NASA NTRS1996

Recrystallized Impact Glasses of the Onaping Formation and the Sudbury Igneous Complex, Sudbury Structure, Ontario, Canada

The origin of the Sudbury Structure and of the associated heterolithic breccias of the Onaping Formation and the Sudbury Igneous Complex have been controversial. While an impact origin of the structure has gained wide acceptance over the last 15 years, the origin of the recrystallized Onaping Formation glasses and of the igneous complex is still being debated. Recently the interpretation of the breccias of the Onaping Formation as suevitic fall-back impact breccias has been challenged. The igneous complex is interpreted either as a differentiated impact melt sheet or as a combination of an upper impact melt represented by the granophyre, and a lower, impact-triggered magmatic body consisting of the norite-sublayer formations. The Onaping Formation contains glasses as fluidal and nonfluidal fragments of various shapes and sizes. They are recrystallized, and our research indicates that they are petrographically heterogeneous and span a wide range of chemical compositions. These characteristics are not known from glasses of volcanic deposits. This suggests an origin by shock vitrification, an interpretation consistent with their association with numerous and varied country rock clasts that exhibit microscopic shock metamorphic features. The recrystallized glass fragments represent individual solid-state and liquid-state vitrified rocks or relatively small melt pods. The basal member lies beneath the Gray and Black members of the Onaping Formation and, where not metamorphic, has an igneous matrix. Igneous-textured melt bodies occur in the upper two members and above the Basal Member. A comparison of the chemical compositions of recrystallized glasses and of the matrices of the Basal Member and the melt bodies with the components and the bulk composition of the igneous complex is inconclusive as to the origin of the igneous complex. Basal Member matrix and Melt Bodies, on average, are chemically similar to the granophyre of the Sudbury Igneous Complex, suggesting that they are genetically related. Our chemical results allow interpretation of the entire igneous complex as a differentiated impact melt. However, they are also consistent with the granophyre alone being the impact melt and the nofite and quartz gabbro beneath it representing an impact-triggered magmatic body. This interpretation is preferred, as it is consistent with a number of field observations. A re-evaluation and extension of structural field studies and of geochemical data, as well as a systematic study of the contact relationships of the various igneous phases of the igneous complex, are needed to establish a Sudbury impact model consistent with all data and observations

Dressler, B. O.↗
DOE OSTI2020

Tensile properties of powder-metallurgical-processed tungsten alloys after neutron irradiation near recrystallization temperatures

The tensile properties of powder-metallurgical-processed Pure W, K-doped W, W-3%Re, and K-doped W-3%Re were examined after neutron irradiation up to 0.7 dpa at 910–1020 °C with a thermal neutron shield in the High Flux Isotope Reactor (HFIR). After irradiation, recrystallized Pure W (R) exhibited a brittle fracture mode, while recrystallized K-doped W-3%Re (R) exhibited a ductile fracture mode at 500 °C. K-doped W-3%Re (R) has fine grains, and hence, contains a considerable number of grain boundaries that act as sinks for irradiation defects. Solid solute Re in the W matrix could improve not only the mechanical properties of W, but also its resistance to neutron irradiation. At 500 °C, the ductility of K-doped W-3%Re after irradiation was significantly higher than that of Pure W. The irradiation at ~1000 °C did not induce hardening of stress-relieved (SR) W materials, but SR W materials tended to exhibit a decrease in the ultimate tensile strength (UTS) and an increase in total elongation (TE). Here, the softening due to the recovery and recrystallization of SR W materials and the hardening due to the formation of irradiation defect clusters were balanced during irradiation at ~1000 °C, and ductility was exhibited without an increase in strength.

36 MATERIALS SCIENCE↗
DOE OSTI2023

Incorporating dynamic recrystallization into a crystal plasticity model for high-temperature deformation of Ti-6Al-4V

During hot deformation of (α + β) titanium alloys, the simultaneous action of strain and temperature in the (α + β) regime facilitates dynamic recovery, dynamic recrystallization (DRX), and phase transformations via non-equilibrium paths. DRX is manifested in the form of fine recrystallized α or β grains. Here, in the present study, a two-phase crystal plasticity finite element framework (CP-DRX) has been developed which incorporates DRX kinetics into the crystal plasticity (CP) model to predict the flow characteristics of Ti-6Al-4V alloys during thermo-mechanical processing. The CP slip system parameters, as well as elastic properties from both α and β phases of Ti, are calibrated for different strain rate conditions. An EBSD-informed two-phase microstructure representation has been utilized in the CP-DRX framework to explore the time-dependent evolution of DRX microstructure and crystal orientation for different strain rate conditions. The proposed CP-DRX can capture the evolution of crystal orientation and plastic flow stress–strain response of polycrystalline Ti-6Al-4V during the deformation process. Furthermore, the proposed model is able to capture the softening behavior, observed in average stress–strain response from experiments performed using a Gleeble thermomechanical simulator and predict the recrystallization texture.

(α+ β)-Titanium (Ti) Alloys↗
DOE OSTI2026

Influence of the as-built microstructure on the recrystallization of an additively manufactured Inconel939 Ni-based superalloy

This study investigates the influence of the as-built microstructure on the recrystallization (RX) behavior and mechanical properties of the Ni-based superalloy Inconel 939 produced by laser powder bed fusion (PBF-LB/M). Two distinct as-built microstructures were obtained by varying the hatch distance (h d ): a columnar, strongly textured condition (h d =50, termed h d 50) and an equiaxed, weakly textured condition (h d =70, termed h d 70)). Both were subjected to nine solution treatments combining three temperatures (1100, 1150, and 1200 °C) and three holding times (1, 4, and 8 h). Comprehensive microstructural characterization was conducted to assess grain morphology, texture, grain boundary character, dislocation density, and precipitate distribution. Recrystallization was found to be significantly slower than in cast counterparts, requiring higher temperatures and longer times for completion. The initial microstructure plays a decisive role: full RX was achieved only in hd70 specimens after treatment at 1200 °C for 8 h, whereas hd50 samples exhibited delayed and incomplete RX under identical conditions. This behavior is attributed to the finer grain size and higher fraction of high-angle grain boundaries in hd70, which promote recrystallization. Mechanical testing revealed that hd70 samples subjected to a 1200 °C/8 h treatment followed by standard double ageing show higher yield and tensile strengths across the investigated temperature range than both printed and cast Inconel939 processed under conventional conditions, albeit with slightly reduced ductility. The enhanced mechanical performance is attributed to the larger grain size, which limits grain boundary sliding. These results demonstrate the critical importance of controlling the as-built microstructure and tailoring post-processing strategies to optimize high-temperature performance of PBF-LB/M Inconel939.

Inconel939↗
DOE OSTI2023

Role of geometric dynamic recrystallization in nanocrystalline alloys

Nanocrystalline and near-nano-grained metals are plagued with an overall lack of ductility and formability. This is in part due to their inability to support the dislocation mechanisms or undergo the same types of transformations that conventional coarse-grained metals access in order to increase their workability. Therefore, despite their advanced properties such as high strength, the manufacturing of such fine-grained metals, which exposes them to multi-axial states of stress in operations such as rolling, drawing, extrusion, forging, and bending, has not been possible. In this work, we address this limitation and highlight an important aspect of geometric dynamic recrystallization (GDRX) in nanocrystalline materials as a way to improve manufacturability. In particular, using two different alloy compositions and two different processing techniques, this study points to the fact that if nanocrystalline or near nano metals can be truly stabilized, they can repeatedly undergo the same types of processes that conventional coarse-grained metals endure, increasing both their formability and hence manufacturability. The results reveal that due to a large number of initial high-angle grain boundaries and large applied compressive strains, GDRX is activated in the absence of any discontinuous dynamic recrystallization (DDRX) or continuous dynamic recrystallization (CDRX). This is a unique aspect of stabilized nanocrystalline materials, as traditionally fine-grained metals are not microstructurally stable enough to accommodate such an event.

36 MATERIALS SCIENCE↗
DOE OSTI2023

3D mapping of residual stresses in growing grains of partially recrystallized Gum Metal

The crystallographic orientations and residual stresses within recrystallizing grains in partially recrystallized beta titanium-Gum Metal-were examined non-destructively in 3D using synchrotron Differential Aperture X-ray Microscopy. Contrary to common assumptions, significant local stresses and stress variations are observed within the recrystallizing grains. The results reveal that the development of these local residual stresses depends on the plastic deformation mode and material's elastic constants, rather than grain properties such as size and orientation, or even the material's yield stress. This work provides insights valuable for the design of advanced materials with heterogeneous microstructures.

36 MATERIALS SCIENCE↗
DOE OSTI2022

High-Rate and Low-Temperature Fabrication of Cu(In,Ga)Se 2 Solar Cells Using AgBr Induced Recrystallization

We present results demonstrating a three-stage, high-rate, low-temperature deposition process for Cu(In,Ga)Se 2 solar cells including a recrystallization step after the second stage, catalyzed by AgBr. The entire deposition and recrystallization process takes place below 450 °C in less than 15 min. Device results with efficiencies exceeding 16% are shown. Here, we achieve very high levels of grain growth and a greater than a 5% absolute increase in device performance because of the recrystallization step relative to an identical process not involving AgBr.

14 SOLAR ENERGY↗
DOE OSTI2020

Rafting-Enabled Recovery Avoids Recrystallization in 3D-Printing-Repaired Single-Crystal Superalloys

The repair of damaged Ni-based superalloy single-crystal turbine blades has been a long-standing challenge. Additive manufacturing by an electron beam is promising to this end, but there is a formidable obstacle: either the residual stress and γ/γ' microstructure in the single-crystalline fusion zone after e-beam melting are unacceptable (e.g., prone to cracking), or, after solutionizing heat treatment, recrystallization occurs, bringing forth new grains that degrade the high-temperature creep properties. Here, a post-3D printing recovery protocol is designed that eliminates the driving force for recrystallization, namely, the stored energy associated with the high retained dislocation density, prior to standard solution treatment and aging. The post-electron-beam-melting, pre-solutionizing recovery via sub-solvus annealing is rendered possible by the rafting (i.e., directional coarsening) of γ' particles that facilitates dislocation rearrangement and annihilation. The rafted microstructure is removed in subsequent solution treatment, leaving behind a damage-free and residual-stress-free single crystal with uniform γ' precipitates indistinguishable from the rest of the turbine blade. Finally, this discovery offers a practical means to keep 3D-printed single crystals from cracking due to unrelieved residual stress, or stress-relieved but recrystallizing into a polycrystalline microstructure, paving the way for additive manufacturing to repair, restore, and reshape any superalloy single-crystal product.

36 MATERIALS SCIENCE↗
DOE OSTI2022

A thermodynamic evaluation of metal halides for the recrystallization of Cu(In,Ga)Se 2

CdTe films are deposited at low temperatures and recrystallized to photovoltaic device quality using CdCl 2 treatments, leading to competitive manufacturing costs. Cu(In,Ga)Se 2 (CIGS) typically requires high-temperature, low-rate depositions to produce high-efficiency devices, resulting in higher costs. A similar metal halide treatment of CIGS has been demonstrated by us previously for some metal halide sources. To understand and optimize the process, a thermodynamic evaluation of candidate metal halides for such treatments is presented as a guide for their selection. By comparing bond dissociation energies, mono- and di-halide compounds are proposed to be ideal compounds to act as transport agents. Known recrystallization and temperature reduction benefits by Ag alloying suggests that Ag-halides should be used to aid transport of all species. The high vapor pressure and mobility of Ga compounds still poses a problem for metal halide treatment resulting in Ga etching and removal of intentional Ga gradients. Less severe but similar issues with In compounds may occur. As a result, Cu compounds have low vapor pressures which may limit transport, however, Cu is highly mobile in CIGS and recrystallization still occurs.

14 SOLAR ENERGY↗
DOE OSTI2025

High-pressure high-temperature melting and recrystallization of nanolamellar high-entropy alloys

Additively manufactured (AM) High Entropy Alloys (HEAs) are notable for their exceptional high-yield strength and large tensile ductility. The nanolamellar Eutectic HEA (EHEA) AlCoCrFeNi 2.1 was fabricated by laser powder bed fusion (L-PBF) in the as-printed form (EHEA1) and subsequently annealed at 1000oC (EHEA2) and 600oC (EHEA3) to achieve a broad range of mechanical properties. EHEA2 and EHEA3 samples were studied using Scanning transmission electron microscopy (STEM), energy dispersive X-ray diffraction (EDXRD) at high-pressures and high temperatures, nanoindentation hardness and modulus measurements. According to EDXRD EHEA2 and EHEA3 are composed of B2 and L1 2 phases. High-pressure high-temperature EDXRD studies show melting for EHEA2 at 1698 ± 25 K at a pressure of 6.5 GPa and melting for EHEA3 at 1598 ± 25 K at a pressure of 5.8 GPa. Post-melt and recrystallized samples were recovered at ambient conditions, and XRD analysis showed retention of B2 and L1 2 phases, although a new σ phase appeared for both EHEA2 and EHEA3 samples due to high-pressure and high-temperature melting and recrystallization experiment. SEM analysis also demonstrated the preservation of the nanolamellar morphology. Nanoindentation studies revealed that recrystallized EHEAs retain their original mechanical property hierarchy, with EHEA3 being 47% harder than EHEA2, largely related to higher content of B2-phase and retention of nanolamellar morphology. We also present Pressure-Volume-Temperature (P-V-T) data for 3-D printed and annealed eutectic high entropy alloys and extract mechanical and thermal properties data.

36 MATERIALS SCIENCE↗
DOE OSTI2023

Depth-dependent recovery of thermal conductivity after recrystallization of amorphous silicon

The depth-dependent recovery of silicon thermal conductivity was achieved after the recrystallization of silicon that had been partially amorphized due to ion implantation. Transmission electron microscopy revealed nanoscale amorphous pockets throughout a structurally distorted band of crystalline material. The minimum thermal conductivity of as-implanted composite material was 2.46 W m −1 K −1 and was found to be uniform through the partially amorphized region. X-ray diffraction measurements reveal 60% strain recovery of the crystalline regions after annealing at 450 °C for 30 min and almost full strain recovery and complete recrystallization after annealing at 700 °C for 30 min. In addition to strain recovery, the amorphous band thickness reduced from 240 to 180 nm after the 450 °C step with nanoscale recrystallization within the amorphous band. A novel depth-dependent thermal conductivity measurement technique correlated thermal conductivity with the structural changes, where, upon annealing, the low thermal conductivity region decreases with the distorted layer thickness reduction and the transformed material shows bulk-like thermal conductivity. Full recovery of bulk-like thermal conductivity in silicon was achieved after annealing at 700 °C for 30 min. After the 700 °C anneal, extended defects remain at the implant projected range, but not elsewhere in the layer. Previous results showed that high point-defect density led to reduced thermal conductivity, but here, we show that point defects can either reform into the lattice or evolve into extended defects, such as dislocation loops, and these very localized, low-density defects do not have a significant deleterious impact on thermal conductivity in silicon.

Huynh, Kenny↗
DOE OSTI2024

Effect of Processing Parameters on Recrystallization During Hot Isostatic Pressing of Stellite-6 Fabricated Using Laser Powder Bed Fusion Technique

Crack-free Stellite-6 alloy was fabricated using the laser powder bed fusion technique equipped with a heating module as the first attempt. Single tracks were printed with a build plate heated to 400 °C to identify the processing window. Based on the melt pool dimensions, two combinations (sample A: 300 W/750 mm/s and sample B: 275 W/1000 mm/s) were identified to print the cubes. The as-printed microstructure comprised FCC-Co dendrites with M7C3 in the interdendritic region. W-rich M6C particles were found in the overlapping regions between the melt pools, matching the Scheil simulations. However, gas pores were observed due to the higher nitrogen and oxygen content of the feedstock requiring hot isostatic pressing (HIP) at 1250 °C and 150 MPa for 2 h. Sample A was partially recrystallized with slightly coarsened M7C3, while sample B underwent complete recrystallization followed by grain growth along with higher coarsening of the M7C3 after HIP. The varying recrystallization behavior can be attributed to the difference in residual stresses and grain aspect ratio in the as-built condition dictated by laser power and scanning speed. The microhardness after HIP was slightly higher than its wrought counterpart, indicating no severe impact of post-processing on the properties of Stellite-6 alloy.

Sridar, Soumya (ORCID:0000000306775408)↗
NASA NTRS1975

A study of the oxide dispersion and recrystallization in NiCrAl prepared from preoxidized powder

The sintered aluminum powder (SAP) technique of dispersion strengthening (formation of an oxide dispersion by preoxidation of metal powders) was applied to atomized powder of a nickel alloy containing, by weight, 17% Cr, 5% Al, and 0.2% Y. The SAP-NiCrAl alloy (without the ytterbium removed by oxdation) was worked by extrusion and rod rolling at 1205 C and by swaging at 760 C. Annealing treatments were applied after working to determine the recrystallization response. The NiCrAlY alloy, similarly prepared from atomized powder, but without a preoxidation treatment, was examined for comparison. The SAP-NiCrAl alloy exhibited oxide particle size and spacing much larger than that usually observed in oxide dispersion strengthened alloys; nonetheless, it was possible to achieve abnormal (secondary) recrystallization in the SAP-NiCrAl alloy as has been reported for other oxide dispersion strengthened alloys. In contrast, the unoxidized NiCrAlY alloy exhibited only primary recrystallization.

Glasgow, T. K.↗
NASA NTRS1975

A study of the oxide dispersion and recrystallization in NiCrAl prepared from preoxidized powder

The SAP technique of dispersion strengthening (formation of an oxide dispersion by preoxidation of metal powders) was applied to atomized powder of the alloy Ni-17Cr-5Al-0.2 Y. SAP-NiCrAl was worked by extrusion and rod rolling at 1205 C and by swaging at 760 C. A variety of annealing treatments were applied after working to determine the recrystallization response. NiCrAlY, similarly prepared from atomized powder, but without a preoxidation treatment, was examined for comparison. The SAP-NiCrAl of this study exhibited oxide particle size and spacing much larger than that usually observed in oxide dispersion strengthened alloys; nonetheless, it was possible to achieve abnormal (secondary) recrystallization in the SAP-NiCrAl as has been reported for other oxide dispersion strengthened alloys. In contrast, unoxidized NiCrAlY exhibited only primary recrystallization.

Glasgow, T. K.↗
NASA NTRS1977

Recrystallization as a controlling process in the wear of some f.c.c. metals

Detailed examination of copper specimens after sliding against 440 C steel in liquid methane at speeds up to 25 m/s and loads of up to 2 kg showed the metal comprising the wear surface to possess a fine cell recrystallized structure. Wear proceeded by the plastic shearing of metal in this near surface region without the occurrence of visible metal transfer. A dynamic balance between the intense shear process at the surface and the nucleation of recrystallized grains was proposed to account for the behavior of the metal at the wear surface. Sliding wear experiments were also conducted on Ag, Cu-10% Al, Cu-10% Sn, Ni and Al. It was found that low wear and the absence of heavy metal transfer were associated with those metals observed to undergo recrystallization nucleation without prior recovery.

Bill, R. C.↗
NASA NTRS1976

Shock-induced fine-grained recrystallization of olivine - Evidence against subsolidus reduction of Fe/2+/

Electron spin resonance (ESR) studies have been carried out on three single grains of terrestrial olivine (Fo90) shock loaded along the 010 line to peak pressures of 280, 330, and 440 kbar. The results indicate that neither metallic Fe similar to that observed in returned lunar soils nor paramagnetic Fe(3+) caused by oxidation of Fe(2+) has been produced in these shock experiments. Trace amounts of Mn (2+) have been detected in both shocked and unshocked olivine. The ESR signals of Mn(2+) show spectral features which are found to correlate with the degree of shock-induced recrystallization observed petrographically. The increasing mass fraction of recrystallized olivine correlates with increasing shock pressures. This phenomenon is modelled assuming it results from the progressive effect of the shock-induced transformation of the olivine to a yet unknown high-pressure phase and its subsequent reversion to the low-pressure olivine phase. The mass fraction of recrystallized material is predicted to be nearly linear with shock pressure.

Ahrens, T. J.↗
NASA NTRS1980

Recrystallization characteristics of oxide dispersion strengthened nickel-base alloys

Electron microscopy was employed to study the process of recrystallization in two oxide dispersion strengthened (ODS) mechanically alloyed nickel-base alloys, MA 754 and MA 6000E. MA 754 contained both fine, uniformly dispersed particles and coarser oxides aligned along the working direction. Hot rolled MA 754 had a grain size of 0.5 microns and high dislocation densities. After partial primary recrystallization, the fine grains transformed to large elongated grains via secondary (or abnormal) grain growth. Extruded and rolled MA 6000E contained equiaxed grains of 0.2 micron diameter. Primary recrystallization occurring during working eliminated virtually all dislocations. Conversion from fine to coarse grains was triggered by gamma prime dissolution; this was also a process of secondary or abnormal grain growth. Comparisons were made to conventional and oxide dispersion strengthened nickel-base alloys.

Hotzler, R. K.↗
NASA NTRS1984

High-quality Silicon Films Prepared by Zone-melting Recrystallization

The graphite strip heater zone melting recrystallization (ZMR) technique is described. The material properties of the ZMR films, and SOI device results are reviewed. Although our ZMR work is primarily motivated by integrated circuit applications, this work evolved in part from earlier research on laser crystallization of thick amorphous GaAs and Si films, which was undertaken with the goal of producing low cost photovoltaic materials. The ZMR growth process and its effect on the properties of the recrystallized films may contribute some insight to a general understanding of the rapid recrystallization of Si for solar cells. Adaptation of ZMR for solar cell fabrication is considered.

Chen, C. K.↗