Data were obtained on the cryogenic fatigue properties of Inconel 718 bar using axial loading and rotating beam fatigue tests. Results also disclosed the fatigue properties of Inconel 718 sheet materials.
Corrosion fatigue tests were conducted on Inconel 718 and Incoloy 903 in distilled water, 500 ppm NaCl, and 3.5% NaCl. Results were compared to the endurance limit in air. For Inconel 718, the corrosion fatigue strength (CFS) IN 3.5% NaCl WAS 328 MPa or 75 percent of the endurance limit. For Incoloy 903, the CFS ranged from 234 MPa in distilled water (68 percent of the endurance limit) to 103 MPa in 3.5% NaCl (30 percent of the endurance limit). Results indicate that, for components which have limited fatigue life, an evaluation of the combined effects of fatigue and the corrosive atmosphere must be considered in projecting useful lifetimes.
Fatigue cracks in additively manufactured (AMed) Inconel 718 (IN-718) in machined surface condition often initiate from persistent slip bands (PSBs) unlike other popular AM alloys such as 17-4 PH stainless steel or Ti-6Al-4V, where fatigue crack initiation is exclusively from volumetric defects; therefore, a competition between PSB- vs. defect- mediated crack initiation clearly exists. To shed light on the factors governing the competition, this study investigates the characteristics of cyclic strain localization, PSB formation, and crack initiation via crystal plasticity (CP) modeling of cyclic loading on polycrystalline aggregates which are then validated by experiments. In this work, a physics-based, free slip distance (FSD) dependent slip strength evolution law is proposed, which is shown to enable the CP model to simulate the heterogeneous strain distribution in IN-718. Implementing a crack initiation criterion based on strain contrast, the locations and lives for crack initiation can also be calculated. It is shown that both FSD and resolve shear stress influence the strain localization and crack initiation behaviors. The distribution of a localization parameter calculated based on the multiplication of FSD and Schmid factor within a grain is found to correlate well with the locations of PSBs. The maximum values of the localization parameters within a microstructure are shown to correlate well with the experimentally obtained crack initiation lives. The presence of volumetric defects in IN-718 generally do not impact strain localization behavior unless their size is large compared to the grain size.
A large number of tests, including tensile, creep, fatigue, and creep-fatigue were performed to characterize the mechanical properties of Inconel 718 (a nickel based superalloy) at 1200 F, the operating temperature for turbine blades. In addition, a few attempts were made to model the behavior of Inconel 718 at 1200 F using viscoplastic theories. The Chaboche theory of viscoplasticity can model a wide variety of mechanical behavior, including monotonic, sustained, and cyclic responses of homogeneous, initially-isotropic, strain hardening (or softening) materials. It is shown how the Chaboche theory can be used to model the viscoplastic behavior of Inconel 718 at 1200 F. First, an algorithm was developed to systematically determine the material parameters of the Chaboche theory from uniaxial tensile, creep, and cyclic data. The algorithm is general and can be used in conjunction with similar high temperature materials. A sensitivity study was then performed and an optimal set of Chaboche's parameters were obtained. This study has also indicated the role of each parameter in modeling the response to different loading conditions.
The microstructure, trapped transmutation gases, stored energy, and mechanical behavior of samples from an irradiated Inconel 718 proton beam window were characterized using transmission electron microcopy, thermal desorption spectrometry (TDS), differential scanning calorimetry (DSC), and tensile testing. In the as-irradiated condition the microstructure contained a high number density of 1–3 nm gas-filled nanocavities. Emissions of trapped gases, H and He, during TDS correlated with peaks of the energy release curves from DSC examinations, which suggest these gases were likely stored in highly stable defect traps. The stored energy from radiation damage saturated at doses of a few dpa and did not increase with increasing radiation dose, but the amount of stored H and He increased with increasing dose. Effects of post-irradiation annealing were studied as well. After exposure to 700 °C, the nanocavities grew only slightly to 2–4 nm in diameter, but after exposure to 900 °C, the cavities grew to 10–20 nm in diameter and electron energy-loss spectroscopy showed these cavities contained a core of He surrounded by a shell of H. Further, this study demonstrated that the irradiation defect structures containing H and He were remarkably stable during irradiation and after exposure up to 700 °C. The effect of the irradiation temperature, defect mobility, and interaction of H, He, and irradiation defects on mechanical behavior provides insight into the processes responsible for the unusual recovery in ductility with increasing radiation dose observed in Inconel 718 after high energy proton and spallation neutron irradiation.
Columbium, for which the United States is 100 percent import reliant, is of strategic importance to the U.S. aerospace industry. A major amount of the Cb is used in Inconel 718. Should Cb sources be disrupted, it may be desired to use a grade of Cb melting stock having greater Sn content then the preferred vacuum rade. Additions of Sn to Inconel 718 were varied from none added to 1 wt %. The Sn additions below 800 ppm had no detrimental effects on 650 C stress rupture behavior; however, 1-wt % Sn severely degraded both life and ductility. Additions of Sn in excess of 200 ppm were slightly detrimental to the 425 C tensile yield strength and ductility. The Sn additions had no effect on the microstructure of Inconel 718 even after stress rupture testing for over 6000 hr at 650 C.
The microstructure and mechanical properties of additively manufactured (AM) alloys can be significantly affected by variations in cooling rates, resulting from different process conditions across different additive manufacturing (AM) platforms. Therefore, it is crucial to understand the effect of manufacturing process on the microstructure and mechanical properties of AM Inconel 718. This study examines three AM processes: laser powder bed fusion, laser powder directed energy deposition, and wire arc additive manufacturing. Results show that fully heat treated laser powder bed fused (L-PBF) and wire arc additively manufactured (WAAM) Inconel 718 specimens exhibit higher strength compared to laser powder directed energy deposited (LP-DED) ones due to finer grain structure in L-PBF and retained dendritic microstructure in WAAM. The ductility in LP-DED Inconel 718 was slightly higher compared to WAAM and L-PBF due to relatively small carbide size, which causes stress concentration in a small material volume, leading to delayed fracture.
Additively manufactured Inconel 718 parts fabricated in three build orientations (horizontal, vertical, and angled at 45 degrees) are tested in fully-reversed bending fatigue mode. Damping measurements via the Impulse Excitation technique are used to assess the defects content in the microstructure and fractography analysis is performed to detect the root cause of failure. Two micro- and macro-scale methodologies of fatigue damage estimation based on the dissipated heat per cycle and the statistical estimation of micro-plastic strain energies are used to assess fatigue damage. It is shown that at a given stress level, the vertically built specimens endure the most fatigue damage before failure while the diagonally built ones sustain the least. As a result, the fatigue life is estimated for arbitrary load amplitudes via a microstructure-sensitive algorithm with acceptable accuracy as compared to the experiments.
A series of tests, performed to determine the strain necessary to initiate intergranular cracking in Inconel 718 as a function of temperature, contained enough scatter near the melting temperature that questions remained as to the best curve of curves to fit to the data. Fracture surface analysis showed that the scatter was due to incipient melting in the grain boundary region. The melting contributed to low fracture strain but had only a small on the incipient cracking strain. Gleeble tests, which could be interrupted by water quenching, were used to study the incipient intergranular melting of Inconel 718. This modified weld simulation test provided a sufficiently rapid quench to preserve the intergranular microstructure created during incipient melting. This structure was studied both microscopically and with energy dispensive X-ray analysis. The implications of incipient melting and low-strain incipient cracking on the development of microfissuring envelopes are discussed.
The effect of hydrogen environments on sustained-load and cyclic-load crack growth in Inconel 718 was investigated using fracture-mechanics-type specimens. The sustained-load crack growth was determined to be a function of heat-treatment condition, temperature, and hydrogen pressure. The threshold stress intensity for subcritical crack growth was independent of hydrogen pressure at pressures greater than 21 MN/sq m (3000 psi). The cyclic-load crack growth rate in Inconel 718 at low and moderate stress intensity ranges increased with increasing hydrogen pressure. Decreasing the cyclic frequency from 1.0 to 0.1 Hz considerably increased the cyclic crack growth rate at 0.069 MN/sq m (10 psi) and at 68.9 MN/sq m (10,000 psi) hydrogen pressure. A series of measurements performed between 1.0 and 0.1 Hz showed that the crack growth rate increased as a complex function of the time per cycle.
This thesis presents the on-going development of methodology for a probabilistic material strength degradation model. The probabilistic model, in the form of a postulated randomized multifactor equation, provides for quantification of uncertainty in the lifetime material strength of aerospace propulsion system components subjected to a number of diverse random effects. This model is embodied in the computer program entitled PROMISS, which can include up to eighteen different effects. Presently, the model includes four effects that typically reduce lifetime strength: high temperature, mechanical fatigue, creep, and thermal fatigue. Statistical analysis was conducted on experimental Inconel 718 data obtained from the open literature. This analysis provided regression parameters for use as the model's empirical material constants, thus calibrating the model specifically for Inconel 718. Model calibration was carried out for four variables, namely, high temperature, mechanical fatigue, creep, and thermal fatigue. Methodology to estimate standard deviations of these material constants for input into the probabilistic material strength model was developed. Using the current version of PROMISS, entitled PROMISS93, a sensitivity study for the combined effects of mechanical fatigue, creep, and thermal fatigue was performed. Results, in the form of cumulative distribution functions, illustrated the sensitivity of lifetime strength to any current value of an effect. In addition, verification studies comparing a combination of mechanical fatigue and high temperature effects by model to the combination by experiment were conducted. Thus, for Inconel 718, the basic model assumption of independence between effects was evaluated. Results from this limited verification study strongly supported this assumption.
This report presents the results of both the fifth and sixth year effort of a research program conducted for NASA-LeRC by The University of Texas at San Antonio (UTSA). The research included on-going development of methodology for a probabilistic material strength degradation model. The probabilistic model, in the form of a postulated randomized multifactor equation, provides for quantification of uncertainty in the lifetime material strength of aerospace propulsion system components subjected to a number of diverse random effects. This model is embodied in the computer program entitled PROMISS, which can include up to eighteen different effects. Presently, the model includes five effects that typically reduce lifetime strength: high temperature, high-cycle mechanical fatigue, low-cycle mechanical fatigue, creep and thermal fatigue. Statistical analysis was conducted on experimental Inconel 718 data obtained from the open literature. This analysis provided regression parameters for use as the model's empirical material constants, thus calibrating the model specifically for Inconel 718. Model calibration was carried out for five variables, namely, high temperature, high-cycle and low-cycle mechanical fatigue, creep and thermal fatigue. Methodology to estimate standard deviations of these material constants for input into the probabilistic material strength model was developed. Using an updated version of PROMISS, entitled PROMISS93, a sensitivity study for the combined effects of high-cycle mechanical fatigue, creep and thermal fatigue was performed. Then using the current version of PROMISS, entitled PROMISS94, a second sensitivity study including the effect of low-cycle mechanical fatigue, as well as, the three previous effects was performed. Results, in the form of cumulative distribution functions, illustrated the sensitivity of lifetime strength to any current value of an effect. In addition, verification studies comparing a combination of high-cycle mechanical fatigue and high temperature effects by model to the combination by experiment were conducted. Thus, for Inconel 718, the basic model assumption of independence between effects was evaluated. Results from this limited verification study strongly supported this assumption.
The effects of repeated weld repairs on the metallurgical characteristics, high cycle fatigue (HCF), and tensile properties of Inconel 718 butt weld joints were determined. A 1/4 in thick plate and a 1/2 in thick plate were used as well as tungsten inert gas welding, and Inconel 718 filler wire. Weld panels were subjected to 2, 6, and 12 repeated repairs and were made in a highly restrained condition. Post weld heat treatments were also conducted with the welded panel in the highly restrained condition. Results indicate that no significant metallurgical anomaly is evident as a result of up to twelve repeated weld repairs. No degradation in fatigue life is noted for up to twelve repeated repairs. Tensile results from specimens which contained up to twelve repeated weld repairs revealed no significant degradation in UTS and YS. However, a significant decrease in elongation is evident with specimens (solution treated and age hardened after welding) which contained twelve repeated repairs. The elongation loss is attributed to the presence of a severe notch on each side (fusion line) of the repair weld bead reinforcement.
Internal hydrogen embrittlement (IHE) and hydrogen environment embrittlement (HEE) tensile and bend crack growth tests were performed on Inconel 718. For the IHE tests, the specimens were precharged to approximately 90 ppm hydrogen by exposure to 34.5 MPa H2 at 650 C. The HEE tests were performed in 34.5 MPa H2. Parameters evaluated were test temperature, strain rate for smooth and notch specimen geometries. The strain rate effect was very significant at ambient temperature for both IHE and HEE and decreased with increasing temperatures. For IHE, the strain rate effect was neglible at 260'C, and for HEE the strain rate effect was neglible at 400 C. At low temperatures, IHE was more severe than HEE, and at high temperatures HEE was more severe than IHE with a cross over temperature about 350 C. At 350 C, the equilibrium hydrogen concentration in Inconel 718 is about 50% lower than the hydrogen content of the precharged IHE specimens. Dislocation hydrogen sweeping of surface absorbed hydrogen was the likely transport mechanism for increasing the hydrogen concentration in the HEE tests sufficiently to produce the same degree of embrittlement as that of the more highly hydrogen charged IHE specimens. The main IHE fracture characteristic was formation of large, brittle flat facets, which decreased with increasing test temperature. The IHE fracture matrix surrounding the large facets ranged between brittle fine faceted to microvoid ductility depending upon strain rate, specimen geometry as well as temperature. The HEE fractures were characteristically fine featured, transgranular and brittle with a significant portion forming a "saw tooth" crystallographic pattern. Both IHE and HEE fractures were predominantly along the {1 1 1) slip and twin boundaries. With respect to embrittlement mechanism, it was postulated that dislocation hydrogen sweeping and hydrogen enhanced localized plasticity were active in HEE and IHE for concentrating hydrogen along (1 1 1) slip and twin planes. Final brittle failure occurred by hydrogen induced planer decohesion.
Here in this study, a novel alloy of modified Inconel 718 produced by laser powder bed fusion is studied before and after in-situ Kr irradiation up to 3 dpa at 200 and 450 °C. Before irradiation, the microstructure consists of dislocation cells having a misorientation angle less than 5° and with an average size of ~500 nm. There are also second phase particles of MC type carbides, Laves phase and oxides such as Y-O, Y-(Ti)-Al-O. While the microstructure consists of stacking fault tetrahedra, faulted and perfect loops after irradiation at 200 °C, dislocation loops are the primary defects at 450 °C. With increasing dose, the size of the defects remains similar at 200 °C while it increases at 450 °C. This has been attributed to the existence of vacancy type defects at 200 °C and the different defect transport mechanisms at different temperatures. Moreover, matrix and second phase particle compositions seem to be similar after irradiation. The sink strengths of the structures have been calculated and superior radiation resistance of this alloy has been attributed to the existence of fine cell boundaries stabilized by the second phase particles produced by additive manufacturing.
Fatigue crack growth tests were conducted to characterize the performance of Inconel 718 and CRES 321 welds, weld heat-affect-zone and parent metal at room temperature laboratory air and liquid nitrogen (-196oC) environments. The results of this study were required to predict the damage tolerance behavior of proposed orbiter main engine hydrogen fuel liner weld repairs. Experimental results show that the room and cryogenic temperature fatigue crack growth characteristics of both alloys are not significantly degraded by the weld repair process. However, both Inconel 718 and CRES 321 exhibited lower apparent toughness within the weld repair region compared to the parent metal.
Electron beam freeform fabrication (EBF3) direct metal deposition processing was used to fabricate an Inconel 718 bulk block deposit. Room temperature tensile properties were measured as a function of orientation and location within the block build. This study is a follow-on activity to previous work on Inconel 718 EBF3 deposits that were too narrow to allow properties to be measured in more than one orientation
The effects of galvanic coupling between D6AC steel, 6061-T6 aluminum, Inconel 718, and graphite-epoxy composite material (G/E) in 3.5% NaCl were studied. Measurements of corrosion potentials, galvanic currents and corrosion rates of the bare metals using weight-loss methods served to establish the need for corrosion protection in cases where D6AC steel and 6061-T6 aluminum are galvanically coupled to G/E in salt water while Inconel 718 was shown to be compatible with G/E. Six tests were made to study corrosion protective methods for eliminating galvanic corrosion in the cases of D6AC steel and 6061-T6 aluminum coupled to G/E. These results indicate that, when the G/E is completely coated with paint or a paint/polyurethane resin combination, satisfactory protection of the D6AC steel is achieved with either a coat of zinc-rich primer or a primer/topcoat combination. Likewise, satisfactory corrosion protection of the aluminum is achieved by coating it with an epoxy coating system.