DOE OSTI2022

On the efficacy of post-build thermomechanical treatments to improve properties of Zirconium fabricated using ultrasonic additive manufacturing

Here, hot-isostatic pressing has been applied to Zirconium plate fabricated using the ultrasonic additive manufacturing (UAM) technique to enhance interfacial bond quality. Specimens heated to 800 C for 1 h at 100 MPa pressure showed grain growth across many prior foil-to-foil interfaces, thereby increasing foil adhesion. In addition to the material softening induced by a loss of Hall-Petch strengthening, premature failure of specimens loaded parallel to the build direction was observed. Premature specimen failure was attributed to the local delamination at prior foil-to-foil boundaries where grain growth was pinned by Ti impurities introduced during the UAM process via the interaction between a Ti-alloy buffer foil and the welded Zr-foils underneath. In addition, the presence of Ti along select foil interfaces resulted in the nucleation and growth of secondary (Zr,Ti)(Fe,Cr) laves phases during higher-temperature thermomechanical processing. Using a combination of micro-scale X-ray computed tomography, fractography, and in-situ digital image correlation, the effect of defects along prior foil-to-foil boundaries was revealed as delamination-assisted plasticity accelerated specimen failure in preferred tensile orientations. These findings underscore the importance of impurity control when optimizing weld quality of higher-strength material systems using ultrasonic welding.

36 MATERIALS SCIENCE↗
DOE OSTI2020

A novel fiber-fretting test for tribological characterization of the fiber/matrix interface

Ceramic matrix composites exhibit excellent high temperature properties and are candidate materials for structural applications from jet engines to nuclear fuel cladding. The strength and deformation behavior of these composites are intrinsically tied to the properties of the fiber/matrix interface. This research introduces a novel technique to evaluate the fundamental friction and wear characteristics of these interfaces. A case study on SiC f /PyC/SiC m composites applies in situ fiber fretting to investigate the kinetic friction coefficient and cyclic wear characteristics of the interphase. The experimental methodology is presented in explicit detail to encourage other researchers to explore the capabilities of this technique. Additionally, testing was carried out as a function of fiber roughness, PyC thickness (≈10, 500, 1200 nm), cycle count (10, 100, 1000), and frequency (1, 5, and 10 Hz). The friction coefficient and wear behavior changed with cycle length due to a transition from adhesive to abrasive mechanisms. SEM fractography provided insights to tribological evolution from adhesive sliding to three-body abrasive wear. The structural disorder at the tribo-surface relating to graphitic content and dangling bond density was investigated using Raman spectroscopy. Properties are contextualized with comparison to uniaxial tensile behavior of the parent composite.

36 MATERIALS SCIENCE↗
DOE OSTI2024

IASCC of 304 SS in BWR environments: Effects of post-irradiation annealing and surface condition

To investigate the impact of low-temperature post-irradiation annealing (PIA) on the stress corrosion cracking of neutron-irradiated 304 stainless steel, constant extension rate tests were conducted in simulated boiling water reactor normal water chemistry (BWR-NWC) and hydrogenated water chemistry (HWC) environments. Ten tensile samples, comprising five as-irradiated and five PIA specimens, were prepared by electropolishing the gauge section of electric discharge machined (EDM) samples. Here, the annealing treatment reduced the yield strength from approximately 550 MPa to around 425 MPa and significantly restored the ductility and the strain hardening capability of the alloy. Consequently, the susceptibility of this material to irradiation-assisted stress corrosion cracking (IASCC) was effectively mitigated, which is more prominent in HWC, as evident from fractography, which indicated a decreased propensity for intergranular (IG) fracture. Furthermore, it was observed that the polished surface facilitated crack initiation more readily than the EDM surface, suggesting that the EDM process suppressed crack initiation to some extent.

Crack initiation↗
DOE OSTI2021

Technological aspects in blanket design: Effects of micro-alloying and thermo-mechanical treatments of EUROFER97 type steels after neutron irradiation

Presently available data on neutron irradiation damage raise doubts on the feasibility of using EUROFER97 steel for a water-cooled starter blanket in a DEMO reactor, since the ductile-to-brittle transition temperature (DBTT) increases significantly for irradiation temperatures below 350°C. The additional DBTT shift caused by H and He transmutation can only be estimated based on very few results with isotopically tailored EUROFER97 steel. Conservative calculations show that the DBTT of EUROFER97 steel could exceed the operating temperature in water-cooled starter blankets within a relatively short time period. This paper presents results from a EUROfusion funded irradiation campaign that was performed in the High Flux Isotope Reactor at Oak Ridge National Laboratory. The paper compares ten newly developed reduced activation ferritic-martensitic (RAFM) steels irradiated to a nominal dose of 2.5 dpa at 300°C. The post-irradiation experiments using Small Specimen Test Technology included hardness, tensile, and fracture mechanics tests combined with fractography and microstructure analysis are presented. Results show that micro-alloying EUROFER97-type steels influenced the mechanical properties but a dominating impact on irradiation damage resistance could not be identified. In contrast, specific thermo-mechanical treatments lead to better DBTT behavior. Discussion about irradiation response to heat treatment conditions is also given. Here, despite requiring data also at high dpa values, the results indicate that with these modified materials an increased lifetime and potentially also an increased operating temperature window can be achieved compared to EUROFER97.

70 PLASMA PHYSICS AND FUSION TECHNOLOGY↗
DOE OSTI2024

Effects of hydrogen partial pressure on crack initiation and growth rate in vintage X52 steel

There is an increasing interest in ensuring compatibility of existing natural gas infrastructure with conveyance of hydrogen, especially for vintage (pre-1970s) pipeline steels. While hydrogen is known to affect the fatigue and fracture resistance of these materials, there is a lack of data on its effects on crack initiation at low hydrogen partial pressure. To address this gap, the current work presents a series of fatigue tests on vintage API Grade X52 steel in pure nitrogen, air and gaseous hydrogen at partial pressures of 1 and 207 bar. Circumferential notch tension (CNT) specimens with direct current potential difference (DCPD) measurements are used to get S–N curves for crack initiation and failure, and compact tension (CT) tests to assess crack growth rates. Results indicate that air accelerates crack initiation, low hydrogen partial pressure affects the crack growth rate, and higher pressures have the largest impact on both. Surprisingly, crack initiation is faster in air than at 1 bar hydrogen partial pressure. The CNT tests also reveal that the orientation of the banded microstructure has no effect on the crack initiation site, but it influences its growth behavior. Moreover, fractography shows that hydrogen also promotes instances of quasi-cleavage and intergranular fracture, linked to embrittlement of the material. Here, these results demonstrate that, while hydrogen may impact the entirety of the fatigue process, its effects on the early stages of damage accumulation become relevant only at larger pressures. More comprehensive studies of crack initiation in hydrogen atmospheres will be critical to future codes and standards for hydrogen infrastructure.

Circumferential notch tension↗
DOE OSTI2025

Ultra-high temperature testing and performance of L-PBF C103

Additive Manufacturing (AM) of refractory alloys is gaining traction as a materials processing route for components subject to extreme temperature environments. Due to the low oxidation resistance of refractory alloys, novel methods for evaluating their elevated temperature performance must be developed. In this work, a Gleeble® 3800 thermomechanical load frame was modified to evaluate the mechanical properties of laser powder bed fusion (L-PBF) consolidated niobium alloy C103 ranging from room temperature (RT) to 1400 °C. The fixturing and sample geometry were designed to accommodate Joule heating and prevent damage to the test chamber. Oxidation of the samples was minimized via testing in vacuum level of 1E-5 Torr. Ultimate tensile strength (UTS), yield strength (YS), elongation, and strain-hardening behavior were determined as a function of temperature. L-PBF C103 presented an average UTS of ∼650 MPa and over 25 % elongation at RT. Above RT, the UTS and YS dropped then leveled off from 500 °C to 1000 °C with values ranging from ∼400 MPa to ∼460 MPa, which is consistent with dynamic strain aging observed in this class of alloys. The strength rapidly declined after 1200 °C to ∼150 MPa at 1400 °C. Fractography indicated ductile fractures for the C103 at all test temperatures, and Electron Backscatter Diffraction (EBSD) analysis revealed a textured microstructure and the presence of dynamic recrystallization within the necked region of the sample tested at 1400 °C.

33 ADVANCED PROPULSION SYSTEMS↗
DOE OSTI2023

Investigating the failure behavior of cast Al-11Ce-0.4Mg alloys using in-situ scanning electron microscopy tensile testing

Within the last decade, research on Al-Ce-Mg alloys has reported promising results for use in cast part applications. In this paper, the failure behavior of cast Al-11Ce-0.4Mg (wt%) was investigated experimentally with focus on the effect the matrix and intermetallic phases have on the fracture propagation behavior at failure. For the first time, in-situ SEM tensile testing was used to study the failure behavior of cast Al-Ce alloys, reporting results for uniaxial, DIC, and single edge notch tensile tests. The results of the in-situ SEM tensile testing were compared with the materials characterization experiments, which included serial sectioning, EBSD, EDS, and fractography. Analysis of EBSD and EDS mapping of cast Al-11Ce-0.4Mg showed that the cast microstructure was a hypereutectic two phase Al-Ce alloy with grains encompassing large complex colonies of laminar eutectic Al 11 Ce 3 intermetallic. The uniaxial tensile results reported the effect casting defects have on the strength and ductility of the alloy, and DIC in-situ testing showed that the eutectic colonies plastically deform less than the matrix phase. In-situ SEM single edge notch tensile testing displayed how the strength of an individual phase affected the crack propagation direction in the alloy. The results of both the materials characterization and in-situ tensile testing experiments on the failure of this alloy revealed further directions for future alloy development that can improve both the strength and fracture toughness of Al-Ce-Mg alloys.

36 MATERIALS SCIENCE↗
DOE OSTI2022

Mechanical joint performances of friction self-piercing riveted carbon fiber reinforced polymer and AZ31B Mg alloy

Carbon fiber reinforced polymer (CFRP) and AZ31B Mg alloy were joined by the friction self-piercing riveting (F-SPR) with different steel rivet shank sizes. With the increase of rivet shank size, lap shear fracture load and mechanical interlock distance increased. Ultrafine grains were formed at the joint in AZ31B as a result of dynamic recrystallization, which contributed to the higher hardness. Fatigue life of the CFRP-AZ31B joint was studied at various peak loads of 0.5, 1, 2, and 3 kN and compared with the resistance spot welded AZ31B-AZ31B from the open literature. The fatigue performance was better at higher peak load (>2 kN) and comparable to that of resistance spot welding of AZ31B to AZ31B at lower peak loads (<1 kN). From fractography, the crack initiation for lower peak load (<1 kN) case was observed at the fretting positions on the top and bottom surfaces of AZ31B sheet. When peak load was increased, fretting between the rivet and the top of AZ31B became more dominant to initiate a crack during fatigue testing.

36 MATERIALS SCIENCE↗
DOE OSTI2020

Tensile behavior and microstructural evolution of a Fe-25Ni-20Cr austenitic stainless steel (alloy 709) from room to elevated temperatures through in-situ synchrotron X-ray diffraction characterization and transmission electron microscopy

Uniaxial tensile tests were done on Fe-25Ni-20Cr Austenitic Stainless Steel (Alloy 709) along with in-situ synchrotron measurement at different temperatures (25 degrees C, 500 degrees C, 700 degrees C and 900 degrees C). The X-Ray diffraction data was collected in-situ in order to follow the phases present as well as to derive the dislocation density as a function of strain through peak broadening analysis based on the modified Williamson-Hall method and see how trends are affected as a function of temperature. The XRD data were complemented by TEM and STEM-EDX characterization done on the post-experiment samples to observe the deformed microstructures. Finally, the paper presents a depiction of the tensile behavior of this advanced steel by interpreting the stress-strain curves and the effect of temperature through the information gained by in-situ XRD and TEM observations as well as fractography done ex-situ on the samples tested to rupture.

36 MATERIALS SCIENCE↗
DOE OSTI2021

Investigation of hardening mechanisms and size effects in proton-irradiated HT-9 steels

Ferritic/martensitic steels, such as HT-9, are known for their complex microstructural features and mechanical properties. Here in this paper, in-situ micro-tensile tests and traditional fractography methods were utilized to study the fracture behavior of proton-irradiated HT-9 steels. First, to evaluate the viability of micro-tensile tests for nuclear material qualification process, meso-tensile tests on as-received HT-9 steels were performed. Fracture mechanisms of unirradiated HT-9 steels at both length scales were compared and underlying mechanisms discussed. The direct comparison of micro- and meso-scale data shows a distinctive size effect demonstrated by the increase in yield stress (YS). Upon completion of initial assessment, specimens were irradiated with 4 MeV + protons to three fluences, all of which were lower than 0.01 displacements per atom (dpa). As expected, the YS increases with irradiation. However, at 7 × 10 -3 dpa, the reversal of the trend was observed, and the YS exhibited sharp decline. We demonstrate that at lower length scales, grain structure has a more profound impact on the mechanical properties of irradiated materials, which provides information needed to fill in the gap in current understanding of the HT-9 fracture at different length scales.

36 MATERIALS SCIENCE↗
DOE OSTI2021

Influence of neutron irradiation on Al-6061 alloy produced via ultrasonic additive manufacturing

Samples of aluminum alloy 6061 produced via ultrasonic additive manufacturing (UAM) were irradiated in the High Flux Isotope Reactor (HFIR) up to 17.3 dpa at ~70°C while in contact with water using perforated rabbit capsules. The irradiation campaign included as-received (AR) material, specimens subjected to various post-weld heat treatments (PWHTs, including hot isostatic pressing [HIP]), and reference (wrought) alloy samples. Mechanical tensile tests, accompanied by digital image correlation (DIC) analysis, fractography, and metallography, were performed as a part of the post-irradiation evaluation. The X- and Y-specimens (i.e., oriented in the sonotrode moving and vibration directions, respectively) showed pronounced radiation hardening and ductility decrease. Specific serration flow behavior and propagation of deformation bands were observed under various material conditions up to 3.5 dpa but disappeared at 17.3 dpa. In all cases, the fracture mechanism of X- and Y-specimens was ductile; ductile dimples dominated the fracture surface. Irradiated X- and Y-specimens showed good performance, regardless of material conditions (AR or PWHT). The performance of Z-specimens oriented in the build direction was strongly dependent on the PWHT. The AR and aged specimens showed fracture stress decrease with dose, and they experienced fracture under irradiation after 3.5 dpa; specimen cross section analysis revealed specific interface degradation that was likely related to corrosion. Recrystallization significantly improved in-reactor performance. Finally, HIP suppressed interface degradation due to recrystallization and pore removal, which led to good in-reactor performance for Z-specimens.

36 MATERIALS SCIENCE↗
DOE OSTI2023

The effects of radiation-induced grain subdivision and dislocations on the fracture properties of uranium dioxide

Microcantilever bending tests were applied on uranium dioxide samples irradiated by 84 MeV Xe ions. Depending on the initial grain sizes, different levels of grain subdivision and dislocation development were observed near the irradiated surface. These radiation damage features were shown to degrade the fracture properties of both samples. The fundamental aspects of the radiation-microstructure-property relationships were discussed in this paper, taking a holistic consideration of the microcantilever bending data, fractography and microstructures. The separate effects of the irradiation-induced grain subdivision and dislocations on the fracture initiation and propagation of uranium dioxide were discussed. In conclusion, it was observed that radiation-induced dislocations and grain subdivision, without the presence of Xe bubbles co-located with the defects, cause reductions in the Young's modulus, fracture strain, and fracture stress, and a transition to intergranular fracture.

36 MATERIALS SCIENCE↗
DOE OSTI2025

Impact of post-irradiation annealing on mechanical performance of irradiated 718 alloy

Here, the effect of post-irradiation annealing on solution-annealed 718 alloy was investigated using advanced mechanical testing, fractography, scanning electron microscopy, and transmission electron microscopy. Specimens were extracted from a proton beam window operated at the Spallation Neutron Source, irradiated with 940 MeV protons to a maximum dose of approximately 9.7 displacements per atom (dpa) at a calculated temperature not exceeding 110 °C while in service. Helium and hydrogen concentrations reached about 1700 and 6900 atomic parts per million (appm), respectively. Despite irradiation and high tensile strength (yield stress over 1 GPa), the material exhibited significant ductility. Annealing at 500 °C, 700 °C, and 900 °C for 30 min resulted in an appreciable decrease in yield strength and an increase in ductility for annealing treatments at 500 °C and 900 °C relative to the strength and ductility of the as-irradiated material. The presence of helium and hydrogen led to cavity formation and cleavage-like brittle features on fractured surfaces; however, high-magnification imaging revealed the presence of small-scale ductile dimples, indicating that the fracture mechanism remained mixed. The annealed specimens retained total elongation levels of 14–33 %, and there was no sudden drop in ductility after heat treatments. The ductility level in the irradiated and annealed material is notable despite the presence of helium and hydrogen.

36 MATERIALS SCIENCE↗
DOE OSTI2026

A comparison of wrought and powder metallurgical FeCrAl claddings under simulated LWR accident transients

Iron-chromium-aluminum (FeCrAl) alloys are potential accident tolerant fuel (ATF) cladding candidates for light-water reactors but are difficult to fabricate as thin-walled tubes via conventional cast-and-wrought routes. Powder metallurgy (PM) offers a manufacturing alternative with improved compositional control, but its transient accident performance has not been directly benchmarked against wrought variants. This study evaluates the burst behavior of commercially developed PM-processed FeCrAl alloys, PM-C26M (Fe-12Cr-6Al-2Mo) and the high precipitate density FA-SMT (Fe-22Cr-5Al-3Mo), under simulated light-water reactor accident transient conditions. Burst testing was conducted using the Severe Accident Test Station with heating rates of 5 °C/s and 50 °C/s and internal pressures ranging from 25 MPa to 100 MPa. PM-C26M reproduced wrought C26M burst behavior within 7–37 °C across the stress range, indicating that PM processing does not compromise transient strength. FA-SMT exhibited markedly higher burst temperatures and reduced heating-rate sensitivity, consistent with its engineered precipitate strengthening. FA-SMT rupture exhibited axial "unzipping" rather than the lateral tearing characteristic of PM- and wrought C26M. Post-test EBSD and fractography indicate that this behavior is strongly correlated with strain-gated intergranular void nucleation associated with the dense precipitate architecture of FA-SMT, a response absent in the comparatively clean PM-C26M matrix and consistent with rupture morphologies reported for oxide-dispersion strengthened (ODS) FeCrAl of similar base-matrix chemistry to PM-C26M. These findings highlight the potential of powder metallurgy as a viable fabrication route for ATF claddings from an accident performance standpoint.

Bell, Sam [ORNL] (ORCID:0000000251905657)↗
DOE OSTI2020

Effect of aging on failure mechanism of Alloy 709 at various temperatures

Alloy 709 is a novel austenitic stainless steel with high temperature creep strength, weldability, and corrosion resistance. These properties make the material suitable for applications in the structure of next-generation nuclear power plants. Enduring high temperatures for an extended period of time in the harsh environments of a nuclear power plant results in thermal aging of the material. Therefore, it is imperative to study the effect of thermal aging on the microstructure and mechanical properties of Alloy 709 before its application in the next generation power plants. In this study, hot-processed (forged + rolled), annealed and quenched ingots of Alloy 709 are aged at 650 °C for 2000 h in air and then tested at various temperatures up to 850 °C in an in-situ heating-loading Scanning Electron Microscope (SEM) equipped with Energy Dispersive Spectroscopy (EDS) and Electron Backscatter Diffraction (EBSD). The effect of testing temperature and aging on microstructural evolutions during tensile testing of as-received and aged samples are studied. Furthermore, both as-received and aged samples displayed serrations and drop in ductility at elevated temperatures, due to the effect of dynamic strain aging (DSA). The occurrence of DSA activity was found within temperatures range of 500 °C–750 °C in as-received and 550 °C - 650 °C in aged samples. The aged samples showed less elongation accompanied by shallower dimples on the fractured surface, indicating less ductile failure mechanism compared to as-received samples. Failure mechanism observations on the fracture surface using SEM fractography are correlated to the observations made on the sample surface using in-situ SEM to achieve a complementary set of information to better understand the failure mechanism of this novel alloy.

36 MATERIALS SCIENCE↗
DOE OSTI2021

A study on the creep behavior of alloy 709 using in-situ scanning electron microscopy

In this research, an experimental evaluation of creep properties of Alloy 709 in the temperature range of 750–850 °C was undertaken. Alloy 709 is a novel austenitic stainless steel with 20% Cr and 25% Ni by wt% that was developed for application in structural components of nuclear power plants. Creep rupture tests were conducted in an in-situ heating-loading and Scanning Electron Microscope (SEM) unit equipped with Electron Backscatter Diffraction (EBSD) detector and Energy Dispersive Spectroscopy (EDS). “Real-time” creep damage mechanisms of Alloy 709 at various stresses and temperatures using a flat, un-notched sample with continuously reducing cross-section is studied so that the failure and maximum creep damage occurred at the center of the sample where the in-situ SEM imaging could be focused. Accelerated creep tests at temperatures and stresses above service conditions were performed by employing multiple blocks of constant loads where the loads were increased once the sample attained constant creep rate, indicating a secondary creep regime. This technique ensures multiple data points can be obtained from the same test, saves the time required for an otherwise long-term creep test and usage of SEM. Further, Coincident Site Lattice (CSL) boundary maps were collected as control maps before testing, and the grain boundaries were observed during the creep test to understand the effect of grain boundary character on the creep damage mechanism. Void growth, grain boundary separation, and sliding were found to be the main creep mechanisms whose rate is dependent on stress and temperature. Failure mechanisms studied on the fracture surface using SEM fractography were correlated to the sample surface observations to create complementary information to better understand the underline creep mechanism of Alloy 709.

36 MATERIALS SCIENCE↗
DOE OSTI2024

Microstructure and mechanical properties of friction stir weld performed on neutron-irradiated 304L steel with helium

As nuclear power plants (NPPs) approach or exceed 40–60 years of service, it may become necessary to repair damaged neutron-irradiated components to prolong longevity. However, fusion welding repair of irradiated steels and metallic materials is challenging because of helium-induced cracking. This study used friction stir welding (FSW) to address helium-related issues, such as helium bubble formation and grain boundary cracking. The microstructure, helium-induced degradation, and mechanical properties of a friction stir weld produced on neutron-irradiated 304L stainless steel with approximately 5.2 appm of helium were characterized. The analysis focused on variations in grain size, texture, and the morphology of helium-induced damage in the friction stir weld. Mechanical properties were characterized on the irradiated base metal (BM) and metallurgical zones of the friction stir weld: the stir zone (SZ), the thermo-mechanically affected zone (TMAZ), and the heat affected zone (HAZ). Only minor scattered porosity in the SZ and TMAZ and a few short microcracks (below 20 μm in length) in the TMAZ were observed, indicating limited helium-induced degradation. Tensile tests revealed good mechanical properties and fractography analysis demonstrated predominantly ductile fracture. In conclusion, the results highlight the immediate and substantial benefits of the FSW approach for repairing or joining helium-containing irradiated materials in NPPs.

36 MATERIALS SCIENCE↗
DOE OSTI2025

Surface smoothing for laser powder-bed Ti-6Al-4V by a transient liquid phase

Surface roughness is the primary driver of fatigue for additively manufactured metals. To address surface roughness, this work introduces a new method to smooth features beyond line-of-sight without material removal. The method applies a coating that triggers local surface remelting by activating a eutectic reaction during heat treatment. The associated liquid phase then wets and isothermally solidifies into a smoother surface. For Ti-6Al-4V fabricated with laser powder bed fusion, samples with and without TLP smoothing (using a Cu coating) were characterized with a suite of techniques, including mechanical testing, electron backscatter diffraction, synchrotron X-ray tomography, and fractography. TLP smoothing reduced surface roughness by 80% and amplified compressive residual stress at the surface by about 50%. With statistically equivalent virtual microstructures, crystal plasticity scrutinized the roles of phases, porosity, and surface roughness. Although the tensile strain-to-failure was reduced to 1% strain, the TLP smoothing process increased high-cycle fatigue strength by about 20% compared to control samples, pointing to future opportunities to optimize the new process through various coating compositions and heat treatment schedules. Overall, this work establishes a new paradigm for treating surfaces of materials for smoothness and compressive residual stress.

Additive manufacturing↗