Observation of [VCu1–Ini2+VCu1–] Defect Triplets in Cu-Deficient CuInS2
Copper indium disulfide (CuInS2) is a semiconductor with a direct energy band gap of 1.53 eV, an optimal value for highly efficient thin-film solar cells. But it has reached only ~ 11 % power conversion efficiency, far less than the theoretically achievable value of ~ 30 %. The cause of this low performance is not understood. A single crystal grown from 1 mol% Cu-deficient melt was studied, using atomic resolution high-angle annular dark-field (HAADF) scanning transmission electron microscopy (STEM) and electron dispersive spectroscopy (EDS). While the bulk crystal is exactly stoichiometric CuInS2, it contains nanometer-thick, structurally coherent, Cu-deficient interphases that form along rotational twin boundaries in the {112} plane. Transition zones from bulk crystal to interphase are observed, where In is seen to move from its normal site InIn in the chalcopyrite structure to a tetrahedral interstitial site Ini, while Cu remains in its normal CuCu position. Two InIn rows of the bulk crystal merge into one row of Ini, causing excess Ini in the interphase. The concentrations of CuCu and Ini reflect a ratio of Cu vacancies, VCu, to excess Ini of ~ 2. Their relative lattice positions, and the high electrical resistivity of the crystal, suggests that VCu and excess Ini ‘precipitate’ as self-compensating, electrically neutral, [VCu1- Ini2+ VCu1-] defect triplets. This is the first atomic-level observation of the ordered defect that has been invoked as the basic structural modifier in chalcopyrite compound homologs. The interphases introduce an optical gap of 1.47 eV. Electron trapping in band tail states, evident from a photoconductivity exponent of 0.54, is the likely cause of an unusually low electron mobility of 0.1 cm2V-1s-1. The overall result is that making CuInS2 slightly copper-poor inserts nanometer-thick layers of the interphase into the bulk crystal. This study shows that apparently conflicting results of the effect of Cu deficiency on CuInS2 thin-film solar cells may be resolved by analyzing structure and composition at nanometer spatial resolution.