

In order to determine their strength potential, the fracture properties of different types of commercial boron fibers were measured before and after application of secondary strengthening treatments. The principal treatments employed were a slight chemical polish, which removed low strength surface flaws, and a heat treatment in oxygen, which contracted the fibers and thereby compressed intrinsic bulk flaws. Those fiber types most significantly strengthened were 200 to 400 micrometers (8 to 16 mil) diameter boron on tungsten fibers produced in a single chemical vapor deposition reactor. The slight polish increased average tensile strenghts from 3.4 to 4.4 CN/m2 (500 to 640 ksi) and reduced coefficients of variation from about 15 to 3 percent. The oxygen heat treatment plus slight polish further improved average strengths to 5.5 GN/m2 (800 ksi) with coefficients near 3 percent. To ascertain whether these excellent properties could be retained after fabrication of B/Al composites, as produced and polished 203 micrometers (8 mil) fibers were thinly coated with aluminum, heat treated at B/Al fabrication temperatures, and then tested in tension and flexure at room temperature. The pre-polished fibers were observed to retain their superior strengths to higher temperatures than the as-produced fibers even though both were subjected to the same detrimental reaction with aluminum.

Dicarlo, J. A.↗

NASA NTRS1982

Prediction of residual tensile strength of transversely impacted composite laminates

The response to low velocity impact of graphite-epoxy T300/5208 composite laminates is discussed. Steel balls of 3/8 inch, 5/8 inch, and 1 inch diameter were the projectiles. Impact energy was limited to 1.2 joules. Impacted specimens were ultrasonically C scanned to determine the impact damaged region. The threshold value of impact energy for impact damage was found to be approximately 0.3 joules. A model was developed to predict the tensile residual strength of impact damaged specimens from fracture mechanics concepts. Impacted specimens were tested in tension to provide a fracture data base. The experimental results agreed well with the predictions from fracture mechanics. In this study, the maximum impact velocity used to simulate the low velocity transverse impact from common objects like tool drops was 10 m/s.

Lal, K. M.↗

NASA NTRS1982

High temperature composites for advanced missile and space transportation systems

A study has been conducted to characterize a state-of-the-art graphite/polyimide composite system by determining mechanical and thermophysical properties of selected laminates over a temperature range of -250 F to 600 F. The material studied was Celion 3000/PMR-15. Material property data obtained from testing included tension, compression and shear strengths, and coefficient of thermal expansion. Environmental conditions examined were: as cured/post-cured, isothermal aged at 600 F, thermal cycled from -250 F to 600 F, and moisture conditioned. This study has provided an initial data base on a graphite/polyimide composite system capable of operating in 500/600 F applications.

Mccleskey, S. F.↗

NASA NTRS1984

Influence of soft inclusions on the strength of wrought materials

The three dimensional soft particles (such as sulfides, silicates and voids) present in most materials are modelled by circular voids in sheet metal. Relationships are sought between the shape and orientation of a hole after rolling and testing in tension. Then, the effect of hole shape and size on mechanical properties is considered experimentally. The presence of voids has a negligible influence on the ultimate tensile stress of ductile materials based on the unperforated area because plastic flow neutralizes the stress intensification present in the elastic region. However, the shape and orientation of the defects are found to play an important role relative to strain at fracture. In certain engineering applications the strain at fracture is more important than the stress at fracture and in this sense the presence of voids are considered to influence the strength of a ductile material.

Pai, D. M.↗

NASA NTRS1985

Fatigue of graphite/epoxy buffer strip panels with center cracks

The effects of fatigue loading on the behavior of graphite/epoxy panels with either S-Glass or Kevlar-49 buffer strips is studied. Buffer strip panels are fatigued and tested in tension to measure their residual strength with crack-like damage. Panels are made with 45/0/-45/90 sub 2s layup with either S-Glass or Kevlar-49 buffer strip material. The buffer strips are parallel to the loading direction and made by replacing narrow strips of the 0-degree graphite plies with strips of either 0-degree S-Glass/epoxy or Kevlar-49/epoxy on a one-for-one basis. The panels are subjected to a fatigue loading spectrum MINITWIST, the shortened version of the standardized load program for the wing lower surface of a transport aircraft. Two levels of maximum strain are used in the spectrum with three durations of the fatigue spectrum. One group of panels is preloaded prior to the application of the fatigue cycling. The preload consists of statistically loading the spectrum in tension until the crack-tip damage zone reaches the ajacent buffer strips. After fatigue loading, all specimens are statistically loaded in tension to failure to determine their residual strengths.

Bigelow, C. A.↗

NASA NTRS1985

Improved stud configurations for attaching laminated wood wind turbine blades

A series of bonded stud design configurations was screened on the basis of tension-tension cyclic tests to determine the structural capability of each configuration for joining a laminated wood structure (wind turbine blade) to a steel flange (wind turbine hub). Design parameters which affected the joint strength (ultimate and fatigue) were systematically varied and evaluated through appropriate testing. Two designs showing the most promise were used to fabricate addiate testing. Two designs showing the most promise were used to fabricate additional test specimens to determine ultimate strength and fatigue curves. Test results for the bonded stud designs demonstrated that joint strengths approaching the 10,000 to 12,000 psi ultimate strength and 5000 psi high cycle fatigue strength of the wood epoxy composite could be achieved.

Fadoul, J. R.↗

NASA NTRS1986

Fracture mechanics of matrix cracking and delamination in glass/epoxy laminates

This study focused on characterizing matrix cracking and delamination behavior in multidirectional laminates. Static tension and tension-tension fatigue tests were conducted on two different layups. Damage onset, accumulation, and residual properties were measured. Matrix cracking was shown to have a considerable influence on residual stiffness of glass epoxy laminates, and could be predicted reasonably well for cracks in 90 deg piles using a simple shear lag analysis. A fracture mechanics analysis for the strain energy release rate associated with 90 deg ply-matrix crack formation was developed and was shown to correlate the onset of 90 deg ply cracks in different laminates. The linear degradation of laminate modulus with delamination area, previously observed for graphite epoxy laminates, was predicted for glass epoxy laminates using a simple rule of mixtures analysis. The strain energy release rate associated with edge delamination formation under static and cyclic loading was difficult to analyze because of the presence of several contemporary damage phenomena.

Caslini, M.↗

NASA NTRS1986

Orientation and temperature dependence of some mechanical properties of the single-crystal nickel-base superalloy Rene N4. I - Tensile behavior

Single crystal specimens of a nickel-base superalloy with axes near 001, 011, and -112 were tested in tension at room temperature, 760, and 980 C. The alloy Rene N-4, was developed for gas turbine engine blades and has the nominal composition 3.7 Al, 4.2 Ti, 4 Ta, 0.5 Nb, 6 W, 1.5 Mo, 9 Cr, 7.5 Co, balance Ni, (all in weight percent). Analysis of slip band traces, specimen axis rotation, and dislocation Burgers vectors showed that at 760 and 980 C primary cube slip supplanted normal octahedral slip for the -112 line-oriented specimens. The other two orientations, which have lower resolved shear stresses on the cube system, exhibited octahedral slip at all three temperatures. The critical resolved shear stress is considerably greater on the cube system than on the octahedral system at room temperature. However, at 760 and 980 C the critical resolved shear stresses on the two systems are about the same. While the room temperature and 980 C yield strengths for the two orientations exhibiting octahedral slip could be rationalized on the basis of resolved shear stress, those at 760 C could not. Such violations of Schmid's law have previously been observed in other superalloys and single phase gamma-prime.

Miner, R. V.↗

NASA NTRS1987

Frequency and load ratio effects on critical strain energy release rate Gc thresholds of graphite/epoxy composites

Graphite/epoxy composite laminates of T300/BP907 and AS6/HST-7 were axial-tension fatigue tested. Tests were conducted at 5 and 10 Hz, and at loading ratios of R = 0.1 and R = 0.5. Edge delamination was monitored as a function of number of fatigue cycles by monitoring stiffness reduction during fatigue testing. Delamination was confirmed and documented using dye-enhanced X-ray and optical photography. Critical strain energy release rates were then calculated. The composites delaminated readily, with loading ratio having a significant influence. Frequency effects were negligible.

Adams, Donald F.↗

NASA NTRS1987

Study of matrix cracking and delamination in glass/epoxy laminates

Caslini, Massimo↗

NASA NTRS1988

Tension fatigue analysis and life prediction for composite laminates

A tension fatigue life prediction methodology for composite laminates is presented. Tension fatigue tests were conducted on quasi-isotropic and orthotropic glass epoxy, graphite epoxy, and glass/graphite epoxy hybrid laminates. Edge delamination onset data were used to generate plots of strain energy release rate as a function of cycles to delamination onset. These plots were then used along with strain energy release rate analyses of delaminations initiating at matrix cracks to predict local delamination onset. Stiffness loss was measured experimentally to account for the accumulation of matrix cracks and for delamination growth. Fatigue failure was predicted by comparing the increase in global strain resulting from stiffness loss to the decrease in laminate failure strain resulting from delaminations forming at matrix cracks through the laminate thickness. Good agreement between measured and predicted lives indicated that the through-thickness damage accumulation model can accurately describe fatigue failure for laminates where the delamination onset behavior in fatigue is well characterized, and stiffness loss can be monitored in real time to account for damage growth.

Obrien, T. K.↗

NASA NTRS1986

Constitutive modelling of single crystal and directionally solidified superalloys

The trend towards improved engine efficiency and durability places increasing demands on materials that operate in the hot section of the gas turbine engine. These demands are being met by new coatings and materials such as single crystal and directionally solidified nickel-base superalloys which have greater creep/fatigue resistance at elevated temperatures and reduced susceptibility to grain boundary creep, corrosion and oxidation than conventionally cast alloys. Work carried out as part of a research program aimed at the development of constitutive equations to describe the elevated temperature stress-strain-time behavior of single crystal and directionally solidified turbine blade superalloys is discussed. The program involves both development of suitable constitutive models and their verification through elevated temperature tension-torsion testing of single crystals of PWA 1480.

Jordan, E. H.↗

NASA NTRS1990

Damage tolerance of woven graphite-epoxy buffer strip panels

Graphite-epoxy panels with S glass buffer strips were tested in tension and shear to measure their residual strengths with crack-like damage. The buffer strips were regularly spaced narrow strips of continuous S glass. Panels were made with a uniweave graphite cloth where the S glass buffer material was woven directly into the cloth. Panels were made with different width and thickness buffer strips. The panels were loaded to failure while remote strain, strain at the end of the slit, and crack opening displacement were monitoring. The notched region and nearby buffer strips were radiographed periodically to reveal crack growth and damage. Except for panels with short slits, the buffer strips arrested the propagating crack. The strength (or failing strain) of the panels was significantly higher than the strength of all-graphite panels with the same length slit. Panels with wide, thick buffer strips were stronger than panels with thin, narrow buffer strips. A shear-lag model predicted the failing strength of tension panels with wide buffer strips accurately, but over-estimated the strength of the shear panels and the tension panels with narrow buffer strips.

Kennedy, John M.↗

NASA NTRS1989

Tension fatigue analysis and life prediction for composite laminates

A methodology is presented for the tension fatigue analysis and life prediction of composite laminates subjected to tension fatigue loading. The methodology incorporates both the generic fracture mechanics characterization of delamination and the assessment of the infuence of damage on laminate fatigue life. Tension fatigue tests were conducted on quasi-isotropic and orthotropic glass epoxy, graphite epoxy, and glass/graphite epoxy hybrid laminates, demonstrating good agreement between measured and predicted lives.

O'Brien, T. K.↗

NASA NTRS1991

Local delamination in laminates with angle ply matrix cracks. Part 2: Delamination fracture analysis and fatigue characterization

Constant amplitude tension-tension fatigue tests were conducted on AS4/3501-6 graphite/epoxy (02/ theta sub 2/ -(theta sub 2))sub s laminates, where theta was 15, 20, 25, or 30 degrees. Fatigue tests were conducted at a frequency of 5 Hz and an R-ratio of 0.1. Dye penetrant enhanced x-radiography was used to document the onset of matrix cracking in the central -(theta) degree plies, and the subsequent onset of local delaminations in the theta/ -(theta) interface at the intersection of the matrix cracks and the free edge, as a function of the number of fatigue cycles. Two strain energy release rate solutions for local delamination from matrix cracks were derived: one for a local delamination growing from an angle ply matrix crack with a uniform delamination growing from an angle ply matrix crack with a triangular shaped delamination area that extended only partially into the laminate width from the free edge. Plots of G(max) vs. N were generated to assess the accuracy of these G solutions. The influence of residual thermal and moisture stresses on G were also quantified. However, a detailed analysis of the G components and a mixed-mode fatigue failure criterion for this material may be needed to predict the fatigue behavior of these laminates.

Obrien, T. Kevin↗

NASA NTRS1992

A viscoplastic model for single crystals

A viscoplastic constitutive model is described in which deformation behavior is postulated on representative slip systems and the behavior of the entire crystal is determined by summing the slip on the active slip systems. By building in the slip geometry known from the metallurgical literature, it is possible to predict the anisotropic deformation behavior and to model in a straightforward manner other phenomena which have been described by metallurgists in crystallographic terms. Elevated temperature tension-torsion tests were run and used to verify the model's predictive abilities. Ratchetting behavior under thermomechanical loading conditions is specifically addressed.

Jordan, E. H.↗

NASA NTRS1993

Damage tolerance and arrest characteristics of pressurized graphite/epoxy tape cylinders

An investigation of the damage tolerance and damage arrest characteristics of internally-pressurized graphite/epoxy tape cylinders with axial notches was conducted. An existing failure prediction methodology, developed and verified for quasi-isotropic graphite/epoxy fabric cylinders, was investigated for applicability to general tape layups. In addition, the effect of external circumferential stiffening bands on the direction of fracture path propagation and possible damage arrest was examined. Quasi-isotropic (90/0/plus or minus 45)s and structurally anisotropic (plus or minus 45/0)s and (plus or minus 45/90)s coupons and cylinders were constructed from AS4/3501-6 graphite/epoxy tape. Notched and unnotched coupons were tested in tension and the data correlated using the equation of Mar and Lin. Cylinders with through-thickness axial slits were pressurized to failure achieving a far-field two-to-one biaxial stress state. Experimental failure pressures of the (90/0/plus or minus 45)s cylinders agreed with predicted values for all cases but the specimen with the smallest slit. However, the failure pressures of the structurally anisotropic cylinders, (plus or minus 45/0)s and (plus or minus 45/90)s, were above the values predicted utilizing the predictive methodology in all cases. Possible factors neglected by the predictive methodology include structural coupling in the laminates and axial loading of the cylindrical specimens. Furthermore, applicability of the predictive methodology depends on the similarity of initial fracture modes in the coupon specimens and the cylinder specimens of the same laminate type. The existence of splitting which may be exacerbated by the axial loading in the cylinders, shows that this condition is not always met. The circumferential stiffeners were generally able to redirect fracture propagation from longitudinal to circumferential. A quantitative assessment for stiffener effectiveness in containing the fracture, based on cylinder radius, slit size, and bending stiffnesses of the laminates, is proposed.

Ranniger, Claudia U.↗

NASA NTRS1944

Fatigue Strength and Related Characteristics of Joints in 24s-t Alclad Sheet

Report includes tension fatigue test results on the following types of samples of 0.040-inch alclad 24s-t: (1) monoblock sheet samples as received and after a post-aging heat treatment, (2) "sheet efficiency" samples (two equally stressed sheets joined by a single transverse row of spot welds) both as received and after post-aging, (3) spot-welded lap-joint samples as received and after post-aging, and (4) roll-welded lap-joint samples. (author)

Russell, H W↗