NASA NTRS2007

Investigation of Low-Cycle Bending Fatigue of AISI 9310 Steel Spur Gears

An investigation of the low-cycle bending fatigue of spur gears made from AISI 9310 gear steel was completed. Tests were conducted using the single-tooth bending method to achieve crack initiation and propagation. Tests were conducted on spur gears in a fatigue test machine using a dedicated gear test fixture. Test loads were applied at the highest point of single tooth contact. Gear bending stresses for a given testing load were calculated using a linear-elastic finite element model. Test data were accumulated from 1/4 cycle to several thousand cycles depending on the test stress level. The relationship of stress and cycles for crack initiation was found to be semilogarithmic. The relationship of stress and cycles for crack propagation was found to be linear. For the range of loads investigated, the crack propagation phase is related to the level of load being applied. Very high loads have comparable crack initiation and propagation times whereas lower loads can have a much smaller number of cycles for crack propagation cycles as compared to crack initiation.

Handschuh, Robert F.↗
NASA NTRS2007

Investigation of Low-Cycle Bending Fatigue of AISI 9310 Steel Spur Gears

An investigation of the low-cycle bending fatigue of spur gears made from AISI 9310 gear steel was completed. Tests were conducted using the single-tooth bending method to achieve crack initiation and propagation. Tests were conducted on spur gears in a fatigue test machine using a dedicated gear test fixture. Test loads were applied at the highest point of single tooth contact. Gear bending stresses for a given testing load were calculated using a linear-elastic finite element model. Test data were accumulated from 1/4 cycle to several thousand cycles depending on the test stress level. The relationship of stress and cycles for crack initiation was found to be semi-logarithmic. The relationship of stress and cycles for crack propagation was found to be linear. For the range of loads investigated, the crack propagation phase is related to the level of load being applied. Very high loads have comparable crack initiation and propagation times whereas lower loads can have a much smaller number of cycles for crack propagation cycles as compared to crack initiation.

Handschuh, Robert F.↗
NASA NTRS1979

Bellows flow-induced vibrations

Results of theoretical and experimental investigations of bellows typical of those found in space shuttle external tanks are presented. Correlation parameters are identified which generalize the alternating stress calculations cited in an earlier study. Alternating stress amplitudes and mean stress levels form the basis of a fatigue analysis incorporating seven ordinate charts for 347 stainless steel, alloy 21 6-9, and Inco 718. A crack propagation model is included with a program for computing bellows fatigue life. Two phase flow and material hardness properties are discussed.

Johnson, J. E.↗
NASA NTRS1994

Evaluation of the fuselage lap joint fatigue and terminating action repair

Terminating action is a remedial repair which entails the replacement of shear head countersunk rivets with universal head rivets which have a larger shank diameter. The procedure was developed to eliminate the risk of widespread fatigue damage (WFD) in the upper rivet row of a fuselage lap joint. A test and evaluation program has been conducted by Foster-Miller, Inc. (FMI) to evaluate the terminating action repair of the upper rivet row of a commercial aircraft fuselage lap splice. Two full scale fatigue tests were conducted on fuselage panels using the growth of fatigue cracks in the lap joint. The second test was performed to evaluate the effectiveness of the terminating action repair. In both tests, cyclic pressurization loading was applied to the panels while crack propagation was recorded at all rivet locations at regular intervals to generate detailed data on conditions of fatigue crack initiation, ligament link-up, and fuselage fracture. This program demonstrated that the terminating action repair substantially increases the fatigue life of a fuselage panel structure and effectively eliminates the occurrence of cracking in the upper rivet row of the lap joint. While high cycle crack growth was recorded in the middle rivet row during the second test, failure was not imminent when the test was terminated after cycling to well beyond the service life. The program also demonstrated that the initiation, propagation, and linkup of WFD in full-scale fuselage structures can be simulated and quantitatively studied in the laboratory. This paper presents an overview of the testing program and provides a detailed discussion of the data analysis and results. Crack distribution and propagation rates and directions as well as frequency of cracking are presented for both tests. The progression of damage to linkup of adjacent cracks and to eventual overall panel failure is discussed. In addition, an assessment of the effectiveness of the terminating action repair and the occurrence of cracking in the middle rivet row is provided, and conclusions of practical interest are drawn.

Samavedam, Gopal↗
NASA NTRS1971

C-130: Results of center wing residual strength and crack propagation test program

Fourteen C-130 airplane center wings which had experienced from approximately 4,000 to 13,000 hours of flight service and its associated fatigue damage were tested to destruction, seven in upbending and seven in downbending. Six wings were tested directly for static residual strength in the fatigue-damaged condition as received from field service. The other eight wings were tested in crack propagation cyclic testing at a prescribed stress level for a maximum of 10,000 cycles. Then the stress level was reduced and testing was continued up to a maximum of 20,000 total cycles. Cyclic testing was performed with constant-amplitude stresses at a stress ratio of +0.1. Maximum cyclic skin stresses were approximately 18,000 psi. At the conclusion of cyclic testing, a static test to destruction was conducted to determine the residual strength of each fatigue-damaged specimen.

Reeder, F. L.↗
NASA NTRS1979

Frequency effect on the fatigue life of a laminated composite

Effects of load frequency on the fatigue behavior of notched (+ or - 45 deg)2s laminated graphite/epoxy composites are investigated. Experimental results are obtained using four frequencies at three load levels. Temperature rises near the center hole are also measured. It is found that when temperature increase during the fatigue test is small, fatigue life increases as the load frequency increases. However, an increase in the near hole temperature results in a reduction in fatigue life. A theoretical model based upon crack propagation in viscoelastic media is presented. The model is modified to account for the temperature effect.

Sun, C. T.↗
NASA NTRS1988

Fatigue life prediction modeling for turbine hot section materials

A major objective of the fatigue and fracture efforts under the Hot Section Technology (HOST) program was to significantly improve the analytic life prediction tools used by the aeronautical gas turbine engine industry. This was achieved in the areas of high-temperature thermal and mechanical fatigue of bare and coated high-temperature superalloys. The cyclic crack initiation and propagation resistance of nominally isotropic polycrystalline and highly anisotropic single crystal alloys were addressed. Life prediction modeling efforts were devoted to creep-fatigue interaction, oxidation, coatings interactions, multiaxiality of stress-strain states, mean stress effects, cumulative damage, and thermomechanical fatigue. The fatigue crack initiation life models developed to date include the Cyclic Damage Accumulation (CDA) and the Total Strain Version of Strainrange Partitioning (TS-SRP) for nominally isotropic materials, and the Tensile Hysteretic Energy Model for anisotropic superalloys. A fatigue model is being developed based upon the concepts of Path-Independent Integrals (PII) for describing cyclic crack growth under complex nonlinear response at the crack tip due to thermomechanical loading conditions. A micromechanistic oxidation crack extension model was derived. The models are described and discussed.

Halford, G. R.↗
NASA NTRS1989

Fatigue life prediction modeling for turbine hot section materials

A major objective of the fatigue and fracture efforts under the NASA Hot Section Technology (HOST) program was to significantly improve the analytic life prediction tools used by the aeronautical gas turbine engine industry. This was achieved in the areas of high-temperature thermal and mechanical fatigue of bare and coated high-temperature superalloys. The cyclic crack initiation and propagation resistance of nominally isotropic polycrystalline and highly anisotropic single crystal alloys were addressed. Life prediction modeling efforts were devoted to creep-fatigue interaction, oxidation, coatings interactions, multiaxiality of stress-strain states, mean stress effects, cumulative damage, and thermomechanical fatigue. The fatigue crack initiation life models developed to date include the Cyclic Damage Accumulation (CDA) and the Total Strain Version of Strainrange Partitioning (TS-SRP) for nominally isotropic materials, and the Tensile Hysteretic Energy Model for anisotropic superalloys. A fatigue model is being developed based upon the concepts of Path-Independent Integrals (PII) for describing cyclic crack growth under complex nonlinear response at the crack tip due to thermomechanical loading conditions. A micromechanistic oxidation crack extension model was derived. The models are described and discussed.

G R Halford↗
NASA NTRS1975

Fracture and fatigue of discontinuously reinforced copper/tungsten composites

The strength, toughness and resistance to cyclic crack propagation of composites consisting of copper reinforced with short tungsten wires of various lengths have been studied and the results compared with the behavior of continuously reinforced composites manufactured by the same method, i.e., by vacuum hot-pressing. It has been found that whereas the resistance to fatigue crack growth of continuously reinforced composites is very similar to that of continuous Al/stainless steel composites reported elsewhere, the addition of short fibers completely changes the mode of fracture, and no direct comparisons are possible. In effect, short fibers inhibit single crack growth by causing plastic flow to be distributed rather than localized, and although these composites are much less strong than continuous fiber composites, they nevertheless have much greater fatigue resistance.

Harris, B.↗
NASA NTRS1980

Cyclic behavior of turbine disk alloys at 650 C

Five gas turbine disk alloys representing a range of strengths and processing methods were tested for resistance to both cyclic crack initiation and propagation at 650 C using a 0.33 Hz fatigue cycle and a cycle incorporating a 900 s tensile dwell. At the low strain ranges pertinent to disks, resistance to crack initiation increased with increasing tensile yield strength among the alloys, though the advantage was somewhat smaller for the creep fatigue cycle. Cyclic crack growth resistance, however, decreased with increasing strength and very markedly so for the dwell cycle.

Cowles, B. A.↗
NASA NTRS1984

Evaluation of long-duration exposure to the natural space environment on graphite-polyimide and graphite-epoxy mechanical properties (A0175)

The primary objective of this experiment is to accumulate the needed operational data associated with the exposure of graphite-polyimide and graphite-epoxy material to the environments of space. The experiment will be mounted in two 3-in.-deep peripheral trays. Graphite-polyimide specimens will occupy 1 1/3 trays and the graphite-epoxy specimens will occupy two-thirds of a tray. The experiment approach requires two matched sets of specimens with traceable records that are maintained for materials processing and specimen quality. After fabrication, one set of each test specimen will be sectioned and structurally tested to serve as a data baseline. After the flight, the other set of specimens will undergo extensive measurements of mechanical properties for comparison with the original data baseline. Structural testing of the graphite-polyimide specimens will provide strength and elastic data in tension, compression, and shear. Transverse tension microcracking and crack propagation will be evaluated by photomicroscopy. Structural testing of the graphite-epoxy specimens will include verification of laminate, core, adhesive, and fatigue properties as applied to the design and analysis of the payload bay door. Microcracking and crack propagation will also be analyzed by photomicroscopy.

Powell, J. H.↗
DOE OSTI2021

Experimental and computational analysis of bending fatigue failure in chopped carbon fiber chip reinforced composites

With a better balance among good mechanical performance, high freedom of design, and low material and manufacturing cost, chopped carbon fiber chip reinforced sheet molding compound (SMC) composites show great potential in different engineering applications. Here in this paper, bending fatigue behaviors of SMC composites considering the heterogeneous fiber orientation distributions have been thoroughly investigated utilizing both experimental and computational methods. First, four-point bending fatigue tests are performed with designed SMC composites, and the local modulus is adopted as a metric to represent the local fiber orientation of two opposing sides. Interestingly, SMC composites with and without large discrepancy in local modulus of opposing sides show different fatigue behaviors. Interrupted tests are conducted to explore the bending fatigue failure mechanism, and the damage processes of valid specimens are also closely examined. We find that the fatigue failure of SMC composites under four-point bending is governed by crack propagation instead of crack initiation. Because of this, the heterogeneous local fiber orientations of both sides of the specimen influence fatigue life. The microstructure of the lower side shows a direct influence while that of the upper side also exhibiting influence which becomes more prominent for high cycle fatigue cases. Furthermore, a hybrid micro–macro computational model is proposed to efficiently study the cyclic bending behavior of SMC composites. The region of interest is reconstructed with a modified random sequential absorption algorithm to conserve all the microstructural details including the heterogeneous fiber orientation, while the rest of the regions are modeled as homogenized macro-scale continua. Combined with a framework to capture the progressive fatigue damage under cyclic bending, the bending fatigue behaviors of SMC composites are accurately captured by the hybrid computational model comparing with our experimental analysis.

36 MATERIALS SCIENCE↗
NASA NTRS1992

Propagation of Flexural Mode AE Signals in GR/EP Composite Plates

It has been documented that AE signals propagate in thin plates as extensional and flexural plate modes. This was demonstrated using simulated AE sources (pencil lead breaks) by Gorman on thin aluminum and gr/ep composite plates and by Gorman and Prosser on thin aluminum plates. A typical signal from a pencil lead break source which identifies these two modes is shown. AE signals from transverse matrix cracking sources in gr/ep composite plates were also shown to propagate as plate modes by Gorman and Ziola. Smith showed that crack growth events in thin aluminum plates under spectrum fatigue loading produced signals that propagated as plate modes. Additionally, Prosser et al. showed that AE signals propagated as plate modes in a thin walled composite tube.

Prosser, W. H.↗
NASA NTRS2003

TF41 Engine Fan Disk Seeded Fault Crack Propagation Test

Uncontained engine failures, although rare in occurrence, can have a catastrophic effect on aircraft performance and safety. Engine disk cracks can eventually lead to these type of failures. A number of techniques to detect engine disk cracks have been developed in recent years. However, these technologies have only been validated by disk spin pit tests, not actual engine tests. Due to this, a project was established to perform seeded fault engine tests on a TF41 engine disk fan. A defect was machined in the first stage fan disk of a TF41 engine. The disk was run in a spin pit to initiate a crack. Once initiated, the disk was run in an actual engine test facility. The engine was cycled by a number of start and stops with the goal of propagating the crack to disk burst through low cycle fatigue. Various crack detection techniques were installed on the engine and run real-time during the test to validate their abilities to detect disk cracks. These techniques were based on methods such as change in mass imbalance using vibration or shaft displacement, change in blade position, acoustic emission, and torsional resonance. At the completion of 4474 test cycles, the crack in the TF41 disk was determined to have grown approximately 0.025 inches. This was far less the predicted crack growth based on a fracture mechanics analysis and finite element stress analysis.

Lewicki, David G.↗
NASA NTRS2006

Simulation of Delamination Propagation in Composites Under High-Cycle Fatigue by Means of Cohesive-Zone Models

A damage model for the simulation of delamination propagation under high-cycle fatigue loading is proposed. The basis for the formulation is a cohesive law that links fracture and damage mechanics to establish the evolution of the damage variable in terms of the crack growth rate dA/dN. The damage state is obtained as a function of the loading conditions as well as the experimentally-determined coefficients of the Paris Law crack propagation rates for the material. It is shown that by using the constitutive fatigue damage model in a structural analysis, experimental results can be reproduced without the need of additional model-specific curve-fitting parameters.

Turon, Albert↗
NASA NTRS1998

Small Crack Growth and Fatigue Life Predictions for High-Strength Aluminium Alloys: Experimental and Fracture Mechanics Analysis - Part 1

The small crack effect was investigated in two high-strength aluminium alloys: 7075-T6 bare and LC9cs clad alloy. Both experimental and analytical investigations were conducted to study crack initiation and growth of small cracks. In the experimental program, fatigue tests, small crack and large crack tests A,ere conducted under constant amplitude and Mini-TWIST spectrum loading conditions. A pronounced small crack effect was observed in both materials, especially for the negative stress ratios. For all loading conditions, most of the fatigue life of the SENT specimens was shown to be crack propagation from initial material defects or from the cladding layer. In the analysis program, three-dimensional finite element and A weight function methods were used to determine stress intensity factors and to develop SIF equations for surface and corner cracks at the notch in the SENT specimens. A plastisity-induced crack-closure model was used to correlate small and large crack data, and to make fatigue life predictions, Predicted crack-growth rates and fatigue lives agreed well with experiments. A total fatigue life prediction method for the aluminum alloys was developed and demonstrated using the crack-closure model.

Wu, X. R.↗
NASA NTRS1998

Investigation of Thermal High Cycle and Low Cycle Fatigue Mechanisms of Thick Thermal Barrier Coatings

Ceramic thermal barrier coatings have attracted increased attention for diesel engine applications. The advantages of using the ceramic coatings include a potential increase in efficiency and power density and a decrease in maintenance cost. Zirconia-based ceramics are the most important coating materials for such applications because of their low thermal conductivity, relatively high thermal expansivity and excellent mechanical properties. However, durability of thick thermal barrier coatings (TBCS) under severe temperature cycling encountered in engine conditions, remains a major question. The thermal transients associated with the start/stop and no-load/full-load engine cycle, and with the in-cylinder combustion process, generate thermal low cycle fatigue (LCF) and thermal high cycle fatigue (HCF) in the coating system. Therefore, the failure mechanisms of thick TBCs are expected to be quite different from those of thin TBCs under these temperature transients. The coating failure is related not only to thermal expansion mismatch and oxidation of the bond coats and substrates, but also to the steep thermal stress gradients induced in the coating systems. Although it has been reported that stresses generated by thermal transients can initiate surface and interface cracks in a coating system, the mechanisms of the crack propagation and of coating failure under the complex LCF and HCF conditions are still not understood. In this paper, the thermal fatigue behavior of an yttria partially stabilized zirconia coating system under simulated LCF and HCF engine conditions is investigated. The effects of LCF and HCF on surface crack initiation and propagation are also discussed.

Zhu, Dong-Ming↗