Residual stress effects on fracture strength of AISI 301 stainless steel and Ti-5Al-2.5Sn titanium cracked thin walled cylinders
Thermal conductivity and electrical resistivity measurements were conducted on two lots of an austenitic stainless steel. Electrical resistivity measurements were performed on the second lot, both before and after the material was hot-swaged and reannealed to a size 1/10 the original diameter. These measurements indicate that this steel can be swaged and reannealed without an appreciable change in thermal conductivity. Electrical resistivity measurements as well as direct thermal conductivity measurements on several specimens from both lots indicate a material variability in these lots of less than 1% in thermal conductivity.
Demand for improved corrosion-resistant steels, coupled with increased emphasis on conserving strategic metals, has led to development of family of stainless steels in which manganese and nitrogen are substituted for portion of usual nickel content. Advantages are approximately-doubled yield strength in annealed condition, better resistance to stress-corrosion cracking, retention of low magnetic permeability even after severe cold working, excellent strength and ductility at cryogenic temperatures, superior resistance to wear and galling, and excellent high-temperature properties.
This report presents the results of high-temperature mechanical property testing and microstructural analysis of laser powder bed fusion (LPBF) 316H stainless steel (SS) conducted during Fiscal Year 2025 (FY25) under the U.S. Department of Energy, Office of Nuclear Energy’s Advanced Materials and Manufacturing Technologies (AMMT) program. The study builds upon prior work by expanding the mechanical property test matrix and advancing a microstructure-based mechanistic understanding of LPBF 316H SS performance, with a focus on the solution annealed (SA, 1100°C for 1 hour) materials. High-temperature tension, creep, fatigue, and creep-fatigue tests were performed. Thermal aging studies were conducted. Advanced characterization techniques, including scanning electron microscopy (SEM), scanning transmission electron microscopy (STEM), and high-energy synchrotron X-ray diffraction, were employed to investigate the microstructural evolution during thermal aging and mechanical testing. It was discovered that the as-built (AB) LPBF 316H SS exhibited precipitation kinetics during thermal aging that are 10–100 times faster than its wrought counterpart due to the presence of high densities of preferred nucleation sites, while the precipitation kinetics in SA LPBF 316H was under investigation. The accelerated precipitation of embrittling phases such as sigma phase in LPBF 316H SS compared to its wrought counterpart led to significant impacts on creep ductility. The influence of laser printing parameters and build orientations on fatigue and creep-fatigue performance was observed. In assessing the creep-fatigue performance, it was discovered that the SA LPBF 316H samples failed in less than 200 cycles under 595°C, 0.5% (strain amplitude) with a 60-minute hold time. This work establishes a mechanistic framework for predicting the long-term behavior of LPBF 316H SS, supporting its rapid qualification under the ASME BPVC. The findings contribute to the broader goal of enabling the deployment of advanced materials in next-generation nuclear energy systems. An outlook for FY26 work, including continued aging studies, mechanical testing, and microstructural characterization, is provided.
Brazing process uses vapor-deposited titanium and an aluminum-zirconium-silicon alloy to prevent formation of brittle intermetallic compounds in stainless steel and aluminum bonding. Joints formed by this process maintain their high strength, corrosion resistance, and hermetic sealing properties.
Materials data handbooks summarize all presently known properties of commercially available structural aluminum alloys 2014, 2219, and 5456 and structural stainless steel alloy 301. The information includes physical and mechanical property data and design data presented in tables, illustrations, and text.
The equipment and techniques for determining the thermal conductivity, electrical resistivity Lorenz ratio, and thermopower characteristics of Fe-22Cr-13Ni-5Mn stainless steel are discussed. The dimensions of the specimen and its preparation are described. The experimental data are represented by arbitrary functions over the entire range and smooth tables are generated from these functions.
This study investigates the additive manufacturing (AM) processing, microstructural evolution, and resulting mechanical and thermal properties of multimaterial components combining 17-4PH stainless steel and pure copper (Cu) fabricated via laser powder directed energy deposition (LP-DED). Conventional tooling steels exhibit limited thermal conductivity, significantly constraining production throughput in high-volume processes. Incorporating Cu, with its superior thermal conductivity, could significantly enhance tool performance, though Cu and steel present metallurgical incompatibilities when processed via AM. A systematic investigation was conducted across compositions ranging from 0 to 100 wt% Cu, revealing critical thresholds influencing solidification behavior, defect formation, microstructure, hardness, and thermal transport. Optical microscopy, electron backscatter diffraction (EBSD), hardness testing, and thermal conductivity measurements provided comprehensive process–structure–property correlations. Severe hot cracking occurred at low-Cu contents (6–25 wt%), aligning generally well with crack susceptibility modeling, with an unexpected discrepancy at 25 wt%. Porosity remained low (≥99% dense) throughout the compositional spectrum. EBSD analysis revealed a transformation from columnar martensitic structures at low-Cu contents to equiaxed FCC Cu-dominated structures at higher Cu concentrations, highlighting the complex microstructural transitions driven by Cu-induced changes in solidification and phase stability. Hardness decreased from 330 HV (pure 17-4PH) to 62 HV (pure Cu), consistent with microstructural changes. Concurrently, thermal conductivity improved substantially from 13.5 W/m K to 367.9 W/m K, emphasizing Cu’s dominant role in thermal transport. The findings highlight the feasibility of leveraging compositional gradients between 17-4PH and Cu to achieve tailored tooling with optimized thermal and mechanical performance.
• A scoping study was undertaken at Savannah River National Laboratory (SRNL) to determine the solidstate resistance-weldability of additively manufactured 304L stainless steel. • Additive manufacturing of pressure-containing boundaries is of interest to numerous industries. • The approach investigated in this study was a low energy, solid state spot weld (pinch weld). • This general approach has been routinely used for conventionally prepared tubing and is now being expanded to additively manufactured components. • This work aimed to understand the impact of AM on the bond quality and weld geometry of pinch welds.
A turbine blade with a porous stainless-steel shell sintered to a supporting steel strut has been fabricated for tests at the NACA by Federal-Mogul Corporation under contract from the Bureau of Aeronautics, Department of the Navy. The apparent permeability of this blade, on the average, more nearly approaches the values specified by the NAGA than did two strut-supported bronze blades in a previous investigation. Random variations of permeability in the present blade are substantialy greater than those of the bronze blades, but projected improvements in certain phases of the fabrication process are expected to reduce these variations.
After long-term thermal aging at 400 °C for 3000 h and 10,000 h, a cast duplex stainless steel exhibits promoted fatigue performance, including enhanced three-stage cyclic hardening and prolonged fatigue life. Utilizing in situ neutron diffraction, the phase-specific stresses are resolved, and their evolutions over entire fatigue cycling reveal the underlying mechanisms of the fatigue enhancement. It is found that the ferrite phase bears a much higher stress than the austenite matrix under both as-received and aged conditions. The enhanced cyclic hardening in Stage I is attributed to the strengthening of both phases due to thermal aging, while the enhancement in Stage III results from the martensitic transformation induced strengthening. The fatigue life is prolonged thanks to the cyclic hardening and the delay of martensitic transformation in the austenite phase after thermal aging.
The ambient and cryogenic temperature mechanical properties and the ambient temperature stress corrosion results of 18-3 Mn (Nitronic 33)stainless steel, longitudinal and transverse, as received and as welded (TIG) material specimens manufactured from 0.063 inch thick sheet material, were described. The tensile test results indicate an increase in ultimate tensile and yield strengths with decreasing temperature. The elongation remained fairly constant to -200 F, but below that temperature the elongation decreased to less than 6.0% at liquid hydrogen temperature. The notched tensile strength (NTS) for the parent metal increased with decreasing temperature to liquid nitrogen temperature. Below -320 F the NTS decreased rapidly. The notched/unnotched (N/U) tensile ratio of the parent material specimens remained above 0.9 from ambient to -200 F, and decreased to approximately 0.65 and 0.62, respectively, for the longitudinal and transverse directions at liquid hydrogen temperature. After 180 days of testing, only those specimens exposed to the salt spray indicated pitting and some degradation of mechanical properties.
The stress and temperature sensitivites of the rupture life and secondary creep rate were examined in detail for a single heat of type 304 stainless steel (9T2796). Assuming that the rupture life has a power law stress dependency, relatively small differences in the stress exponent were observed over a broad range of stress and temperature. In contrast, large changes were observed for equivalent parameter for secondary creep rate. As a result of these differences, the Monkman-Grant correlation was sensitive to stress and temperature below 650 C. Metallurgical studies based on light and transmission electron microscopy suggested that the temperature and stress sensitivities of secondary creep rate at temperatures below 650 C were related to features of the substructure not present at higher temperature. Specifically, the presence of a fine dislocation network stabilized by precipitates altered the stress and temperature sensitivities relative to what might be expected from high temperature studies.
Irradiated and unirradiated tensile and fatigue specimens of AISI 310 stainless steel and Ti-5Al-2.5Sn were tested in the range of 100 to 10,000 cycles to failure to determine the applicability of the method of universal slopes to irradiated materials. Tensile data for both materials showed a decrease in ductility and increase in ultimate tensile strength due to irradiation. Irradiation caused a maximum change in fatigue life of only 15 to 20 percent for both materials. The method of universal slopes predicted all the fatigue data for the 310 SS (irradiated as well as unirradiated) within a life factor of 2. For the titanium alloy, 95 percent of the data was predicted within a life factor of 3.
A series of axial-torsional, inphase, strain-controlled, low-cycle fatigue tests were performed at room temperature on tubular specimens of 304 stainless steel. The program was conducted in cooperation with the task group on multiaxial fatigue research of ASTM committee E-09. The objective was to quantify the variability in multiaxial test results among several laboratories. Only included is data which was generated at the NASA Lewis Research Center's High Temperature Fatigue and Structures Laboratory. The experimental equipment and procedures used are described. The tubular specimens were polished on the outer surface to aid in the use of a cellulose film surface replication technique for crack detection. However, cracking initiated predominantly on the internal surface for all specimens. Honing of the bore of the tubular specimens lessened but did not entirely eliminate this problem. The observed fatigue lives are compared with lives calculated from three multiaxial life models. Constants for the life prediction models were obtained from uniaxial and torsional tests performed on the same heat of material. The observed fatigue lives agreed with calculated lives to within a factor of two for all but one of the life prediction models.
Thermal desorption spectroscopy (TDS), along with Auger electron spectroscopy, was used to study the desorption of H2 and CO from baked 304 and 347 stainless-steel samples exposed only to residual gases. Both 347 and 304 samples gave identical TDS spectra. The spectra for CO contained a sharp leading peak centered in the temperature range 410-440C and an exponentially increasing part for temperatures higher than 500C, with a small peak around 600C appearing as a shoulder. The leading peak followed a second-order desorption behavior with an activation energy of 28+/-2 kcal/mol, suggesting that the rate-limiting step for this peak is most likely a surface reaction that produces the CO molecules in the surface layer. The amount of desorbed CO corresponding to this peak was approximately 0.5X10(exp 14) molecules/cm(exp 2) . The exponentially rising part of the CO spectrum appeared to originate from a bulk diffusion process. The TDS spectrum for H2 consisted of a main peak centered also in the temperature range 410-440C, with two small peaks appearing as shoulders at approximately 500 and 650C. The main peak in this case also displayed a second-order behavior with an activation energy of 14+/-2 kcal/mol. The amount of desorbed H2, approximately 1.9X 10(exp 15) molecules/cm(exp 2) , appeared to be independent of the concentration of hydrogen in the bulk, indicating that the majority of the desorbed H2 originated from the surface layer.
Axial-load fatigue tests were conducted at room temperature on notched and unnotched sheet specimens of 17-7 PH stainless steel in Condition TH 1050. The notched specimens had theoretical stress-concentration factors of 2.32, 4.00, and 5.00. All specimens were tested under completely reversed loading. S-N curves are presented for each specimen configuration and ratios of fatigue strengths of unnotched specimens to those of notched specimens are given. Predictions of the fatigue behavior of notched specimens near the fatigue limit were made.
Measurements of activation areas are used to investigate the effect of hydrogen on the kinetics of dislocation glide during cyclic deformation in cold-worked 316L stainless steel. Non-charged and hydrogen-precharged (H-precharged) specimens were tested in low cycle fatigue (LCF) under plastic strain control. A series of plastic strain rate changes was performed periodically at the peak true plastic strain from the first cycle to half-life, and at various plastic strain values around stable hysteresis loops near half-life to determine the operational activation area, Δ a ∗. Both material conditions demonstrate a rapid increase in Δ a ∗ during the initial rapid softening followed by a region of approximately constant values coinciding with a reduced rate of softening. Near half-life, hydrogen reduces Δ a ∗ at a given true stress due to its effect on the activation distance and obstacle spacing. The magnitudes of Δ a ∗ reveal that bypassing solutes, cutting forest dislocations, and initiating cross slip are important mechanisms of thermally activated dislocation glide at all amplitudes, except hydrogen suppresses cross slip at the lowest plastic strain amplitudes. These results are supported by electron microscopy characterization of deformed microstructures. A Haasen plot analysis indicates that forest dislocations control the kinetics of deformation in both material conditions. It also reveals the presence of athermal obstacles in both non-charged and H-precharged conditions, likely dense dislocation tangles and cell walls. Additionally, the effect of hydrogen on microstructure evolution (by reducing the propensity for cross slip) leads to a dependence of athermal stress on plastic strain amplitude.