DOE OSTI2022

Laboratory Accelerated Cyclic Corrosion Testing and On-Road Corrosion Testing of AA6××× Coupled to Carbon Fiber-Reinforced Plastics

Structures made from a combination of aluminum alloy (AA) and carbon fiber-reinforced plastic (CFRP) are susceptible to galvanic corrosion of the AA in harsh atmospheric conditions, such as might exist for closure panels in automotive applications. It is important to understand the galvanic corrosion behavior of these materials under laboratory conditions as that might allow prediction of performance in real environments. This work tested specially designed AA6×××-CFRP coupons, including AA6111 and AA6022, connected to CFRP made from two different carbon fiber fabrics (twill and random) with the aim of understanding the corrosion behaviors in a laboratory cyclic exposure chamber and during on-road exposure. The extent of corrosion was assessed by galvanic current measurements, optical profilometry, cross-sectional area analysis, and microscopic analysis. Based on the results, it was determined that the corrosion susceptibilities and morphologies observed in CFRP/AA couples tested in an environmental chamber for 12 weeks were in correspondence with those of the coupons subjected to on-road testing for 1 y in Columbus, OH.

Materials Science↗
NASA NTRS1991

Corrosion of metal particle and metal evaporated tapes

Very high coercivity metal particle (MP) and metal evaporated (ME) tapes are being used in 8mm video and digital audio tape applications, and more recently in digital data recording applications. In view of the inherent susceptibility of such media to environmental corrosion, a number of recent studies have addressed their long term stability and archivability. These studies have used an accelerated corrosion test based either on elevated temperature-humidity or polluting gas atmospheres known as Battelle tests. A comparison of the Battelle test results performed at different laboratories reveals a large variation from one location to another, presumably due to incorrect replication of the Battelle condition. Furthermore, when the Battelle tests are performed on enclosed cartridges, it is quite possible that diffusion limits the penetration of the extremely low concentration polluting gaseous species to the inner layers of the tapes during the short time of the accelerated test, whereas in real life these diffusion limitations may not apply. To avoid this uncertainty, the corrosion behavior of commercial 8mm MP and ME tapes when cassettes without their external plastic cases were exposed to 50 deg C and 80 percent RH for 7.5 weeks is investigated.

Speliotis, Dennis E.↗
NASA NTRS2011

Microencapsulation of Corrosion Indicators for Smart Coatings

A multifunctional smart coating for the autonomous detection, indication, and control of corrosion is been developed based on microencapsulation technology. This paper summarizes the development, optimization, and testing of microcapsules specifically designed for early detection and indication of corrosion when incorporated into a smart coating. Results from experiments designed to test the ability of the microcapsules to detect and indicate corrosion, when blended into several paint systems, show that these experimental coatings generate a color change, indicative of spot specific corrosion events, that can be observed with the naked eye within hours rather than the hundreds of hours or months typical of the standard accelerated corrosion test protocols.. Key words: smart coating, corrosion detection, microencapsulation, microcapsule, pH-sensitive microcapsule, corrosion indicator, corrosion sensing paint

Li, Wenyan↗
DOE OSTI2020

Corrosion of Commercial Mg–Al Alloys: AZ31B, AM60, and AZ91D

Aqueous corrosion, atmospheric corrosion, and ionic liquid dissolution studies were performed on commercial alloys AZ31B, AM60, and AZ91D and compared with previously reported results for single-phase binary Mg–Al alloys containing similar Al concentrations (αMg-2 at% Al, αMg-5 at% Al, and Mg-8 at% Al). Polarization studies in 0.6 M NaCl were used to characterize the aqueous free corrosion behavior during 20-h free immersion. Accelerated corrosion testing was performed using a rotating-disk electrode which revealed the evolution of an Al-rich mud-cracking and platelet morphology. Atmospheric droplet testing showed rapid pH increases that depended on the Al concentration in the alloy. Time-dependent contact angle measurements showed that the degree of droplet wetting increased during free corrosion by ~50° over 20 h in 0.6 M NaCl. Ionic liquid dissolution studies in 1:2 M choline chloride:urea deep eutectic solvent were performed in order to examine the current-voltage behavior of these alloys in the absence of water and hydrogen reduction. The results of these studies revealed the formation of nanowire corrosion morphologies within a honeycomb lattice structure which we attribute to selective dissolution of Mg via a two-dimensional stepflow process

25 ENERGY STORAGE↗
NASA NTRS1992

Electrochemical Impedance Of Inorganic-Zinc-Coated Steel

Report describes preliminary experiments to evaluate both direct-current and alternating-current electrochemical impedance measurements as candidate techniques for use in accelerated corrosion testing of mild-steel panels coated with inorganic zinc-rich primers and exposed to seaside air. Basic idea behind experiments to compare electrochemical impedance measurements with anticorrosion performances of coating materials to determine whether measurements can be used to predict performances. Part of continuing program to identify anticorrosion coating materials protecting steel panels adequately for as long as 5 years and beyond.

Macdowell, Louis G.↗
NASA NTRS1984

A study of environmental characterization of conventional and advanced aluminum alloys for selection and design. Phase 1: Literature review

A review of the literature is presented with the objectives of identifying relationships between various accelerated stress corrosion testing techniques, and for determining the combination of test methods best suited to selection and design of high strength aluminum alloys. The following areas are reviewed: status of stress-corrosion test standards, the influence of mechanical and environmental factors on stress corrosion testing, correlation of accelerated test data with in-service experience, and procedures used to avoid stress corrosion problems in service. Promising areas for further work are identified.

Sprowls, D. O.↗
NASA NTRS1984

A study of environmental characterization of conventional and advanced aluminum alloys for selection and design. Phase 2: The breaking load test method

A technique is demonstrated for accelerated stress corrosion testing of high strength aluminum alloys. The method offers better precision and shorter exposure times than traditional pass fail procedures. The approach uses data from tension tests performed on replicate groups of smooth specimens after various lengths of exposure to static stress. The breaking strength measures degradation in the test specimen load carrying ability due to the environmental attack. Analysis of breaking load data by extreme value statistics enables the calculation of survival probabilities and a statistically defined threshold stress applicable to the specific test conditions. A fracture mechanics model is given which quantifies depth of attack in the stress corroded specimen by an effective flaw size calculated from the breaking stress and the material strength and fracture toughness properties. Comparisons are made with experimental results from three tempers of 7075 alloy plate tested by the breaking load method and by traditional tests of statistically loaded smooth tension bars and conventional precracked specimens.

Sprowls, D. O.↗
NASA NTRS1986

Accelerating Corrosion in Solar-Cell Tests

In simple electrochemical cell, two silicon solar cells serve as anode and cathode, respectively. Electrolytic medium and voltage between them accelerate corrosion and migration interactions between cell metal contacts and plastic encapsulant. Degradation of metal contacts becomes evident in few hours. Although developed specifically for cells with Ti/Pd/Ag contacts, technique readily adapted to other metal combinations.

Shalaby, H. M.↗