Results for “cracking” — Page 21

NASA NTRS1984

Crack growth direction in unidirectional off-axis graphite epoxy

An anisotropic elasticity crack tip stress analysis is implemented using three crack extension direction criteria (the normal stress ratio, the tensor polynominal and the strain energy density) to predict the direction of crack extension in unidirectional off axis graphite-epoxy. The theoretical predictions of crack extension direction are then compared with experimental results for 15 deg off axis tensile coupons with center cracks. Specimens of various aspect ratios and crack orientations are analyzed. It is shown that only the normal stress ratio criterion predicts the correct direction of crack growth.

Herakovich, C. T.↗

NASA NTRS1985

Closure of fatigue cracks at high strains

Experiments were conducted on smooth specimens to study the closure behavior of short cracks at high cyclic strains under completely reversed cycling. Testing procedures and methodology, and closure measurement techniques, are described in detail. The strain levels chosen for the study cover from predominantly elastic to grossly plastic strains. Crack closure measurements are made at different crack lengths. The study reveals that, at high strains, cracks close only as the lowest stress level in the cycle is approached. The crack opening is observed to occur in the compressive part of the loading cycle. The applied stress needed to open a short crack under high strain is found to be less than for cracks under small scale yielding. For increased plastic deformations, the value of sigma sub op/sigma sub max is observed to decrease and approaches the value of R. Comparison of the experimental results with existing analysis is made and indicates the limitations of the small scale yielding approach where gross plastic deformation behavior occurs.

Iyyer, N. S.↗

NASA NTRS1986

Effect of additional heat treatment of 2024-T3 on the growth of fatigue crack in air and in vacuum

In order to determine the influence of ductility on the fatigue crack growth rate of aluminum alloys, fatigue tests were carried out on central notched specimens of 2024-T3 and 2024-T8 sheet material. The 2024-T8 material was obtained by an additional heat treatment applied on 2024-T3 (18 hours at 192 C), which increased the static yield strength from 43.6 to 48.9 kgf/sq mm. A change in the ultimate strength was not observed. Fatigue tests were carried out on both materials in humid air and in high vacuum. According to a new crack propagation model, crack extension is supported to be caused by a slip-related process and debonding triggered by the environment. This model predicts an effect of the ductility on the crack growth rate which should be smaller in vacuum than in humid air; however, this was not confirmed. In humid air the crack-growth rate in 2024-T8 was about 2 times faster than in 2024-T3, while in vacuum the ratio was about 2.5. Crack closure measurements gave no indications that crack closure played a significant role in both materials. Some speculative explanations are briefly discussed.

Louwaard, E. P.↗

NASA NTRS1986

Line Spring Model and Its Applications to Part-Through Crack Problems in Plates and Shells

The line spring model is described and extended to cover the problem of interaction of multiple internal and surface cracks in plates and shells. The shape functions for various related crack geometries obtained from the plane strain solution and the results of some multiple crack problems are presented. The problems considered include coplanar surface cracks on the same or opposite sides of a plate, nonsymmetrically located coplanar internal elliptic cracks, and in a very limited way the surface and corner cracks in a plate of finite width and a surface crack in a cylindrical shell with fixed end.

Erdogan, F.↗

NASA NTRS1985

Crack growth in unidirectional graphite-epoxy under biaxial loading

An anisotropic elasticity crack tip stress analysis is implemented using three crack extension direction criteria (the normal stress ratio, the tensor polynominal and the strain energy density) to predict the direction of crack extension in unidirectional of axis graphite-epoxy. The theoretical predictions of crack extension direction are then compared with experimental results for 15 deg off axis tensile coupons with center cracks. Specimens of various aspect ratios and crack orientations are analyzed. It is shown that only the normal stress ratio criterion predicts the correct direction of crack growth.

Beuth, J. L., Jr.↗

NASA NTRS1985

Crack growth direction in unidirectional off-axis graphite-epoxy

An anisotropic elasticity crack tip stress analysis is implemented using three crack extension direction criteria (the normal stress ratio, the tensor polynominal and the strain energy density) to predict the direction of crack extension in unidirectional off axis graphite-epoxy. The theoretical predictions of crack extension direction are then compared with experimental results for 15 deg off axis tensile coupons with center cracks. Specimens of various aspect ratios and crack orientations are analyzed. It is shown that only the normal stress ratio criterion predicts the correct direction of crack growth.

Herakovich, C. T.↗

NASA NTRS1987

Energy dissipation associated with crack extension in an elastic-plastic material

Crack extension in elastic-plastic material involves energy dissipation through the creation of new crack surfaces and additional yielding around the crack front. An analytical procedure, using a two-dimensional elastic-plastic finite element method, was developed to calculate the energy dissipation components during a quasi-static crack extension. The fracture of an isotropic compact specimen was numerically simulated using the critical crack-tip-opening-displacement (CTOD) growth criterion. Two specimen sizes were analyzed for three values of critical CTOD. Results from the analyses showed that the total energy dissipation rate consisted of three components: the crack separation energy rate, the plastic energy dissipation rate, and the residual strain energy rate. All three energy dissipation components and the total energy dissipation rate initially increased with crack extension and finally reached constant values.

Shivakumar, K. N.↗

NASA NTRS1987

Energy dissipation associated with crack extension in an elastic-plastic material

Crack extension in elastic-plastic material involves energy dissipation through the creation of new crack surfaces and additional yielding around the crack front. An analytical procedure, using a two-dimensional elastic-plastic finite element method, was developed to calculate the energy dissipation components during a quasi-static crack extension. The fracture of an isotropic compact specimen was numerically simulated using the critical crack-tip-opening-displacement (CTOD) growth criterion. Two specimen sizes were analyzed for three values of critical CTOD. Results from the analysis showed that the total energy dissipation rate consisted of three components: the crack separation energy rate, the plastic energy dissipation rate, and the residual strain energy rate. All three energy dissipation components and the total energy dissipation rate initially increased with crack extension and finally reached constant values.

Shivakumar, K. N.↗

NASA NTRS1988

The mode 3 crack problem in bonded materials with a nonhomogeneous interfacial zone

The mode 3 crack problem for two bonded homogeneous half planes was considered. The interfacial zone was modelled by a nonhomogeneous strip in such a way that the shear modulus is a continuous function throughout the composite medium and has discontinuous derivatives along the boundaries of the interfacial zone. The problem was formulated for cracks perpendicular to the nominal interface and was solved for various crack locations in and around the interfacial region. The asymptotic stress field near the tip of a crack terminating at an interface was examined and it was shown that, unlike the corresponding stress field in piecewise homogeneous materials, in this case the stresses have the standard square root singularity and their angular variation was identical to that of a crack in a homogeneous medium. With application to the subcritical crack growth process in mind, the results given include mostly the stress intensity factors for some typical crack geometries and various material combinations.

Erdogan, Fazil↗

NASA NTRS1988

Cracking of coated materials under transient thermal stresses

The crack problem for a relatively thin layer bonded to a very thick substrate under thermal shock conditions is considered. The effect of surface cooling rate is studied by assuming the temperature boundary condition to be a ramp function. Among the crack geometries considered are the edge crack in the coating layer, the broken layer, the edge crack going through the interface, the undercoat crack in the substrate and the embedded crack crossing the interface. The primary calculated quantity is the stress intensity factor at various singular points and the main variables are the relative sizes and locations of cracks, the time, and the duration of the cooling ramp. The problem is solved and rather extensive results are given for two material pairs, namely a stainless steel layer welded on a ferritic medium and a ceramic coating on a steel substrate.

Rizk, A. A.↗

NASA NTRS1989

Treatment of singularities in cracked bodies

Three-dimensional finite-element analyses of middle-crack tension (M-T) and bend specimens subjected to mode I loadings were performed to study the stress singularity along the crack front. The specimen was modeled using 20-node isoparametric elements. The displacements and stresses from the analysis were used to estimate the power of singularities using a log-log regression analysis along the crack front. The analyses showed that finite-sized cracked bodies have two singular stress fields of the form rho = C sub o (theta, z) r to the -1/2 power + D sub o (theta, phi) R to the lambda rho power. The first term is the cylindrical singularity with the power -1/2 and is dominant over the middle 96 pct (for Poisson's ratio = 0.3) of the crack front and becomes nearly zero at the free surface. The second singularity is a vertex singularity with the vertex point located at the intersection of the crack front and the free surface. The second term is dominant at the free surface and becomes nearly zero away from the the boundary layer. The thickness of the boundary layer depends on Poisson's ratio of the material and is independent of the specimen type. The thickness of the boundary layer varied from 0 pct to about 5 pct of the total specimen thickness as Poisson's ratio varied from 0.0 to 0.45. Because there are two singular stress fields near the free surface, the strain energy release rate (G) is an appropriate parameter to measure the severity of the crack.

Shivakumar, K. N.↗

NASA NTRS1988

Line spring model and its applications to part-through crack problems in plates and shells

The line spring model is described and extended to cover the problem of interaction of multiple internal and surface cracks in plates and shells. The shape functions for various related crack geometries obtained from the plane strain solution and the results of some multiple crack problems are presented. The problems considered include coplanar surface cracks on the same or opposite sides of a plate, nonsymmetrically located coplanar internal elliptic cracks, and in a very limited way the surface and corner cracks in a plate of finite width and a surface crack in a cylindrical shell with fixed end.

Erdogan, Fazil↗

NASA NTRS1988

An experimental study of the closure behavior of short and long cracks

Experiments were conducted on 2024-T3 aluminum specimens. The laser-based interferometric strain/displacement optical system was used to measure crack opening displacement. The displacement data were measured near the crack tip, at the crack mouth, and at other locations along the crack line for both short and long cracks. The dependence of opening load ratio on measurement locations was observed. The ratio decreased systematically as the measurement locations moved away from the crack tip. However, the ratio stayed roughly the same for the near tip surface measurements at various crack lengths.

Su, X.↗

NASA NTRS1990

Radial Cracks Would Signal Wearout Of Turbine Blades

Nonfatal defects made to appear before fatal ones. Proposed to design turbine blades to crack radially before they crack chordwise. Advance radial cracking promoted in design by adjusting thermal stresses and net bending stresses. Prior appearance of radial crack or cracks in used blade serves as warning that more-threatening chordwise crack or cracks may subsequently appear. Blade replaced before it fails.

Paulus, Donald E.↗

NASA NTRS1989

Three-dimensional aspects of plasticity-induced fatigue crack closure

A three-dimensional elastoplastic finite element analysis of fatigue crack growth and closure in a center-crack tension specimen was performed in order to investigate the crack opening stress as a function of specimen thickness under constant amplitude loading conditions. Elastic-perfectly plastic conditions were assumed and cycle loading was kept at R = 0.1. Firstly, by imposing proper boundary conditions on the three-dimensional model, a plane strain analysis was carried out. The ratio of stabilized opening stress over the maximum applied stress under plane strain conditions was found to be 0.28. Secondly, the model thickness was varied under fully three-dimensional conditions, and crack-opening stresses were determined for each specimen thickness. The crack-opening stress is found to vary through the thickness for the center crack tension specimen. On the specimen surface and in the midplane the crack-opening stress levels tend to two-dimensional solutions for plane stress and plane strain conditions, respectively.

Chermahini, R. G.↗

NASA NTRS1989

Surface crack problems in plates

The mode I crack problem in plates under membrane loading and bending is reconsidered. The purpose is to examine certain analytical features of the problem further and to provide some new results. The formulation and the results given by the classical and the Reissner plate theories for through and part-through cracks are compared. For surface cracks the three-dimensional finite element solution is used as the basis of comparison. The solution is obtained and results are given for the crack/contact problem in a plate with a through crack under pure bending and for the crack interaction problem. Also, a procedure is developed to treat the problem of subcritical crack growth and to trace the evolution of the propagating crack.

Joseph, P. F.↗

NASA NTRS1989

Internal state variable approach for predicting stiffness reductions in fibrous laminated composites with matrix cracks

A mathematical model utilizing the internal state variable concept is proposed for predicting the upper bound of the reduced axial stiffnesses in cross-ply laminates with matrix cracks. The axial crack opening displacement is explicitly expressed in terms of the observable axial strain and the undamaged material properties. A crack parameter representing the effect of matrix cracks on the observable axial Young's modulus is calculated for glass/epoxy and graphite/epoxy material systems. The results show that the matrix crack opening displacement and the effective Young's modulus depend not on the crack length, but on its ratio to the crack spacing.

Lee, Jong-Won↗

NASA NTRS1989

Cracking of coated materials under transient thermal stresses

The crack problem for a relatively thin layer bonded to a very thick substrate under thermal shock conditions is considered. The effect of surface cooling rate is studied by assuming the temperature boundary condition to be a ramp function. Among the crack geometries considered are the edge crack in the coating layer, the broken layer, the edge crack going through the interface, the undercoat crack in the substrate and the embedded crack crossing the interface. The primary calculated quantity is the stress intensity factor at various singular points and the main variables are the relative sizes and locations of cracks, the time, and the duration of the cooling ramp. The problem is solved and rather extensive results are given for two material pairs, namely a stainless steel layer welded on a ferritic medium and a ceramic coating on a steel substrate.

Rizk, A. A.↗