Comparing Synthetic Routes and Thermal Characteristics of Alternate APO Variants
Low density, high-strength, temperature-resistant foams see widespread application in the aerospace and weapons fields due to their excellent qualities as structural supports. In these demanding environments, the most common formulation is a three-phase syntactic foam containing APOCure-601, BMI, and carbon or glass microballoons. Of these, APOCure-601 and BMI form the polymer resin amino-poly(oxadiazole) bismaleimide (APO-BMI), also known as Legacy APO or S-1,2-Ethyl-APO. In manufacturing this foam, the selective laser sintering (SLS) additive manufacturing technique is quickly gaining prominence, over more traditional injection molding since SLS allows for 3D printing of materials and reduces overall cost and waste production. That said, SLS also requires a narrow window between the melt and cure temperatures for a successful print. SLS printing of APO-BMI is therefore difficult since the compound possesses a broad window between its melting and curing temperatures, and also requires several post-cure steps or complete polymerization. This work explores synthesis optimization and thermal characteristics for variant Apo-BMI structures by observing the effect that alternative heteroatoms in the APO linkages, geometries 0f the BMI groups, and bridge structure identities impart on the resultant material. Synthetic methods for these altered structures were established in batch, with some others further converted to continuous flow chemistry, a method that produces materials in a continuous stream and is highly reproducible and readily scaled. Additionally, each structural change significantly altered the melt and cure properties for each APO variant, which is advantageous for SLS manufacturing.