Stress corrosion cracking of titanium alloys at ambient temperature in aqueous solutions
Stress corrosion tests of titanium alloys in distilled and aqueous salt solutions at ambient temperatures employing single edge notched specimens
SEARCH · Search NASA
Search indexed NASA NTRS and DOE OSTI research on propulsion, heat transfer, battery materials and energy systems. Follow report and document links to the original sources.
Quote a phrase for an exact phrase match. Source license links do not imply unrestricted reuse.
Stress corrosion tests of titanium alloys in distilled and aqueous salt solutions at ambient temperatures employing single edge notched specimens
The stress corrosion susceptibility of two powder metallurgy (P/M) alloys, Al-Li-Cu and Al-Li-Cu-Mg two mechanically attrited (M/A) alloys, Al-Li-Cu and Al-Li-Mg; and two wrought, ingot alloys, X-2020 and AA7475, are compared. Time-dependent fracture in an aqueous sodium chloride environment under alternate immersion condition was found to vary significantly between alloys. The stress corrosion behavior of the two powder metallurgy processed alloys was studied in detail under conditions of crack initiation, static crack growth, and fatigue crack growth. A variety of stress corrosion tests were performed including smooth surface, time-to-failure tests; potentiostatic tests on smooth surfaces exposed to constant applied strain rates; and fracture mechanics-type tests under static and cyclic loads. Both alloys show surface pitting and subsequent intergranular corrosion. Pitting is more severe in the magnesium-bearing alloy and is associated with stringer particles strung along the extrusion direction as a result of P/M processing.
The stress corrosion susceptibility of two powder metallurgy (P/M) alloys, Al-Li-Cu and Al-Li-Cu-Mg; two mechanically attrited (M/A) alloys, Al-Li-Cu and Al-Li-Mg; and two wrought, ingot alloys, X-2020 and AA7475, are compared. Time-dependent fracture in an aqueous sodium chloride environment under alternate immersion condition was found to vary significantly between alloys. The stress corrosion behavior of the two powder metallurgy processed alloys was studied in detail under conditions of crack initiation, static crack growth, and fatigue crack growth. A variety of stress corrosion tests were performed including smooth surface, time-to-failure tests; potentiostatic tests on smooth surfaces exposed to constant applied strain rates; and fracture mechanics-type tests under static and cyclic loads. Both alloys show surface pitting and subsequent intergranular corrosion. Pitting is more severe in the magnesium-bearing alloy and is associated with stringer particles strung along the extrusion direction as a result of P/M processing.
Titanium alloy stress corrosion cracking at ambient temperature in aqueous salt solutions
Stress corrosion cracking susceptibility of titanium alloys in nitrogen tetroxide and aqueous and hot salt environments
Stress corrosion cracking of titanium alloys at ambient temperature in aqueous solution
Aluminum concentration effects on stress corrosion cracking of titanium alloys at ambient temperatures in aqueous solutions of salt
Stress corrosion cracking of titanium alloys at ambient temperature in aqueous solutions
Stress corrosion cracking of titanium alloys at ambient temperature in aqueous solutions
Stress corrosion cracking of titanium alloys at ambient temperature in aqueous solutions
Stress corrosion cracking tests of titanium alloys at ambient temperature in aqueous solutions
Aluminum concentration effects on stress corrosion cracking of titanium alloys in aqueous solutions
Metal composition effects on stress corrosion cracking of titanium alloys in nitrogen tetroxide, water, and salt
Stress corrosion data for titanium alloys in aqueous, hot salt, and nitrogen dioxide environments
The intermetallic compound T1 (Al2CuLi) is suspected to play an important role in the localized corrosion at subgrain boundaries in Al-Li-Cu alloys. The intermetallic was synthesized for characterization of its corrosion behavior. Experiments performed included open circuit potential measurements, potentiodynamic polarization, and corrosion rate vs. pH in solutions whose pH was varied over the range of 3 to 11. Subgrain boundary pitting and continuous subgrain boundary corrosion are discussed in terms of the data obtained. Evidence suggesting the dealloying of copper from this compound is also presented.
Amorphous metallic films of Mo49Ru33B18 and Mo82B18 have been prepared by magnetron sputtering, and their corrosion behavior was investigated and compared with amorphous liquid-quenched Mo49Ru33B18 and crystalline Mo i acidic and basic solutions. Sputtered Mo49Ru33B18 showed lower corrosion rates compared with liquid-quenched Mo49Ru33B18, owing to the superior surface smoothness and uniformity of the former. Amorphous Mo82B18 showed low corrosion rates in both acidic and basic aqueous solutions. Comparison of the corrosion properties of Mo49Ru33B18 with Mo82B18 and Mo demonstrates the roles of the alloys' constituents. Ru significantly extends the passive region to high-anodic potentials, but, at less-anodic potentials, Mo82B18 has the lowest corrosion rate.
Electrochemistry of freshly generated titanium surfaces and stress corrosion cracking in aqueous solutions and in molten salts
Stress corrosion tests of Al-Li-Cu powder metallurgy alloys are described. Alloys investigated were Al-2.6% Li-1.4% and Al-2.6% Li-1.4% Cu-1.6% Mg. The base properties of the alloys were characterized. Process, heat treatment, and size/orientational effects on the tensile and fracture behavior were investigated. Metallurgical and electrochemical conditions are identified which provide reproducible and controlled parameters for stress corrosion evaluation. Preliminary stress corrosion test results are reported. Both Al-Li-Cu alloys appear more susceptible to stress corrosion crack initiation than 7075-T6 aluminum, with the magnesium bearing alloy being the most susceptible. Tests to determine the threshold stress intensity for the base and magnesium bearing alloys are underway. Twelve each, bolt loaded DCB type specimens are under test (120 days) and limited crack growth in these precracked specimens has been observed. General corrosion in the aqueous sodium chloride environment is thought to be obscuring results through crack tip blunting.