NASA NTRS1981

The application of probabilistic design theory to high temperature low cycle fatigue

Metal fatigue under stress and thermal cycling is a principal mode of failure in gas turbine engine hot section components such as turbine blades and disks and combustor liners. Designing for fatigue is subject to considerable uncertainty, e.g., scatter in cycles to failure, available fatigue test data and operating environment data, uncertainties in the models used to predict stresses, etc. Methods of analyzing fatigue test data for probabilistic design purposes are summarized. The general strain life as well as homo- and hetero-scedastic models are considered. Modern probabilistic design theory is reviewed and examples are presented which illustrate application to reliability analysis of gas turbine engine components.

Wirsching, P. H.↗
NASA NTRS1971

Rolling-element fatigue lives of through-hardened bearing materials.

Rolling-element fatigue tests were run with eight through-hardened bearing materials at 150 F. One-half in. dia balls of each material were run in five-ball fatigue testers. Care was taken to maintain constant all variables known to affect rolling-element fatigue life. The longest lives at 150 F were obtained with AISI 52100. Ten-percent lives of the other materials ranged from 7 to 78 percent of that obtained with 52100. A trend is indicated toward decreased rolling-element fatigue life with increased total weight percent of alloying elements. Three groups of 120-mm bore ball bearings made from AISI M-1, AISI M-50, and WB-49 were fatigue tested at an outer-race temperature of 600 F. The 10-percent lives of the M-50 and M-1 bearings exceeded the calculated AFBMA life by factors of 13 and 6, respectively. The bearings with WB-49 races showed lives less than AFBMA life. The results of the bearing tests at 600 F correlate well with the results of the five-ball fatigue data at 150 F.

Parker, R. J.↗
NASA NTRS1975

Determination of structural engineering properties of incoloy 903 and CTX-1 alloys

Tension, notched tension, compression, density, thermal conductivity, and thermal expansion tests were conducted on Incoloy 903 over the temperature range 20 K (-423 F) through 1033 K (1400 F). Fracture toughness tests were performed at room temperature (RT). Creep and rupture tests were conducted at 811 K (1000 F), 922 K (1200 F), and 1033 K (1400 F) for this alloy. Transverse unnotched and notched fatigue tests at R = 0.1 were performed at RT and 922 K (1200 F). For CTX-1 alloy, tension, Charpy V-notch impact, density, thermal conductivity, and thermal expansion tests were conducted over the temperature range 20 K (-423 F) through 1033 K (1400 F). Poisson's ratio was determined at RT, 811 K (1000 F), 922 K (1200 F), and 1033 K (1400 F). Notched tension and compression tests were performed at 20 K (-423 F), RT, and 922 K (1200 F); plane strain fracture toughness tests were conducted at RT, 77 K (-320 F), and 20 K (-423 F). Creep and rupture tests were performed at 811 K (1000 F), 922 K (1200 F), and 1033 K (1400 F); longitudinal unnotched and notched fatigue tests at R = 0.1 were conducted at RT and 922 K (1200 F). Results are presented and discussed.

Ruff, P. E.↗
NASA NTRS1986

Flight service evaluation of composite helicopter components

This report presents an assessment of composite helicopter tail rotor spars and horizontal stabilizers, exposed to the effects of the environment, after up to five and a half years of commercial service. This evaluation is supported by test results of helicopter components and panels which have been exposed to outdoor environmental effects since September 1979. Full scale static and fatigue tests have been conducted on graphite/epoxy and Kevlar/epoxy composite components obtained from Sikorsky Model S-76 helicopters in commercial operations in the Gulf Coast region of Louisiana. Small scale static and fatigue tests are being conducted on coupons obtained from panels under exposure to outdoor conditions in Stratford, Connecticut and West Palm, Florida. The panel layups are representative of the S-76 components. Additionally, this report discusses the results of moisture absorption evaluations and strength tests on the S-76 components and composite panels with up to five years of outdoor exposure.

Mardoian, G. H.↗
DOE OSTI2023

Enhancement in Mechanical Properties of Bulk Nanocrystalline Aluminum by Grain Boundary Strengthening Mechanism

In the present work, commercially pure aluminum (Al) powders were milled at cryogenic temperatures (a) without magnesium (Mg) and (b) with 5 wt.% Mg powders for different durations. The cryomilled powders were analyzed using scanning electron microscopy (SEM), transmission electron microscopy (TEM), and x-ray diffraction (XRD) to determine the changes in particle morphology, elemental composition, and crystallite size. The results showed a reduction in crystallite size with the increase in cryomilling duration. Thereafter, the spark plasma sintering (SPS) process was carried out to manufacture bulk samples. The mechanical properties of the bulk SPS samples were assessed by conducting microhardness, tensile, and fatigue tests. The Vickers microhardness tests showed improved hardness for the Al-Mg bulk samples as compared to pure Al. The Al-Mg samples also showed an increase in tensile strength with increasing cryomilling time. Fatigue test results showed an improvement in Al-Mg components' high-cycle fatigue response. Furthermore, the mechanism for the enhancement in mechanical properties as a result of crystallite size reduction and grain boundary strengthening by the addition of Mg dopant is also discussed.

36 MATERIALS SCIENCE↗
NASA NTRSDate not supplied

Delamination Depth Imaging for Quasi-Static and Fatigue Load Testing Using Passive Thermography

Passive thermography is used to monitor small increases in temperature resulting from delamination damage formation in composite hat-stiffened panels during both quasi-static and fatigue loading. It has been observed that rapid damage formation produces heating. This is composed of two heat generation components. The first component is an instantaneous response due to an irreversible thermoelastic strain release. The second component is mechanical heating, at the interface of failure, due to fracture damage. This produces a transient rise in temperature as the heat diffuses to the surface. The first component defines the thermal start time for the transient response. A one-dimensional thermal model is fitted to the data pixel by pixel, to produce imagery of the damage depth. The results are compared to ultrasonic and X-ray CT data.

Passive thermography↗
NASA NTRS1991

Local delamination in laminates with angle ply matrix cracks. Part 2: Delamination fracture analysis and fatigue characterization

Constant amplitude tension-tension fatigue tests were conducted on AS4/3501-6 graphite/epoxy (02/ theta sub 2/ -(theta sub 2))sub s laminates, where theta was 15, 20, 25, or 30 degrees. Fatigue tests were conducted at a frequency of 5 Hz and an R-ratio of 0.1. Dye penetrant enhanced x-radiography was used to document the onset of matrix cracking in the central -(theta) degree plies, and the subsequent onset of local delaminations in the theta/ -(theta) interface at the intersection of the matrix cracks and the free edge, as a function of the number of fatigue cycles. Two strain energy release rate solutions for local delamination from matrix cracks were derived: one for a local delamination growing from an angle ply matrix crack with a uniform delamination growing from an angle ply matrix crack with a triangular shaped delamination area that extended only partially into the laminate width from the free edge. Plots of G(max) vs. N were generated to assess the accuracy of these G solutions. The influence of residual thermal and moisture stresses on G were also quantified. However, a detailed analysis of the G components and a mixed-mode fatigue failure criterion for this material may be needed to predict the fatigue behavior of these laminates.

Obrien, T. Kevin↗
NASA NTRS1994

Surface Fatigue Life of High Temperature Gear Materials

Three high temperature gear materials were evaluated using spur gear surface fatigue tests. These materials were, VASCO max 350, VASCO matrix 2, and nitralloy N and were evaluated for possible use in high temperature gear applications. The fatigue life of the three high temperature gear materials were compared with the life of the standard AISI 9310 aircraft gear material. Surface fatigue tests were conducted at a lubricant inlet temperature of 321 K (120 F), a lubricant outlet temperature of 350 K (170 F), a maximum Hertz stress of 1.71 GPa (248 ksi), a speed of 10,000 rpm, and with a synthetic paraffinic lubricant. The life of the nitralloy N was approximately the same as the AISI 9310, the life of the VASCO max 350 was much less than the AISI 9310 while the life of the VASCO matrix 2 was several times the life of the AISI 9310. The VASCO max 350 also showed very low fracture toughness with approximately half of the gears failed by tooth fracture through the fatigue spall. The VASCO matrix 2 had approximately 10-percent fracture failure through the fatigue spalls indicating moderate to good fracture toughness.

Townsend, Dennis P.↗
NASA NTRS1981

Effects of ultra-clean and centrifugal filtration on rolling-element bearing life

Fatigue tests were conducted on groups of 65-mm bore diameter deep-groove ball bearings in a MIL-L-23699 lubricant under two levels of filtration to determine the upper limit in bearing life under the strictest possible lubricant cleanliness conditions. Bearing fatigue lives, surface distress and weight loss were compared to previous bearing fatigue tests in contaminated and noncontaminated oil filters having absolute removal ratings of 3, 30, 49, and 105 microns, with lubricant and sump temperatures maintained at 347 K. Ultra clean lubrication was found to produce bearing fatigue lives that were approximately twice that obtained in previous tests with contaminated oil using 3 micron absolute filtration. It was also observed that the centrifugal oil filter has the same effectiveness as a 30 micron absolute filter in preventing surface damage.

Loewenthal, S. H.↗
NASA NTRS1975

Effects of environment on the fatigue of graphite-epoxy composites

Torsional and flexural fatigue tests were performed on both uniaxial (0 deg) and crossplied (plus or minus 45 deg) graphite-epoxy materials at temperatures of 24 and 74 C in environments of air and water. The results of the torsion testing showed that the number of cycles required to cause an initial decrease in stiffness as well as the rate of stiffness loss was a function of temperature and environment; the most significant losses were noted for tests at the higher temperature in water. The torsional fatigue specimens were subsequently tested in four-point bending to determine the effect of torsional damage on longitudinal properties. This damage caused changes in the flexural stiffness, failure stress, and failure energy, depending on the stress and environmental histories. The flexural fatigue tests also showed a significant effect of water (at 24 C) on the material behavior. These results are compared with the results of previous investigations and are discussed in terms of proposed damage mechanisms.

Sumsion, H. T.↗
NASA NTRS1975

Environmental effects on the torsion and flexure fatigue properties of graphite-epoxy composites

Effects of torsional and flexural fatigue on the long-time integrity of advanced graphite-epoxy structural composites have been investigated. Reversed (R = - 1) and unidirectional (R = 0) torsional fatigue tests were made on unidirectional, cross-plied and woven graphite fiber materials in air and water at room temperature and at 74 C. Flexural fatigue tests (4-point bending) with R = - 1 were run in air and water at room temperature, and at R = 0 in air. Results show that in torsional cycling, both water environment and higher test temperature contribute to significant degradation of torsional stiffness. The degradation of stiffness from torsional stress cycling was observed to be much greater with R = - 1 than with simple R = 0 cycling. The effect of environment is also greater in the fully reversed cycling.

Sumsion, H. T.↗
DOE OSTI2023

Update on the Current R&D Activity in the U.S.

This presentation is to fulfil DOE commitment to GIF VHTR Materials PMB. Notched creep rupture testing: Weldment V-notch specimen test finished. 800C 60MPa, 15,716 hour rupture life. Two double V-notch specimen tests have finished. Crack growth tests: System modification was required for creep and creep-fatigue testing, Epsilon 3548COD Extensometer has been ordered, to allow load-line displacement measurements, to be paired with direct current potential drop already used to measure crack length, Sample redesigned in accordance to ASTM E2760 and E1457 to allow for both creep and creep-fatigue crack growth rate testing. Alloy 800H Weldments (1/2) and Alloy 800H Weldments (2/2), Variable Fatigue Testing, and Multi=axial Stress Relaxation. Continue work to finish 800H model, examine ?universal? constitutive model form.

11 NUCLEAR FUEL CYCLE AND FUEL MATERIALS↗
NASA NTRS1976

Environmental Effects on Graphite-Epoxy Fatigue Properties

Effects of torsional and flexural fatigue on the long-time Integrity of advanced graphite-epoxy structural composites have been investigated. Torsional fatigue tests were run at stress ratios of R = 0 (zero to maximum, repeated) and R = -1 (zero mean stress) on unidirectional, angleply, and woven graphite fiber materials in air and water at room temperature and at 74 C. Flexural fatigue tests (four-point bending) with R = -1 were run in air and water at room temperature, and with R = 0 in air. Results show that, in torsional cycling, both water environment and higher test temperature contribute to significant degradation of torsional stiffness. The degradation of stiffness from torsional stress cycling was observed to be much greater with R = -1 than with simple R = 0 cycling. The effect of environment also is greater in the fully reversed cycling. Flexural fatigue results on +/- 30 deg material show a large fatigue effect, with fatigue limits of less than 50% and 30% of the static failure strength for specimens tested under stress ratios of R = 0 and R = -1, respectively. Compliance measurements indicate that the final failures are preceded by damage initiation and accumulation, which begins at about 1% of the specimen life.

Sumsion, H. T.↗
NASA NTRS2013

Engineering Evaluation of International Low Impact Docking System Latch Hooks

The international Low Impact Docking System (iLIDS) provides a structural arrangement that allows for visiting vehicles to dock with the International Space Station (ISS) (Fig 1). The iLIDS docking units are mechanically joined together by a series of active and passive latch hooks. In order to preserve docking capability at the existing Russian docking interfaces, the iLIDS latch hooks are required to conform to the existing Russian design. The latch hooks are classified as being fail-safe. Since the latch hooks are fail-safe, the hooks are not fracture critical and a fatigue based service life assessment will satisfy the structural integrity requirements. Constant amplitude fatigue testing to failure on four sets of active/passive iLIDS latch hooks was performed at load magnitudes of 10, 11, and 12 kips. Failure analysis of the hook fatigue failures identified multi-site fatigue initiation that was effectively centered about the hook mid-plane (consistent with the 3D model results). The fatigue crack initiation distribution implies that the fatigue damage accumulation effectively results in a very low aspect ratio surface crack (which can be simulated as thru-thickness crack). Fatigue damage progression resulted in numerous close proximity fatigue crack initiation sites. It was not possible to determine if fatigue crack coalescence occurs during cyclic loading or as result of the fast fracture response. The presence of multiple fatigue crack initiation sites on different planes will result in the formation of ratchet marks as the cracks coalesce. Once the stable fatigue crack becomes unstable and the fast fracture advances across the remaining ligament and the plane stress condition at a free-surface will result in failure along a 45 deg. shear plane (slant fracture) and the resulting inclined edge is called a shear lip. The hook thickness on the plane of fatigue crack initiation is 0.787". The distance between the shear lips on this plane was on the order of 0.48" and it was effectively centered about the mid-plane of the section. The numerous ratchet marks between the shear lips on the fracture initiation plane are indicative of multiple fatigue initiation sites within this region. The distribution of the fatigue damage about the centerline of the hook is consistent with the analytical results that demonstrate peak stress/strain response at the mid-plane that decreases in the direction of the hook outer surfaces. Scanning electron microscope images of the failed sections detected fatigue crack striations in close proximity to the free surface of the hook radius. These findings were documented at three locations on the fracture surface : 1) adjacent to the left shear lip, 2) adjacent to the right shear lip, and 3) near the centerline of the section. The features of the titanium fracture surface did not allow for a determination of a critical crack size via identification of the region where the fatigue crack propagation became unstable. The fracture based service life projections where benchmarked with strain-life analyses. The strainrange response in the hook radius was defined via the correlated finite element models and the modified method of universal slopes was incorporated to define the strain-life equation for the titanium alloy. The strain-life assessment confirmed that the fracture based projections were reasonable for the loading range of interest. Based upon the analysis and component level fatigue test data a preliminary service life capability for the iLIDS active and passive hooks of 2 lifetimes is projected (includes a scatter factor of 4).

Martinez, J.↗
NASA NTRS2022

Statistical Distribution of Gear Surface Fatigue Lives at High Reliability

The reliability of gears is important for a wide variety of applications, and the gearing community has a desire for better prediction of fatigue life at very high reliability. To improve predictions, a set of 950 NASA-conducted gear surface fatigue test results were gathered, pooled together using the general standardized Weibull variate, and then fit to a Weibull three-parameter distribution. An iterative fitting method was developed and then applied to the gear fatigue data to determine the values of the distribution parameters. Additional analyses were done using bearing and gear data that demonstrate a trend of increasing minimum life coefficient as correlated to the timeframe of the fatigue testing, and material cleanliness is proposed as a primary explanation for such correlation. It is noted that this observed trend supports published findings from analytical modeling and experimental studies that improvements to material cleanliness improves minimum fatigue life. Further use and study of the three-parameter Weibull distribution is recommended as a tool to quantify fatigue life most accurately in the high reliability regime.

gear↗
NASA NTRS1987

Frequency and load ratio effects on critical strain energy release rate Gc thresholds of graphite/epoxy composites

Graphite/epoxy composite laminates of T300/BP907 and AS6/HST-7 were axial-tension fatigue tested. Tests were conducted at 5 and 10 Hz, and at loading ratios of R = 0.1 and R = 0.5. Edge delamination was monitored as a function of number of fatigue cycles by monitoring stiffness reduction during fatigue testing. Delamination was confirmed and documented using dye-enhanced X-ray and optical photography. Critical strain energy release rates were then calculated. The composites delaminated readily, with loading ratio having a significant influence. Frequency effects were negligible.

Adams, Donald F.↗