NASA NTRSDate not supplied

Morphological evolution and transition at nanoscale in BSTO ceramic materials

Considerable efforts have been devoted for the development of low cost ferroelectric and clean energy storage multifunctional materials. Modification in design and production of a low cost material with well proven process provides pathway for high energy density dielectric energy storage. We studied fluorine doped a commercially well-established material system barium strontium titanate with two different concentrations of dopants and studied the morphological transition and its effect on properties. It was observed that sample with higher concentration transitioned much faster into glassy state, followed by growth of fibers which turned into a self-arranged bird nest type shape. The sample with lower concentration changed slowly into glassy state and only few fibers were farmed. Dielectric was highly dependent on processing methods and shows variation with crystallinity of material, temperature and cooling conditions during processing. In the higher concentration range, we observed nano-scale interface breakdown very similar to that of solid-liquid interface breakdown during crystal growth.

dielectric↗
DOE OSTI2020

GeoMelt{sup R} In-Container Vitrification (ICV){sup TM} for Fukushima Daiichi Water Treatment Secondary Wastes - 20212

The Japanese government is supporting development work implemented jointly by Veolia subsidiaries Kurion Japan, K.K., Veolia Nuclear Solutions (VNS), Inc., and Veolia Nuclear Solutions Federal Services, LLC for treating radioactive waste generated from Fukushima Daiichi Nuclear Power Station (NPS) water treatment using the GeoMelt{sup TM} In-Container Vitrification (ICV){sup TM} technology. The initial work consisted of glass formulation and engineering-scale testing which was completed in 2018, in the frame of an IRID (International Research Institute for Nuclear Decommissioning) program as part of a project subsidized by Japan's Ministry of Economy, Trade and Industry (METI). The Fukushima Daiichi NPS Mid- and Long-Term Road-map requires investigation of methods to stabilize solid wastes (and to immobilize radioisotopes in the wastes) generated as a result of emergency response and decommissioning activities. Cooling water treatment has resulted in a significant amount of solid and slurry secondary wastes (mostly adsorbents and ion-exchange materials) which will require processing at some point. GeoMelt{sup R} ICV{sup TM} is a joule-heated melter technology which uses a refractory-lined single-use container combining the melter and disposal container. There is no pouring required nor concerns with refractory corrosion which allows the process to accommodate a wide range of waste chemistries and high waste loadings. The testing described here consisted of three engineering-scale melts, each processing between 212 kg and 240 kg of waste simulants, glass formers, and non-radioactive cesium (Cs) and strontium (Sr) tracers. Continuous isokinetic stack sampling of off-gas emissions was performed for each test in order to calculate Cs and Sr retention in the glass wasteform. Single-pass retention of Cs in the final glass wasteform ranged from 91.46 to 99.30%, and single-pass retention of Sr ranged from 99.76 to 100%. Planned particulate recycle will increase these retention levels. Melt 1 processed a mixture of KUR-EH (a zeolite-based ion-exchange material), simulated Advanced Liquid Processing System (ALPS) Carbonate and Iron Slurries, and glass additives. Melt 2 processed a mixture of KUR-EH, KUR-TSG (a titanate-based adsorbent), and glass additives. Melt 3 processed a mixture of KUR-EH, simulated barium sulfate/iron ferrocyanide sludge (AREVA sludge), and glass additives. Waste loadings for these melts ranged from 70 weight percent (wt%) to 82 wt%. Vitrification produces a waste form much denser than the stored water treatment secondary waste wastes, resulting in significant volume reduction. Volume reductions for the three tests ranged from 74 to 79 vol%. Vitrification produces a chemically durable wasteform. Pacific Northwest National Laboratory (PNNL) tested three glass samples from each engineering-scale melt) by the Materials Characterization Center 1 (MCC-1) test, an international standard leach test of the chemical durability of nuclear waste glasses. PNNL also obtained one U.S. reference glass (EA Glass) and two Japan reference glasses P0798) and tested these under the same MCC-1 conditions (90 deg. C, 10 m-1, DIW, and 7, 14, 28-day) as the GeoMelt{sup R} ICV{sup TM} glasses. The GeoMelt{sup R} ICV{sup TM} glasses exhibited lower total normalized releases and 14- to 28-day normalized release rates than the three reference glasses. These results suggest that the GeoMelt{sup R} ICV{sup TM} glasses have durabilities on par with high-level waste glasses under standard test conditions. Post-melt process sampling and analysis indicated no Cs migration into the melter refractory materials and very little deposition of Cs or Sr onto the melter hood or off-gas piping internals. The results of the testing indicated good Cs retention in the glass, high volume reduction and waste loadings, and excellent chemical durability. These factors are important to minimize treatment costs and to protect workers and the environment. (authors)

12 MANAGEMENT OF RADIOACTIVE AND NON-RADIOACTIVE W↗
DOE OSTI2021

An Efficient Bifunctional Air Electrode for Reversible Protonic Ceramic Electrochemical Cells

One of the main bottlenecks that limits the performance of reversible protonic ceramic electrochemical cells (R-PCECs) is the sluggish kinetics of the oxygen reduction and evolution reactions (ORR and OER). Here, the significantly enhanced ORR and OER kinetics and stability of a conventional La 0.6 Sr 0.4 Co 0.2 Fe 0.8 O 3-δ (LSCF) air electrode by an efficient catalyst coating of barium cobaltite (BCO) is reported. The polarization resistance of a BCO-coated LSCF air electrode at 600 oC is 0.16 Ω cm 2 , about 30% of that of the bare LSCF air electrode under the same conditions. Further, a R-PCEC with the BCO-coated LSCF air electrode shows exceptional performance in both fuel cell (maximum power density of 1.16 W cm -2 at 600 ºC) and electrolysis (current density of 1.80 A cm -2 at 600 ºC at 1.3 V) modes. Finally, the performance enhancement is attributed mainly to the facilitated rate of oxygen surface exchange.

32 ENERGY CONSERVATION, CONSUMPTION, AND UTILIZATI↗
DOE OSTI2025

Shape‐Stabilization of Phase Change Materials with Carbon‐Conscious Poly(hydroxy)Urethane Foams

Thermal energy regulation is a significant challenge, contributing to over 30% of annual greenhouse gas emission (GHG) emissions. Phase change materials (PCMs) offer a promising solution by storing thermal energy, which can enable the reuse of waste heat for heating and cooling; however, developing materials for shape-stabilized PCMs remains crucial. This work investigates a self-foaming poly(hydroxy)urethane (PHU), derived from a non-isocyanate polyurethane (NIPU), as a porous support for shape-stabilizing paraffinic and salt hydrate PCMs. PHU-encapsulated paraffinic PCMs exhibited excellent thermal stability over repeated cycles. Thermal stability with salt hydrate PCMs, specifically calcium chloride hexahydrate (CaCl 2 •6H 2 O), is achieved by the incorporation of 5 wt.% barium carbonate (BaCO 3 ) into the PHU foam. This enabled stable cycling for over 48 cycles with desirable thermal properties, i.e., a melting point ≈30 °C, high enthalpy (ca. 138 J g −1 per cycle), and a consistent freezing point ≈20 °C, making it suitable for applications in buildings and electric vehicle battery insulation. Also, incorporating graphite (1.5–10 wt.%) into the foam enhanced the thermal conductivity of shape-stabilized CaCl 2 •6H 2 O during heating and cooling cycles. Overall, the approach detailed here offers a carbon-conscious and chemically tunable material for thermal energy storage.

25 ENERGY STORAGE↗