Impact of Arsenic- and Indium-Terminated InGaAs Stressors on Carrier Confinement, Strain, Defects, and Transport Properties of Tensile-Strained Ge
Device-quality tensile-strained Ge (ε-Ge) grown on a large bandgap semiconductor with superior electrical and optical carrier confinement is essential for group-IV-based optoelectronics. Properties of ε-Ge active layers synthesized on In 0.24 Ga 0.76 As buffers with two different surface terminations─arsenic-rich and indium-rich─were experimentally demonstrated, highlighting the factors not considered in theoretical calculations. High-resolution X-ray diffraction and Raman spectroscopy analyses of these ε-Ge/In 0.24 Ga 0.76 As heterostructures confirmed the fully strained (1.6%) and partially relaxed (0.82%) nature of the ε-Ge bonded with arsenic-terminated (Ge As-terminated ) and indium-terminated (Ge In-terminated ) In 0.24 Ga 0.76 As stressors, respectively. High-resolution cross-sectional transmission electron microscopy showed a coherent, sharp, and fully strained ε-Ge/In 0.24 Ga 0.76 As heterointerface in the Ge As-terminated heterostructure, whereas microtwin defects were present in the Ge In-terminated heterostructure. These heterostructures were further characterized by evaluating the minority carrier lifetimes, high for Ge As-terminated (525 ns) and low for Ge In-terminated (69 ns), using the photoconductive decay technique. Moreover, band alignment was constructed using X-ray photoelectron spectroscopy, where the Ge As-terminated heterostructure revealed that both holes and electrons were confined within the ε-Ge active layer as a type-I band alignment with ΔE V, As-terminated = 0.22 eV and ΔE C,As-terminated = 0.38 eV. On the other hand, the Ge In-terminated heterostructure exhibited a type-II band alignment with ΔE V,In-terminated = – 0.02 eV and ΔE C,In-terminated = 0.53 eV. Furthermore, the magnetotransport properties revealed high mobility (321 cm 2 /(V s)) with single-electron transport in Ge As-terminated heterostructure and low mobility (3.34 cm 2 /(V s)) with multihole transport in the Ge In-terminated heterostructure. Therefore, preferring the ε-Ge on the arsenic-rich surface of In 0.24 Ga 0.76 As stressor over the indium-rich surface during material synthesis offers device-quality materials with high carrier lifetime and superior carrier confinement, which can provide an opportunity to fabricate efficient group-IV-based optoelectronic devices.