NASA NTRS1994

Thermomechanical Fatigue Damage/Failure Mechanisms in SCS-6/Timetal 21S [0/90](Sub S) Composite

The thermomechanical fatigue (TMF) deformation, damage, and life behaviors of SCS6/Timetal 21S (0/90)s were investigated under zero-tension conditions. In-phase (IP) and out-of-phase (OP) loadings were investigated with a temperature cycle from 150 to 650 deg C. An advanced TMF test technique was used to quantify mechanically damage progression. The technique incorporated explicit measurements of the macroscopic (1) isothermal static moduli at the temperature extremes of the TMF cycle and (2) coefficient of thermal expansion (CTE) as functions of the TMF cycles. The importance of thermal property degradation and its relevance to accurate post-test data analysis and interpretation is briefly addressed. Extensive fractography and metallography were conducted on specimens from failed and interrupted tests to characterize the extent of damage at the microstructure level. Fatigue life results indicated trends analogous to those established for similar unidirectional(0) reinforced titanium matrix composite systems. High stress IP and mid to low stress OP loading conditions were life-limiting in comparison to maximum temperature isothermal conditions. Dominant damage mechanisms changed with cycle type. Damage resulting from IP TMF conditions produced measurable decreases in static moduli but only minimal changes in the CTE. Metallography on interrupted and failed specimens revealed extensive (0) fiber cracking with sparse matrix damage. No surface initiated matrix cracks were present. Comparable OP TMF conditions initiated environment enhanced surface cracking and matrix cracking initiated at (90) fiber/matrix (F/M) interfaces. Notable static moduli and CTE degradations were measured. Fractography and metallography revealed that the transverse cracks originating from the surface and (90) F/M interfaces tended to converge and coalesce at the (0) fibers.

Castelli, Michael G.↗
NASA NTRS1965

Carbon and graphite research

Structural changes accompanying creep deformation of pyrolytic carbon and electron micrography and fractography of glassy carbons

ELECTRON MICROSCOPY↗
NASA NTRSDate not supplied

High-Cycle Fatigue Behavior of SiC-based Ceramic Matrix Composites (CMCs) at High Temperatures

High-cycle fatigue (HCF) behavior of a melt-infiltrated, pre-preg SiC/SiC ceramic matrix composite (CMC) was investigated using dogbone tensile specimens without and with simulated cooling holes at 1500 and 2400 °F. The CMC material used for this study was fabricated by GE Aviation and had a ply configuration of [0/90/0]3. HCF tests were conducted with an R-ratio of 0.6 and a cyclic frequency of 30 Hz. Runout in HCF was defined as 30 million cycles. Monotonic tensile tests were conducted at room temperature (RT) on as-received CMC specimens and on runout HCF specimens to determine residual tensile strengths. Digital image correlation (DIC) and acoustic emission (AE) techniques were used to monitor the initiation and progression of damage in RT tensile tests on specimens with and without holes. Microscopy was performed on the polished edge of specimens without cooling holes and on the polished face of specimens with cooling holes that were tested in HCF and achieved runout. Comparisons were made with baseline specimens. Fractography was performed to examine the fracture surfaces of samples that failed under different loading conditions.

Ceramic Matrix Composites↗
NASA NTRS2024

Bending Performance of Tungsten Printed Via Laser Powder Bed Fusion With Ceramic Dispersion Modified Powder Feedstock

Additively manufactured tungsten is a candidate refractory material for high-temperature aerospace and nuclear fusion/fission applications. The printability of pure tungsten is challenged by cracking defects arising from the metal’s high brittle-to-ductile transition temperature and low solubility of interstitial impurities. Furthermore, the cast microstructure inherent to the laser powder bed fusion (L-PBF) process has limited strength compared to worked microstructures common in wrought tungsten. Aside from process-related techniques to mitigate defects and increase strength (e.g., heated build chambers, multi-laser systems, low oxygen environmental control, etc.), micro-alloying additions can positively influence tungsten printability and strength. In this work, pure tungsten L-PBF feedstock was modified with 1 wt% additions of ceramic compound nano-powders. Wrought and printed bars were evaluated in four-point bending. Flexural strength and fractography were primary means of comparison to assess the effect of the feedstock modification on printed tungsten mechanical performance.

Additive Manufacturing↗
NASA NTRS1968

Structural modes of fracture.

Structural modes of fracture, analyzing brittle, ductile, fatigue and stress corrosion fractures using fractography

Gerberich, W. W.↗
NASA NTRS1973

Failure analysis of aluminum alloy components

Analysis of six service failures in aluminum alloy components which failed in aerospace applications is reported. Identification of fracture surface features from fatigue and overload modes was straightforward, though the specimens were not always in a clean, smear-free condition most suitable for failure analysis. The presence of corrosion products and of chemically attacked or mechanically rubbed areas here hindered precise determination of the cause of crack initiation, which was then indirectly inferred from the scanning electron fractography results. In five failures the crack propagation was by fatigue, though in each case the fatigue crack initiated from a different cause. Some of these causes could be eliminated in future components by better process control. In one failure, the cause was determined to be impact during a crash; the features of impact fracture were distinguished from overload fractures by direct comparisons of the received specimens with laboratory-generated failures.

Johari, O.↗
NASA NTRS1972

An investigation of plastic fracture in aluminum alloys

The brittle fracture of many high strength alloys such as steel, titanium, and aluminum was shown to occur by a process called plastic fracture. According to this process microscopic voids form at impurity particles, then grow and coalesce to cause the final rupture. To further understand the role of impurities, four aluminum alloys were investigated: 2024-T851, 2124-T851, 7075-T7351 and 7079-T651. Fractography, quantitative metallography, and microprobe studies assessed the roles of various impurity particles relative to these alloys.

Low, J. R., Jr.↗
NASA NTRS1974

Auger spectroscopy of fracture surfaces of ceramics

Results of Auger electron spectroscopy (AES) studies of fracture surfaces in a series of ceramic materials, including Al2O3, MgO, and Si3N4, which were formed using different processing techniques. AES on the fractured surface of a lunar sample is also discussed. Scanning electron micrograph fractography is used to relate the surface chemistry to the failure mode. Combined argon ion sputtering and AES studies demonstrate the local variations in chemistry near the fracture surface. The problems associated with doing AES in insulators are also discussed, and the experimental techniques directed toward solving them are described.

Marcus, H. L.↗
NASA NTRS1975

Deposition rate and substrate temperature effects on the structure and properties of bulk-sputtered OFHC Cu and Cu-0.15Zr

Bulk-sputtered OFHC Cu and Cu-0.15 Zr used as inner walls of advanced regeneratively cooled thrust chambers are evaluated as to microstructure, surface topography, and fractography. It is found that under conditions of low substrate temperature, crystallite size and openness of the structure increase with increasing deposition rate for both materials. At elevated temperatures, an equiaxed ductile structure of OFHC Cu is produced only at low deposition rates; at higher deposition rate, open structures are observed with recrystallized equiaxed grains within large poorly bonded crystallites. The Cu-0.15 Zr alloy sputtered from the hollow cathode using a diode discharge shows open-type structures for all conditions evaluated. The use of a triode discharge in generating a dense non-voided structure of Cu-0.15 Zr is discussed.

Hecht, R. J.↗
NASA NTRS1977

Investigation of the fracture mechanism in Ti-5Al-2.5Sn at cryogenic temperatures

The influence of microstructure on the fracture mechanism and plane-strain fracture toughness of Ti-5Al-2.5Sn was studied through the use of fractography and metallographic sectioning techniques. One-inch thick plates of extra low interstitial (ELI) and normal interstitial Ti-5Al-2.5Sn were mill annealed at 815 C followed by either air or furnace cooling. These variations in composition and cooling rate resulted in differences in the volume fraction and internal structure of the iron-stabilized phase, and in the crystallographic texture and ordering of the alpha matrix. The tensile properties of these plates were determined at 20 K, 77 K, and 295 K. The air-cooled ELI plate was the toughest material evaluated.

Vanstone, R. H.↗
NASA NTRS1977

A fundamental approach to adhesion: Synthesis, surface analysis, thermodynamics and mechanics

The effects of composites as adherends was studied. Several other variables were studied by fractography: aluminum powder adhesive filler, fiber glass cloth scrim or adhesive carrier, new adhesives PPQ-413 and LARC-13, and strength-test temperature. When the new results were juxtaposed with previous work, it appeared that complex interactions between adhesive, adherend, bonding, and testing conditions govern the observed strength and fracture-surface features. The design parameters likely to have a significant effect upon strength-test results are listed.

Dwight, D. W.↗
NASA NTRS1977

The effect of microstructure and strength on the fracture toughness of an 18 Ni, 300 grade maraging steel

Fractography and metallographic sectioning were used to investigate the influence of microstructure and strength on the fracture toughness (KIc) and fracture mechanism of an 18 Ni, 300 grade maraging steel. Increased yield strength from 1442 to 2070 MN/m squared through precipitation hardening results in a KIc loss from 143 to 55 MN/m superscript 3/2. Ti (C,N) Ti2S, and TiC inclusions in sizes from 1 to 8, 1 to 15, and 0.1 to 2 microns respectively serve as sites for void nucleation and lead to fracture by the dimpled rupture process in all strength levels considered. TiC nucleated dimples occupy more than half the fracture in all conditions. Void nucleation rate and resultant number of dimples per unit area of fracture increase with increasing yield strength. Average dimple size decreases with increasing strength and/or overaging which follows from the decreasing amount of stable void growth measured by sectioning tensile specimens. Void growth is assisted by crack branching along a path of TiC inclusions. Coalescence occurs in the highest strength materials by a combination of TiC void nucleation and premature separation at strengthening precipitates.

Psioda, J. A.↗
NASA NTRS1978

Fractographic evaluation of creep effects on strain-controlled fatigue-cracking of AISI 304LC and 316 stainless steel

Analysis of high temperature low cycle fatigue of AISI 304LC and 316 stainless steels by the method of strainrange partitioning results in four separate strainrange versus life relationships, depending upon the way in which creep-strain and plastic strain are combined within a cycle. Fractography is used in this investigation of the creep-fatigue interaction associated with these cycles. The PP and PC-cycle fractures were transgranular. The PC-cycle resulted in fewer cycles of initiation and shorter total cyclic life for the same applied inelastic strainrange. The CC-cycle had mixed transgranular and intergranular fracture, fewer cycles of initiation and shorter cycle life than PP or PC. The CP-cycle had fully integranular cracking, and failed in fewer cycles than were required for cracks to initate for PP,PC, and CC.

Oldrieve, R. E.↗
NASA NTRS1979

A fundamental approach to adhesion: Synthesis, surface analysis, thermodynamics and mechanics

Adherend surfaces and fractography were studied using electron spectroscopy for chemical analysis and scanning electron microscopy/energy dispersive analysis of X-rays. In addition, Auger Electron Spectroscopy with depth profiling capability was used. It is shown that contamination of adhesion systems plays an important role not only in determining initial bond strengths but also in the durability of adhesive bonds. It is concluded that the analytical techniques used to characterize and monitor such contamination.

Chen, W.↗
NASA NTRS1980

3500-hour durability testing of ceramic materials for automotive gas turbine engines

A two-year durability program was performed by AiResearch Phoenix to evaluate four commercially available ceramic materials under simulated automotive gas turbine combustor discharge conditions. These conditions included extended cyclic thermal exposures up to 2500 F and 3500 hr. The four materials selected for evaluation were Norton NCX-34 hot pressed silicon nitride, AiResearch RBN 101 reaction bonded silicon nitride, Carborundum pressureless sintered alpha-SiC and Pure Carbon Co. (British Nuclear Fuels, Ltd.) Refel reaction sintered silicon carbide. These materials were initially exposed to 350 hr/1750 cycles at 1200 and 1370 C. Subsequent exposures to 1050, 2100 and 3500 hr were performed on those materials maintaining 50% of baseline strength after the initial exposure. Additional evaluations of exposed bars included dimensional and weight changes, dye penetrant, specific damping capacity changes, SEM fractography, and X-ray diffraction.

Carruthers, W. D.↗