Fractal coatings on various low-cost and high-temperature metallic substrates such as SS316, SS347, In800H, In740H, In625, Haynes 230, etc. were fabricated employing our patented novel electrodeposition process at various deposition potentials and deposition times, as well as chemical etching. The best combination of the materials and processing conditions were co-optimized for the reliable and repeatable fabrication of the multifunctional coatings. Surface morphologies were examined using SEM and AFM, and fractal characterization was done using a 3D optical surface profiler. Fractal dimension was used to identify successful fabrication and material parameters. The mechanical durability of the coatings was evaluated using several standardized tests, such as sand abrasion (ASTM D968) and adhesion (ASTM D3359), to fully characterize and demonstrate the mechanical durability of the fabricated surfaces. HTF immersion tests on the fractal multifunctional coatings were conducted based on a modification of the ASTM D870, which is established for static water immersion testing. To calculate the corrosion rates and descaled weight loss of the samples subjected to thermal exposure for different time durations (100 h, 300 h, 500 h, and optionally 750 h) to estimate the corrosion rate. While protecting the substrates from corrosion is an important goal, an allied goals is also to examine the post-corrosion temperature stability and properties of the molten salts themselves due to the dissolution of the constituents of the alloys and the corrosion products from the coatings that cause “fouling” of the molten salts. Fouling characteristics of the different molten salt HTFs exposed to coated and uncoated substrates were investigated. Finally, considering a prototype molten salt/sCO2 heat exchanger, cost/performance model is developed to demonstrate that the coatings on low-cost alloys such as stainless steel provide lower levelized cost of heat exchanger compared to high nickel content Ha230.