Probing the surface chemistry for reverse water gas shift reaction on Pt(1 1 1) using ambient pressure X-ray photoelectron spectroscopy
Using ambient pressure XPS (APXPS), we explored carbon dioxide (CO 2 ) adsorption and CO 2 hydrogenation on Pt(1 1 1) single crystal surface to observe the activation of CO 2 and the subsequent reaction mechanism. In pure CO 2 , we observed CO adsorbates and adsorbed oxygen on Pt(1 1 1) derived from CO 2 dissociation at room temperature. The introduction of H 2 (at a pressure ratio of 1:1 (H 2 :CO 2 )) increased the production of CO across all temperatures by facilitating the removal of surface oxygen. As a consequence, the surface could expose sites that could then be utilized for producing CO. Under these conditions, the reverse water–gas shift (RWGS) reaction was observed starting at 300 °C. At higher H 2 partial pressure (10:1 (H 2 :CO 2 )), the RWGS reaction initiated at a lower temperature of 200 °C and continued to enhance the conversion of CO 2 with increasing temperatures. Our results revealed that CO 2 was activated on a clean Pt(1 1 1) surface through the dissociation mechanism to form adsorbed CO and O at room temperature and at elevated temperatures. Introducing H 2 facilitated the RWGS as adsorbed oxygen was consumed continuously to form H 2 O, and adsorbed CO desorbed from the surface at elevated temperatures. This work clearly provides direct experimental evidence for the surface chemistry of CO 2 dissociation and demonstrates how hydrogen impacts the RWGS reaction on a platinum surface.