DOE OSTI2022

Mechanical response and microstructure evolution from multiaxial stress relaxation in textured zircaloy nuclear cladding

Modern energy markets provide motivation for nuclear reactors to increase operational flexibility and load following capacity of existing reactor designs. The operational power changes result in fuel pellet expansion and contraction resulting in pellet-cladding mechanical interaction (PCMI) and high cladding stresses that are strongly related to stressed corrosion cracking (SCC) which can lead to fuel rod failure. This work aims to quantify the stress fields in cladding with a focus on multiaxial stress relaxation response from an imposed strain and the resulting microstructure changes in textured zircaloy claddings. Stress relaxation tests resulting in multiaxial stress fields are performed to measure the material response of Zircaloy-4 nuclear cladding. Multiple experiments using samples from the same piece of cladding are performed so samples with the same processing history may be removed at strategic points throughout mechanical testing for microstructure characterization. The microstructure evolution is analyzed with mechanical response to evaluate the static recovery impact on crystallographic texture and grain morphology. Experiments are performed at Idaho National Laboratory using an experimental device capable of applying internal pressure and independent axial load to commercial nuclear cladding at elevated temperatures with stress- or strain-controlled experimental capability. X-ray diffraction and electron backscatter diffraction are used for microstructure analysis. Rheological models are used to visualize the multiaxial stress-strain relationships and isolate elastic, plastic, and viscoplastic material properties for analysis.

11 NUCLEAR FUEL CYCLE AND FUEL MATERIALS↗
DOE OSTI2025

Ductility evaluation of nitrided Zircaloy-4 cladding by ring compression testing

Here, this study evaluated the embrittlement of Zircaloy-4 cladding by dry air and dry nitrogen environments as a function of process temperature and duration of exposure. A Netzsch thermogravimetric analyzer was used to measure the mass gain of cladding sections over time with specified temperature and gas flow programs. Oxidation of Zircaloy in dry air produced a brittle ZrO 2 layer with ductile unreacted metal. In contrast, nitridation of Zircaloy had a slower reaction rate but produced a brittle cladding that was more easily breached during ring compression tests. The ring compression tests demonstrated that ductility of Zircaloy cladding decreases as nitrogen pickup increases; a ductile-to-brittle transition occurs near a mass gain of 2.1 wt %. Nitridation showed minimal temperature dependency in ductility degradation, whereas oxidation showed significant temperature dependency in ductility degradation, with severe embrittlement occurring at 1200 °C. Optical micrographs confirmed the formation of uniform ZrN layers (approximately 12 µm thick) on the cladding surface, indicating that cladding embrittlement is primarily the result of nitrogen diffusion rather than metal layer thinning.

36 MATERIALS SCIENCE↗
DOE OSTI2024

Enhanced Stress Relaxation Behavior via Basal ⟨a⟩ Dislocation Activity in Zircaloy-4 Cladding

Herein this work evaluates the stress relaxation behavior of textured Zircaloy-4 cladding to understand how mechanical anisotropy influences pellet-cladding interactions. Uniaxial and biaxial stress relaxation tests are performed using full-tube axial tension and internal pressurization, respectively, aiming to achieve 0.25%, 1%, and 2% equivalent strains in the cladding samples at a temperature of 300°C. Internal pressure relaxation test results display enhanced stress relaxation compared to axial testing results, particularly for samples loaded beyond yield. Results of electron backscatter diffraction indicate increased deformation microstructure during loading and increased strain homogenization and recovery during relaxation for samples loaded via internal pressurization. Analysis indicates that the increased production and activity of basal ⟨a⟩ dislocations play a significant role in the enhanced relaxation measured in samples subjected to internal pressurization.

11 NUCLEAR FUEL CYCLE AND FUEL MATERIALS↗
DOE OSTI2020

Burst behavior of nuclear grade FeCrAl and Zircaloy-2 fuel cladding under simulated cyclic dryout conditions

A novel experiment to simulate cyclic dryout in boiling water reactors has been developed to better understand the performance of nuclear grade FeCrAl cladding in a BWR during dryout conditions caused by an Anticipated Operational Occurrence or Anticipated Transient Without SCRAM - both of which are Design Basis Accidents. Internally pressurized C26 M FeCrAl alloy cladding and Zircaloy-2 cladding were subjected to rapid 300°-650 °C thermal cycling in a steam environment; actual maximum temperatures were found to vary between materials but were always above 650 °C. In the range of 32–55 MPa hoop stress, Zircaloy-2 cladding burst within 1–16 cycles (about 100 s of dryout duration above 600 °C), while at 76 MPa hoop stress, C26 M cladding remained virtually undeformed after completing 54 cycles (over 1000 s of dryout duration above 600 °C). Higher temperature 300°-700 °C and 300°C–800 °C cycling experiments had to be performed to induce C26 M burst – failure occurred after 20 cycles in the former and during the first cycle in the latter. Zircaloy-2 and C26 M failure criteria were used to generate hoop stress specific dryout lifetimes. Overall, the simulated cyclic dryout experiments show that nuclear grade C26 M cladding has significantly enhanced survivability under dryout conditions relative to Zircaloy-2.

11 NUCLEAR FUEL CYCLE AND FUEL MATERIALS↗
DOE OSTI2020

System code evaluation of near-term accident tolerant claddings during pressurized water reactor station blackout accidents

Following the Fukushima Daiichi nuclear accident in 2011, researches on Accident-tolerant fuels (ATFs) are currently of high interest in not only the nuclear industry but also governmental and international organizations. In this work, a quantitative evaluation of the performance of monolithic FeCrAl cladding and Cr-coated Zircaloy cladding has been performed for Pressurized Water Reactor (PWR) Station Blackout (SBO) accidents. A generic PWR model has been built in system thermal-hydraulics code TRACE based on the Surry Nuclear Power Station with counter-current natural circulation modelling capability for hotleg and steam generator U-tube components during the accidents. The base model results are then compared to MELCOR and RELAP simulations to verify the system component implementation in TRACE. Two PWR SBO scenarios were investigated, including: short-term SBO and long-term SBO with early reactor coolant pump (RCP) seal failure. These scenarios are defined to be very similar to the accidents studied in the State-of-the-Art Reactor Consequence Analysis (SOARCA) project. TRACE code is modified to reflect the oxidation kinetics of FeCrAl and Cr-coating. Larson-Miller creep rupture model is also implemented in TARCE using its built-in control systems to simulate the creep rupture of hotlegs. Additionally, the comparison between the TRACE models with and without the counter-current flow modeling resulted in significant difference when comparing ATF cladding to Zircaloy for short term SBO, while it marginal impacted the performance during long term SBO with RCP seal failure. For short term SBO, both ATF cladding underwent hot leg creep rupture ~20 min after Zircaloy cladding. While Zircaloy and Cr-coated cladding had generated significant amount of hydrogen gas (>10 kg) before the creep rupture event, FeCrAl cladding had only generated <0.5 kg of hydrogen gas. For long term SBO with RCP seal failure, significant hydrogen generation and fuel melting was predicted before hot leg creep rupture for the ATF cladding while providing only 10–20 min additional coping time compared to Zircaloy.

73 NUCLEAR PHYSICS AND RADIATION PHYSICS↗
DOE OSTI2024

Fatigue Testing and Characterization of Pre-hydrided Zircaloy-4 Cladding Tubes

The solubility of hydrogen in Zircaloy-4 (Zry-4) at the cladding operating temperature is near 100 wt. ppm. Above this solubility limit, excess hydrogen precipitates as δ-hydride platelets in the cladding material. Because of the effect of the thermal gradient across the cladding thickness on the migration and precipitation of hydrogen, hydride rims are often observed at the cladding outer surface; under excessive corrosion conditions hydride blisters are possible. It is well known that the fatigue of metal alloys, especially high cycle fatigue, is sensitive to the status of surface including the microstructure, roughness, and residual stress. Thus, the question considered herein, is whether excessive hydrogen pickup modifies the microstructure such that it has a degradation effect on the fatigue performance of cladding during operation. This report describes the evaluation of fatigue performance of a pre-hydrided Zry-4 cladding. A commercial Zry-4 was polished and pre-hydrided to 800 ppm and 1300 ppm H contents. The fatigue testing was conducted under strain control at 5 Hz with fully-reversed bending by using a cyclic integrated reversible bending fatigue tester (CIRFT). Six specimens with 1300 ppm and one specimen with 800 ppm were tested. Significant variation in test results were observed. While two of the 1300 ppm specimens failed with less than 1 ×10 5 cycles (at 0.32% and 0.41%), the four other samples did not fail over the strain amplitude range of 0.25% to 0.38%. Interestingly, the fracture initiation site of the failed samples was on the outside diameter (OD) surface rather than on the inside diameter (ID) surface as is typical for the as-polished cladding. This suggested a degrading effect of the hydriding process. Subsequently, three of the unfailed specimens were then further tested at ~0.43% to observe where failure initiation occurred. Significant variation was also observed in these three specimens. One specimen failed at ~9000 cycles while the two others failed at 43000 and 1.06 ×10 5 cycles. The performance here correlated to the location of failure initiation; failure initiated on the OD in the sample that failed after 9000 cycles while it initiated on the ID in the sample that failed after 43000 and 1.06 ×10 5 cycles. Flat features at the OD initiation sites suggest a brittle hydride feature on the surface of those samples was the cause of the degradation in fatigue performance, though the overall hydrogen levels in all samples was similar. A summary of all the observations is provided below: • The un-failed specimens with 1300 ppm H were cycled to failure with a higher amplitude near 0.43%. In addition, the fatigue-treated specimen tended to have a longer fatigue at the same induced amplitude. • Fractography revealed a mixed failure mode for the pre-hydrided specimen. Particularly, the specimen with fracture initiation site (FIS) located on the outer diameter surface of tube tended to have a shorter fatigue life than that of FIS on the inner diameter surface. • Etched cross section was shown to have hydride platelets aligned with tube longitudinal axis as expected, and the density of hydrides is at the similar level as in literature data. Meanwhile, a LECO procedure was applied for hydrogen concentration measurement, which showed the measured hydrogen contents are close to the nominal value. • With the polished cladding tube as baseline, O’Donnell-Lager (O-L) analysis showed that a decrease of about 50% in reduction-of-area (RA) would be needed for the O-L fitting to the fatigue data of 1300 ppm cladding. The suggestion for the next steps is provided.

11 NUCLEAR FUEL CYCLE AND FUEL MATERIALS↗
DOE OSTI2022

A study on texture stability and the biaxial creep behavior of as-hydrided CWSR Zircaloy-4 cladding at the effective stresses from 55 MPa to 65 MPa and temperatures from 300°C to 400°C

The creep rupture of high burnup used nuclear fuel (> 45 GWD/MTU) cladding is regarded as one of the failure mechanisms during long-term dry storage. A high amount of zirconium hydride in the cladding matrix would degrade the mechanical properties of the cladding especially leading to delayed hydride cracking. To better understand the influence of zirconium hydride on the biaxial thermal creep performance and the crystalline texture stability of Zircaloy-4 cladding, the pressurized tube technique is applied to test the durability of the as-hydrided material. Tests were performed on as-received Zircaloy-4 tubular specimens as well as-hydrided ones with targeted 300 wt parts per million (wppm) or 750 wppm hydrogen. The biaxial creep experiments were conducted at temperatures from 300 degrees C to 400 degrees C and at equivalent stresses at mid-wall from 55 MPa to 65 MPa. The hydridation process prior to creep tests induces the formation of FCC delta-hydride platelets along the circumferential direction of the tube. This alignment and phase structure of hydride show no significant change after biaxial creep tests. The creep strain-rate negatively depends on the hydrogen content. The synchrotron wide-angle X-ray diffraction (WAXD) technique and electron backscatter diffraction (EBSD) analysis were applied for the study of the crystallographic orientation relationship. zirconium-to-hydride grain orientation follows Shoji-Nishiyama crystallographic relationship. This relationship is stable before and after creep deformation. These results of creep performance and texture stability of Zircaloy-4 claddings can help support the design basis of interim and long-term dry storage facilities.

creep↗
DOE OSTI2023

The deformation and burst behavior of Zircaloy-4 cladding tubes with hydride rim features subject to internal pressure loads

This study is motivated by the desire to conduct a separate effects test replicating specific aspects of an in-pile pulse reactor test on high exposure light water reactor (LWR) fuel rods. The principal purpose of the tests was to determine whether temperature and or hydrogen concentration thresholds exist in assessing the vulnerability of a stress relieved zirconium alloy cladding tubes to low strain ruptures. A secondary objective was to determine whether observations of the cladding stress during deformation could aid in the understanding of the crack formation and propagation in cladding tubes with hydride rim features. Here, the study utilized artificially hydrided Zircaloy-4 cladding tubes and an isothermal, internal pressure test that was controlled with an in-situ strain measurement. The test results show a clear transition in failure vulnerability between room temperature and 150 °C. Below 150 °C, cladding tubes rupture at very low uniform plastic strain—even at relatively modest cladding hydrogen levels. At and above 150 °C, cladding tubes only rupture at low uniform plastic strain if the cladding hydrogen content is greater than 500 ppm and usually experience at least some modest amount of plastic deformation prior to rupture. Post-test metallographs from non-ruptured cladding tubes show numerous primary cracks forming in the hydride rim and arresting at the metal/hydride interface. This observation combined with the decrease in bulk yielding of hydrided cladding tubes when compared to fresh non-hydrided tubes leads to the conclusion that the fracture stress of the hydride rims is related to and bounded by the yield stress of the zirconium metal. Some evidence is presented for a change in crack propagation mechanism from one of void formation on hydride plates and linkage at temperatures below 150 °C to more classical ductile shearing beneath the primary crack tip at temperatures above 150 °C. This apparent change in crack propagation mechanism may help explain the observed temperature and hydrogen concentration thresholds.

11 NUCLEAR FUEL CYCLE AND FUEL MATERIALS↗
DOE OSTI2024

In-situ determination of strain during transient burst testing and the temperature dependence of Zircaloy-4 claddings

Understanding fuel system behavior during postulated loss-of-coolant accidents is pertinent for continued safe and efficient operation of light water reactors, particularly as higher burnups are being pursued and safety margins re-evaluated. Conventional mechanical models for the incumbent Zr alloys typically rely on the assumption that steady-state creep is the dominant fuel cladding response during transient accident conditions. To investigate this assumption, simulated accident burst testing was performed on Zircaloy-4 claddings with balloon behavior measured in-situ. Here, two distinct loading conditions were utilized during burst testing: (1) constant-gas-inventory where pressure was allowed to increase with temperature and (2) constant pressure. In-situ strains and strain rates were measured via 2-dimensional digital image correlation techniques and synchronized with temperature to determine deformation dependencies. The temperature dependence of strain rate was characterized by a two segment Arrhenius relationship, with a distinct transition between the high and low temperature/strain regimes. The average activation energy of the lower temperature/strain regime was 328 ± 25 kJ/mol, in agreement with the ~320 kJ/mol used for conventional LOCA models. However, the higher temperature/strain segment, which encompassed most of ballooning, showed increased activation energies as well as a dependence on whether the burst region was in view. For tests that burst away from the camera view, the average high temperature/strain segment activation energy was 635 ± 150 kJ/mol. For samples where the rupture opening formed in view, the average activation energy was 1015 ± 179 kJ/mol. This observed shift in temperature dependence indicates a transition in deformation mechanism at the end of life, possibly to time independent failure mechanisms, which has not yet been visualized in the literature for Zr alloys. Parameters at the transition points were analyzed to determine thresholds for this change in behavior, which occurred at an average hoop strain of 6.9 ± 2.1 %.

36 MATERIALS SCIENCE↗
DOE OSTI2025

Step-loaded creep testing of Zircaloy-4 cladding at higher temperatures in the α-phase

A refined understanding of zirconium-based cladding thermomechanical performance during rapid transients is essential for enhancing the safety and operation of light-water reactors. Traditional models for zirconium alloys under accident conditions generally assume that creep dominates fuel cladding performance. Here, these historic models have largely remained unchanged and serve as the basis for safety criteria development. As the U.S. nuclear industry pursues higher burnup levels, the increased release of fission gases during transients raises the risk of cladding failure in the low-temperature hcp α-phase, making the fidelity of these models of greater importance. Creep testing was conducted from 550–700°C with 25–120 MPa applied hoop stresses to investigate Zircaloy-4 deformation at accident-relevant temperatures in the α-phase. Step-loading was employed to capture creep behavior across a wide stress range from a single sample. The stress-strain rate data at higher temperatures (650 and 700°C) were well-described by isotropic versions of the Erbacher and Kaddour models, while the lower temperature data (550 and 600°C) were underpredicted by both anisotropic and isotropic model variants. Greater strain rates during the initial loading step at 650 and 700°C were attributed to recrystallization and grain growth of sub-micron crystallites. Yet, texture analysis revealed the basal split texture remained after testing. These observations produced results suggesting Zircaloy-4 claddings experience higher creep rates across the α-phase than previously thought, possibly related to dynamic anisotropy due to temperature dependent activation of deformation mechanisms, effects of biaxial loading, and variation in material condition between the current testing used in previous model development.

36 MATERIALS SCIENCE↗
DOE OSTI2024

Fuel performance analysis of Cr-coated Zircaloy-4 cladding during a prototypical LOCA event using BISON

Here, deformation and failure of chromium (Cr) coated Zircaloy-4 (Zry-4) were studied in loss-of-coolant accident (LOCA) conditions using the BISON fuel performance code. The BISON validation model simulating Halden research reactor experiments was extended to include Cr coatings and higher rod internal pressures to simulate high-burnup fuel. The transient simulations show Cr coatings help relieve stress in the Zry-4 substrate during the transient, delaying the onset of high-temperature creep, which leads to ballooning and bursting of the cladding. A nominal Cr coating thickness of 30 µm delays clad failure by 26 seconds and increases the clad burst temperature by 40 K. A parametric study showed that time to failure and burst temperature both increase with coating thickness, and Cr-coated cladding offers burst resistance under a wide range of rod internal pressures simulating high-burnup fuel. Results indicate that a thin Cr coating provides resistance against ballooning and bursting of cladding during LOCA events.

11 NUCLEAR FUEL CYCLE AND FUEL MATERIALS↗
DOE OSTI2024

Source term analysis of FeCrAl accident tolerant fuel using MELCOR

It has been established that incremental improvements in beyond design basis accident performance can be achieved through accident tolerant fuel (ATF). However, they have the potential to recover margin with respect to conventional fuel and therefore enhance plant economics through uprate or cycle length increase. To realize this potential, it is necessary to quantify the reduction in source term due to use of ATF, and correspondingly how this is affected by increasing the cycle length and/or burnup. This requires development of a risk informed analysis methodology for ATF under high burnup conditions, which is being developed within LWRS. To this end, a MELCOR simulation of FeCrAl ATF in a recovered Large Break LOCA (LBLOCA) scenario has been developed, using a model based on the Zion Pressurized Water Reactor (PWR). The new user defined material capability, along with the inclusion of detailed neutronics- and depletion-derived parameters such as core power distribution, decay heat behavior, and fission product inventories, allows a more detailed simulation of FeCrAl clad material properties and behavior than has previously been possible using MELCOR. These detailed FeCrAl results were compared with a zircaloy clad model to investigate the differences between the two clad types and quantify the benefits of FeCrAl ATF with an 18-month cycle. Next, the fuel cycle with ATF was extended to 24 months, to determine whether any additional safety margin provided by FeCrAl ATF could be leveraged to implement high burnup FeCrAl-clad fuel while retaining the same operating and safety limits as current zircaloy-clad fuel. For the particular scenario analyzed, the delay to fuel failure from using ATF was of the same order as the LOCA recovery time, and hence significant in reducing fission product release, with the 24-month FeCrAl core performing better than the 18-month zircaloy core. It is noted that for other transients, the reduction in release due to using FeCrAl may be less significant. Furthermore, the material model developed here can be used in such further studies in support of determining the overall source term.

11 NUCLEAR FUEL CYCLE AND FUEL MATERIALS↗
DOE OSTI2021

Post Examination of Candidate NpO 2 Targets for 238 Pu Production

Four targets composed of sintered NpO 2 pellets enclosed in Zircaloy cladding were irradiated in the High Flux Isotope Reactor for 2 to 4 cycles to determine if an oxide pellet and Zircaloy cladding would be usable candidates for 238 Pu production. The pellets were sintered to a high fraction of theoretical density (TD) and melt wires were placed in small holes that had been drilled in the center of selected pellets to determine if the pellet centers exceeded desirable operating temperatures. After irradiation, the targets were punctured to determine the internal target pressure and the fission gas release. None of the targets had excessive pressure, and fission gas release was in the range of 4 to 38%. The targets were then cut into segments for radiochemical analysis, and metallography (MET) mounts were created to examine the pellet microstructure and to search for the melt wires to determine if they had melted. Three of the four targets resulted in successful MET mounts; the two-cycle pellets were too friable to be handled. No signs of pellet melting were noted, and unfortunately, none of the melt wires could be recovered. The results indicate that this pellet/clad design offers a practical option for 238 Pu production.

36 MATERIALS SCIENCE↗
DOE OSTI2021

Creating Hydride Rim Structures in Zircaloy 4 Cladding Tubes to Mimic High Burnup

During their long service in commercial light water reactors, zirconium alloy cladding tubes are subject to oxidation and subsequent hydrogen pickup which can degrade the materials mechanical properties [1]. These degradations can lead to premature cladding ruptures during reactor power transients [2] as well as negatively impact the claddings post quench ductility following high temperature steam oxidation in thermal hydraulic transients [3]. Hydrogen has low solid solubility in zirconium and usually precipitates as brittle zirconium hydride platelets in the cladding metal matrix. Due to temperature driven diffusion (Soret effect) and the grain texture of stress relieved zirconium metal tubes, these hydrides precipitate with a circumferential orientation near the outer surface of the cladding tubes forming a hydride rim which can serve as a site for crack initiation during circumferential ‘hoop’ loading of the cladding [4rim formation][5]. In order to better understand the effect of hydride rims on the fracture behavior of stress relieved zirconium alloy cladding tubes a procedure to produce these rim-like structures is being developed at Idaho National Laboratory (INL).

11 NUCLEAR FUEL CYCLE AND FUEL MATERIALS↗
DOE OSTI2024

Hydrogen Effects on Cladding Performance during Simulated Loss of Coolant Accident Testing

Fresh Zircaloy cladding segments were charged with hydrogen and subjected to simulated Loss of Coolant Accident (LOCA) conditions to assess the impact of hydrogen on the cladding mechanical performance and rupture resistance. The cladding rupture temperature decreased by 10 °C for every 100 wppm H added into the system for two different internal pressurization cases. Post-test analysis showed a loss of ductility with increasing hydrogen content, evident through decreased balloon sizes, smaller rupture openings, and sharper rupture interfaces. Digital image correlation was used to map the cladding strain in situ for two cladding segments. An elevated intermediate temperature uniform strain was visible for the hydride cladding, occurring prior to the decreased ductility during balloon and rupture determined from posttest fractography and microscopy. The thermal stability of Zr alloys as a function of hydrogen concentration and the thermal stability of Zr hydride as a function of temperature are likely responsible for the uniform deformation behavior at intermediate temperatures. The present framework for rapid assessment of hydrogen effects on cladding rupture can be utilized as an initial comparison to high burnup cladding thermomechanical response to a LOCA, where local regions may contain high concentrations of precipitated Zr hydride phase.

11 NUCLEAR FUEL CYCLE AND FUEL MATERIALS↗
DOE OSTI2024

Hydrogen Effects on Cladding Performance during Simulated Loss of Coolant Accident Testing

Fresh Zircaloy cladding segments were charged with hydrogen and subjected to simulated Loss of Coolant Accident (LOCA) conditions to assess the impact of hydrogen on the cladding mechanical performance and rupture resistance. The cladding rupture temperature decreased by 10 °C for every 100 wppm H added into the system for two different internal pressurization cases. Post-test analysis showed a loss of ductility with increasing hydrogen content, evident through decreased balloon sizes, smaller rupture openings, and sharper rupture interfaces. Digital image correlation was used to map the cladding strain in situ for two cladding segments. An elevated intermediate temperature uniform strain was visible for the hydride cladding, occurring prior to the decreased ductility during balloon and rupture determined from posttest fractography and microscopy. The thermal stability of Zr alloys as a function of hydrogen concentration and the thermal stability of Zr hydride as a function of temperature are likely responsible for the uniform deformation behavior at intermediate temperatures. The present framework for rapid assessment of hydrogen effects on cladding rupture can be utilized as an initial comparison to high burnup cladding thermomechanical response to a LOCA, where local regions may contain high concentrations of precipitated Zr hydride phase.

11 NUCLEAR FUEL CYCLE AND FUEL MATERIALS↗
DOE OSTI2024

Hydrothermal Corrosion of Latest Generation of FeCrAl Alloys for Nuclear Fuel Cladding

After the Fukushima nuclear disaster, the nuclear materials community has been vastly investing in accident tolerant fuel (ATF) concepts to modify/replace Zircaloy cladding material. Iron–chromium–aluminum (FeCrAl) alloys are one of the leading contenders in this race. In this study, we investigated FA-SMT (or APMT-2), PM-C26M, and Fe17Cr5.5Al over a time period of 6 months in simulated BWR environments and compared their performance with standard Zirc-2 and SS316 materials. Our results implied that water chemistry along with alloy chemistry has a profound effect on the corrosion rate of FeCrAl alloys. Apart from SS316 and Zirc-2 tube specimens, all FeCrAl alloys showed a mass loss in hydrogen water chemistry (HWC). FA-SMT displayed minimal mass loss compared to PM-C26M and Fe17Cr5.5Al because of its higher Cr content. The mass gain of FeCrAl alloys in normal water chemistry (NWC) is significantly less when compared to Zirc-2.

36 MATERIALS SCIENCE↗