Cements are a critical component in well construction, as they act to prevent well fluid and gas escape, prevent corrosion of the casing, and strengthen the wellbore to prevent deformation. Under the high temperature/pressure conditions common in geothermal systems, the injection of cold water for energy production is expected to induce cyclic damage to the borehole cement through the rapid temperature fluctuations. These “thermal shocks” are expected to cause casing shrinkage, annulus formation, and cement tensile stresses. To understand the effect of cold water injection on the wellbore environment, a set of rock-cement-steel samples were created to simulate the structure of a geothermal well. Lightweight thermally-insulating cement blends were tested under thermal shock conditions in this study. In each test, the samples were pressurized to an effective pressure of ~3.5 MPa and placed at high temperatures. Thermal shocks were performed by injecting cold water (~10-15 °C) through the samples at a constant rate while keeping the samples at high temperatures until the sample temperature stopped decreasing and deformation ceased. Eight thermal shock tests were conducted with each sample – two at 100 °C and six at 200 °C. Post-tests analysis was then conducted by cutting open each sample to examine the damage in each component of the simulated wellbore. Experimental results suggest that all samples experienced similar degrees of axial and lateral contraction during cold water injection, but for the most part this contraction is recoverable when injection halts. Post-test analysis revealed that fly ash cenosphere pre-treatment had the best effect on improving thermal shock resistance in the cement blends. Thermomechanical modeling of likely stress paths experienced by the cements during heating/cooling cycles shows that elasto-plastic cement constitutive behavior results in most plastic strain occurring during the initial heating steps, with mostly elastic strain occurring during the thermal shock cycles. In conclusion, this agrees with experimental evidence, suggesting that cement damage from shocking occurs via other mechanisms such as chemical alteration, corrosion, and fatigue.