Cesium Batch Contact Equilibrium Testing of Crystalline Silicotitanate (CST) Sieve Cuts in SRS Average Simulant and Examination of CST Samples Aged in Caustic and Simulant in Support of Tank Closure Cesium Removal 1A (TCCR-1A)
Batch contact testing to determine cesium equilibrium loading on Crystalline Silicotitanate ion exchange media in Savannah River Site Average Waste Simulant at 25 °C indicated that smaller diameter particles isolated by sieving pretreated CST media may load slightly higher (<10%) amounts of cesium, though the differences are within analytical uncertainty. In addition, ion exchange media sub-samples stored in 2-4 M NaOH and caustic simulant solutions for ~2.5 years were examined by optical microscopy and the 3 M NaOH sample was also analyzed to determine whether changes in the particle size distribution occurred during storage. No visual indications of particle attrition or agglomeration were observed for any sample. Particle size analysis indicated that a slight decrease occurred in the average particle diameter following contact with 3 M NaOH (541 µm average diameter versus 566 µm for the pretreated CST prior to contact). A small increase (from 0 to <0.5 wt. %) in the number of particles ranging from 271 and 322 µm was also observed for the CST sample contacted with 3 M NaOH relative to a sample of the original pretreated material. However, this small change could be due to sub-sampling differences or analytical uncertainty. It does not appear that small particles are formed to a significant degree during CST caustic contact or that small particles which do form (presumably from attrition of larger particles during pretreatment) load significantly more cesium than the bulk material. Minimal other negative consequences were observed associated with CST extended caustic or simulant contact, except for the tendency for more concentrated salt solutions to form some salt crystals which deposit on the media over time.