DOE OSTI2020

BACKFLIP Project: Determination of BACKsheet Material Properties: A Comparison of Market-Benchmark Technologies to Novel Non-Fluoro-Based Co-Extruded Backsheet Materials and Their Correlation and Impact on PV Module Degradation Rates

Quantifying degradation rate of backsheets will help procuring materials for 30+ years. Today most backsheets on the market have a laminated PET core; polyolefin materials may provide better properties for backsheets (barrier to water, mechanical properties through UV and hydrolytic environments, etc.). End-of-life regulations may require fluorine-free backsheet products in future global markets. Parametrized equation predicting the service life of backsheets, and validated by both lab and outdoor extensive testing. Technical and commercial confidence to the entire value chain: from backsheet and module manufacturers to the downstream community (IPP, banks, developers) that materials of higher quality can help reduce finance costs, therefore driving down LCOE. A fast track PV module market adaptation for novel high-quality materials, such as co-extruded polyolefin-core backsheets, by obtaining unbiased durability data.

14 SOLAR ENERGY↗
DOE OSTI2019

Thermally Conductive Backsheets (TCB) for Reduced Operating Temperatures

The performance of photovoltaic (PV) modules is primarily influenced by the plane of array (POA) irradiance and their operating temperature. The lower the module operating temperature, the higher is its performance. Increasing a module’s operating temperature reduces its power output due to an increase in the semiconductor’s intrinsic carrier density, leading to a reduction in the open-circuit voltage and, subsequently, reducing the maximum power point voltage. Reducing the operating temperature lowers the levelized cost of energy (LCOE) via increased energy production (i.e., more kilowatt hour over the life of the asset) and increased service lifetime (years in the field). The module operating temperature is dictated by the weather parameters and the thermal properties of module construction materials. The primary weather parameters influencing the PV module temperature are: the ambient temperature (directly related), irradiance (directly related), and wind speed (inversely related). The primary thermal properties of module construction materials influencing the PV module temperature are: the optical transmissivity and thermal conductivity of superstrate, the thermal conductivity of substrate, the thermal conductivity of encapsulant and the efficiency of the encapsulated solar cells. The primary goal of this study is to reduce the operating temperature of PV modules using thermally conductive backsheet (TCB) substrates developed by the industry. The temperature of PV modules installed in a large multi-MW plant can also be influenced by their physical locations in the plants due to the influence of wind direction. A thermal mapping of PV plants has also been investigated and presented in this study. The most commonly used PV backsheet material has been polyvinyl fluoride (DuPont trade name “Tedlar”)-based backsheet, which typically has three layers: Tedlar–polyethylene terephthalate (PET)–Tedlar (TPT). The primary goal of this project is to reduce the module operating temperature below the benchmark TPT backsheet temperature using newly developed TCBs by the industry. The overall approach of this project involves six focus areas: i) select and procure one TPT and thirteen promising TCBs available in the industry; ii) construct a large number of 1-cell and 9-cell modules using benchmark TPT and selected TCBs [all other construction materials are fixed and they are: glass superstrate, EVA encapsulant, mono-Si cell and junction box]; iii) to identify best performing TCBs, monitor the long-term field operating temperatures of the constructed modules which are installed in three climatic conditions (hot-low wind [Mesa, AZ], hot-high wind [Maricopa County, AZ] and temperate [Cumberland County, NC]; iv) to identify the most durable TCB, perform extended accelerated reliability testing of modules constructed with best three TCBs and benchmark TPT; v) to predict module temperature, develop physical and empirical thermal models with and without thermal properties of all construction materials in the modules, respectively; and vi) to determine the influence of wind speed and direction on the module operating temperature in a plant, and perform thermal mapping of PV modules in two large PV plants [Maricopa County, AZ and Cumberland County, NC]. The key achievements of this project are listed below: Backsheet selection: 14 backsheets were procured after an extensive literature and industry search. Finally, based on the thermal and other selection criteria, 1 TPT and 4 thermally conductive backsheets were selected for this project. Fabrication of mini modules: 50 one-cell modules were fabricated in year 1 for thermal performance evaluation. The module design was changed to nine-cell module at start of year 2 to mimic commercial design. 20 nine-cell modules were fabricated in year 2 for thermal performance evaluation. 28 four-cell modules were fabricated in year 3 for accelerated stress-testing. Thermal conductivity of backsheets: Year 1 TCBs showed at least 8% higher thermal conductivities than TPT. Year 2 and 3 TCBs showed at least 20% higher thermal conductivities than TPT. Installation of mini PV modules at three sites: 6 one-cell modules and 8 nine-cell modules were installed at AZ-1 site [Mesa, AZ]. 12 one-cell modules and 6 nine-cell modules were installed at each of two powerplants (AZ-2 [Maricopa County, AZ] and NC sites). Nominal operating cell temperatures (NOCT) of mini PV modules: NOCT of TCBs were observed to be lower than TPT with differences as high as 2°C. Comparison of thermal performance: The median operating temperature of one-cell modules was found to be reduced by 2°C by using TCB_A modules compared to TPT modules on several days in a month for few months in a year. The median temperature improvement of 4oC was achieved at several instances on a few days, but not all days, in a year using multiple TCBs compared to TPT. The final project milestone of achieving median temperature improvement of 5oC was achieved at several instances on a few days, but not all days, in a year using TCB_A compared to TPT. Empirical thermal model (without the need of construction material properties): Empirical thermal model for one-cell module was developed based on the input data of irradiance, wind speed and ambient temperatures. The primary input data differentiator for temperature differences between TPT and TCBs appears to be the irradiance level (solar gain). Accelerated durability testing: 20 four-cell modules using 4 backsheets (1 TPT and 3 TCBs) were exposed to Damp Heat 1000 hours (8 modules), UV/Thermal cycling (50 cycles)/Humidity freeze (10 cycles) test sequence (8 modules) and UV Weathering for qualification (8 modules). All the modules with four selected backsheets passed the stress tests per the retest guidelines of IEC 61215 standard for the backsheet change. Simplified comparative LCOE analysis: Using backsheet-specific power degradation levels in the accelerated tests (for TCB_A and TPT only), efficiency, service lifetime and assuming same cost for all backsheets, the LCOE of modules using TCB_A is determined to be lower than TPT. Due to lower operating temperature of TCB_A-based modules compared to TPT-based modules, the operating efficiency and service life of TCB_A-based modules are calculated to be higher than TPT-based modules. Temperature mapping of PV power plants: A distinct temperature difference (as high as 4°C) has been observed between the modules located in various parts of a single PV plant.

14 SOLAR ENERGY↗
DOE OSTI2024

Monitoring of Photovoltaic (PV) Performance and Degradation: Integrated Renewable Energy Systems (IRES) - PV Monitoring Task

The Integrated Renewable Energy System (IRES) testbed demonstration at the Pacific Northwest National Laboratory (PNNL) Sequim campus includes development of a suite of capabilities for tracking the performance of photovoltaic (PV) renewable energy components located on a floating platform (floating PV) and on a shoreline building rooftop. The marine environment represents potentially harsh and corrosive conditions for PV modules. Compared to terrestrial PV, potential concerns for offshore PV arising from high humidity and occasional contact with saltwater, marine wildlife, and aquaculture. These environmental factors can reduce electricity generation efficiency and increase the risk of electrical faults, polymer insulation or jacketing degradation and hydrolysis of the PV cell encapsulant materials. Offshore PV modules may also be exposed to lower temperatures and buoyant and vibrating motions with a floating platform. It is not clear how the long-term performance of floating PV will be affected by these factors. To understand expected energy generation through solar cells on a floating platform, monitoring of the performance of PV modules in the marine environment is needed. This report outlines a plan for long-term testing of IRES PV components utilizing resources of the PNNL Material Aging and Detection (MAaD) Science team and the Marine and Coastal Research Laboratory (MCRL). Equipment applicable for onsite testing and real-time monitoring of the PV performance associated with environmental conditions including temperature, solar irradiance, shading and soiling is included. In case of performance loss, equipment for fault detection, failure analysis, material testing, and further troubleshooting are also available. Through establishment of this capabilities, the enabling IRES project sets the stage for future research to advance off-shore and near-shore energy options for businesses and communities.

14 SOLAR ENERGY↗
DOE OSTI2021

PV in the circular economy, a dynamic framework analyzing technology evolution and reliability impacts

Rapid, terawatt-scale deployment of photovoltaic (PV) modules is required to decarbonize the energy sector. Despite efficiency and manufacturing improvements, material demand will increase, eventually resulting in waste as deployed modules reach end of life. Circular choices for decommissioned modules could reduce waste and offset virgin materials. We present PV ICE, an open-source python framework using modern reliability data, which tracks module material flows throughout PV life cycles. We provide dynamic baselines capturing PV module and material evolution. PV ICE includes multimodal end of life, circular pathways, and manufacturing losses. We present a validation of the framework and a sensitivity analysis. Results show that manufacturing efficiencies strongly affect material demand, representing >20% of the 9 million tons of waste cumulatively expected by 2050. Reliability and circular pathways represent the best opportunities to reduce waste by 56% while maintaining installed capacity. Shorter-lived modules generate 81% more waste and reduce 2050 capacity by 6%.

14 SOLAR ENERGY↗
DOE OSTI2015

High-efficiency plasma treatment for surface modification of LPCVD ZnO

Plasma treatment of LPCVD Boron-doped ZnO aimed at surface modification of the films has been performed. We have shown that five minutes treatment with RF magnetron Ar plasma can be sufficient to transform surface morphology from as-deposited V-type to U-type, which better suits the growth and enhances the properties of post-deposited microcrystalline silicon as a material for PV modules. Effect of plasma treatment on optical and electrical properties and surface morphology has been studied. Comparative analysis of the acquired results has shown that short time treatment can provide required changes in surface morphology without significant deterioration of structure and electrical and optical properties of treated films, while long time treatment results in reduction of electronic properties most probably caused by excess defect formation at the surface of ZnO films. These results show that, despite promising outlooks, RF magnetron plasma treatment of ZnO for the production of PV modules requires careful optimization.

36 MATERIALS SCIENCE↗
DOE OSTI2025

BACKFLIP: A Comparison of Market-Benchmark Backsheet Technologies to Novel Non-Fluoro-Based Coextruded Materials and Their Correlation and Impact on PV Module Degradation Rates: Final Results of the Study at 4000 Hours or 2 Years

As the photovoltaic (PV) industry is rapidly expanding around the world, there has been an increasing interest in extending the lifespan of PV modules. Concern has also emerged regarding the recyclability of modules and their component materials, including fluoropolymer-based backsheets. Laminated polyethylene-terephthalate (PET) core backsheets have traditionally been used in the PV industry, but new, co-extruded polyolefin (PO) backsheets show promise as an improved alternative. Mini-module and coupon samples of seven different backsheets (made of layers including contemporary PET and fluoropolymers, novel PO, and polyamide (PA) materials) were run through hygrometric- or UV photolytic-accelerated aging to identify and better understand each material's degradation modes and the backsheets' field reliability. In addition to the artificial aging, the natural weathering methods used in this study are described. The comprehensive set of chemical, mechanical, and structural characterizations at intermittent read points in this study is presented, including: visual appearance and color; gloss; mechanical tensile testing; I-V performance; electroluminescence (EL) imaging; dielectric breakdown; FTIR-chemical structure; X-ray-polymer structure (WAXS); and DSC-crystalline content. After 4000 h of accelerated aging or 2y of outdoor aging, a strong correlation occurs between initial physical characteristics (mechanical tensile test) and operating performance (EL and I-V characteristics).

14 SOLAR ENERGY↗
DOE OSTI2020

Durability of ionomer encapsulants in photovoltaic modules

Ethylene vinyl acetate (EVA) has for decades been the preferred material for photovoltaic (PV) module encapsulation. However, while it is relatively inexpensive and initially adheres well to module components, EVA discolors with age and - as interfacial adhesion degrades - becomes susceptible to delamination, ultimately resulting in reduced module efficiency and shortened service lifetimes. As potential replacements for EVA, ionomer thermoplastic materials cure faster, are more resistant to discoloration and potential induced degradation, and do not evolve corrosive acetic acid, making them compatible with new device materials such as perovskites. Since there is limited information on ionomer durability for PV module applications, a series of field and accelerated laboratory aging studies were conducted to assess ionomer interface stability in the presence of terrestrial environmental stressors. It is shown that adhesion to the glass and cell interfaces of PV modules is inferior to EVA, both before and after aging, rendering ionomers particularly susceptible to delamination after short timeframes. Potential solutions to improve ionomer adhesion are discussed.

14 SOLAR ENERGY↗
DOE OSTI2021

Towards validation of combined-accelerated stress testing through failure analysis of polyamide-based photovoltaic backsheets

Abstract Novel methods for advancing reliability testing of photovoltaic (PV) modules and materials have recently been developed. Combined-accelerated stress testing (C-AST) is one such method which has demonstrated reliable reproduction of some field-failures which were not reproducible by standard certification tests. To increase confidence and assist in the development of C-AST, and other new testing protocols, it is important to validate that the failure modes observed and mechanisms induced are representative of those observed in the field, and not the product of unrealistic stress conditions. Here we outline a method using appropriate materials characterization and modelling to validate the failure mechanisms induced in C-AST such that we can increase confidence in the test protocol. The method is demonstrated by applying it to a known cracking failure of a specific polyamide (PA)-based backsheet material. We found that the failure of the PA-based backsheet was a result of a combination of stress factors. Photo-oxidation from ultra-violet (UV) radiation exposure caused a reduction in fracture toughness, which ultimately lead to the cracking failure. We show that the chemical and structural changes observed in the backsheet following C-AST aging were also observed in field-aged samples. These results increase confidence that the conditions applied in C-AST are representative of the field and demonstrates our approach to validating the failure mechanisms induced.

14 SOLAR ENERGY↗
DOE OSTI2016

Development of Cu(In,Ga)Se2 Test Coupons for Potential Induced Degradation Studies

We report on the design, fabrication and accelerated testing of fully encapsulated small area coupons (approximately 7.5cm x 7.5 cm) for the purpose of researching potential induced degradation in Cu(In, Ga)Se2 based PV modules. The fabrication of these coupons enables the study of the solar cells and the materials used in PV module manufacturing such as top and bottom glass covers of different composition (soda-lime glass, high temperature glass, alkaline-free glass, etc), plastic-based top covers, ethylene vinyl acetate and edge seal encapsulation materials. The coupons can also be used to emulate framed and frameless modules that utilize either monolithically interconnected modules or singular cell type of modules. The design of the coupons, their fabrication, the materials used and their testing for 1000 hours under 85 degrees C and 85% RH conditions are presented.

14 SOLAR ENERGY↗
DOE OSTI2018

Passive Cooling of Photovoltaics with Desiccants

As part of efforts to reduce photovoltaic (PV) costs and improve reliability/durability, temperature control needs to be closely examined in a number of ways including novel passive cooling technology. Modest PV module operating temperature reductions can increase PV power output by 10% or more. The higher the operating temperature of a typical PV device, the lower the overall PV conversion efficiency. Because some incident light is converted to heat in PV cells, the PV module heats up (typically 25 degrees C above ambient temperature in full sun), and the overall energy output of the PV system is reduced (typically a 10% power loss for every 20 degrees C to 30 degrees C increase in temperature). We are integrating material on the PV module that adsorbs water from the air at night when the PV module temperature is cool and the relative humidity in the air is typically high. This sorbed water evaporates as the PV module heats up during the day, taking the excess heat with it and thus effectively cooling the PV module (see Fig. 1). Initial experiments with this novel passive cooling have demonstrated that PV module operating temperatures may be reduced nearly 30 degrees C with evaporative cooling. In this paper, we describe 1) novel materials development, 2) initial modeling that predicts how the cooling will work in different environments, and 3) results demonstrating the PV operating temperature reductions achieved to date.

14 SOLAR ENERGY↗
DOE OSTI2022

Correspondence: Bill of Materials Variation and Module Degradation in Utility-Scale PV Systems

We report photovoltaic (PV) modules of the same make and model are often assembled with different bills of materials (BOMs). In this correspondence, we revisit two case studies of utility-scale silicon PV systems in which these differing BOMs were associated with faster-than-expected degradation. In one of the sites, we found that different metallization paste had been used for grid lines in some cells leading to loss of contact to the cell and severe series resistance degradation. We provide details on the observation of this mechanism at two additional sites not described in the original article. In a second case study, we found that two different types of cell had been used, and that they could be distinguished by their back contact. Cells with uniform back contacts suffered from light and elevated temperature induced degradation (LeTID), while those with local back contacts did not. We also briefly describe BOM variations observed at other sites to illustrate the extent of the challenge. Our results from both sites underscore that variations in BOM, even among modules of the same make and model can lead to reliability challenges.

14 SOLAR ENERGY↗
DOE OSTI2019

Human Health Risk Assessment Methods for PV (Part 2: Breakage Risks)

Photovoltaic (PV) modules are designed and tested for long-term durability in harsh outdoor environments, but a small percentage may break during installation or operation. Some industry stakeholders have expressed concerns regarding potential human exposure to hazardous materials should a PV module break in the field. To evaluate these concerns, screening-level risk assessment methods are presented that can estimate emissions that may occur when broken PV modules are exposed to rainwater, estimate the associated chemical concentrations in soil, groundwater and air, and finally compare these exposure-point concentrations to health-protective screening levels based on 1 x 10-6 cancer risk and hazard quotient of 1. The screening-level methods can be used to decide whether further evaluation of potential health risks is warranted. A few example scenarios demonstrate application of the methods. Specifically, this report presents an analysis of potential human health impacts associated with rainwater leaching from broken modules for two PV technologies, focusing on release of the highest-prioritized chemical element for each: lead (Pb) content in crystalline-silicon (c-Si) PV modules and cadmium (Cd) content in thin film cadmium telluride (CdTe) PV modules. The prioritization of these chemical elements for analysis is based on stakeholder interest. Because the methodology is chemical-specific, the risk assessment results for these chemicals cannot be directly generalized to other chemicals, although the risk assessment methodology can be applied to other chemicals.

14 SOLAR ENERGY↗
DOE OSTI2017

Degradation Analysis of Field-Exposed Photovoltaic Modules with Non-Fluoropolymer-Based Backsheets

The selection of polymeric materials utilized in photovoltaic (PV) modules has changed relatively little since the inception of the PV industry, with ethylene-vinyl acetate (EVA), polyethylene terephthalate (PET), and fluoropolymer-based laminates being the most widely adopted primary components of the encapsulant and backsheet materials. The backsheet must serve to electrically insulate the solar cells and protect them from the effects of weathering. Due to continued downward pressure on cost, other polymeric materials are being formulated to withstand outdoor exposure for use in backsheets to replace either the PET film, the fluoropoymer film, or both. Because of their relatively recent deployment, less is known about their reliability and if they are durable enough to fulfill the greater than or equal to 25 year warranties of current PV modules. This work presents a degradation analysis of field-exposed modules with polyamide- and polyester-based backsheets. Modules were exposed for up to five years in different geographic locations: USA (Maryland, Ohio), China, and Italy. Surface and cross-sectional analysis included visual inspection, colorimetry, glossimetry, and Fourier-transform infrared spectroscopy. Each module experienced different types of degradation depending on the exposure site, even for the same material and module brand. For instance, the polyamide-based backsheet experienced hairline cracking and greater yellowing and chemical changes in China (Changsu, humid subtropical climate), while in Italy (Rome, hot-summer Mediterranean climate) it underwent macroscopic cracking and greater losses in gloss. Spectroscopic studies have permitted identification of degradation products and changes in polymer structure over time. Comparisons are made to fielded modules with fluoropolymer-based backsheets, as well as backsheet materials in accelerated laboratory exposures. Implications for qualification testing and service life prediction of the non-fluoropolymer-based backsheets are discussed.

14 SOLAR ENERGY↗
DOE OSTI2020

Task 12 PV Sustainability - Human Health Risk Assessment Methods for PV, Part 3: Module Disposal Risks

End-of-life management is important for addressing large future photovoltaic (PV) waste volumes and conserving raw materials for use in new PV modules. In regions without regulatory mandates for PV recycling, end-of-life PV modules can be disposed in accordance with general waste laws. Given the use of various metals as raw materials in semiconductor compounds and electrical contacts in commercial PV modules, some stakeholders have raised concerns regarding potential environmental impacts if PV modules are subject to improper disposal instead of being recycled or disposed in sanitary landfills, as is required in most world regions. To evaluate these concerns, screening-level risk assessment methods are developed herein that evaluate potential human health risks from groundwater and surface (air, soil, surface water) exposure pathways. The methods estimate potential impacts from disposal of end-of-life (EOL) PV modules in non-sanitary landfills under the following worst-case conditions: no leachate collection or groundwater monitoring, no liner for preventing leachate migration, uncovered waste, and lack of stormwater management. Examining worst-case conditions allows the exploration of maximum potential risk to attempt to ensure disposal does not increase health risk above regulatory thresholds. Specifically, this report presents an analysis of potential human health risks associated with non-sanitary landfill disposal for three PV technologies, focusing on release of the highest-prioritized chemical element for each: lead (Pb) in crystalline-silicon (c-Si) PV modules, cadmium (Cd) in thin film cadmium telluride (CdTe) PV modules, and selenium (Se) in thin film copper indium selenide (CIS) PV modules. The prioritization of these chemical elements for analysis is based on stakeholder interest. Because the methodology is chemical-specific, the risk assessment results for these chemicals cannot be directly generalized to other chemicals, although the risk assessment methodology can be applied to other chemicals. If the chemicals chosen are indeed the ones presenting greatest risk, then the results herein should represent the upper bound of health risk from exposure to a single constituent.

14 SOLAR ENERGY↗
DOE OSTI2021

Standards development for modules in high temperature micro-environments

Photovoltaic (PV) module qualification standards, IEC 61215 and IEC 61730, were designed to apply to “general open-air climates” and IEC 61730 specifically indicated applicability of ambient air temperature of 40°C. Additionally, these standards provided allowances for so-called “open rack mounted PV modules” without a clear definition of “open-rack.” These implied restrictions and allowances meant that hotter climates or thermally restrictive installation methods may not be covered by these often customer-mandated certification standards. This is particularly salient for the significant growth regions of the Middle East and India that would be expected to operate at significantly higher temperatures. The applicability of these documents raised issues over the definition of “open rack” and the fact that the geographic location is just as important as the mounting configuration in assessing the impact of the micro-environment of a PV module. This work summarizes the scientific background for IEC Technical Specification 63126:2020 ED1, titled “Guidelines for qualifying PV modules components and materials for operation at high temperatures.” This standard was recently published by the IEC and is the first step in a systematic effort to rework these standards to address the question of temperature more directly. Instead of specifying a mounting condition, we specify different suites of tests suitable for a system (PV module, mounting style, and location) defined by the 98th percentile cell temperature. With a defined temperature regime to work from, this allowed us to use existing literature research combined with additional modeling work to determine, which tests would need to be modified. This resulted in suggested changes to material thermal indices, thermal cycling temperatures, hot spot testing, ultraviolet testing, and bypass diode testing among other tests and characteristics described in this study.

14 SOLAR ENERGY↗
DOE OSTI2024

Tough Break: Many Factors Make Glass Breakage More Likely

We have seen cases of glass in PV modules breaking differently, and more often, than it did five years ago. There have been many changes to PV module design and materials in that time. But there is probably no single change that is responsible for the problem. Here we summarize the current thinking on PV glass breakage in utility-scale power plants. We share insights from multiple still-running projects at NREL.

14 SOLAR ENERGY↗
DOE OSTI2024

Material characterization of seven photovoltaic backsheets using seven accelerated test conditions

A variety of polymeric backsheet materials can be found in fielded photovoltaic (PV) modules, mostly based on fluoropolymer and polyethylene terephthalate (PET) materials. Cost reduction and sustainability considerations drive the recent development of alternative backsheet materials and designs [1]. In some fielded PV installations, polymeric materials are susceptible to environmental degradation in the form of backsheet cracking. To prevent backsheet degradation that can result in a module failure, thorough laboratory reliability testing is needed. In this report we studied the durability of seven commercial and experimental PV backsheets through accelerated stress testing using seven photolytic, hygrometric, and custom tests with the goal to understand if novel fluoropolymer-free backsheets are sufficiently environmentally durable to be commercialized. We divided the mechanisms observed during aging into two categories: core degradation and surface degradation. Although core degradation due to hydrolysis was observed in all commercial PET-, and polyamide (PA)-based backsheets aged with 85 degrees C/85% relative humidity, this test is unlikely to be field relevant. Photo-oxidative reactions on the exposed surface during UV weathering affected all seven backsheets regardless of the outer layer polymer material and additives. This degradation was limited to the outermost micrometers of the surface, except for backsheets containing PA-12, which resulted in surface cracking. A custom test combining UV with water spray caused the most severe backsheet degradation, including surface erosion and loss of insulating properties in polyolefin (PO)- and PA-based backsheets. This highlights the importance of combined accelerated stress testing to screen for complex backsheet degradation mechanisms. We also showed that, with material and design optimization, coextruded experimental PO-based backsheets have the potential to be a durable alternative to commercial PET- and fluoropolymer-based PV backsheets.

14 SOLAR ENERGY↗