DOE OSTI2021

Aging mechanisms of filled cross-linked polyethylene (XLPE) cable insulation material exposed to simultaneous thermal and gamma radiation

Thermal and simultaneous thermal and gamma radiation aging experiments were conducted on an industry grade cross-linked polyethylene (XLPE) cable insulation material, which is a composite material with XLPE as polymer matrix and various additives and fillers. Reverse engineering was conducted to identify and quantify the material composition given that this information was not revealed by the cable manufacture. Samples were then aged at temperatures of 60, 90, and 115 °C, exposed to gamma radiation for total doses of 0 to 324 kGy, and at dose rates of 0 to 540 Gy/h. Aging mechanisms were studied using various materials characterization techniques including pyrolysis gas chromatography mass spectrometry (Py-GCMS), differential scanning calorimetry (DSC), nuclear magnetic resonance spectroscopy (NMR), and gel-fraction tests. Results show that the flame-retardant components were decomposed into smaller molecules when the material was exposed to gamma radiation, while no changes were observed when the samples were aged thermally without gamma radiation. With exposure to gamma radiation, the crystalline phase of the XLPE were damaged by gamma radiation introducing defects in the crystals, resulting in smaller and less perfect crystals. The dominance of chain scission or chain reformation process largely depends on the chain mobility, which is decided by the aging temperature. Chain scission was seen to dominate when the material was exposed to gamma radiation at 60 °C. Chain cross-linking slightly dominated when the material was exposed to gamma radiation at 90 °C and became more dominant with exposure to gamma radiation at 115 °C. No significant change to the XLPE polymer matrix was observed when the samples were exposed to thermal aging without gamma radiation. Finally, antioxidant is more effective in protecting the XLPE polymer matrix under thermal aging, but less effective with sample exposure to gamma radiation.

38 RADIATION CHEMISTRY, RADIOCHEMISTRY, AND NUCLEA↗
DOE OSTI2023

Dose Rate Effects on Degradation of Nuclear Power Plant Electrical Cable Insulation at a Common Dose

The intent of this report is to address an identified knowledge gap in relating accelerated aging of nuclear electrical cables to service aging: dose rate effects (DRE). Here, DRE refer to gamma radiation-induced polymer degradation being a function of dose rate in addition to total absorbed dose. The concern raised is that historical qualification conducted at higher dose rates to simulate service lifetime may underestimate insulation degradation that occurs at lower dose rates in service. In the work described herein, common nuclear cable insulation materials—cross-linked polyethylene (XLPE) and ethylene propylene diene elastomer (EPDM)—were subjected to accelerated aging at ambient temperature (26°C) at different gamma dose rates of 100, 200 and 1800 Gy/h for select exposure durations to achieve constant total doses of 170, 210 and 300 kGy to evaluate DRE. First, the cable insulation material types investigated are described. Then, the accelerated aging experimental process involving gamma irradiation applied to the insulation specimens at room temperature and different dose rates is discussed. Then, the experimental characterization techniques used to perform this work are elucidated. These include elongation at break (EAB), mass change, yellowness index (YI), carbonyl index (CI), density, indenter modulus (IM), and relaxation constant (t). Theory of polymer degradation is discussed, and characterization results and discussion are provided. Finally, concluding remarks are made. The findings from this work and cited prior work reveal that DRE are material dependent, even between similar material categories (e.g., XLPE). In the case of the EPDM studied, degradation of ductility was observed to be greater at higher dose rate for the same total dose, indicating accelerated gamma aging to be more conservative than extended aging. Thus, conclusions regarding the conservatism of historical qualification likely require additional consideration for specific materials and conditions in question. The results of this study support the contention that, due to inherent limitations and uncertainties associated with prediction of cable remaining useful life from accelerated aging experiments, trending of installed cable insulation health status will be more practical and useful for safe and efficient cable aging management repair and replace decisions than lifetime prediction from historical qualification. The combination of material robustness demonstrated by the qualification process and ongoing monitoring of cable health status combine to provide confidence in continued safe use of existing nuclear cables. Additional research into effective and efficient condition monitoring methods for non-destructive evaluation of installed cables is needed to support aging cable management, including material studies to inform interpretation of measured results.

21 SPECIFIC NUCLEAR REACTORS AND ASSOCIATED PLANTS↗
DOE OSTI2022

Investigation of Inverse Temperature Effects During Thermal-Radiation Aging of Semicrystalline Cable Insulation

Inverse temperature effects were observed for semi-crystalline polymers subjected to combined thermal and irradiation aging. The mechanical durability of materials aged at low temperatures degrades with dose faster than at high temperatures. In this paper, two crosslinked polyethylene (XLPE) and two ethylene propylene rubber (EPR) type nuclear cable insulations were exposed to thermal-radiation aging at 100Gy/h up to 30Mrad and three temperatures (26°C, 50°C, 90°C). Their mass change and color change after aging were analyzed.

Ni, Yelin↗
DOE OSTI2021

Transition to Online Cable Insulation Condition Monitoring

Nuclear power plant cables were originally qualified for 40 year life and generally have not required specific test verification to assure service availability through the initial plant qualification period. However, license renewals to 60 and 80 years of operation require a cable aging management program that depends on some form of test and verification to assure fitness for service. Environmental stress (temperature, radiation, chemicals, water, and mechanical) varies dramatically within a nuclear power plant and, in some cases, cables have degraded and required repair or replacement before their qualified end-of-life period. In other cases, cable conditions have been mild and dependable cable performance confirmed to extend well beyond the initial qualified life. Most offline performance-based testing requires cables to be de-coupled and de-energized for specially trained technicians to perform testing. These offline tests constitute an expensive operational burden that limits the economic viability of nuclear power plants. Although initial investment may be higher, new online test practices are emerging as options or complements to offline testing that avoid or minimize the regularly scheduled offline test burden. These online methods include electrical and fiber-optic partial discharge measurement, spread spectrum time or frequency domain reflectometry, distributed temperature profile measurements, and local interdigital capacitance measurement of insulation characteristics. Introduction of these methods must be supported by research to confirm efficacy plus either publicly financed or market driven investment to support the start-up expense of cost-effective instrumentation to monitor cable condition and assure reliable operation. This work summarizes various online cable assessment technologies plus introduces a new cable motor test bed to assess some of these technologies in a controlled test environment.

Glass, Samuel W.↗
DOE OSTI2022

Non-Conductor-Contact Surface Wave Reflectometry for Cable Insulation Damage Detection

Here, this paper presents a non-conductor-contact surface wave-based reflectometry technique to detect and locate missing or damaged insulation and/or jacket of electrical cables. The described sensor may be uniquely and practically implemented on live cables as a non-destructive evaluation (NDE) method since it may be applied to the outer insulation/jacket of a cable and requires no direct contact to the conductor. The innovation lies in a high-frequency surface wave launcher that can introduce broadband signals in the GHz frequencies that insure maximum electromagnetic (EM) energy localization within the insulation and/or jacket material. By further processing the reflection data in the frequency domain, the location and severity of insulation damage is detected. Simulated results of thin, thick, short, and long cables show the results expected from small, medium, and large damage regions. For example, the detection of 40 mm-long damage region at 40 m distance on a 50 m long cable (2.44 cm diameter) is demonstrated. Experimental results are presented that validate simulation findings.

Non Destructive Evaluation↗
DOE OSTI2020

Interdigital Capacitance Sensor for Cable Insulation Test and Monitoring

A substantial body of work suggests feasibility to measure cable jacket and insulation conditions using various forms of interdigital capacitance (IDC) sensors. The sensors can either be used to manually test local cable conditions or as permanently installed sensors. Eligible cables subject to these measurements do not include shielded cables but the set of candidate cables is expanded from only unjacketed cables by the ability to assess insulation condition through the jacket. Dual gap IDC sensors are confirmed to be able to sense the insulation condition beneath a polymer jacket and, moreover, the IDC is the only known way to assess the insulation condition through the jacket. PNNL has filed a patent for this approach and is exploring commercial partnerships to exploit IDC technology for actionable field measurements.

NDE, cable, IDC, capacitance, permittivity, insula↗
DOE OSTI2021

Monitoring Degradation of Nuclear Cable Insulation Subjected To Sequential and Simultaneous Thermal and Radiation Aging

Predicting useful remaining life of cables in nuclear power plants is a topic of growing interest as plant continue to age. A typical electrical cable consists of polymeric materials, such as the cable jacket and insulation, which are susceptible to degradation due to exposure to both elevated temperatures and gamma irradiation over decades of service. In this work two insulation materials, crosslinked polyethylene (XLPE) and ethylene propylene diene (EPDM) elastomer, were characterized to quantify aging using total color difference and indenter modulus. Since the effects of thermal and gamma radiation are not additive but coupled, the effects of different aging scenarios including sequential and simultaneous aging were also evaluated. In the case of sequential aging, two aging scenarios were explored where the order in which thermal and gamma radiation received were altered. Total color difference of XLPE showed that sequentially aged insulation specimens, which received radiation first, degraded slightly more at maximum exposure than specimens which received thermal first. Similarly, in the case of EPDM, the extent of degradation evaluated using total color difference was found to be most severe in the case of sequentially aged insulation specimens which received radiation first. Indenter modulus was found to be insensitive to aging for XLPE but trended for EPDM. The largest variations were observed for the sequentially aged insulation specimens which received radiation first, similar to what was observed for total color difference.

Pallaka, Madhusudhan Reddy↗
DOE OSTI2022

Effect of Semiconducting Layer on Cable Insulation Damage Detection Using Surface Wave Reflectometry

This paper presents a study of the effect of the semiconducting layer present in medium and high voltage cables on surface wave propagation and its feasibility in detecting insulation damage on cables. Simulation studies were conducted using Ansys High Frequency Structure Simulator (HFSS). It was observed that attenuation increased with thicker semiconducting layer and higher conductivity of the layer. For instance, on a 24.4 mm diameter power cable, the electric field strength associated with a 1 GHz surface wave declines with distance and fades away after 30 m when a 2 mm thick semiconducting layer is present. More results as a function of semiconducting layer thickness, material conductivity and permittivity, distance of a damaged section, etc. will be presented.

reflectometry, unshielded power cable, semiconduct↗
DOE OSTI2022

Extension of Cable Electrical Assessment Techniques to Detect and Discriminate Radiation Aging on Cable Insulation Systems (Abstract)

The purpose of this study of the electrical responses of gamma radiation aged low voltage nuclear cables is to advance tools to determine cable condition (extent of damage) and identify degradation location along the cable length. The developed technology will provide nuclear plant operators with the options to focus cable repair, mitigation, or replacement efforts locally and avoid wholesale cable replacement.

42 ENGINEERING↗
DOE OSTI2020

Comparative Analysis of Capacitive Sensors with Different Geometrical layouts for Cable Insulation Degradation Detection

This paper presents a comparative analysis between an Interdigital Capacitor (IDC) sensor and a Serpentine Capacitive (SRC) sensor. The effects of electrode layouts on sensor performance are studied by means of finite element simulation where the geometrical dimensions (except electrode length) and material characteristics of both sensors are identical. Conformal IDC and SRC sensors with equal sensor area are modeled on a cable surface. The simulation results show a tradeoff between IDC and SRC sensors in terms of sensitivity and penetration depth. The SRC sensor shows 13.3% increase in sensitivity and 16.8% increase in capacitance compared to the IDC sensor, though the electric field penetration depth of the SRC sensor is 18.8% lower than the IDC sensor. In addition, the effects of change in electrode width, inter-electrode gap, and number of electrodes on SRC and IDC sensor comparative performance are evaluated.

Interdigital Capacitance, Serpentive Capacitive Se↗
DOE OSTI2019

Simulation and Experimental Results of Interdigital Capacitor (IDC) Sensors to Monitor Insulation Degradation of Cables

The efficacy of using interdigital capacitor (IDC) sensors to monitor cable insulation aging was studied through electromagnetic simulations and experimental measurements. Simulation results on both planar and conformal dielectric materials indicated that IDCs on thin substrates and with conducting backplanes provide superior performance in terms of higher capacitance. An airgap study showed that even a very small airgap between the sensor and the cable’s insulation results in significant reduction in capacitance; therefore, airgaps should be minimized. Finally, cables that underwent accelerated aging exposure in an oven were tested using fabricated IDC sensors. Measurement results showed a 12.5% increase in capacitance when the IDC was pressed against the insulation versus a 91.3% increase in capacitance when the IDC was pressed against the jackets of the cables for cable specimens ranging from unaged to aged 35 days.

Cable NDE, Interdigital Capacitance↗
DOE OSTI2021

Evaluation of Oxygen Consumption as a Sensitive Measure of Electrical Cable Polymer Insulation Degradation

Polymers used as dielectric materials in nuclear grade electrical cables, such as cross-linked polyethylene (XLPE) and ethylene-propylene rubber (EPR), are long-lived and durable. Estimating the decades-long useful service life of polymers experimentally in a feasible timeframe of weeks or months requires greatly accelerated aging in the laboratory at elevated temperatures and/or gamma dose rates. Many limitations of accelerated aging, such as due to artefacts of the process including diffusion limited oxidation and dose rate effects, have been identified that can make accurate lifetime prediction at service conditions challenging. This can be due to differences in degradation mechanisms between rapid and extended aging or to the presence of induction periods during which early aging is undetectable using common metrics of polymer insulation characterization such as tensile elongation at break. Conceptually, an ideal measure of aging would track clearly and predictably with material changes throughout the lifecycle of the evolving material state from early aging through end of useful life. With such a metric accelerated aging could be performed at much milder conditions, conditions closer to those found in long term service, and end of life calculated from the early data. Oxygen consumption has previously been proposed as a sensitive measure of insulation polymer oxidation that might meet such desirable characteristics. In this work, nuclear cable insulation samples of the two most common types, XLPE and EPR, from two of the most sourced manufacturers, RSCC and The Okonite Company, were subjected to gamma irradiation at dose rates of 100, 200, and 300 Gy/hr for up to 42 days at 26°C. The aged samples were used to evaluate oxygen consumption as a sensitive measure of aging for these materials and these conditions. For comparison and validation, the aged samples were also characterized using the more conventional tests of mass change, density, carbonyl index, and yellowness index. For both materials, oxygen consumption during irradiation was found to track consistently with applied dose—oxygen consumption rate was linear with time. Mass change and carbonyl index were also clearly proportional to exposure dose. Yellowness index, a surface sensitive measure, was observed to increase linearly with dose at low exposure levels before plateauing. Sample density was not observed to change under the conditions explored. Oxygen consumption was found to be a particularly sensitive metric to measure the degradation of polymeric cable insulation exposed to radiation. Oxygen consumption was compared to Arrhenius and time-temperature-superposition methods for activation energy calculation using literature date and found to be a useful and viable alternative for lifetime prediction. The techniques developed in this work are anticipated to be valuable in the estimation of insulation aging rates under mild conditions approaching service conditions. Direction comparison of useful life prediction by oxygen consumption with prediction via Arrhenius methodology for thermal aging and existing methods for radiation and combined thermal/radiation aging would serve to further validate this promising approach and refine our understanding of material-specific aging rates.

36 MATERIALS SCIENCE↗
DOE OSTI2021

Quantifying Properties for a Mechanistic, Predictive Understanding of Aqueous Impact on Aging of Medium and Low Voltage AC and DC Cabling in Nuclear Power Plants

To address the gap in knowledge in understanding degradation in relevant service conditions, this project aimed to develop a mechanistic, predictive model of medium and low voltage cable failure based on the primary environmental degradation parameters of aqueous immersion time, temperature, and the oxidation extent. To do so, we took a two-fold approach toward evaluating degradation as related to the aqueous condition. First, we evaluated the chemical, mechanical, and electrical properties of polymers that comprise the cabling insulation under varied aqueous conditions at different temperatures. Secondly, we evaluated the performance of insulation materials under similar accelerated aging conditions in addition to the dielectric breakdown of the cabling under submersion conditions. Thermal oxidation and immersion of LDPE thin films were done using a Parr vessel and the extent of oxidation was monitored using the carbonyl index from ATR-FTIR spectrum, a ratio quantifying the carbonyl functionality produced on the LDPE film surface. Increasing the temperature, oxidation time, and oxygen pressure increased the water-vapor permeability and the carbonyl content. Thermogravimetric analysis of the films confirmed that there is indeed an initial weight loss of the smaller molecular weight molecules and volatiles. At higher temperatures, there is a secondary mass loss. Up to 70°C, the mass loss curves were similar until 80°C, when the aged films decreased at a much greater rate with respect to increasing temperature. This was seen in the 10, 50, 90% weight loss temperatures. The mechanical properties of sheet PP and HDPE as well as injection molded LDPE, HDPE, HDPP dog bones were plotted with respect to the time spent in the Parr vessel during thermal oxidation. For the sheet PP and HDPE, the UTS and the modulus of elasticity decreased while the elongation increased. The injection-molded LDPE, HDPE, and HDPP dog bones experienced a similar trend where the changes in the properties were within experimental uncertainty. This analysis of LDPE in dry and immersive oxygen-rich environments is an important baseline for future experiments looking at other degradation mechanisms. A predictive aging model for low-density polyethylene insulative cable housings was developed. This model revealed a combination of physical and chemical processes which lead to an increase in permeability and a decrease in strength of the insulator. In creating this predictive model, a gap of knowledge in the literature was revealed in two areas: understanding how the crystallinity of a polymer changes with time and visualizing the predicted pores formed through the insulator which leads to failure. Developing and using an adapted ATR-FTIR method, crystallinity was monitored and compared to bulk crystallinity found via DSC. Inhomogeneity in crystallinity changes were observed but the FTIR method but was found to be less reliable. Pore visualization was found utilizing electrical impedance spectroscopy saturated aged polyethylene films with synthesized citrate-capped gold nanoparticles, and chloroauric acid precursor. results indicate a decreasing impedance of the polyethylene films caused by the transport of ions through the film. SEM imaging was then performed for elemental analysis of the films and counter electrodes for the presence of ions. Chloride and gold ions were detected; however, no nanoparticles were found. This gives an estimated pore size of at least 0.3 nm through the aged film. Cyclic submergence of polyethylene and polypropylene in aqueous solutions of copper sulfate and Harrison’s solution were examined. It was discovered that aging in these mixed conditions and at 90°C did cause a small, yet significant increase to tensile strength for both unaged polyethylene and polypropylene. The PE and PP in cycled and submerged conditions did not have tensile strengths significantly different from dry-aged after 16 weeks. For both solutions, it was determined that capacitance increases with both water tree depth and cable temperature and is relatively independent of changing water tree AR. As for resistance, there is no apparent change between depth percentages of 10 and 80 for both solutions. This is because the water tree has not yet entered the conductor and thus there is no shorting current flowing through the tree yet. Between 80 and 100% water tree depth, it is observed that for both solutions there is a rapid decrease in resistance because the tree is now impacting the conductor shield and allowing shorting current to flow through it. The relationship between resistance and temperature was found to be inversed. As temperature increases, resistance decreases for both water tree solutions with distilled water having the most apparent difference across the range of temperatures simulated. With regards to water tree AR, resistance was found to be relatively independent at depth percentages of 10, 50, and 70, but there was some relationship at 100% depth for both solutions. At this depth, as water tree AR increased, resistance was found to also increase. Through the examination of voltage and electric field distribution plots, it was confirmed for EPR cables that increasing water tree depth leads to increasing distortion. The increase in shorting current at 100% depth for aqueous copper sulfate compared to distilled water was also visualized. Lastly, the relationship between shorting current and temperature for narrow water trees was visualized and validated using the distribution plots. This study has led to a better understanding of the effect of cable temperature, water tree solution, and geometry of the tree region on cable degradation. Furthermore, this study has documented simulation results of water tree degradation in EPR MV cables, which had been previously lacking in information. Future work in this area will add frequency into the mix and examine what effect it has on the rate of cable degradation as a result of water treeing. To compliment the work being carried by UMD on different polymer chemistries, harvested medium voltage (MV) cables were selected for accelerated aging study at ORNL. These medium voltage cables are representative of the vintages and materials that are currently in use at existing nuclear power plants (NPPs). These cables were immersed in water at 90°C and energized for a period of two years at elevated voltage. Partial discharge was measured during this period of time to track potential degradation. Unfortunately, due to the absence of failure, the extent of integration between the UMD techniques and the harvested MV insulation was limited. However, based on the findings and from the UMD research in the previous sections on polyethylene and polypropylene, follow-on characterization for harvested MV cable insulation should focus on sample preparation to take advantage of the UMD techniques to better understand mechanistic degradation in MV cable insulations. This would include: 1.) Utilization of solutions and impedance measurement insulation to track permeability in harvested and accelerated aging insulation samples, 2.) Adaptation of gold nanoparticle synthesis for electrical impedance spectroscopy with supporting SEM characterization to study pore formation in harvested and accelerated aged insulation samples, & 3.) ATR-FTIR crystallinity with multiple temperature dependent harvested MV cable insulation under different air and submerged accelerated aging. In addition, low voltage dielectric spectroscopy and high voltage dissipation factor, tan δ, could be implemented as a condition monitoring tool for harvested MV cable insulation in submerged environments.

24 POWER TRANSMISSION AND DISTRIBUTION↗
DOE OSTI2020

Development of an In-Situ Method for Cable Condition Monitoring in Nuclear Power Plants (SBIR Phase IIB Final Report)

This is the final report of a Small Business Innovation Research (SBIR) project that Analysis and Measurement Services Corporation (AMS) has conducted for the U.S. Department of Energy (DOE) over a seven-and-a-half year period (February 2013 through April 2020 with the awards of Phase I, Phase II and Phase IIB projects). The goal of the project was to design, develop, validate, and demonstrate a technique for in-situ testing of cable insulation polymers that will identify, locate, and provide the degree of aging for cables commonly used in nuclear power plants. During the Phase I project, AMS established that the frequency domain reflectometry (FDR) technique can successfully identify and measure cable insulation degradation that can be trended with aging. In Phase II, AMS performed extensive cable aging studies to correlate FDR measurements with other laboratory condition monitoring techniques and developed aging condition categories to quantify the severity of insulation degradation. In Phase IIB, the project expanded the research to include a wider variety of cable polymers that are used in the commercial nuclear power industry. This work also involved developing acceptance criteria to objectively assess age-related cable degradation while sharing the results of this research with industry, academia, and national laboratories to advance the state of the art in cable aging management technologies. The products developed under this research project provide the nuclear industry with an effective condition monitoring tool to support safe and long-term plant operation. Throughout the project, collaborations and support were received from a variety of industry organizations and individuals including DOE National Laboratories as well as nuclear plant utilities and several other industry experts and cable manufacturers. Contributions from these organizations included the donation of new cables, naturally aged cables, and research collaboration. The validation and commercialization of the products of this project were achieved through opportunities to test and demonstrate the technologies’ capabilities on-site at nuclear power generation and research facilities as well as in the laboratory alongside industry peers and cable testing service companies. The research resulted in a technology that can be used to identify, locate, and quantify age-related degradation in several types of cable polymers. This included developing software and hardware as well as the methodology for using the FDR technique to assess age-related degradation of installed cables. The technology developed under this project can provide nuclear plant management, engineers, and technicians with an in-situ electrical test method to determine if in-service cables need to be replaced, monitored on a periodic basis, or show no evidence of significant age-related degradation that may require action. Near the end of this Phase IIB project, the FDR product was sold to a nuclear power utility in South Korea. This sale of a dedicated aging assessment tool is the beginning of a comprehensive contract with the expectation of twelve (12) units sold to that country. Additionally, the FDR technology has been sold to several industry organizations including a nuclear research institute and the Diablo Canyon nuclear power plant. This technology is also being leased by other nuclear industry service companies for incorporation into aging management programs. The cable testing technology that was developed under this project was also integrated into a comprehensive cable aging assessment service that is being offered to the nuclear industry at the request of U.S. nuclear utilities and is currently part of onsite testing services provided by AMS.

21 SPECIFIC NUCLEAR REACTORS AND ASSOCIATED PLANTS↗
DOE OSTI2021

Flexible Fabric-Based IDC Sensors for Conformal Curved Surface Applications

Interdigital capacitor (IDC) sensors are attractive in-situ sensors that can be used to measure permittivity variations in materials. Such sensors could be powerful enablers for cable insulation aging detection. Since insulation aging is correlated with a change in its material permittivity an IDC can measure that change via its measured capacitance. A new thin, flexible fabric-based IDC sensor is introduced for application on conformal curved surfaces such as an electrical cable surface. A multielectrode IDC and its backplane were fabricated using conductive copper polyester taffeta fabrics that were adhesively bonded to nonconductive polyester fabric. The sensor because of its soft flexible structure eliminates the problem of sensor conductor damage which is common for printed circuit board (PCB) type sensors when conformed to the surface of a cable. It also significantly reduces the airgap between the electrodes and the surface that they must contact in order to measure the capacitance. Airgap reduction and consistency are important in order to accurately predict permittivity variations in cable insulation material due to aging. Both PCB-based sensors and the new fabric-based sensors were built and tested on unaged cables and cables that underwent accelerated aging. Results demonstrate the proposed advantages of the novel fabric-based IDC sensor.

interdigital capacitor sensor, IDC, NDE, PCB senso↗