Fabrication of Advanced Nanocarbon-Metal Composites for Improved Energy Efficiency
We fabricated nanocarbon metal composites (NCMC) of Al alloys with a process called “electrocharging assisted process” (EAP). This method consists of the application of a high current to a mixture of liquid metal and carbon particles. We investigated aluminum alloys (6061 and 1350) and used activated carbon and graphite powder as the source of carbon. The high current induces the formation of carbon chains and ribbons in the liquid metal. Upon solidification of the metal an epitaxial relation between the carbon nanostructures and the metal lattice is produced. The purpose of the project was to find the parameters during the reaction that would give rise to a high density of nanoribbons extending throughout the metal such that the electrical conductivity and the mechanical strength of the composite increased and that the method could be extended to large scale manufacturing. For this purpose, we designed two reactors for the incorporation of nanocarbon ribbons in aluminum metal. The first reactor was designed to have more control of the region with the high current density. However, there were problems with getting good mixing of the carbon in small volumes. A second reactor was designed with a stirrer that allowed for better mixing of the carbon by the introduction of argon gas through the shaft of the stirrer. NCMC were fabricated with a series of parameters to understand the role of current, time of applied current, type and shape of the cathode electrode and stirring speed of the mixture. We analyzed the composites by Raman scattering to gain information on the crystallite size of the nanocarbon, XRD to obtain the crystal structure of the composite, SEM and TEM to characterize the grain size of the aluminum grains and the quality of the crystal structure. We also measured the electrical conductivity and mechanical properties of selected samples. The nanocomposites showed increase in crystallite size of the nanocarbon with a linear dependence of the crystallite size on the duration of the applied current. There is a minimum current density necessary for the crystallite size to increase compared to the ~ 10 nm size of the activated carbon source used in the fabrication. The electrical conductivity of the nanocomposites increased with crystallite size of the nanocarbon and with the concentration of converted carbon. The maximum increase in electrical conductivity was 5.7% above the baseline for samples with ~ 4 wt % nanocarbon with crystallite size larger than 30 nm. These samples presented a hardness ~ 8% higher than the baseline samples with no carbon.