DOE OSTI2019

Effect of Nb Content on Microstructures and Mechanical Properties of Ti-xNb-2Fe Alloys

β-Type Ti-Nb-based alloys exhibit satisfactory biocompatibility and low Young’s modulus for biomedical applications. The microstructure and mechanical properties of a series of Ti-(14, 16, 18, 20, 22, 24)Nb-2Fe alloys fabricated by arc melting were investigated by XRD, optical microscopy, and tensile tests. Both ω and α″ phases existed in the Ti-14Nb-2Fe alloy, while just a single β phase existed in the other alloys. Twinning is an important deformation mechanism that causes work hardening and twinning-induced plasticity. It was found in the Ti-(14, 16, 18, 20)Nb-2Fe alloys and not in the Ti-22Nb-2Fe alloy. The Ti-14Nb-2Fe alloy exhibited the highest tensile strength and the highest Young’s modulus owing to the existence of the ω phase. The tensile strength decreased gradually from 830 MPa (highest) for the Ti-14Nb-2Fe alloy to 540 MPa (lowest) for the Ti-24Nb-2Fe alloy with an increase in the Nb content. The Young’s modulus decreased from 90 GPa for the Ti-14Nb-2Fe alloy to 63 GPa for the Ti-22Nb-2Fe alloy and then increased to 71 GPa for the Ti-24Nb-2Fe alloy. Elongation shows the same trend as the Young’s modulus. The Ti-22Nb-2Fe alloy, with a low Young’s modulus of 63 GPa, tensile strength of 570 MPa, and 15% elongation, was found suitable for biomedical applications. The Ti-20Nb-2Fe alloy also exhibits a high tensile strength, a Young’s modulus ratio of 9.24 × 10{sup −3}, and 18% elongation and is thus considered another valuable Ti alloy for biomedical applications.

36 MATERIALS SCIENCE↗
NASA NTRS1998

Surface Chemistry, Microstructure, and Tribological Properties of Cubic Boron Nitride Films

This report deals with the surface chemistry, microstructure, bonding state, morphology, and friction and wear properties of cubic boron nitride (c-BN) films that were synthesized by magnetically enhanced plasma ion plating. Several analytical techniques - x-ray photoelectron spectroscopy, transmission electron microscopy and electron diffraction, Fourier transform infrared spectroscopy, atomic force microscopy, and surface profilometry - were used to characterize the films. Sliding friction experiments using a ball-on-disk configuration were conducted for the c-BN films in sliding contact with 440C stainless-steel balls at room temperature in ultrahigh vacuum (pressure, 10(exp -6), in ambient air, and under water lubrication. Results indicate that the boron-to-nitrogen ratio on the surface of the as-deposited c-BN film is greater than 1 and that not all the boron is present as boron nitride but a small percentage is present as an oxide. Both in air and under water lubrication, the c-BN film in sliding contact with steel showed a low wear rate, whereas a high wear rate was observed in vacuum. In air and under water lubrication, c-BN exhibited wear resistance superior to that of amorphous boron nitride, titanium nitride, and titanium carbide.

Watanabe, Shuichi↗
DOE OSTI2024

Effect of Heat Treatment on Microstructure and Mechanical Property of 316L Stainless Steel Produced by Laser Powder Bed Fusion

The advanced non-light water reactor designs (Gen IV reactors), including molten salt/ very high temperature/ sodium-cooled and lead-cooled fast reactors, typically operate at higher temperatures and more extreme radiation conditions than light water reactors. An intrinsic part of the deployment and progress of Gen IV reactor designs is selecting the most suitable structural material for a specific application. Additive manufacturing (AM), a fairly new process of making physical, three-dimensional objects from a computer design file, is going to completely change the way of design, build and certify nuclear systems. It offers a range of opportunities to produce complex geometries from existing materials, offers new routes for processing of previously difficult to process materials, allows for design of new high-performance materials, and finally facilitates hybridization of dissimilar materials. This emerging technology has successfully produced cars, wind turbine blade molds and even live cells. It could also open up big opportunities for the nuclear industry to quickly deploy technologies at a fraction of the cost. So far, AM techniques have been preliminarily applied in the field of nuclear reactors, including the classical parts such as the pressure vessel of a small reactor with 508-III steel, the bottom nozzle of a fuel assembly with 304L steel, the fuel cladding with zirconium alloy and the integrated impeller of a pump and the multi-channel valve body with 316L steel [6,7]. The AM applications for operating nuclear reactors started in auxiliary plant components and have slowly migrated to metallic reactors and core components, but many of these are not safety critical components. Although many parts used for nuclear reactors have been fabricated by AM techniques, practical applications in engineering are still a long way off due to the uncertainty factors focused on the processing, material properties, analysis methods and application standards, which feeds the safety and life-cycle of the nuclear reactor. Due to rapid, repeated heating and cooling during production, a high dislocation density was present in the AM material. This microstructure feature is unstable at elevated temperature while high temperature is one of the typical operation environments for nuclear reactors. Thus, it is important to understand the thermal effect on the microstructure of AM material. The objectives of this study are to investigate the effect of heat treatment on the microstructure and mechanical properties of 316L stainless steel produced by laser powder bed fusion additive manufacturing, and to determine an appropriate heat treatment practice that will be applied to the lightweight AM lattice-structured material with the same chemistry. The heat treatment study consisted of annealing the samples at a temperature range of 800 to 1200 oC with a 50 oC increment for different times (1-24 hours), followed by vacuum or air cooling. Microstructural characterization was carried out by Scanning Electron Microscope (SEM). Grain size and crystallographic orientation were investigated by Electron Backscatter Diffraction (EBSD). Vickers hardness tests with a 0.5 kg load were employed to determine the hardness of samples after different heat treatments. After heat treatment, the random crystallographic orientation was preserved, and the volume fraction of high-angle grain boundaries (grain boundary misorientation =15 oC) remained the same. The dislocation density decreased with annealing temperature due to recovery. The fine subgrain structures in the as-printed specimen were quite stable up to 1200 oC. Minimal recrystallization was observed up to 1200 oC. Recrystallization initiated only after 8.5 hours at 1200 oC. The SEM images did not show obvious dependence of microstructure on cooling rate. The hardness of the specimens decreased with increasing annealing temperature as a result of the decrease in dislocation density. It is interesting to note that the AM material showed very similar hardness to the wrought material when annealing at similar temperature, although the microstructures are very different. Annealing at 1050 oC for 1 hour followed by air cooling was selected as the heat treatment procedure for the lattice designed lightweight AM 316L material.

36 MATERIALS SCIENCE↗
DOE OSTI2019

Microstructure and Mechanical Properties of a SiO{sub 2} Ceramic and TC4 Alloy Joint Brazed with a Nanocomposite Filler

Vacuum brazing of TC4 alloy and SiO{sub 2} ceramic was achieved using a nano-AgCuNi braze alloy. The melting temperature of nano-AgCu powders was analyzed by differential scanning calorimeter. Furthermore, the effects of the Ni content on the microstructure and mechanical properties of the joints were studied. The results showed that the melting temperature of the nano-AgCu filler was 774 °C. A decrease in the melting temperature of 6 °C was observed, compared with the general AgCu filler, and this decrease enabled the interfacial reaction of the joint to begin earlier. The typical interfacial microstructure of the TC4/nano-AgCuNi/SiO{sub 2} ceramic joint brazed at 950 °C for 10 min was TC4/α-Ti + Ti{sub 2}(Cu,Ni) + Ti{sub 2}(Ni,Cu) hypereutectoid structure/Ti{sub 2}(Cu,Ni) compound with α-Ti + Ti{sub 2}(Cu,Ni) + Ti{sub 2}(Ni,Cu) hypereutectic structure/Ti{sub 4}O{sub 7} + TiSi{sub 2}/SiO{sub 2} ceramics. The homogeneous microstructure of α-Ti + Ti{sub 2}(Cu,Ni) + Ti{sub 2}(Ni,Cu) hypereutectoid structure primarily existed in the diffusion layer. Additionally, the refined α-Ti + Ti{sub 2}(Cu,Ni) + Ti{sub 2}(Ni,Cu) hypereutectic structure created via a eutectic reaction and Ti{sub 2}(Cu,Ni) compound was distributed in the brazing seam. The Ni content could influence the formation of Ti-Cu-Ni ternary intermetallic compounds (IMCs). An increase in Ni led to an increase in the α-Ti + Ti{sub 2}(Cu,Ni) + Ti{sub 2}(Ni,Cu) hypereutectic structure in the brazing seam. The shear strength of the brazed joints first increased and then decreased with the increase in the nano-Ni content, and the optimal shear strength of 30.1 MPa was achieved at 10 wt.% Ni. The increase in the α-Ti + Ti{sub 2}(Cu,Ni) + Ti{sub 2}(Ni,Cu) hypereutectic structure and the decrease in brittle compounds enhanced the shear strength of the joint. Fracture analysis of the joints brazed at 950 °C for 10 min indicated that the cracks mainly occurred in SiO{sub 2} ceramic.

36 MATERIALS SCIENCE↗
DOE OSTI2022

Friction stir welding and self-ion irradiation effects on microstructure and mechanical properties changes within oxide dispersion strengthened steel $\mathrm{MA956}$

We report the joining process for oxide dispersion strengthened (ODS) alloys remains a key challenge facing the nuclear community. The microstructure and mechanical properties were characterized in the base material and friction stir welded ODS MA956 irradiated with 5 MeV Fe 2+ ions from 400 to 500°C up to 25 dpa. Nanoindentation was performed to assess changes in hardness and yield stress, and the dispersed barrier hardening (DBH) model was applied to described results. A combination of scanning transmission electron microscopy (STEM) and atom probe tomography (APT) were used to assess evolution of the microstructure including dispersoids, network dislocations and dislocation loops, nanoclusters, and solid solution concentrations. Overall, softening was observed as a result of increased dose, which was exacerbated at 500°C. The formation and coarsening of new dispersoids was noted while nanoclusters tended to dissolve in the base material, and were not observed in the stir zone. Solute nanocluster evolution was identified as a primary driver of the changes in mechanical properties.

36 MATERIALS SCIENCE↗
DOE OSTI2018

Effects of Chromium Additions upon Microstructure and Mechanical Properties of Cold Drawn Pearlitic Steel Wires

Cr-containing pearlitic steel wires were prepared through cold drawing and simulated galvanization process. Effect of chromium microalloying on microstructural and mechanical properties of the steel wires was investigated. Experimental results show that size of pearlitic colonies of the steel rods decreased as Cr content increased from 0.2 to 0.6 wt.%; meanwhile, interlamellar spacing was little affected because of isothermal phase transition in salt bath. The tensile strength of the pearlitic steel rods was increased from 1480 to 1550 MPa. The tensile strength of the Cr-containing cold drawn wires (ε = 1.58) was increased about 33%, and the torsion circle of the wires were about 15 with cleavage fracture. After annealing at 450 °C for 2 min, tensile strength of the wires increased, but torsion circle was decreased to less than 5. As the annealing time increased, the torsion circle of the steel wires with 0.2 wt.% Cr was improved to about 10 with cleavage fracture, while the torsion performance of the wires having high Cr contents remained low because of delamination fracture. The cementite platelets in Cr-containing wires turned into cementite crystal particles during cold drawing. Microstructure observation and thermal analysis have confirmed that thermal stability of cementite was enhanced with the increase of Cr content.

36 MATERIALS SCIENCE↗
NASA NTRS1991

The effect of copper, chromium, and zirconium on the microstructure and mechanical properties of Al-Zn-Mg-Cu alloys

The present study evaluates the effect of the systematic variation of copper, chromium, and zirconium contents on the microstructure and mechanical properties of a 7000-type aluminum alloy. Fracture toughness and tensile properties are evaluated for each alloy in both the peak aging, T8, and the overaging, T73, conditions. Results show that dimpled rupture essentially characterize the fracture process in these alloys. In the T8 condition, a significant loss of toughness is observed for alloys containing 2.5 pct Cu due to the increase in the quantity of Al-Cu-Mg-rich S-phase particles. An examination of T8 alloys at constant Cu levels shows that Zr-bearing alloys exhibit higher strength and toughness than the Cr-bearing alloys. In the T73 condition, Cr-bearing alloys are inherently tougher than Zr-bearing alloys. A void nucleation and growth mechanism accounts for the loss of toughness in these alloys with increasing copper content.

Wagner, John A.↗
DOE OSTI2018

Microstructure and Mechanical Properties of a Ag Micro-Alloyed Mg-5Sn Alloy

Effects of 1.5 wt.% Ag addition and solid solution + artificial ageing at 160 °C on the microstructure and mechanical properties of a Mg-5Sn alloy have been studied. The results show that Ag addition has significantly hardened the solution-treated Mg-5Sn alloy. During the ageing process, the hardness increase rate and the strength and ductility of the Mg-5Sn alloy at each state are also improved by Ag addition. The improved strengthening behavior is primarily attributed to the refinement distribution of the Mg{sub 2}Sn precipitates, the enhanced precipitation process, and the synergistic strengthening effect of Mg{sub 2}Sn and a metastable plate DO{sub 19} phase formed at lower ageing temperature. For each solution-treated alloy, the strength and ductility are higher than the corresponding cast ones. Ageing further enhances the yield strength, and the ductility of the Mg-5Sn-1.5Ag alloy is also increased after ageing. The fracture surfaces of the both peak-aged alloys exhibit the characteristic of a mixture of quasi-cleavage and ductile fracture.

36 MATERIALS SCIENCE↗
DOE OSTI2019

Investigation on Microstructure and Mechanical Properties of TA10–Q245R Composite Plate Formed by Explosive Welding

The titanium alloy TA10 and the carbon steel Q245R are welded by explosive welding, and post-weld heat treatment (PWHT) is carried out for the TA10–Q245R composite plate. Microstructure and mechanical properties of the composite plate are investigated both in as-welded (AW) condition and after PWHT, respectively. Results show that, in AW condition, the bonding interface of composite plate presents wavy morphology, and at both sides of the interface plastic deformation is generated to a certain degree. Near the interface interdiffusion zone of alloying elements exists, and no Fe-Ti intermetallic compound is produced at the interface. SEM images indicate that the tensile fracture of composite plate presents the characteristic of ductile fracture, and no defects such as gas pores or impurities are found on the surface of shear fracture. After PWHT, the interfacial microstructure of the composite plate is obviously changed. Compared with the mechanical properties of the composite plate in AW condition, both tensile strength and shear strength of the composite plate are decreased to a certain extent after PWHT. With various factors into consideration, the suitable heat treatment procedure of TA10–Q245R composite plate is determined as follows: 550 °C × 1.5 h.

36 MATERIALS SCIENCE↗
DOE OSTI2018

Microstructure and mechanical properties development of micro channel tubes in extrusion, rolling and brazing

Highlights: • Rolling and brazing greatly affect the properties of micro-channel tubes (MCTs). • The properties of MCTs are investigated by the evolution of the microstructure. • Strength is decreased by 47% at 5%-rolling reduction ratio and 3-minute brazing. • Ductile fracture mode is observed by OM at failure of MCTs under inner pressure. - Abstract: In addition to extrusion, the post-processing of rolling and brazing has significant effect on the mechanical properties of multi-port tubes. The aluminum micro channel tubes, especially the seam welding zone in the internal webs, are investigated in terms of mechanical tests, microstructure characterization, and finite element analysis. The effect of the post-process of rolling are quantified by varying amount of rolling reduction ratios. Tensile strength and pressure bearing capacity are determined by tensile tests and burst pressure tests, respectively. The evolution of the microstructure within the seam wielding zone is characterized by Electron backscattered diffraction (EBSD) and optical microscopy (OM). The fracture profile observed by OM indicates ductile fracture mode. The pressure bearing capacity is reduced by ~47% at 5% reduction ratio of rolling followed by 3-minute brazing, where largest grains are obtained due to abnormal grain growth.

36 MATERIALS SCIENCE↗
DOE OSTI2024

Review of Solid State Consolidation Processing Techniques of ODS Steels (Hot Extrusion, Hot Isostatic Pressing, Spark Plasma Sintering, and Stir Friction Consolidation): Resulting Microstructures and Mechanical Properties

This paper reviews the solid-state consolidation processing techniques for Oxide Dispersion Strengthened steels and compares them in terms of the resulting microstructure and reported mechanical properties. Synthesis techniques include hot extrusion, hot isostatic pressing, spark plasma sintering and friction consolidation. The effects of process parameters on the resulting microstructures and performance are discussed for each technique. Average oxide size, average grain size, and porosity are compared across techniques, as well as mechanical strength and ductility. Across consolidation techniques where temperature can be controlled, a low sintering temperature with a high sintering pressure is favorable for keeping oxide sizes, grain sizes, and porosity low. The use of yttrium and titanium for oxide formation has been evidenced to reduce oxide sizes, and tungsten additions have been shown to improve strength. Current literature suggests that the more mature hot extrusion technique produces stronger steel with consistently fine oxides, while other alternative solid-state consolidation, while promising, offer margin for improvement.

36 MATERIALS SCIENCE↗
DOE OSTI2018

Grain Refinement, Microstructure and Mechanical Properties Homogeneity of Mg-Gd-Y-Nd-Zr Alloy During Multidirectional Forging

Multidirectional forging (MDF) of Mg-Gd-Y-Nd-Zr alloy was performed under decreasing temperature condition. The grain refinement, microstructure and mechanical properties homogeneity of Mg-Gd-Y-Nd-Zr alloy during MDF process were investigated. The results show that the grain refinement mechanism of Mg-Gd-Y-Nd-Zr alloy during MDF process was dynamic recrystallization. The dynamic precipitations were observed after MDF process, which were mainly located at the grain boundaries and had a significant influence on the grain refinement, and the amount of dynamic precipitations increased as the MDF passes increase. The microstructure of the billet was not homogeneous due to the deformation and temperature inhomogeneity during MDF process. Optimization MDF process has been proposed, which benefited the microstructure homogeneity and reduced the amount of the dynamic precipitations. Based on the optimization MDF process, the elongation to fracture significantly increased.

36 MATERIALS SCIENCE↗
DOE OSTI2018

Microstructure and Mechanical Properties of Cast Al-5Zn-2Mg Alloy Subjected to Equal-Channel Angular Pressing

In the present work, cast Al-5Zn-2Mg alloy was processed through equal-channel angular pressing (ECAP) in route B{sub C} up to four number of passes. Microstructure and mechanical properties were investigated on processed and unprocessed materials. In cast condition, the material was composed of dendritic structure. After homogenization treatment, large-sized grains were observed. After ECAP processing, significant grain refinement was observed. After ECAP processing, high-density dislocations and high degree of misorientation between the grains were observed. In cast material, rod-shaped precipitates were observed, while, after ECAP processing, spherical-shaped precipitates were observed. ECAP processing leads to a noticeable improvement in the mechanical properties of the material. After four passes, 122% improvement in the microhardness and 135% improvement in the ultimate tensile strength of the material were observed. After three passes, a slight decrease in the mechanical properties was observed. This is attributed to the dissolution of the metastable η′ phase, annihilation of dislocations, dynamic recrystallization and texturing during ECAP processing. Brittle fracture mode was observed in tensile testing cast and homogenized samples. After ECAP processing, fracture mode was changed into shear fracture mode.

36 MATERIALS SCIENCE↗
DOE OSTI2018

Microstructure and Mechanical Properties of Rapidly Cooled Friction Stir Welded Ti-6Al-4V Alloys

Two mm-thick Ti-6Al-4V alloy plates were friction stir butt welded under natural- and rapid-cooling conditions. The microstructures and mechanical properties of joints were investigated and compared. The rapid cooling via spraying cooling liquid nitrogen on the plate top surface was beneficial to obtaining a narrower cross section and finer and more uniform grains in the stir zone than those obtained by natural cooling. Joint tensile strength of 1021 MPa and elongation of 1.88% under the rapid-cooling condition respectively reached 102.7 and 150.4% of those under the natural-cooling condition, respectively. The uniform-and-compact equiaxed grains led to equiaxed dimples on the fracture surface, which demonstrated a ductile fracture of the welding joints.

36 MATERIALS SCIENCE↗
DOE OSTI2019

Influence of FSW Repairing Process on the Microstructures and Mechanical Properties of Friction Stir-Welded 6082Al Alloy

When two 42-mm 6082Al plates were welded by friction stir welding (FSW), a discontinuously distributing groove defect is formed on the surface of the joint. Subsequently, the FSW repairing process was conducted at the defect location. The influence of the repairing process on the microstructures and mechanical properties of the joints were studied, and a description of the softening mechanism of the repaired joints is provided. The results show that TMAZ at the advance side is the weakest zone of the as-welded joints. The repairing process increases the heat input into the joints and thus promotes the coarsening and transformation of the precipitates in the joints, which further weakens the repaired joints. The average tensile strength of the joints repaired with a 24-mm pin is 205 MPa, which is 91% of that of the as-welded joint. The tensile strength generally increases when the size of the repaired pin decreases. The average tensile strength of the joints repaired with an 8-mm pin is 220 MPa, which is equivalent to the initial joints.

36 MATERIALS SCIENCE↗
DOE OSTI2022

Dynamic Data-Driven Multiscale Modeling for Predicting Microstructure and Mechanical Properties of 316L Stainless Steel

We have developed a long short-term memory stacked ensemble (LSTM-SE) surrogate modeling approach that can provide rapid predictions of microstructural evolution and the resultant mechanical properties of American Iron and Steel Institute (AISI) 316L series stainless steel (316LSS) fuel cladding under conditions of varying temperature and radiation dose rate. To acquire training data, we developed and implemented a kinetic Monte Carlo (KMC) model to simulate precipitation kinetics of M 23 C 6 , γ', and G phases within SS316L cladding. Experimentally reported precipitation kinetics of SS316L in literature were linked to the kinetic parameters of the simulated precipitation in our KMC model. The model was then used to simulate microstructure evolution under synthetically generated treatments of varying temperature and radiation dose rate, for periods of up to 3000 hours. Changes in volume fraction, number density, and particle size of precipitates were recorded, and particle area fractions were correlated using statistical methods to develop the surrogate model. Simultaneously, the mechanical properties of the simulated microstructures were evaluated using microstructure-based finite element method (FEM) analysis to determine the elastic modulus, yield stress, ultimate tensile strength, and elongation to failure of the aged microstructures. Using this approach, our surrogate model can predict precipitation behavior within 0.25% volume fraction and mechanical properties within 6% relative error from the values predicted by the KMC and FEM models using 50 training simulations as input. The trained recurrent neural network-based model can return estimations of precipitation kinetics and mechanical properties ~1000 times faster than the physics-based codes. This work demonstrates, as a proof of concept, that reactor material service lifetimes under variable service conditions can be predicted for a statistics-based model from a practicably obtainable dataset.

36 MATERIALS SCIENCE↗
DOE OSTI2018

Microstructure and Mechanical Properties of Al-Mg-Sc-Zr Alloy Variable Polarity Plasma Arc Welding Joint

Al-Mg-Sc-Zr alloy plates were welded by variable polarity plasma arc welding (VPPAW) with Sc-containing filler wire. The microstructure and mechanical properties were investigated. Results show that the weld zone and heat-affected zone (HAZ) are narrow due to the high concentrated heat input of VPPAW. Primary Al{sub 3}(Sc,Zr) particles are nice nucleating sites for α-Al, which can significantly refine the grains of α-Al, helping the weld zone maintain an outstanding strength. The unmelted Al{sub 3}(Sc,Zr) precipitates of the base metal aggregated near the fusion boundary result in the formation of a fine equiaxed grains zone, which improves the bonding degree between the weld zone and the base metal. The Al{sub 3}(Sc,Zr) precipitates in the HAZ have excellent inhibition effect on recrystallization. According to the observed microhardness distribution and microstructure characteristics, the microstructure model of welded joint is obtained. The fractured position of welded joint locates in the weld zone. The tensile strength of the welded joint without reinforcing rib is 330 MPa. The welding coefficient reaches 74%.

36 MATERIALS SCIENCE↗
DOE OSTI2018

Microstructure and Electromagnetic Shielding Properties of Mg-Zn-Ce-Y-Zr Alloys

Microstructure and electromagnetic interference shielding properties of extruded Mg-Zn-Ce-Y-Zr alloys were systematically investigated. A bimodal grain structure of fine recrystallized grains and deformed grains was observed in the alloys. Yttrium (Y) and cerium (Ce) refined the recrystallized grains. Mg-Zn-Ce phase, Mg{sub 3}Zn{sub 3}Y{sub 2} phase and a few precipitates containing Zn and Zr were observed. Y and Ce additions changed the texture of the alloys. When the total rare earth content reached 4 wt.%, the texture was remarkably weaker than other studied alloys. The shielding capacity increased first and then decreased with Y contents. The value of shielding effectiveness for the extruded Mg-5Zn-1Ce-2Y-0.6Zr alloys reached 79-118 dB in the frequency range of 30 MHz-1.5 GHz, which was significantly higher than that of some aluminum alloys. The addition of Y and Ce is effective in improving the shielding capacity in Mg alloys. The electrical conductivity and second phases in the alloys were important in enhancing shielding effectiveness. The texture and precipitation exerted significant effect on electrical conductivity. In addition, subsequently aging treatment evidently improved shielding effectiveness.

36 MATERIALS SCIENCE↗