The effect of grain boundary yield and disconnections on grain boundary fracture strength
During high-temperature interfacial strain, e.g., creep or sintering, grain boundaries will sample non-equilibrium states associated with the non-equilibrium disconnections that mediate strain. This work tests the hypothesis that those non-equilibrium states should affect the mechanical properties of the grain boundary. High-temperature bicrystal tensile strain experiments performed on Sc-doped ZrO 2 as a function of strain rate enable the observation of fracture before and after grain boundary yield. Yielded boundaries exhibit a median fracture strength ≈ 50 % lower than those that did not yield. Molecular dynamics simulations performed on boundaries with and without interstitial-type disconnection loops indicate that the presence of those loops reduce the failure stress.