NASA NTRS1985

High temperature, short term tensile strength of C6000/PMR-15 composites

Tensile tests were conducted on 0 unidirectionally reinforced Celion 6000 graphite fibers in PMR-15 polyimide matrix. Tensile strengths for coupons subjected to short and long term uniform temperatures were obtained. Thick coupons, heated on one side to produce significant transient through thickness temperature gradients, were tested and compared to the strength of specimens with uniform temperature distributions. All coupons were radiantly heated and reached maximum test temperatures within 15 sec. Tensile loads were applied to the coupons after 15 sec of elevated temperature exposure. Loading rates were selected so that specimen failures occurred within a maximum of 45 sec after reaching the test temperature. Results indicate that significant tensile strength remains beyond the material post cure temperature.

Digiovanni, P. R.↗
NASA NTRS1997

Damage Initiation and Ultimate Tensile Strength of Scaled [0 deg n/90 deg n/0 deg n]sub T Graphite-Epoxy Coupons

Previous research on scaling effects in composite materials has demonstrated that the stress levels at first ply failure and ultimate failure of composite laminates are dependent on the size of the laminate. In particular, the thickness dimension has been shown to be the most influential parameter in strength scaling of composite coupons loaded in tension. Geometrically and constitutively scaled laminates exhibit decreasing strength with increasing specimen size, and the magnitude of the strength-size effect is a function of both material properties and laminate stacking sequence. Some of the commonly used failure criteria for composite materials such as maximum stress, maximum strain, and tensor polynomial (e.g., Tsai-Wu) cannot account for the strength-size effect. In this paper, three concepts are developed and evaluated for incorporating size dependency into failure criteria for composite materials. An experimental program of limited scope was performed to determine the first ply failure stress in scaled cross-ply laminates loaded in tension. Test specimens were fabricated of AS-4/3502 graphite-epoxy composite material with laminate stacking sequences of [0 deg n/90 deg n/o deg n]subT where n=1-6. Two experimental techniques were used to determine first ply failure, defined as a transverse matrix crack in the 90 deg ply: (1) step loading with dye penetrant x-ray of the specimen at each load interval, and (2) acoustic emission. The best correlation between first ply failure analysis and experimental data was obtained using a modified Weibull approach which incorporated the residual thermal stress and the outer ply constraint, as well as the ply thickness effect. Finally, a second set of experiments was performed to determine the tensile response and ultimate failure of the scaled cross-ply laminates. The results of these experiments indicated no influence of specimen size on tensile response or ultimate strength.

Jackson, Karen E.↗
NASA NTRS2012

Large-Scale Weibull Analysis of H-451 Nuclear- Grade Graphite Specimen Rupture Data

A Weibull analysis was performed of the strength distribution and size effects for 2000 specimens of H-451 nuclear-grade graphite. The data, generated elsewhere, measured the tensile and four-point-flexure room-temperature rupture strength of specimens excised from a single extruded graphite log. Strength variation was compared with specimen location, size, and orientation relative to the parent body. In our study, data were progressively and extensively pooled into larger data sets to discriminate overall trends from local variations and to investigate the strength distribution. The CARES/Life and WeibPar codes were used to investigate issues regarding the size effect, Weibull parameter consistency, and nonlinear stress-strain response. Overall, the Weibull distribution described the behavior of the pooled data very well. However, the issue regarding the smaller-than-expected size effect remained. This exercise illustrated that a conservative approach using a two-parameter Weibull distribution is best for designing graphite components with low probability of failure for the in-core structures in the proposed Generation IV (Gen IV) high-temperature gas-cooled nuclear reactors. This exercise also demonstrated the continuing need to better understand the mechanisms driving stochastic strength response. Extensive appendixes are provided with this report to show all aspects of the rupture data and analytical results.

Nemeth, Noel N.↗
NASA NTRS1993

Global/local interlaminar stress analysis of a grid-stiffened composite panel

A global/local procedure for the computation of the interlaminar stress components at the skin wrap, skin core, and wrap core interfaces for an advanced concept stiffened panel, is described. The procedure consists of a global model of two dimensional shell elements that is used to design a grid stiffened panel with blade type stiffeners, a local model of three dimensional solid elements that is used to compute interlaminar stress components, and a scheme devised to assign displacement boundary conditions for a local model that are based on displacement and rotation data of a few nodes of the global model. A global panel was designed according to strength, stiffness, and stability criteria associated with the design of traditional aircraft wing panels. Interlaminar normal and shearing stress components, computed via the local model, were found to be well below typical tensile normal and shearing strengths of a graphite epoxy material.

Wiggenraad, J. F. M.↗
NASA NTRS1999

Lamb wave characterization of the effects of long-term thermal-mechanical aging on composite stiffness

Lamb waves offer a promising method of evaluating damage in composite materials. The Lamb wave velocity is directly related to the material parameters, so an effective tool exists to monitor damage in composites by measuring the velocity of these waves. The Lamb Wave Imager (LWI) uses a pulse/receive technique that excites an antisymmetric Lamb mode and measures the time-of-flight over a wide frequency range. Given the material density and plate thickness, the bending and out-of-plane shear stiffnesses are calculated from a reconstruction of the dispersion curve. In this study, the time-of-flight as well as the elastic stiffnesses D11, D22, A44, and A55 for composite samples which have undergone combined thermal and mechanical aging are obtained. The samples examined include a baseline specimen with 0 cycles, specimens which have been aged 2350 and 3530 cycles at high strain levels, and one specimen aged 3530 cycles at low strain levels.

Aircraft↗
DOE OSTI2025

Summary of Graphite Data Stored within NDMAS

The Graphite Technology Development Project provides data to support the design of graphite core components within specific reactor service conditions of the next generation of high-temperature, gas-cooled nuclear reactors. Physical, mechanical, and thermal properties of nuclear grade graphite were characterized for specimens that were unirradiated, irradiated, and irradiated under various stress conditions. The material properties include diameter, length, mass, density, compressive strength, tensile strength, flexural strength, modulus, resistivity, thermal diffusivity, and thermal expansion coefficient. Baseline graphite specimens are unirradiated from different grades (2114, IG-110, NBG-17, NBG-18, and PCEA) and different types used in different characterization tests (compressive, flexural, tensile, one-inch cylinder, and quarter-inch cylinder). The Advanced Graphite Creep (AGC) irradiation specimens are from a much larger number of grades and cylinder types (creep, piggyback, and pencil). For baseline graphite, characterization data for 7,756 specimens extracted from thirteen graphite billets were captured to the NDMAS database. For AGC experiments, four irradiation campaigns have been completed: AGC-1, AGC-2, AGC-3, and AGC-4. The ongoing HDG-1 (High-Dose Graphite) experiment, which began irradiation with Cycle 168B on August 26, 2020, includes specimens previously irradiated in AGC-2 in addition to the specimens originally destined for AGC-5.. Besides the characterization data, the AGC data includes irradiation monitoring and physics data representing the irradiation conditions of AGC specimens. Currently, all data for AGC-1, AGC-2, and AGC-3 have been captured to the NDMAS database. Only AGC-4 pre-irradiation and irradiation monitoring data have been captured, and HDG-1 pre-irradiation data are in process of being captured for unirradiated specimens. To date, a total of 38,149 material property records have been captured into NDMAS database for baseline and AGC specimens. All characterization data are qualified for use according to their perspective data verification reports. For the AGC irradiation campaigns, a total of 41,502 qualified physics calculation records were added for AGC-1, AGC-2, and AGC-3. Finally, a total of 173,698,505 AGC irradiation monitoring data records (thermocouple temperature, gas flow rate, gas pressure, gas moisture, applied load, and specimen displacement) have been captured to NDMAS; the majority of those records (~94%) are qualified data records.

11 - NUCLEAR FUEL CYCLE AND FUEL MATERIALS↗
NASA NTRS1978

Correlation of fiber composite tensile strength with the ultrasonic stress wave factor

An ultrasonic-acoustic technique was used to indicate the strength variations of tensile specimens of a graphite-epoxy composite. A 'stress wave factor' was determined and its value was found to depend on variations of the fiber-resin bonding as well as fiber orientation. The fiber orientations studied were 0 deg (longitudinal), 10 deg (off-axis), 90 deg (transverse), (0 deg/+ or - 45 deg/0) symmetrical, and (+ or - 45 deg) symmetrical. The stress wave factor can indicate variations of the tensile and shear strengths of composite materials. The stress wave factor was also found to be sensitive to strength variations associated with microporosity and differences in fiber-resin ratio.

Vary, A.↗
NASA NTRS1978

Correlation of Fiber Composite Tensile Strength with the Ultrasonic Stress Wave Factor

An ultrasonic-acoustic technique was used to indicate the strength variations of tensile specimens of a graphite-epoxy composite. A stress wave factor was determined and its value was found to depend on variations of the fiber-resin bonding as well as fiber orientation. The fiber orientations studied were 0 deg (longitudinal), 10 deg (off-axis), 90 deg (transverse), 0 deg + or - 45 deg/0 deg symmetrical, and + or - 45 deg] symmetrical. The stress wave factor can indicate variations of the tensile and shear strengths of composite materials. The stress wave factor was also found to be sensitive to strength variations associated with microporosity and differences in fiber-resin ratio.

Vary, A.↗
NASA NTRS1982

Prediction of residual tensile strength of transversely impacted composite laminates

The response to low velocity impact of graphite-epoxy T300/5208 composite laminates is discussed. Steel balls of 3/8 inch, 5/8 inch, and 1 inch diameter were the projectiles. Impact energy was limited to 1.2 joules. Impacted specimens were ultrasonically C scanned to determine the impact damaged region. The threshold value of impact energy for impact damage was found to be approximately 0.3 joules. A model was developed to predict the tensile residual strength of impact damaged specimens from fracture mechanics concepts. Impacted specimens were tested in tension to provide a fracture data base. The experimental results agreed well with the predictions from fracture mechanics. In this study, the maximum impact velocity used to simulate the low velocity transverse impact from common objects like tool drops was 10 m/s.

Lal, K. M.↗
NASA NTRS2008

Reliability Assessment of Graphite Specimens under Multiaxial Stresses

An investigation was conducted to predict the failure strength response of IG-100 nuclear grade graphite exposed to multiaxial stresses. As part of this effort, a review of failure criteria accounting for the stochastic strength response is provided. The experimental work was performed in the early 1990s at the Oak Ridge National Laboratory (ORNL) on hollow graphite tubes under the action of axial tensile loading and internal pressurization. As part of the investigation, finite-element analysis (FEA) was performed and compared with results of FEA from the original ORNL report. The new analysis generally compared well with the original analysis, although some discrepancies in the location of peak stresses was noted. The Ceramics Analysis and Reliability Evaluation of Structures Life prediction code (CARES/Life) was used with the FEA results to predict the quadrants I (tensile-tensile) and quadrant IV (compression-tension) strength response of the graphite tubes for the principle of independent action (PIA), the Weibull normal stress averaging (NSA), and the Batdorf multiaxial failure theories. The CARES/Life reliability analysis showed that all three failure theories gave similar results in quadrant I but that in quadrant IV, the PIA and Weibull normal stress-averaging theories were not conservative, whereas the Batdorf theory was able to correlate well with experimental results. The conclusion of the study was that the Batdorf theory should generally be used to predict the reliability response of graphite and brittle materials in multiaxial loading situations.

Sookdeo, Steven↗
NASA NTRS1991

Interlaminar stress analysis at the skin-stiffener interface of a grid-stiffened composite panel

Results are presented of an analysis of the interlaminar stress components at the skin-wrap, skin-core, and wrap-core interfaces for an advanced-concept stiffened panel using a global/local finite element procedure. The procedure consists of a global model of two-dimensional shell elements that is used to design a grid-stiffened panel with blade-type stiffeners, a local model of three-dimensional solid elements that is used to compute interlaminar stress components, and a scheme devised to assign displacement boundary conditions for the local model that are derived from displacement and rotation data of a few nodes of the global model. The interlaminar stresses for this panel design were found to be well below typical tensile normal and shearing strengths of a graphite-epoxy material.

Wiggenraad, J. F. M.↗
NASA NTRS1961

Structural and High-Temperature Tensile Properties of Special Pitch-Coke Graphites

The room-temperature structural properties and the tensile properties up to 5000 F (275O C) were determined for ten grades of specially prepared petroleum-coke coal-tar-pitch graphites which were graphitized at 5430 F (3000 C). One impregnation with coal-tar pitch increased the bulk density from 1.41 to 1.57 g/cm3 and the maximum strength at 4500 F (2500 C) from 4000 to 5700 psi. None of the processing parameters studied had a marked effect on the closed porosity or the X-ray structure or the per cent graphitization. The coarse-particle filler resulted in the lowest coefficient of thermal expansion and the fine-particle filler in the highest coefficient. A marked improvement in uniformity of tensile strength was observed. A standard-deviation analysis gave a one-sigma value of approximately 150 psi for one of these special grades and values of 340-420 psi for three commercial grades.

GRAPHITE↗
NASA NTRS1975

Development of high temperature resistant graphite fiber coupling agents

Surface treatments were investigated as potential coupling agents to improve the elevated temperature shear strength retention of polyimide/graphite and polyphenylquinoxaline/graphite composites. The potential coupling agents were evaluated by fiber strand tensile tests, fiber and composite weight losses at 533 and 588K, and by interlaminar shear strength retention at 533 and 588K. The two surface treatments selected for more extensive evaluation were a coating of Ventromer T-1, a complex organometallic reaction product of titanium tetrachloride and trimethyl borate, and a polyphenylquinoxaline (PPQ) sizing which was pyrolyzed in nitrogen to form a carbonaceous layer on the fiber. Pyrolyzed polyphenylquinoxaline is a satisfactory coupling agent for polyimide/Thornel 300 graphite fiber composites. During 1000 hours aging at 588K such composites lose a little over half their transverse tensile strength, and suffer a slight loss in flexural modulus. No degradation of flexural strength or interlaminar shear strength occured during 1000 hours aging at 588K. None of the coupling agents examined had a markedly beneficial effect with polyphenylquinoxaline composites.

Griffin, R. N.↗
NASA NTRS1995

Construction material processed using lunar simulant in various environments

The manufacture of construction materials from locally available resources in space is an important first step in the establishment of lunar and planetary bases. The objective of the CoMPULSIVE (Construction Material Processed Using Lunar Simulant In Various Environments) experiment is to develop a procedure to produce construction materials by sintering or melting Johnson Space Center Simulant 1 (JSC-1) lunar soil simulant in both earth-based (1-g) and microgravity (approximately 0-g) environments. The characteristics of the resultant materials will be tested to determine its physical and mechanical properties. The physical characteristics include: crystalline, thermal, and electrical properties. The mechanical properties include: compressive tensile, and flexural strengths. The simulant, placed in a sealed graphite crucible, will be heated using a high temperature furnace. The crucible will then be cooled by radiative and forced convective means. The core furnace element consists of space qualified quartz-halogen incandescent lamps with focusing mirrors. Sample temperatures of up to 2200 C are attainable using this heating method.

Chase, Stan↗
NASA NTRS2010

Braze Development of Graphite Fiber for Use in Phase Change Material Heat Sinks

Hamilton Sundstrand (HS), together with NASA Johnson Space Center, developed methods to metallurgically join graphite fiber to aluminum. The goal of the effort was to demonstrate improved thermal conductance, tensile strength and manufacturability compared to existing epoxy bonded techniques. These improvements have the potential to increase the performance and robustness of phase change material heat sinks that use graphite fibers as an interstitial material. Initial work focused on evaluating joining techniques from 4 suppliers, each consisting of a metallization step followed by brazing or soldering of one inch square blocks of Fibercore graphite fiber material to aluminum end sheets. Results matched the strength and thermal conductance of the epoxy bonded control samples, so two suppliers were down-selected for a second round of braze development. The second round of braze samples had up to a 300% increase in strength and up to a 132% increase in thermal conductance over the bonded samples. However, scalability and repeatability proved to be significant hurdles with the metallization approach. An alternative approach was pursued which used nickel and active braze allows to prepare the carbon fibers for joining with aluminum. This approach was repeatable and scalable with improved strength and thermal conductance when compared with epoxy bonding.

Quinn, Gregory↗
NASA NTRS2011

Braze Development of Graphite Fiber for Use in Phase Change Material Heat Sinks

Hamilton Sundstrand (HS), together with NASA Johnson Space Center, developed methods to metallurgically join graphite fiber to aluminum. The goal of the effort was to demonstrate improved thermal conductance, tensile strength and manufacturability compared to existing epoxy bonded techniques. These improvements have the potential to increase the performance and robustness of phase change material heat sinks that use graphite fibers as an interstitial material. Initial work focused on evaluating joining techniques from four suppliers, each consisting of a metallization step followed by brazing or soldering of one inch square blocks of Fibercore graphite fiber material to aluminum end sheets. Results matched the strength and thermal conductance of the epoxy bonded control samples, so two suppliers were down-selected for a second round of braze development. The second round of braze samples had up to a 300% increase in strength and up to a 132% increase in thermal conductance over the bonded samples. However, scalability and repeatability proved to be significant hurdles with the metallization approach. An alternative approach was pursued which used a nickel braze allow to prepare the carbon fibers for joining with aluminum. Initial results on sample blocks indicate that this approach should be repeatable and scalable with good strength and thermal conductance when compared with epoxy bonding.

Quinn, Gregory↗