Tensile properties of co-rolled Zr/U-10Mo fuel at ambient and elevated temperatures
The United States High Performance Research Reactor (USHPRR) initiative is currently interested in replacing high-enriched uranium fuel in research reactors with high-assay low-enriched uranium fuel. Here, this work aimed to assist in that mission by providing tensile and bend test data on bare U-Mo and tensile test data on co-rolled Zr/U-10Mo plates at differing thicknesses (0.285 mm, 0.300 mm, and 0.465 mm) and temperatures (293 K, 473 K, and 623 K). Yield strength and ultimate tensile strength values are reported along with an in-depth comparison of how temperature, rolling direction, thickness, and the presence of the Zr-interlayer affect mechanical properties. Results showed that yield strength and ultimate tensile strength in Zr/U-10Mo foils lower as temperature increases by approximately 300 MPa from 293 to 473 K, and another 100 MPa from 473 to 623 K. Additionally it was found that with increased temperature, there is less differentiation in fuel necking and delamination behavior, as well as a greater perceived elongation to fracture. The elastic modulus of co-rolled mini-plates does not follow the volumetric rule of mixtures in terms of averaged strength and is actually lower than the reported moduli of both Zr and U-10Mo.