Failure Morphologies of Cyclically Oxidized ZrO2-Based Thermal Barrier Coatings

Plasma-sprayed thermal barrier coatings (TBC s) were thermal cycle tested in air at 1163 C until spallation of the top coat. Each thermal cycle consisted of a 45 minute exposure at the elevated temperature followed by a 15 minute cool to ambient temperature. The TBC s consisted of a ZrO2-based top coat containing various amounts of Y2O3, and/or Yb2O3, Gd2O3, and Nd2O3 applied by air plasma spraying and an MCrAlY bond coat applied by low pressure plasma spraying. The substrate was a single-crystal, Ni-based superalloy. The time to failure of the top coat varied from tens to hundreds of thermal cycles based on composition and spray parameters. The bond coat/top coat interface morphology and sample cross sections were examined by SEM and optical microscopy. The failure morphology following the cyclic oxidation testing will be discussed in relationship to the properties of the ceramic top coats.

Nesbit, James A.↗

A review of liquid lubricant thermal/oxidative degradation

The fundamental processes occurring during the thermal and oxidative degradation of hydrocarbons are reviewed. Particular emphasis is given to various classes of liquid lubricants such as mineral oils, esters, polyphenyl ethers, C-ethers, and fluorinated polyethers. Experimental techniques for determining thermal and oxidative stabilities of lubricants are discussed. The role of inhibitors and catalysis is also covered.

Jones, W. R., Jr.↗

Oxidation-based model for thermal barrier coating life

A procedure is described for modeling the lives of thermal barrier coatings subjected to high-temperatrue environments. The models is used to calculate cycles-to-failure as a function of heating cycle duration. It is based on the presumption that oxidation is the single important time-dependent factor which limits the life of these coatings, and that oxidation-induced strains combine with cyclic strains to promote slow crack growth in the ceramic layer. Good agreement is obtained between calculated and experimental lives for specimens tested in a furnace. This shows that an oxidation-based approach is promising. The importance of reproducible specimen preparation is also discussed.

Miller, R. A.↗

Oxidation instability of SiC and Si3N4 following thermal excursions

The effect of thermal excursion and thermal cycling on the oxidation stability of chemical vapor-deposited (CVD) SiC and Si3N4 was studied at 1350 C. Thermal cycling alone produced no noticeable change in oxidation kinetics. However, TEM showed that oxide scales grown in cycles consist of alternating layers of SiO2 and Si2N2O. When the oxidation of CVD SiC or Si3N4 at 1350 C was interrupted with a 1.5-h annealing in Ar at 1500 C, the kinetics of reoxidation at 1350 C were found to be drastically increased. The SiC and Si3N4 then oxidized essentially at the same rate, which is over 50 times the preannealing rate, and comparable to the expected oxidation rate of these materials at 1500 C.

Ogbuji, Linus U. J. T.↗

Root Cause Assessment of Pressure Drop Rise of a Packed Bed of Lithium Hydroxide in the International Space Station Trace Contaminant Control System

The trace contaminant control system (TCCS) located in the International Space Station s (ISS) U.S. laboratory module employs physical adsorption, thermal catalytic oxidation, and chemical adsorption to remove trace chemical contamination produced by equipment offgassing and anthropogenic sources from the cabin atmosphere. The chemical adsorption stage, consisting of a packed bed of granular lithium hydroxide (LiOH), is located after the thermal catalytic oxidation stage and is designed to remove acid gas byproducts that may be formed in the upstream oxidation stage. While in service on board the ISS, the LiOH bed exhibited a change in flow resistance that leading to flow control difficulties in the TCCS. Post flight evaluation revealed LiOH granule size attrition among other changes. An experimental program was employed to investigate mechanisms hypothesized to contribute to the change in the packed bed s flow resistance. Background on the problem is summarized, including a discussion of likely mechanisms. The experimental program is described, results are presented, and implications for the future are discussed.

Aguilera, Tatiana↗

A stochastic model of turbulent mixing with chemical reaction: Nitric oxide formulation in a plug-flow burner

A stochastic model of turbulent mixing was developed for a reactor in which mixing is represented by n-body fluid particle interactions. The model was used to justify the assumption (made in previous investigations of the role of turbulent mixing on burner generated thermal nitric oxide and carbon monoxide emissions) that for a simple plug flow reactor, composition nonuniformities can be described by a Gaussian distribution function in the local fuel:air equivalence ratio. Recent extensions of this stochastic model to include the combined effects of turbulent mixing and secondary air entrainment on thermal generation of nitric oxide in gas turbine combustors are discussed. Finally, rate limited upper and lower bounds of the nitric oxide produced by thermal fixation of molecular nitrogen and oxidation of organically bound fuel nitrogen are estimated on the basis of the stochastic model for a plug flow burner; these are compared with experimental measurements obtained using a laboratory burner operated over a wide range of test conditions; good agreement is obtained.

Flagan, R. C.↗

Defect Clustering and Nano-phase Structure Characterization of Multicomponent Rare Earth-Oxide-Doped Zirconia-Yttria Thermal Barrier Coatings

Advanced thermal barrier coatings (TBCs) have been developed by incorporating multicomponent rare earth oxide dopants into zirconia-based thermal barrier coatings to promote the creation of the thermodynamically stable, immobile oxide defect clusters and/or nanophases within the coating systems. In this paper, the defect clusters, induced by Nd, Gd, and Yb rare earth dopants in the zirconia-yttria thermal barrier coatings, were characterized by high-resolution transmission electron microscopy (TEM). The TEM lattice imaging, selected area diffraction (SAD), and electron energy-loss spectroscopy (EELS) analyses demonstrated that the extensive nanoscale rare earth dopant segregation exists in the plasma-sprayed and electron-physical-vapor-deposited (EB PVD) thermal barrier coatings. The nanoscale concentration heterogeneity and the resulting large lattice distortion promoted the formation of parallel and rotational defective lattice clusters in the coating systems. The presence of the 5-to 100-nm-sized defect clusters and nanophases is believed to be responsible for the significant reduction of thermal conductivity, improved sintering resistance, and long-term high temperature stability of the advanced thermal barrier coating systems.

Zhu, Dongming↗

Pressure Engineering Promising Transparent Oxides with Large Conductivity Enhancement and Strong Thermal Stability

Abstract Transparent conducting oxides (TCO) with high electrical conductivity and high visible light transparency are desired for a wide range of high‐impact engineering. Yet, usually, a compromise must be made between conductivity and transparency, limiting the practical application of a TCO to the next level. Furthermore, TCO performance is highly sensitive to composition, so conventional synthesis methods, such as chemical doping, cannot unravel the mysteries of the quantitative structure–performance relationship. Thus, improving the fundamental understanding or creating materials‐by‐design has limited success. Here, a strategy is proposed to modulate the lattice and electronic and optical properties precisely by applying pressure on a TCO. Strikingly, after compression–decompression treatment on the indium titanium oxides (ITiO), a highly transparent and metastable phase with two orders of magnitude enhancement in conductivity is synthesized from an irreversible phase transition. Moreover, this phase possesses previously unattainable filter efficiency on hazardous blue light up to 600 °C, providing potential for healthcare‐related applications with strong thermal stability up to 200 °C. These results demonstrate that pressure engineering is a clean and effective tool for tailoring functional materials that are not achievable by other means, providing an exciting alternative property‐tuning dimension in materials science.

37 INORGANIC, ORGANIC, PHYSICAL, AND ANALYTICAL CH↗

Silicon-slurry/aluminide coating

A low cost coating protects metallic base system substrates from high temperatures, high gas velocity ovidation, thermal fatigue and hot corrosion and is particularly useful fo protecting vanes and blades in aircraft and land based gas turbine engines. A lacquer slurry comprising cellulose nitrate containing high purity silicon powder is sprayed onto the superalloy substrates. The silicon layer is then aluminized to complete the coating. The Si-Al coating is less costly to produce than advanced aluminides and protects the substrates from oxidation and thermal fatigue for a much longer period of time than the conventional aluminide coatings. While more expensive Pt-Al coatings and physical vapor deposited MCrAlY coatings may last longer or provide equal protection on certain substrates, the Si-Al coating exceeded the performance of both types of coatings on certain superalloys in high gas velocity oxidation and thermal fatigue and increased the resistance of certain superalloys to hot corrosion.

Deadmore, D. L.↗

Evaluation of Ultra-High Temperature Ceramics for Propulsion Application

Ultra-high temperature ceramic (UHTC) materials consisting of zirconium diboride or hafnium diboride plus silicon carbide offer a combination of properties that make them candidates for airframe leading edges on sharp-bodied reentry vehicles. These UHTC perform well in the environment for such applications, i.e. low pressure air. The purpose of this study was to examine three of these materials under conditions more representative of a propulsion environment, i.e. higher oxygen and total pressure. Results of stren$h and fracture toughness measurements, furnace oxidation, and thermal shock exposures are presented. The poor oxidation resistance of UHTCs is the predominant factor limiting their applicability to propulsion.

Levine, Stanley R.↗

Advanced Anode for Internal Reforming and Thermal Management in Solid Oxide Fuel Cells

Solid oxide fuel cell (SOFC) is an efficient and clean electrical power generation system compared to conventional combustion based technologies with energy efficiency reaching as high as 85-90% in co-generation mode (electricity and heat). Other advantages of SOFCs are hybridization, modularity of construction, small CO 2 foot print per kWh of generated electricity and fuel flexibility. Hydrocarbons present in the gaseous fuel is utilized in SOFCs by internal or external reforming. There are two different internal reforming concepts: Direct Internal Reforming (DIR) and Indirect Internal Reforming (IIR). For DIR operation, the endothermic reforming reaction and the exothermic reaction from the oxidation reaction are operated together in the single unit eliminating the requirement for a separate fuel reformer. This configuration also simplifies the overall system design, making SOFC more attractive and efficient means of producing electrical power. The main advantage of the DIR type of operation is that the H 2 or CO consumption by the electrochemical reaction could directly promote the conversion of methane at the anode side of the fuel cell resulting in high conversion and high efficiency. The DIR operation, however, requires an anode material that has desired dual catalytic (hetero and electro) properties for reforming reaction and electrochemical reactions. The anode materials also need to remain resistant to carbon formation at the operating temperature and atmosphere with stable cell performance. Another requirement is to match the reforming reactions and electrochemical reactions to avoid local cooling or overheating, which can result in mechanical failure due to thermally induced stresses. Direct internal reforming (DIR) of hydrocarbon fuels simplifies the overall SOFC system design making it more attractive and efficient for producing electrical power. Low cost alloy anodes for distributed internal reforming of methane and other hydrocarbon fuels offer increased fuel-flexibility, reliability, and long term performance stability of solid oxide fuel cells (SOFC). The research program examined modification of the chemical compositions and microstructure of high entropy alloy (HEA) anode materials using thermochemical calculations and process simulation and modeling to achieve distributed reforming over the entire anode to eliminate hot zones. Cell fabrication and testing of the HEA anodes using button cell configuration has been performed to demonstrate the advantages of new anode over traditional Ni-YSZ anodes for distributed reforming and carbon free operation. Technical accomplishments include identification and synthesis of HEA carbon-resistant anode, demonstration of reduction in reforming rate confirmed by GC and modelling data validating effectiveness for thermal management in cell/stacks, electrochemical testing of HEA anode in single cell (HEA-GDC||YSZ||LSM-YSZ) and Characterization of pretest and posttest anode materials by TEM and SEM-EDS confirming carbon-free operation.

30 DIRECT ENERGY CONVERSION↗

Preliminary investigation of zirconium boride ceramals for gas-turbine blade applications

Zirconium boride ZrB2 ceramals were investigated for possible gas-turbine-blade application. Included in the study were thermal shock evaluations of disks, preliminary turbine-blade operation, and observations of oxidation resistance. Thermal shock disks of the following three compositions were studied: (a) 97.5 percent ZrB2 plus 2.5 percent B by weight; (b) 92.5 percent ZrB2 plus 7.5 percent B by weight; and (c) 100 percent ZrB2. Thermal shock disks were quenched from temperatures of 1800 degrees, 2000 degrees, 2200 degrees, and 2400 degrees F. The life of turbine blades containing 93 percent ZrB2 plus 7 percent B by weight was determined in gas-turbine tests. The blades were run at approximately 1600 degrees F and 15,000 to 26,000 rpm. The thermal shock resistance of the 97.5 percent ZrB2 plus 2.5 percent boron ceramals compares favorably with that of TiC plus Co and TiC plus Ni ceramals. Oxidation of the disks during the thermal shock evaluation was slight for the comparatively short time (8.3 hr) up through 2000 degrees F. Oxidation of a specimen was severe, however, after 100 hours at 2000 degrees F. The turbine blade performance evaluation of the 93 percent ZrB2 plus 7 percent B composition was preliminary in scope ; no conclusions can be drawn.

Hoffman, Charles A↗

Vacuum Plasma Spray of CuCrNb Alloy for Advanced Liquid - Fuel Combustion Chambers

The copper-8 atomic percent chromium-4 atomic percent niobium (CuCrNb) alloy was developed by Glenn Research Center (formally Lewis Research Center) as an improved alloy for combustion chamber liners. In comparison to NARloy-Z, the baseline (as in Space Shuttle Main Engine) alloy for such liners, CuCrNb demonstrates mechanical and thermophysical properties equivalent to NARloy-Z, but at temperatures 100 C to 150 C (180 F to 270 F) higher. Anticipated materials related benefits include decreasing the thrust cell liner weight 5% to 20%, increasing the service life at least two fold over current combustion chamber design, and increasing the safety margins available to designers. By adding an oxidation and thermal barrier coating to the liner, the combustion chamber can operate at even higher temperatures. For all these benefits, however, this alloy cannot be formed using conventional casting and forging methods because of the levels of chromium and niobium, which exceed their solubility limit in copper. Until recently, the only forming process that maintains the required microstructure of CrNb intermetallics is powder metallurgy formation of a billet from powder stock, followed by extrusion. This severely limits its usefulness in structural applications, particularly the complex shapes required for combustion chamber liners. Vacuum plasma spray (VPS) has been demonstrated as a method to form structural articles including small combustion chambers from the CuCrNb alloy. In addition, an oxidation and thermal barrier layer can be formed integrally on the hot wall of the liner that improve performance and extend service life. This paper discusses the metallurgy and thermomechanical properties of VPS formed CuCrNb versus the baseline powder metallurgy process, and the manufacturing of small combustion chamber liners at Marshall Space Flight Center using the VPS process. The benefits to advanced propulsion initiatives of using VPS to fabricate combustion chamber liners while maintaining the superior CuCrNb properties are also presented.

Zimmerman, Frank↗

Oxidation behavior of a thermal barrier coating

Thermal barrier coatings, consisting of a plasma sprayed calcium silicate ceramic layer and a CoCrAlY or NiCrAlY bond coat, were applied on B-1900 coupons and cycled hourly in air in a rapid-response furnace to maximum temperatures of 1030, 1100, or 1160 C. Eight specimens were tested for each of the six conditions of bond-coat composition and temperature. Specimens were removed from test at the onset of failure, which was taken to be the formation of a fine surface crack visible at 10X magnification. Specimens were weighed periodically, and plots of weight gain vs time indicate that weight is gained at a parabolic rate after an initial period where weight was gained at a much greater rate. The high initial oxidation rate is thought to arise from the initially high surface area in the porous bond coat. Specimen life (time to first crack) was found to be a strong function of temperature. However, while test lives varied greatly with time, the weight gain at the time of specimen failure was quite insensitive to temperature. This indicates that there is a critical weight gain at which the coating fails when subjected to this test.

Miller, R. A.↗

RF surface resistance tuning of superconducting niobium via thermal diffusion of native oxide

Recently, Nb superconducting radio frequency cavities vacuum heat treated between 300 and 400°C for a few hours have exhibited very high quality factors (~5 × 10 10 at 2.0 K). Secondary ion mass spectrometry measurements of O, N, and C show that this enhancement in RF surface conductivity is primarily associated with interstitial O alloying via dissolution and diffusion of the native oxide. We use a theory of oxide decomposition and O diffusion to quantify previously unknown parameters crucial in modeling this process. RF measurements of a vacuum heat-treated Nb superconducting radio frequency cavity confirm the minimized surface resistance (higher Q 0 ) previously expected only from 800 °C diffusive alloying with N.

75 CONDENSED MATTER PHYSICS, SUPERCONDUCTIVITY AND↗

Ceramic Adhesive and Methods for On-Orbit Repair of Re-Entry Vehicles

This adhesive is capable of repairing damaged leading edge components of reentry vehicles while in space, and is novel with regard to its ability to be applied in the vacuum of space, and in a microgravity environment. Once applied, the adhesive provides thermal and oxidation protection to the substrate (in this case, reinforced carbon/carbon composites, RCCs) during re-entry of a space vehicle. Although there may be many formulations for repair adhesives, at the time of this reporting, this is the first known adhesive capable of an on-orbit repair. The adhesive is an engineered ceramic material composed of a pre-ceramic polymer and refractory powders in the form of a paste or putty that can be applied to a scratched, cracked, or fractured composite surface, covering and protecting the damaged area. The adhesive is then "cured" with a heat cycle, thereby cross-linking the polymer into a hardened material and bonding it to the substrate. During the heat of reentry, the material is converted to a ceramic coating that provides thermal and oxidative stability to the repaired area, thus allowing the vehicle to pass safely from space into the upper atmosphere. Ceramic powders such as SiC, ZrB2 and Y2O3 are combined with allylhydridopolycarbosilane (AHPCS) resin, and are mixed to form a paste adhesive. The material is then applied to the damaged area by brush, spatula, trowel, or other means to fill cracks, gaps, and holes, or used to bond patches onto the damaged area. The material is then cured, in a vacuum, preferably at 250F (approximately equal to 121C) for two hours. The re-entry heating of the vehicle at temperatures in excess of 3,000F (approximately equal to 1,650C) then converts this material into a ceramic coating. This invention has demonstrated advantages in resistance to high temperatures, as was demonstrated in more than 100 arc-jet tests in representative environments at NASA. Extensive testing verified oxidation protection for the repaired substrate (RCC), and confirmed that the microstructure of the resulting repair leads to durability and resistance to melting or flow. Its processability and working life in a vacuum was demonstrated by NASA astronauts in glovebox processing studies, as well as on-orbit in the open space shuttle bay. All of these advantages increase the working life of NASA vehicles, as well as improve safety for any crew on a manned vehicle. The adhesive, trademarked NOAX(TM). or Non-Oxide Adhesive Experimental, flew on all space shuttle missions from Return To Flight (STS-114) until the final flight (STS- 135) as a crack repair material for the leading edges and nose cap of the vehicle. NOAX(TM) was patented under U.S. Patents 7,628,878 and 7,888,277.

Riedell, James A.↗