NASA NTRS2000

Characterization of Molybdate Conversion Coatings for Aluminum Alloys by Electrochemical Impedance Spectroscopy

Electrochemical impedance spectroscopy (EIS) was used to investigate the corrosion inhibiting properties of newly developed proprietary molybdate conversion coatings on aluminum alloy 2024-T3 under immersion in aerated 5% (w/w) NaCl. Corrosion potential and EIS measurements were gathered for six formulations of the coating at several immersion times for two weeks. Nyquist as well as Bode plots of the data were obtained. The conversion-coated alloy panels showed an increase in the corrosion potential during the first 24 hours of immersion that later subsided and approached a steady value. Corrosion potential measurements indicated that formulations A, D, and F exhibit a protective effect on aluminum 2024-T3. The EIS spectra of the conversion-coated alloy were characterized by an impedance that is higher than the impedance of the bare alloy at all the immersion times. The low frequency impedance, Z(sub lf) (determined from the value at 0.05 Hz) for the conversion-coated alloy was higher at all the immersion times than that of the bare panel. This indicates improvement of corrosion resistance with addition of the molybdate conversion coating. Scanning electron microscopy (SEM) revealed the presence of cracks in the coating and the presence of cubic crystals believed to be calcium carbonate. Energy dispersive spectroscopy (EDS) of the test panels revealed the presence of high levels of aluminum, oxygen, and calcium but did not detect the presence of molybdenum on the test panels. X-ray photoelectron spectroscopy (XPS) indicated the presence of less than 0.01 atomic percent molybdenum on the surface of the coating.

Calle, Luz Marina↗
NASA NTRS1991

Effect of thermal exposure, forming, and welding on high-temperature, dispersion-strengthened aluminum alloy: Al-8Fe-1V-2Si

The feasibility of applying conventional hot forming and welding methods to high temperature aluminum alloy, Al-8Fe-1V-2Si (FVS812), for structural applications and the effect of thermal exposure on mechanical properties were determined. FVS812 (AA8009) sheet exhibited good hot forming and resistance welding characteristics. It was brake formed to 90 deg bends (0.5T bend radius) at temperatures greater than or equal to 390 C (730 F), indicating the feasibility of fabricating basic shapes, such as angles and zees. Hot forming of simple contoured-flanged parts was demonstrated. Resistance spot welds with good static and fatigue strength at room and elevated temperatures were readily produced. Extended vacuum degassing during billet fabrication reduced porosity in fusion and resistance welds. However, electron beam welding was not possible because of extreme degassing during welding, and gas-tungsten-arc welds were not acceptable because of severely degraded mechanical properties. The FVS812 alloy exhibited excellent high temperature strength stability after thermal exposures up to 315 C (600 F) for 1000 h. Extended billet degassing appeared to generally improve tensile ductility, fatigue strength, and notch toughness. But the effects of billet degassing and thermal exposure on properties need to be further clarified. The manufacture of zee-stiffened, riveted, and resistance-spot-welded compression panels was demonstrated.

Kennedy, J. R.↗
NASA NTRS1946

Effect of Brake Forming on the Strength of 24S-T Aluminum-alloy Sheet

Tests were made to determine the effect of brake forming on the strength of 24S-T aluminum alloy sheet that had been formed to an inside bend radius of three times the sheet thickness. The results for both directions of the grain of the material showed that the compressive yield stresses were appreciably increased, that the tensile yield stresses were moderately increased, that the ultimate tensile stresses were only slightly increased, that the elongations were considerably reduced, and that the shapes of the tensile and compressive stress-strain curves were markedly changed.

Heimerl, George J↗
NASA NTRS1938

The Torsional and Bending Deflection of Full-Scale Aluminum-Alloy Propeller Blades Under Normal Operating Conditions

The torsional deflection of the blades of three full-scale aluminum-alloy propellers operating under various loading conditions was measured by a light-beam method. Angular bending deflections were also obtained as an incidental part of the study. The deflection measurements showed that the usual present-day type of propeller blades twisted but a negligible amount under ordinary flight conditions. A maximum deflection of about 1/10 degree was found at a v/nd of 0.3 and a smaller deflection at higher values of v/nd for the station at 0.70 radius. These deflections are much smaller than would be expected from earlier tests, but the light-beam method is considered to be much more accurate than the direct-reading-transit method used in the previous test.

Hartman, Edwin P↗
NASA NTRS1998

Stress Ratio Effects on Crack Opening Loads and Crack Growth Rates in Aluminum Alloy 2024

The effects of stress ratio (R) and crack opening behavior on fatigue crack growth rates (da/dN) for aluminum alloy (AA) 2024-T3 were investigated using constant-delta K testing, closure measurements, and fractography. Fatigue crack growth rates were obtained for a range of delta K and stress ratios. Results show that constant delta K fatigue crack growth for R ranging from near 0 to 1 is divided into three regions. In Region 1, at low R, da/dN increases with increasing R. In Region 2, at intermediate R, fatigue crack growth rates are relatively independent of R. In Region 3, at high R, further increases in da/dN are observed with increasing R.

Riddell, William T.↗
DOE OSTI2025

Understanding Oxide–Metal Interactions During Hot Isostatic Pressing to Diffusion Bond Aluminum Alloy 6061 Plates

The interaction between Mg, Si, and Al 2 O 3 during hot isostatic pressing diffusion bonding of aluminum alloy 6061 (AA6061) plates was investigated through thermodynamic calculations and experimental microstructural characterization. Thermodynamic calculations as functions of temperature, pressure, and composition revealed that the interaction among Mg, Si, and Al 2 O 3 yields Mg 2 Si and either MgO + Al or MgAl 2 O 4 + Al, facilitating the reduction of Al 2 O 3 and allowing Al/Al metallic bonds to form. Total pressure variation had a negligible influence on the oxygen partial pressure, and consequently, the reaction product formation. Oxygen partial pressure variation as a function of temperature and initial amount of Al 2 O 3 determined the formation of either MgO or MgAl 2 O 4 . Experimental Hot Isostatic Pressure (HIP) bonding at 723 K and 833 K under a constant pressure of 1017 atm documented the cooling rate-dependent formation of β–Mg 2 Si precipitates. High-resolution transmission electron microscopy imaging and selected area electron diffraction patterns verified the formation of β–Mg 2 Si and MgO at the interface but did not detect MgAl 2 O 4 . In conclusion, findings from this study clarify the role of thermochemical interactions in oxide disruption and bonding mechanisms during HIP diffusion bonding of AA6061 and provide guidance for optimizing joining processes for monolithic nuclear fuel assemblies.

11 - NUCLEAR FUEL CYCLE AND FUEL MATERIALS↗
NASA NTRS1977

Evaluation of mechanical property data on the 2219 aluminum alloy and application of the data to the design of liquid hydrogen tankage

The potential use of thin guage 2219 aluminum alloy for airborne liquid hydrogen tankage was examined. Existing data were processed using the Newman two parameter equation, a prediction was made for the life expectancy of a hypothetical liquid hydrogen tank, and additional experimental data were generated in an attempt to correct the deficiencies in the existing data.

Witzell, W. E.↗
NASA NTRS1985

A study of spectrum fatigue crack propagation in two aluminum alloys. 2: Influence of microstructures

The important metallurgical factors that influence both constant amplitude and spectrum crack growth behavior in aluminum alloys were investigated. The effect of microstructural features such as grain size, inclusions, and dispersoids was evaluated. It was shown that a lower stress intensities, the I/M 7050 alloy showed better fatigue crack propagation (FCP) resistance than P/M 7091 alloy for both constant amplitude and spectrum testing. It was suggested that the most important microstructural variable accounting for superior FCP resistance of 7050 alloy is its large grain size. It was further postulated that the inhomogenous planar slip and large grain size of 7050 limit dislocation interactions and thus increase slip reversibility which improves FCP performance. The hypothesis was supported by establishing that the cyclic strain hardening exponent for the 7091 alloy is higher than that of 7050.

Telesman, J.↗
NASA NTRS1941

Effect of alternately high and low repeated stresses upon the fatigue strength of 25S-T aluminum alloy

Fatigue tests were made on one lot of 3/4 inch diameter rolled-and-drawn 25S-T aluminum-alloy rod normal in composition and tensile properties. The specimens were tested at 3500 cycles per second in a rotating-beam fatigue test machine. Tests were made for three ratios (20:1, 50:1, and 200:1) of the number of cycles applied at low stress to the number applied at high stress. In general, failure occurred when the number of cycles at either the low or the high stress approached the ordinary fatigue curve for the material, regardless of the sequence in which the stresses were applied.

Stickley, G W↗