NASA/ORNL/AFRL Project Work on EBM LSHR: Additive Manufacturing of High-Temperature Gamma-Prime Strengthened Ni-Based Superalloys

Powder-bed fabrication of aerospace alloys may revolutionize production by eliminating the need for extensive machining and expensive tooling. Heated-bed electron-beam melting (EBM) offers advantages over non-heated laser additive manufacturing (AM) methods, including lower residual stress, reduced risk of contamination, slower cooling rates, and faster build times. NASA Glenn Research Center has joint project work with Oak Ridge National Lab and the Air Force Research Laboratory to explore the feasibility of fabricating advanced Ni-based gamma-prime superalloys with EBM AM.

additive manufacturing↗

An Abrupt Transition to an Intergranular Failure Mode in the Near-Threshold FCG Regime in Ni-Based Superalloys

Cyclic near-threshold FCG behavior of two disk superalloys was evaluated, and was shown to exhibit an unexpected sudden failure mode transition from a mostly transgranular failure mode at higher stress intensities to an almost completely intergranular failure mode in the threshold regime. The change in failure modes was associated with a crossover effect in which the conditions that produced higher FCG rates in the Paris regime resulted in lower FCG rates and increased ΔKth values in the threshold region. High resolution scanning and transmission electron microscopy was used to carefully characterize the crack tips at these near-threshold conditions. Formation of stable Al-oxide followed by Cr and Ti oxides was found to occur at the crack tip prior to formation of unstable oxides. To contrast with the threshold failure mode regime, a quantitative assessment of the role that the intergranular failure mode has on cyclic FCG behavior in the Paris regime was also performed. It was demonstrated that the even a very limited intergranular failure content dominates the FCG response under mixed mode failure conditions.

fatigue crack growth↗

Segregation-Assisted Plasticity in Ni-Based Superalloys

Correlative high resolution transmission electron microscopy and energy dispersive X-ray spectroscopy are used to study deformation-induced planar faults in the single crystal superalloy MD2 crept at 800°C and 650 MPa. Segregation of Cr and Co at microtwins, APBs, CISFs/SISFs and CESFs/SESFs is confirmed and quantified. The extent of this is found to depend upon the fault type, being most pronounced for the APB. The CESF/SESF is studied in detail due to its role as a precursor of the microtwins causing the majority of plasticity under these conditions. Quantitative modelling is carried out to rationalize the findings; the experimental results are consistent with a greater predicted velocity for the lengthening of the CESF/SESF { compared with the other types of fault { and hence confirm its role in the diffusion-assisted plasticity needed for the microtwinning mechanism to be operative.

Barba, D.↗

An Abrupt Transition to an Intergranular Failure Mode in the Near-Threshold Fatigue Crack Growth Regime in Ni-Based Superalloys

Cyclic near-threshold fatigue crack growth (FCG) behavior of two disk superalloys was evaluated and was shown to exhibit an unexpected sudden failure mode transition from a mostly transgranular failure mode at higher stress intensity factor ranges to an almost completely intergranular failure mode in the threshold regime. The change in failure modes was associated with a crossover of FCG resistance curves in which the conditions that produced higher FCG rates in the Paris regime resulted in lower FCG rates and increased Kth values in the threshold region. High-resolution scanning and transmission electron microscopy were used to carefully characterize the crack tips at these near-threshold conditions. Formation of stable Al-oxide followed by Cr-oxide and Ti-oxides was found to occur at the crack tip prior to formation of unstable oxides. To contrast with the threshold failure mode regime, a quantitative assessment of the role that the intergranular failure mode has on cyclic FCG behavior in the Paris regime was also performed. It was demonstrated that even a very limited intergranular failure content dominates the FCG response under mixed mode failure conditions.

Telesman, J.↗

Investigation of Stacking Fault and Antiphase Boundary Segregation in Ni-Based Superalloys Using Density Functional Theory

Ni-base superalloys have a long history of use in jet turbine engines, and efforts to improve their performance in that application are ongoing. It is known that the precipitation of the Ni3Al γ' phase within the disordered FCCγ phase strengthens the overall material. However, in the high-temperature environment found inside a turbine engine during operation, creep can cause the γ' phase to transform to different, weaker phases along stacking faults, leading to a deterioration of performance. In the γ' phase one mode of creep deformation is the formation of stacking fault ribbons, which consist of intrinsic stacking faults further shearing into antiphase boundaries (APBs). It is also known that certain alloying additions exhibit segregation to stacking faults. If segregating elements could be identified which segregate to the intrinsic stacking fault, but not to the APB, the inclusion of such elements could lead to improved creep strength in these alloys. To investigate this possibility, a density functional investigation of the segregation of W, Mo and Cr to both a superlattice intrinsic stacking fault (SISF) and an APB was performed. It was found that W, Mo and Cr all exhibit segregation to the SISF. In contrast, for the APB, Cr was either energy-neutral, or segregates, depending on the presence of additional nearby Cr, or on the specific lattice site upon which it was placed, while Mo and W did not segregate. Because W and Mo segregate to the SISF but not to the APB, the inclusion of these elements could provide a degree of protection against creep-related deterioration.

Good, Brian S.↗

Producing Next Generation Superalloys Through Advanced Characterization and Manufacturing Techniques

NASA is currently working towards developing the next generation high temperature alloys for various aerospace and energy applications. Through advanced microscopy and computational insights, a novel atomic scale strengthening mechanism was discovered in Ni-base superalloys. This new local phase transformation strengthening technique has been successfully implemented resulting in new disk alloys with substantial improvements in creep strength over current state-of-the-art. Furthermore, additive manufacturing has been leveraged to produce dispersion strengthened (DS), multi-principal element alloys (MPEA) without the use of traditional mechanical alloying or chemical reactions. This new processing technique has successfully resulted in 99.9% dense oxide dispersion strengthened NiCoCr alloy parts. High temperature mechanical testing of the DS alloys showed significant improvements in strength and ductility over the baseline NiCoCr. As a result, this recently discovered processing route opens a new alloy design and production path that is synergistic between additive manufacturing and dispersion strengthening, possibly enabling a new generation of high-performance alloys.

Smith, Timothy M.↗

Additive Manufacturing of Oxide Dispersion Strengthened (ODS) Nickel-Based Superalloys

Additive manufacturing of oxide dispersion strengthened (ODS) Ni-based superalloys, via powder bed techniques, could enable near-net-shape manufacturing of intricately shaped components for aerospace applications. This has the potential to transform the design and manufacturing of hot sections of engines which face demands for ever-rising operating temperatures. The goal of this project is to lay the scientific foundation for additive manufacturing of ODS alloys. The objective of this poster is to present work to date as well as proposed future work.

Wilson, Laura G.↗

Effect of Alloying Additions on Twinning in Ni-based Superalloys

Micro-twinning is the dominant creep deformation mechanism in Ni-based superalloys at temperatures above 700 °C. We use atomistic simulations to study two mechanisms of twin nucleation and growth that are characterized by qualitatively different rate limiting processes. In case of the mechanism proposed by Kolbe, the rate limiting process is diffusion-mediated atomic reshuffling. In case of the other mechanism, we proposed recently, the rate limiting process is nucleation of Shockley partial dislocation. We demonstrate the effects of alloying additions on functionality of these mechanisms.

Valery V Borovikov↗

Relationship Between Unusual High-Temperature Fatigue Crack Growth Threshold Behavior in Superalloys and Sudden Failure Mode Transitions

An investigation of high temperature cyclic fatigue crack growth (FCG) threshold behavior of two advanced nickel disk alloys was conducted. The focus of the study was the unusual crossover effect in the near-threshold region of these type of alloys where conditions which produce higher crack growth rates in the Paris regime, produce higher resistance to crack growth in the near threshold regime. It was shown that this crossover effect is associated with a sudden change in the fatigue failure mode from a predominant transgranular mode in the Paris regime to fully intergranular mode in the threshold fatigue crack growth region. This type of a sudden change in the fracture mechanisms has not been previously reported and is surprising considering that intergranular failure is typically associated with faster crack growth rates and not the slow FCG rates of the near-threshold regime. By characterizing this behavior as a function of test temperature, environment and cyclic frequency, it was determined that both the crossover effect and the onset of intergranular failure are caused by environmentally driven mechanisms which have not as yet been fully identified. A plausible explanation for the observed behavior is proposed.

Fatigue Crack Growth Thresholds; Grain boundary ox↗

Relationship Between Unusual High-Temperature Fatigue Crack Growth Threshold Behavior in Superalloys and Sudden Failure Mode Transitions

An investigation of high temperature cyclic fatigue crack growth (FCG) threshold behavior of two advanced nickel disk alloys was conducted. The focus of the study was the unusual crossover effect in the near-threshold region of these type of alloys where conditions which produce higher crack growth rates in the Paris regime, produce higher resistance to crack growth in the near threshold regime. It was shown that this crossover effect is associated with a sudden change in the fatigue failure mode from a predominant transgranular mode in the Paris regime to fully intergranular mode in the threshold fatigue crack growth region. This type of a sudden change in the fracture mechanisms has not been previously reported and is surprising considering that intergranular failure is typically associated with faster crack growth rates and not the slow FCG rates of the near-threshold regime. By characterizing this behavior as a function of test temperature, environment and cyclic frequency, it was determined that both the crossover effect and the onset of intergranular failure are caused by environmentally driven mechanisms which have not as yet been fully identified. A plausible explanation for the observed behavior is proposed.

Fatigue Crack Growth Thresholds; Grain boundary ox↗

Microstructural and Creep Properties of Boron- and Zirconium-Containing Cobalt-Based Superalloys

The effects of micro-additions of boron and zirconium on grain-boundary (GB) structure and strength inpolycrystalline γ(f.c.c.) plus γ’(L12) strengthened Co-9.5Al-7.5W-X at. % alloys (X=0-Ternary, 0.05B, 0.01B,0.05Zr, and 0.005B-0.05Zr at. %) are studied. Creep tests performed at 850 °C demonstrate that GB strength and cohesion limit the creep resistance and ductility of the ternary B- and Zr-free alloy due to intergranular fracture. Alloys with 0.05B and 0.005B-0.05Zr both exhibit improved creep strength due to enhanced GB cohesion,compared to the baseline ternary Co-9.5Al-7.5W alloy, but alloys containing 0.01B or 0.05Zr additions displayed no benefit. Atom-probe tomography (APT) is utilized to measure GB segregation, where B and Zr are demonstrated to segregate at GBs. A Gibbsian interfacial excess of 5.57 ± 1.04 atoms nm(exp) -2 was found for B at aGB in the 0.01B alloy and 2.88 ± 0.81 and 2.40 ± 0.84 atoms nm2 for B and Zr, respectively, for the 0.005B-0.05Zr alloy. The GBs in the highest B-containing (0.05B) alloy exhibit micrometer-sized boride precipitates with adjacent precipitate denuded-zones (PDZs), whereas secondary precipitation at the GBs is absent in theother four alloys. The 0.05B alloy has the smallest room temperature yield strength, by 6%, which is attributedto the PDZs, but it exhibits the largest increase in creep strength (with an ~2.5 order of magnitude decrease inthe minimum strain rate for a given stress at 850 °C) over the baseline Co-9.5Al-7.5W alloy.

Creep↗

Residual Stress Measurements of Ni-base Superalloys through Neutron Diffraction

Linear friction welding (LFW) is being considered for joining single crystal to polycrystalline nickel-base alloys for advanced high temperature gas turbine disks. Unfortunately, the transient thermal cycle during the welding generates undesirable residual stresses. Additionally, upon thermal treatment to relieve these residual stresses the weld joints often crack. To understand this issue, state-of-the-art neutron diffraction was performed near weld joints to quantify the residual stresses created by varying linear friction weld conditions. The residual stresses were measured along three orthogonal axes in both the polycrystalline LSHR and single crystal SC-180 alloys. Residual stress measurements using a contour method were used to compare the calculations obtained by neutron diffraction. The results suggest high residual stresses can be successfully reduced using both pre- and post-weld processing steps. Moreover, the effect of grain size and pre-heat temperatures on the LFW process were explored.

Superalloys↗

Effect of a Large Population of Seeded Alumina Inclusions on Crack Initiation and Small Crack Fatigue Crack Growth in Udimet 720 Nickel-Base Disk Superalloy

Crack initiation, crack coalescence and small crack growth behavior were monitored for over 400 seeded inclusions during interrupted low cycle fatigue testing conducted on the P/M Udimet 720 nickel disk alloy at 650°C. Two types of seeded alumina inclusions with average sizes of 54 μm and 122 μm were used in the study performed at varying loading conditions resulting in LCF lives ranging from 2,000 cycles to over 1,000,000 cycles. The fatigue behavior was sub-categorized into four groups. Visual maps detailing inclusion size/cycle history were developed. The effect of surface residual stresses on the fatigue life was also investigated.

Superalloys↗

Microstructural Evolution and Mechanical Properties of LP-DED NASA HR-1 – A Hydrogen Resistant AM Superalloy for Space Propulsion Applications

The National Aeronautics and Space Administration (NASA) has actively pursued metal additive manufacturing (AM) technologies for spaceflight applications since the late 2000s. AM offers transformative advantages in cost, schedule, part consolidation, and design flexibility. Among the various AM techniques, laser powder directed energy deposition (LP-DED) is particularly well suited for fabricating complex geometries with fine feature resolution. In propulsion systems that utilize high-pressure gaseous hydrogen—such as liquid hydrogen rocket engines—hydrogen environment embrittlement (HEE) presents a serious threat to material performance 1,2 . Mechanical property degradation under these conditions can compromise component reliability, especially under cyclic loading. To address this challenge, NASA developed NASA HR-1 (Hydrogen Resistant-1) as a solution for liquid rocket engine components operating in hydrogen-rich environments, using the LP-DED technique 3-9 . A key component in a liquid rocket engine is the exhaust nozzle, which is typically regeneratively cooled (regen) due to the high heat flux. NASA HR-1 was specifically developed for regen nozzle applications using hydrogen as a propellant, providing resistance to HEE, a critical issue for many materials. The AM version of NASA HR-1 was also formulated to achieve high ultimate tensile strength, along with high yield strength and ductility in this environment 5,6 . Low-cycle fatigue (LCF) is another important consideration in nozzle design, as components are expected to endure multiple starts and missions. Additionally, the LP-DED version of the alloy exhibits improved thermal conductivity compared to its wrought counterpart, which benefits nozzle cooling. Overall, NASA HR-1 offers an excellent balance of high strength, HEE resistance, LCF performance, thermal conductivity, and ductility to meet the demanding requirements of channel-cooled nozzles and other components used with hydrogen and other propellants. The LP-DED–processed NASA HR-1 requires several post-processing heat treatment steps to achieve the material properties desirable for its intended application 6 . These steps include stress relief, homogenization, solution annealing, and aging for precipitation hardening. The stress relief treatment mitigates residual stresses accumulated during the LP-DED process and minimizes the potential for distortion. Homogenization, a common step for AM materials, reduces elemental segregation and promotes recrystallization to develop a more equiaxed grain structure. The subsequent solution annealing treatment heats the part to a solid solution temperature to dissolve the undesirable η-phase that forms during cooling from homogenization, followed by rapid cooling to retain an η-phase–free microstructure. Finally, aging promotes precipitation of the strengthening γ′ phase in the alloy. The integration of compositional design and optimized thermal processing enables high-quality LP-DED NASA HR-1 components with excellent microstructural and mechanical stability. Improved chemical and microstructure homogeneity enhances ductility and fatigue resistance—both critical for safe and reliable operation in high-pressure hydrogen environments. NASA has successfully fabricated and hot-fire tested multiple subscale and full-scale channel wall nozzles using LP-DED NASA HR-1 5,6, 9-14 . These efforts included process refinements to support thin-wall construction and various channel geometries. Throughout development, several key observations emerged. After homogenization, the as-built columnar grain structure transforms into a fully equiaxed microstructure. However, subsequent treatments—such as solution annealing and aging—result in changes that are more difficult to track. The grain structure remains largely unchanged, and the γ′ precipitates, typically 5–10 nm in diameter, are beyond the resolution of scanning electron microscopy (SEM). While transmission electron microscopy (TEM) can resolve these fine precipitates, TEM sample preparation is time-consuming and difficult for LP-DED material. As an alternative, differential scanning calorimetry (DSC) offers a useful, qualitative approach to monitor precipitate evolution throughout different stages of heat treatment. The overall goal is to improve the understanding of how heat treatment affects the microstructure and mechanical performance of LP-DED NASA HR-1. This paper presents heat treatment design considerations, microstructural characterization, mechanical testing – including tensile and LCF testing in both air and hydrogen environments.

Superalloy↗