Investigation of cavitation damage of a mechanical pump impeller in high temperature potassium quarterly progress report no. 2, 1 mar. - 2 jul. 1965
Cavitation damage of turbopump impeller in high temperature potassium
CAVITATION↗
SEARCH · Search NASA
Results for “damage mechanisms”
Search indexed NASA NTRS and DOE OSTI research on propulsion, heat transfer, battery materials and energy systems. Follow report and document links to the original sources.
Quote a phrase for an exact phrase match. Source license links do not imply unrestricted reuse.
Investigation of cavitation damage of a mechanical pump impeller in high temperature potassium quarterly progress report no. 1, 7 dec. 1964 - 28 feb. 1965
Cavitation damage prediction from mixed flow centrifugal pump impeller in endurance testing in high temperature potassium
CAVITATION↗
Micro-mechanical analysis of damage growth and fracture in discontinuous fiber reinforced metal matrix composites
An experimental verification is presented for a new two parameter fracture model based on the equivalent remote biaxial stresses (ERBS). A detailed comparison is made between the new theory and the constant K(sub IC) approach of linear elastic fracture mechanics (LEFM). Fracture is predicted through a failure curve representing the change in a variable fracture toughness K(sub IC) with the ERBS ratio B(sub E). The nonsingular term (T) in the series expansion of the near crack-tip transverse stress is included in the model. Experimental results for polymethyl methacrylate (PPMA) show that the theory can account for the effects of geometry on fracture toughness as well as indicate the initiation of crack branching. It is shown that the new criterion predicts failure for PMMA with a 95 percent confidence zone which is nearly three times smaller than that of the LEFM K(sub IC) approach.
Goree, James G.↗
The effect of acute microgravity on mechanically-induced membrane damage and membrane-membrane fusion events
Although it is unclear how a living cell senses gravitational forces there is no doubt that perturbation of the gravitational environment results in profound alterations in cellular function. In the present study, we have focused our attention on how acute microgravity exposure during parabolic flight affects the skeletal muscle cell plasma membrane (i.e. sarcolemma), with specific reference to a mechanically-reactive signaling mechanism known as mechanically-induced membrane disruption or "wounding". Both membrane rupture and membrane resealing events mediated by membrane-membrane fusion characterize this response. We here present experimental evidence that acute microgravity exposure can inhibit membrane-membrane fusion events essential for the resealing of sarcolemmal wounds in individual human myoblasts. Additional evidence to support this contention comes from experimental studies that demonstrate acute microgravity exposure also inhibits secretagogue-stimulated intracellular vesicle fusion with the plasma membrane in HL-60 cells. Based on our own observations and those of other investigators in a variety of ground-based models of membrane wounding and membrane-membrane fusion, we suggest that the disruption in the membrane resealing process observed during acute microgravity is consistent with a microgravity-induced decrease in membrane order.
Parabolic Flight↗
The Effect of Acute Microgravity on Mechanically-Induced Membrane Damage and Membrane-Membrane Fusion Events
Although it is unclear how a living cell senses gravitational forces there is no doubt that perturbation of the gravitational environment results in profound alterations in cellular function. In the present study, we have focused our attention on how acute microgravity exposure during parabolic flight affects the skeletal muscle cell plasma membrane (i.e. sarcolemma), with specific reference to a mechanically-reactive signaling mechanism known as mechanically-induced membrane disruption or "wounding". This response is characterized by both membrane rupture and membrane resealing events mediated by membrane-membrane fusion. We here present experimental evidence that acute microgravity exposure can inhibit membrane-membrane fusion events essential for the resealing of sarcolemmal wounds in individual human myoblasts. Additional evidence to support this contention comes from experimental studies that demonstrate acute microgravity exposure also inhibits secretagogue-stimulated intracellular vesicle fusion with the plasma membrane in HL-60 cells. Based on our own observations and those of other investigators in a variety of ground-based models of membrane wounding and membrane-membrane fusion, we suggest that the disruption in the membrane resealing process observed during acute microgravity is consistent with a microgravity-induced decrease in membrane order.
Clarke, Mark, S. F.↗
Cumulative damage in the mechanics of viscoelastic fracture
Kinetic energy of body fracture, and loading functions of fracture theory for linear viscoelastic bodies
Jones, W. B., Jr.↗
Mechanisms of fatigue damage in boron/aluminum composites
Tensile fatigue tests were conducted on several laminates of boron/aluminum (6061-0). In laminates with 0 deg fibers on the outside, an analysis that identifies "shakedown" conditions predicted the stress amplitude below which no fatigue damage accumulated. A fatigue damage accumulation model which relates matrix fatigue cracking and the overall laminate properties is described. A model for the saturation damage stage development is presented, that identical laminates, tested in directions 90 deg apart (such that one layup has 90 deg outer plies and the other 0 deg), have different fatigue behaviors due to the stacking sequence. The 90 deg plies on the surface develop cracks earlier than predicted by shakedown. An attempt was made to explain this stacking sequence effect. Variable load history effects on the fatigue damage response were investigated. Tests reveal that for a given stress ratio the specimen seeks the saturation damage state for the largest stress range to which it is subjected. It was also found that little damage is generated by shifting a given stress range down, whereas significant damage may be created by shifting it upward. The laminate stresses were always tensile.
Johnson, W. S.↗
Mechanisms of fatigue damage in boron/aluminum composites
(Previously announced in STAR as N81-16135)
Johnson, W. S.↗
Mechanisms of cell damage in agitated microcarrier tissue culture reactors
Cells growing on microcarriers may be damaged by collisions of the microcarrier against another microcarrier or the reactor agitator. Bead-bead collisions are caused by small-scale turbulence, which can also cause high local shear stress on the cells. The cells are also exposed to 10-20 Hz cyclic shear stress by bead rotation.
Cherry, Robert S.↗
The effect of thermal damage on the mechanical properties of polymer regrinds
Reprocessed polymers are subjected to high processing temperatures that result in the breakdown of molecular chains and changes in the molecular structures. These phenomena are reflected in the mechanical properties of materials. Practically every regrind is seen as a new material. These experiments deal with the molding, regrinding, and reprocessing of test specimens for the study of their mechanical properties. The comparative test data from each recycled material would give students an insight of the molecular structures and property degradation. Three important rheological and mechanical properties such as melt flow, impact strength, and flexural strength are to be determined. These properties play key roles in the selection of engineering materials. The material selected for demonstration was Makrolon 3000L, a polycarbonate thermoplastic from Bayer AG. The thermal degradation due to repeated processing is reflected in the decrease in molecular weight and breakdown of molecular chains causing increase in melt flow. The Izod-impact resistance and the flexural strength deteriorate gradually.
Kundu, Nikhil K.↗
Micro-mechanical analysis of damage growth and fracture in discontinuous fiber reinforced metal matrix composites
The near-crack-tip stresses in any planar coupon of arbitrary geometry subjected to mode 1 loading may be equated to those in an infinite center-cracked panel subjected to the appropriate equivalent remote biaxial stresses (ERBS). Since this process can be done for all such mode 1 coupons, attention may be focused on the behavior of the equivalent infinite cracked panel. To calculate the ERBS, the constant term in the series expansion of the crack-tip stress must be retained. It is proposed that the ERBS may be used quantitatively to explain different fracture phenomena such as crack branching.
Goree, James G.↗
Evaluation of the mechanical properties and damage tolerance of five new toughened matrix composite materials
Notched and unnotched tension and compression properties of quasi-isotropic laminates are presently evaluated, in conjunction with compression-after-impact (CAI) strengths, for the cases of five different carbon fiber-reinforced/toughened matrix composites. For a given impact energy, CAIs were dependent on impact velocities. When compared with other matrix-toughened materials, the five presently considered were more damage-tolerant than such aircraft primary structure composite systems as T300/5208.
Cano, Roberto J.↗
Computer simulation of initial events in the biochemical mechanisms of DNA damage
Understanding the systematic and quantitative correlation between the physical events of energy deposition by ionizing radiation and the ensuing chemical and biochemical processes leading to DNA damage is one of the goals in radiation research. Significant progress has been made toward achieving the stated goal by using theoretical modeling techniques. These techniques are strongly dependent on computer simulation procedures. A review of such techniques with details of various stages of simulation development, including a comparison with available experimental data, is presented in this article.
Non-NASA Center↗
Simulation of Delamination Under High Cycle Fatigue in Composite Materials Using Cohesive Models
A new thermodynamically consistent damage model is proposed for the simulation of high-cycle fatigue crack growth. The basis for the formulation is an interfacial degradation law that links Fracture Mechanics and Damage Mechanics to relate the evolution of the damage variable, d, with the crack growth rate da/dN. The damage state is a function of the loading conditions (R and (Delta)G) as well as the experimentally-determined crack growth rates for the material. The formulation ensures that the experimental results can be reproduced by the analysis without the need of additional adjustment parameters.
Camanho, Pedro P.↗
A fracture mechanics analysis of impact damage in a thick composite laminate
Graphite/epoxy filament-wound cases (FWC) for the solid rocket motors of the space shuttle are being made by NASA. The FWC cases are wound with AS4W graphite fiber impregnated with an epoxy resin and are about 1.4 inches or more thick. Graphite-epoxy composite laminates, unlike metals, can be damaged easily by low velocity impacts of objects like dropped tools. The residual tension strength of the FWC laminate, after impact, is being studied at Langley Research Center. The conditions that give minimum visual evidence of damage are being emphasized. A fracture mechanics analysis was developed to predict the residual strength, after impact, using radiographs to measure the size of the damage and an equivalent surface crack to represent the damage.
Poe, C. C., Jr.↗
Effects of HF Treatments on Tensile Strength of Hi-Nicalon Fibers
Tensile strengths of as-received Hi-Nicalon fibers and those having a dual BN/SiC surface coating, deposited by chemical vapor deposition, have been measured at room temperature. These fibers were also treated with HF for 24 h followed by tensile strength measurements. Strengths of uncoated and BN/SiC coated Hi-Nicalon fibers extracted from celsian matrix composites, by dissolving away the matrix in HF for 24 h, were also determined. The average tensile strength of uncoated Hi-Nicalon was 3.19 +/- 0.73 GPa with a Weibull modulus of 5.41. The Hi-Nicalon/BN/SiC fibers showed an average strength of 3.04 q 0.53 GPa and Weibull modulus of 6.66. After HF treatments, the average strengths of the uncoated and BN/SiC coated Hi-Nicalon fibers were 2.69 +/- 0.67 GPa and 2.80 +/- 0.53 GPa and the Weibull moduli were 4.93 and 5.96, respectively. The BN/SiC coated fibers extracted from the celsian matrix composite exhibited a strength of 2.38 +/- 0.40 GPa and a Weibull modulus of 7.15. The strength of the uncoated Hi-Nicalon fibers in the composite was so severely degraded that they disintegrated into small fragments during extraction with HF. The uncoated fibers probably undergo mechanical surface damage during hot pressing of the composites. Also, the BN layer on the coated fibers acts as a compliant layer which protects the fibers from mechanical damage during composite processing. The elemental composition and thickness of the fiber coatings were deten-nined using scanning Auger analysis. Microstructural analyses of the fibers and the coatings were done by scanning electron microscopy and transmission electron microscopy. Strengths of fibers calculated using average and measured fiber diameters were in good agreement. Thus, the strength of fibers can be evaluated using an average fiber diameter instead of the measured diameter of each filament.
Bansal, Narottam P.↗
Effects of Interface Modification on Mechanical Behavior of Hi-Nicalon Fiber-Reinforced Celsian Matrix Composites
Unidirectional celsian matrix composites having approx. 42 volume percent of uncoated or BN/SiC-coated Hi-Nicalon fibers were tested in three-point bend at room temperature. The uncoated fiber-reinforced composites showed catastrophic failure with strength of 210 +/- 35 MPa and a flat fracture surface. In contrast, composites reinforced with BN/SiC-coated fibers exhibited graceful failure with extensive fiber pullout. Values of first matrix cracking stress and strain were 435 +/- 35 MPa and 0.27 +/- 0.01 %, respectively, with ultimate strength as high as 960 MPa. The elastic Young's modulus of the uncoated and BN/SiC-coated fiber-reinforced composites were measured as 184 q 4 GPa and 165 +/- 5 GPa, respectively. Fiber push-through tests and microscopic examination indicated no chemical reaction at the uncoated or coated fiber-matrix interface. The low strength of the uncoated fiber-reinforced composite is probably due to degradation of the fibers from mechanical surface damage during processing. Because both the coated and uncoated fiber reinforced composites exhibited weak interfaces, the beneficial effect of the BN-SiC dual layer is primarily the protection of fibers from mechanical damage during processing.
Bansal, Narottam P.↗
Particulate erosion mechanisms
Particulate damage and erosion of ductile metals are today plaguing design and field engineers in diverse fields of engineering and technology. It was found that too many models and theories were proposed leading to much speculation from debris analysis and failure mechanism postulations. Most theories of solid particle erosion are based on material removal models which do not fully represent the actual physical processes of material removal. The various mechanisms proposed thus far are: melting, low-cycle fatigue, extrusion, delamination, shear localization, adhesive material transfer, etc. The experimental data on different materials highlighting the observed failure modes of the deformation and cutting wear processes using optical and scanning electron microscopy are presented. The most important mechanisms proved from the experimental observations of the specimens exposed to both spherical and angular particles are addressed, and the validity of the earlier theories discussed. Both the initial stages of damage and advanced stages of erosion were studied to gain a fundamental understanding of the process.
Veerabhadrarao, P.↗