DOE OSTI2023
Tungsten-188 is in widespread use in 188 W(t 1/2 = 69 d )/ 188 Re(t 1/2 = 16.9 h ) biomedical generators. Oak Ridge National Laboratory has been providing this product to the world since 1999. At ORNL, 188 W is produced via irradiation in ORNL’s High Flux Isotope Reactor (HFIR). Enriched 186 W targets in the form of sintered metallic pellets or rings achieve a compact loading in the irradiation vessel, providing a high yield per unit target. The enrichment of the target is >90% 186 W, and this isotope undergoes double neutron capture to produce the desired 188 W product. While 188 W is produced by neutron bombardment, 191 Os(t 1/2 = 15.4 d ) is simultaneously produced as a by-product and expected to be separated from 188 W by postirradiation treatment.In the current processing pathway, the irradiated W metal rings are first converted into an oxide form of WO 3 by heating the irradiated W metal target at 750°C in a quartz reaction vessel inside a vertical furnace under a constant flow of air. During heating, W metal reacts with oxygen in the air to produce WO 3 , which is soluble in 6 M NaOH for preparation of 188 W product. This oxidation process also converts 188 Os (the decay daughter of 188 W) and 191 Os (15.4 d , the irradiation produced byproduct) into OsO 4 , a highly volatile and toxic gas. The gaseous effluents driven from the quartz reaction vessel are passed through a scrubbing array to remove OsO 4 before the air is discharged from the process. This heterogeneous oxidation method simultaneously achieves goals of (1) converting metal target to a soluble oxide form and (2) removing volatile OsO 4 away from the solid WO 3 product by air flow and absorbing the harmful Os species by the scrubbing array. But this method has two potential problems as well: (1) O 2 reacts with only W metal at high temperatures, not with W alloyed with other elements. The O 2 –W reaction will be retarded when formation of WRe or WC occurs, or even when a layer of non-W materials on the surface of the irradiated W rings.; (2) 100% absorption of OsO 4 of high yield (>90%) from the reaction of Os + O 2 is a strict requirement to the OsO 4 scrubbing system--so NaOH scrubbers of a redundant size (2x 1.5 L) are in use for safety reasons.To resolve above two potential problems, direct dissolution of the irradiated W metal target by a selected reagent is a preferred pathway to avoid heating step with generation of tremendous amount of volatile OsO 4 . Hydrogen peroxide (H 2 O 2 ) is such a candidate to dissolve W in forms of either metal or alloys, although literature lacks information of solubilities of Re or Os in H 2 O 2 . With experimental results of dissolving non-radioactive W, Re and Os in H 2 O 2 under various conditions, this report illustrates a method of H 2 O 2 dissolution for irradiated W target, with a complete dissolution of W and Re, but ≤10% dissolution of Os (converted into gaseous OsO 4 and carried out into a scrubbing for absorption) during processing irradiated W target. The portion of undissolved Os can be separated from W solution by a follow up filtration step. Solubilities of W, Re and Os in H 2 O 2 at a temperature range from 14° to 50°C are presented. And a dissolution rate of W metal per surface area of W metal in H 2 O 2 is calculated based on results of dissolving a W metal cylinder of known surface area in H 2 O 2 at room temperature without stirring.
07 ISOTOPE AND RADIATION SOURCES↗